CN106700995A - Formaldehyde-free environment-friendly adhesive and preparation method thereof - Google Patents

Formaldehyde-free environment-friendly adhesive and preparation method thereof Download PDF

Info

Publication number
CN106700995A
CN106700995A CN201611165376.3A CN201611165376A CN106700995A CN 106700995 A CN106700995 A CN 106700995A CN 201611165376 A CN201611165376 A CN 201611165376A CN 106700995 A CN106700995 A CN 106700995A
Authority
CN
China
Prior art keywords
parts
adhesive
environmental protection
epoxy resin
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201611165376.3A
Other languages
Chinese (zh)
Inventor
周春毅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuzhong District Dome High Polymer Material Technology Research Institute
Original Assignee
Wuzhong District Dome High Polymer Material Technology Research Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuzhong District Dome High Polymer Material Technology Research Institute filed Critical Wuzhong District Dome High Polymer Material Technology Research Institute
Priority to CN201611165376.3A priority Critical patent/CN106700995A/en
Publication of CN106700995A publication Critical patent/CN106700995A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a formaldehyde-free environment-friendly adhesive and a preparation method thereof. The adhesive is made of, by weight parts, 30-40 parts of bisphenol A epoxy resin, 20-30 parts of polyamide resin, 3-6 parts of curing agent, 2-5 parts of diatomaceous earth, 3-6 parts of polyvinyl alcohol, 1-3 parts of magnesium oxide, 0.3-1 part of sodium alginate, 0.3-1 part of dibutyl phthalate, 3-6 parts of triethanolamine and 2-4 parts of terpene resin. The proportion of each ingredient is optimized, the stability and bonding strength of the adhesive are improved, the made adhesive is green and environmentally friendly, and harmful gas is not generated in the using process.

