CN106723941A - A kind of abrasion resistant fibrous floor-cleaning machine disc brush silk - Google Patents
A kind of abrasion resistant fibrous floor-cleaning machine disc brush silk Download PDFInfo
- Publication number
- CN106723941A CN106723941A CN201611120744.2A CN201611120744A CN106723941A CN 106723941 A CN106723941 A CN 106723941A CN 201611120744 A CN201611120744 A CN 201611120744A CN 106723941 A CN106723941 A CN 106723941A
- Authority
- CN
- China
- Prior art keywords
- wear
- parts
- resisting
- silk core
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of abrasion resistant fibrous floor-cleaning machine disc brush silk, the disc brush silk includes the wear-resisting silk core of multi beam and the fiber sheath being wrapped on wear-resisting silk core outer surface；The wear-resisting silk core is made up of at least two abrasive filaments or polyamide monofilament；The fiber sheath can be single or multiple lift.Compared with prior art, the present invention is using using abrasive filaments or polyamide monofilament as grinding silk core, fiber sheath is wound with the outer surface of wear-resisting silk core, the brush wire bundle so that fiber surface and wear-resisting silk core are fitted completely, the present invention improves the hardness and grinding intensity and cleaning capacity of wear-resisting silk core, because wear-resisting silk core is fettered by fiber sheath, when stress after being made floor-cleaning machine disc brush, energy resistance to compression keeps wire body hardness, and the multiply abrasive filaments or polyamide monofilament of wear-resisting silk core are used as individual combination, increase grinding, polishing and cleaning area, anti-leak-stopping brush.
Description
Technical field
The present invention relates to brush filament preparing technical field, and in particular to a kind of abrasion resistant fibrous floor-cleaning machine disc brush silk.
Background technology
Brush filament is widely used in the multiple fields such as product packaging, communications and transportation, industrial and agricultural production.Brush filament is in use
Wearability be itself performance important indicator.Existing floor-cleaning machine brush filament due to being all that spinning is formed, its diameter be all by
Extruder die panel aperture determines, causes what silk toughness from the beginning to the end and bending strength and polishing dynamics were just as.It is existing
The wear-resisting silk core having is fettered by fiber sheath, and resistance to compression is unable to when being made stress after floor-cleaning machine disc brush and wire body hardness is kept, while
Grinding, polishing and cleaning area are smaller when using, and the possibility for leaking brush is larger.
The content of the invention
The present invention is intended to provide a kind of abrasion resistant fibrous floor-cleaning machine disc brush silk.
The present invention provides following technical scheme：
A kind of abrasion resistant fibrous floor-cleaning machine disc brush silk, it is characterised in that the disc brush silk includes the wear-resisting silk core of multi beam and winding
Fiber sheath on wear-resisting silk core outer surface；The wear-resisting silk core is made up of at least two abrasive filaments or polyamide monofilament；Institute
It can be single or multiple lift to state fiber sheath.
The fiber sheath is that the material of fiber yarn is a kind of Fypro, polyester fiber or polyolefine fiber etc.,
Or the mixture of the polyolefine fiber such as Fypro or polyester fiber etc. is entwined in wear-resisting silk core outer surface.
The diameter of the industrial brush filament of the wear-resisting silk core of multiply and the fiber sheath composition being wrapped on wear-resisting silk outer surface
Scope is in 2mm~10mm.
The combination of the wear-resisting silk core and fiber sheath can be bonded using adhesive, also can using heating fiber sheath with
The mode that wear-resisting silk core is bonded.
The adhesive is made up of the raw material of following parts by weight：Polyester resin A20-40 parts, polyester resin B10-30 parts,
Curing agent 3-12 parts, mixed solvent 12-36 parts, 12-25 parts of polyethylene wax powder dispersion, dibutyl phthalate 0.9-1.1
Part, neoprene 48-52 parts, stearic acid 0.4-0.6 parts, tetramethylthiuram disulfide 0.05-0.07 parts.
Compared with prior art, the beneficial effects of the invention are as follows：The present invention using using abrasive filaments or polyamide monofilament as
Grinding silk core, fiber sheath is wound with the outer surface of wear-resisting silk core so that fiber surface and wear-resisting silk core are fitted brush filament completely
Beam, the present invention improves the hardness and grinding intensity and cleaning capacity of wear-resisting silk core, because wear-resisting silk core is fettered by fiber sheath, when
When being made stress after floor-cleaning machine disc brush can resistance to compression keep wire body hardness, and the multiply abrasive filaments of wear-resisting silk core or polyamide monofilament are made
It is individual combination, increases grinding, polishing and cleaning area, anti-leak-stopping brush.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
A kind of abrasion resistant fibrous floor-cleaning machine disc brush silk of embodiment 1, the disc brush silk includes the wear-resisting silk core of multi beam and is wrapped in resistance to
Fiber sheath on mill silk core outer surface；The wear-resisting silk core is made up of at least two abrasive filaments or polyamide monofilament；The fibre
Dimension table layer can be single or multiple lift.
The fiber sheath is that the material of fiber yarn is a kind of Fypro, polyester fiber or polyolefine fiber etc.,
Or the mixture of the polyolefine fiber such as Fypro or polyester fiber etc. is entwined in wear-resisting silk core outer surface.
The diameter of the industrial brush filament of the wear-resisting silk core of multiply and the fiber sheath composition being wrapped on wear-resisting silk outer surface
Scope is in 2mm~10mm.