Description

A kind of adhesive without aldehyde environmental protection and preparation method thereof
Technical field
The present invention relates to adhesive technical field, and in particular to a kind of adhesive without aldehyde environmental protection and preparation method thereof.
Background technology
At present, adhesive has been widely used in the production and life of people, particularly in furniture manufacturing industry, dress The industries such as decoration industry and shoe industry are repaiied to be widely used.The adhesive type for using at present is a lot, but existing general glue Stick all contains the composition that formaldehyde, benzene, toluene etc. are toxic to human body.The environment that these toxic components give people causes serious dirt Dye, and health is endangered, these harmful components have certain injury to eyes, skin, respiratory system and PFT, long-term to inhale Entering a small amount of formaldehyde can also cause slow poisoning, trigger stronger mutagenicity and carcinogenicity.As can be seen here, a kind of environmental protection is produced Adhesive be the development of following adhesive trend.
The content of the invention
In view of the shortcomings of the prior art, the invention provides a kind of adhesive without aldehyde environmental protection and preparation method thereof.
To realize object above, the present invention is achieved by the following technical programs:
A kind of adhesive without aldehyde environmental protection, is made up of the raw material of following weight portion:Bisphenol A type epoxy resin 30-40 parts, it is poly- Amide resin 20-30 parts, curing agent 3-6 parts, diatomite 2-5 parts, polyvinyl alcohol 3-6 parts, magnesia 1-3 parts, sodium alginate 0.3-1 parts, dibutyl phthalate 0.3-1 parts, triethanolamine 3-6 parts, terpene resin 2-4 parts.
Preferably, it is made up of the raw material of following weight portion:32 parts of bisphenol A type epoxy resin, 26 parts of polyamide, solidification 4 parts of agent, 4 parts of diatomite, 5 parts of polyvinyl alcohol, 2 parts of magnesia, 0.5 part of sodium alginate, 0.5 part of dibutyl phthalate, three 5 parts of monoethanolamine, 3 parts of terpene resin.
Preferably, it is made up of the raw material of following weight portion:38 parts of bisphenol A type epoxy resin, 25 parts of polyamide, solidification 4.5 parts of agent, 5 parts of diatomite, 6 parts of polyvinyl alcohol, 2 parts of magnesia, 0.6 part of sodium alginate, 0.6 part of dibutyl phthalate, 5 parts of triethanolamine, 3.5 parts of terpene resin.
Preferably, the curing agent is 2-ethyl-4-methylimidazole.
The preparation method of the adhesive without aldehyde environmental protection, step is as follows:Each raw material is weighed in proportion to be placed in batch mixer, with 600-900r/min rotating speeds continuously stir 30-40min, filtering, are placed in removing residual bubble in vacuum drying chamber, obtain final product asphalt mixtures modified by epoxy resin Fat adhesive.
Beneficial effect of the present invention:The present invention makes it have excellent with epoxy resin and polyamide as main component Mechanical property and adhesive property, are used as auxiliary agent, and optimize matching somebody with somebody for each component by adding diatomite, terpene resin, sodium alginate Than, the stability and adhesion strength of adhesive are improved, adhesive environmental protection of the invention does not produce harmful gas during use Body.
Specific embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with the embodiment of the present invention, Technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is the present invention one Divide embodiment, rather than whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art are not making The every other embodiment obtained under the premise of creative work, belongs to the scope of protection of the invention.
Embodiment 1:
A kind of adhesive without aldehyde environmental protection, 38 parts of bisphenol A type epoxy resin, 25 parts of polyamide, 2- ethyl -4- methyl 4.5 parts of imidazoles, 5 parts of diatomite, 6 parts of polyvinyl alcohol, 2 parts of magnesia, 0.6 part of sodium alginate, dibutyl phthalate 0.6 Part, 5 parts of triethanolamine, 3.5 parts of terpene resin.
The preparation method of the adhesive without aldehyde environmental protection, step is as follows:Each raw material is weighed in proportion to be placed in batch mixer, with 800r/min rotating speeds continuously stir 40min, filtering, are placed in removing residual bubble in vacuum drying chamber, obtain final product epoxy resin gluing Agent.
Embodiment 2:
A kind of adhesive without aldehyde environmental protection, is made up of the raw material of following weight portion:32 parts of bisphenol A type epoxy resin, polyamides 26 parts of polyimide resin, 4 parts of 2-ethyl-4-methylimidazole, 4 parts of diatomite, 5 parts of polyvinyl alcohol, 2 parts of magnesia, sodium alginate 0.5 Part, 0.5 part of dibutyl phthalate, 5 parts of triethanolamine, 3 parts of terpene resin.
The preparation method of the adhesive without aldehyde environmental protection, step is as follows:Each raw material is weighed in proportion to be placed in batch mixer, with 750r/min rotating speeds continuously stir 35min, filtering, are placed in removing residual bubble in vacuum drying chamber, obtain final product epoxy resin gluing Agent.
Embodiment 3:
A kind of adhesive without aldehyde environmental protection, is made up of the raw material of following weight portion:35 parts of bisphenol A type epoxy resin, polyamides 22 parts of polyimide resin, 3.5 parts of 2-ethyl-4-methylimidazole, 3 parts of diatomite, 6 parts of polyvinyl alcohol, 1.5 parts of magnesia, sodium alginate 0.5 part, 0.5 part of dibutyl phthalate, 3.5 parts of triethanolamine, 4 parts of terpene resin.
The preparation method of the adhesive without aldehyde environmental protection, step is as follows:Each raw material is weighed in proportion to be placed in batch mixer, with 600r/min rotating speeds continuously stir 40min, filtering, are placed in removing residual bubble in vacuum drying chamber, obtain final product epoxy resin gluing Agent.
Embodiment 4:
A kind of adhesive without aldehyde environmental protection, is made up of the raw material of following weight portion:40 parts of bisphenol A type epoxy resin, polyamides 20 parts of polyimide resin, 6 parts of 2-ethyl-4-methylimidazole, 2 parts of diatomite, 6 parts of polyvinyl alcohol, 1 part of magnesia, 1 part of sodium alginate, 0.3 part of dibutyl phthalate, 6 parts of triethanolamine, 2 parts of terpene resin.
The preparation method of the adhesive without aldehyde environmental protection, step is as follows:Each raw material is weighed in proportion to be placed in batch mixer, with 800r/min rotating speeds continuously stir 30min, filtering, are placed in removing residual bubble in vacuum drying chamber, obtain final product epoxy resin gluing Agent.
Embodiment 5:
A kind of adhesive without aldehyde environmental protection, is made up of the raw material of following weight portion:30 parts of bisphenol A type epoxy resin, polyamides 30 parts of polyimide resin, 3 parts of 2-ethyl-4-methylimidazole, 5 parts of diatomite, 3 parts of polyvinyl alcohol, 3 parts of magnesia, sodium alginate 0.3 Part, 1 part of dibutyl phthalate, 3 parts of triethanolamine, 4 parts of terpene resin.
The preparation method of the adhesive without aldehyde environmental protection, step is as follows:Each raw material is weighed in proportion to be placed in batch mixer, with 900r/min rotating speeds continuously stir 40min, filtering, are placed in removing residual bubble in vacuum drying chamber, obtain final product epoxy resin gluing Agent.
It should be noted that herein, such as first and second or the like relational terms are used merely to a reality Body or operation make a distinction with another entity or operation, and not necessarily require or imply these entities or deposited between operating In any this actual relation or order.And, term " including ", "comprising" or its any other variant be intended to Nonexcludability is included, so that process, method, article or equipment including a series of key elements not only will including those Element, but also other key elements including being not expressly set out, or also include being this process, method, article or equipment Intrinsic key element.In the absence of more restrictions, the key element limited by sentence "including a ...", it is not excluded that Also there is other identical element in process, method, article or equipment including the key element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations;Although with reference to the foregoing embodiments The present invention has been described in detail, it will be understood by those within the art that:It still can be to foregoing each implementation Technical scheme described in example is modified, or carries out equivalent to which part technical characteristic;And these modification or Replace, do not make the spirit and scope of the essence disengaging various embodiments of the present invention technical scheme of appropriate technical solution.

Claims (5)

1. it is a kind of without aldehyde environmental protection adhesive, it is characterised in that be made up of the raw material of following weight portion:Bisphenol A type epoxy resin 30-40 parts, polyamide 20-30 parts, curing agent 3-6 parts, diatomite 2-5 parts, polyvinyl alcohol 3-6 parts, magnesia 1-3 parts, Sodium alginate 0.3-1 parts, dibutyl phthalate 0.3-1 parts, triethanolamine 3-6 parts, terpene resin 2-4 parts.
2. as claimed in claim 1 without the adhesive of aldehyde environmental protection, it is characterised in that be made up of the raw material of following weight portion:It is double 32 parts of phenol A types epoxy resin, 26 parts of polyamide, 4 parts of curing agent, 4 parts of diatomite, 5 parts of polyvinyl alcohol, 2 parts of magnesia, sea 0.5 part of mosanom, 0.5 part of dibutyl phthalate, 5 parts of triethanolamine, 3 parts of terpene resin.
3. as claimed in claim 1 without the adhesive of aldehyde environmental protection, it is characterised in that be made up of the raw material of following weight portion:It is double 38 parts of phenol A types epoxy resin, 25 parts of polyamide, 4.5 parts of curing agent, 5 parts of diatomite, 6 parts of polyvinyl alcohol, 2 parts of magnesia, 0.6 part of sodium alginate, 0.6 part of dibutyl phthalate, 5 parts of triethanolamine, 3.5 parts of terpene resin.
4. as claimed in claim 1 without the adhesive of aldehyde environmental protection, it is characterised in that the curing agent is 2- ethyl -4- methyl Imidazoles.
5. as claimed in claim 1 without the preparation method of the environmentally friendly adhesive of aldehyde, it is characterised in that step is as follows:In proportion Weigh each raw material to be placed in batch mixer, 30-40min is continuously stirred with 600-900r/min rotating speeds, filter, be placed in vacuum drying chamber Interior removing residual bubble, obtains final product epoxy resin adhesive.
CN201611165376.3A 2016-12-16 2016-12-16 Formaldehyde-free environment-friendly adhesive and preparation method thereof Withdrawn CN106700995A (en)