The combination of the wear-resisting silk core and fiber sheath can be bonded using adhesive, also can using heating fiber sheath with
The mode that wear-resisting silk core is bonded.
The adhesive is made up of the raw material of following parts by weight：Polyester resin A30 parts, polyester resin B20 parts, curing agent
9 parts, it is 24 parts of mixed solvent, 20 parts of polyethylene wax powder dispersion, 1.0 parts of dibutyl phthalate, 50 parts of neoprene, stearic
Sour 0.5 part, 0.06 part of tetramethylthiuram disulfide.
A kind of abrasion resistant fibrous floor-cleaning machine disc brush silk of embodiment 2, the disc brush silk includes the wear-resisting silk core of multi beam and is wrapped in resistance to
Fiber sheath on mill silk core outer surface；The wear-resisting silk core is made up of at least two abrasive filaments or polyamide monofilament；The fibre
Dimension table layer can be single or multiple lift.
The fiber sheath is that the material of fiber yarn is a kind of Fypro, polyester fiber or polyolefine fiber etc.,
Or the mixture of the polyolefine fiber such as Fypro or polyester fiber etc. is entwined in wear-resisting silk core outer surface.
The diameter of the industrial brush filament of the wear-resisting silk core of multiply and the fiber sheath composition being wrapped on wear-resisting silk outer surface
Scope is in 2mm~10mm.
The combination of the wear-resisting silk core and fiber sheath can be bonded using adhesive, also can using heating fiber sheath with
The mode that wear-resisting silk core is bonded.
The adhesive is made up of the raw material of following parts by weight：Polyester resin A20 parts, polyester resin B10 parts, curing agent
3 parts, it is 12 parts of mixed solvent, 12 parts of polyethylene wax powder dispersion, 0.9 part of dibutyl phthalate, 48 parts of neoprene, stearic
Sour 0.4 part, 0.05 part of tetramethylthiuram disulfide.
A kind of abrasion resistant fibrous floor-cleaning machine disc brush silk of embodiment 3, the disc brush silk includes the wear-resisting silk core of multi beam and is wrapped in resistance to
Fiber sheath on mill silk core outer surface；The wear-resisting silk core is made up of at least two abrasive filaments or polyamide monofilament；The fibre
Dimension table layer can be single or multiple lift.
The fiber sheath is that the material of fiber yarn is a kind of Fypro, polyester fiber or polyolefine fiber etc.,
Or the mixture of the polyolefine fiber such as Fypro or polyester fiber etc. is entwined in wear-resisting silk core outer surface.
The diameter of the industrial brush filament of the wear-resisting silk core of multiply and the fiber sheath composition being wrapped on wear-resisting silk outer surface
Scope is in 2mm~10mm.
The combination of the wear-resisting silk core and fiber sheath can be bonded using adhesive, also can using heating fiber sheath with
The mode that wear-resisting silk core is bonded.
The adhesive is made up of the raw material of following parts by weight：Polyester resin A20-40 parts, polyester resin B30 parts, it is solid
12 parts of agent, 36 parts of mixed solvent, 25 parts of polyethylene wax powder dispersion, 1.1 parts of dibutyl phthalate, neoprene 52
Part, 0.6 part of stearic acid, 0.07 part of tetramethylthiuram disulfide.
It is obvious to a person skilled in the art that the invention is not restricted to the details of the one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be in other specific forms realized.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires to be limited rather than the explanation, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each
Implementation method only includes an independent technical scheme, and this narrating mode of specification is only this area for clarity
Specification an as entirety, the technical scheme in each embodiment should can also be formed this by technical staff through appropriately combined
Art personnel may be appreciated other embodiment.
Claims (5)
1. a kind of abrasion resistant fibrous floor-cleaning machine disc brush silk, it is characterised in that the disc brush silk includes the wear-resisting silk core of multi beam and is wrapped in
Fiber sheath on wear-resisting silk core outer surface；The wear-resisting silk core is made up of at least two abrasive filaments or polyamide monofilament；It is described
Fiber sheath can be single or multiple lift.
2. a kind of abrasion resistant fibrous floor-cleaning machine disc brush silk according to claim 1, it is characterised in that the fiber sheath is fine
The material for tieing up yarn is a kind of Fypro, polyester fiber or polyolefine fiber etc., or Fypro or polyester it is fine
The mixture of the polyolefine fibers such as dimension etc. is entwined in wear-resisting silk core outer surface.
3. a kind of abrasion resistant fibrous floor-cleaning machine disc brush silk according to claim 1, it is characterised in that the wear-resisting silk core of multiply
The diameter range of the industrial brush filament constituted with the fiber sheath being wrapped on wear-resisting silk outer surface is in 2mm~10mm.
4. a kind of abrasion resistant fibrous floor-cleaning machine disc brush silk according to claim 1, it is characterised in that the wear-resisting silk core with it is fine
The combination of dimension table layer can be bonded using adhesive, also can be by the way of heating fiber sheath is bonded with wear-resisting silk core.
5. a kind of abrasion resistant fibrous floor-cleaning machine disc brush silk according to claim 4, it is characterised in that the adhesive is by following
The raw material composition of parts by weight：Polyester resin A20-40 parts, polyester resin B10-30 parts, curing agent 3-12 parts, mixed solvent 12-
36 parts, 12-25 parts of polyethylene wax powder dispersion, dibutyl phthalate 0.9-1.1 parts, neoprene 48-52 parts, stearic acid
0.4-0.6 parts, tetramethylthiuram disulfide 0.05-0.07 parts.