CN106700771A - Heat-resistant coating - Google Patents
Heat-resistant coating Download PDFInfo
- Publication number
- CN106700771A CN106700771A CN201510494343.2A CN201510494343A CN106700771A CN 106700771 A CN106700771 A CN 106700771A CN 201510494343 A CN201510494343 A CN 201510494343A CN 106700771 A CN106700771 A CN 106700771A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatomite
- silicone oil
- methyl
- silica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of building coatings, in particular to a heat-resistant coating. The coating is prepared from components in parts by mass as follows: 2.3-4.5 parts of calcium silicate, 3-9 parts of sodium dodecyl benzene sulfonate, 1.8-3.3 parts of sodium tripolyphosphate, 4-10 parts of methyl silicone oil, 3.5-5.6 parts of hollow glass beads, 20-35 parts of waterborne acrylic resin, 8-15 parts of ethylenediamine methylene phosphate, 12-18 parts of diatomite and 5-11 parts of silicon dioxide. With the adoption of the formula, materials with the low heat conductivity coefficients are adopted as heat-resistant materials, and the flame-retardant effect is good; the components are low in cost and available, the process is simple and convenient, and popularization and application are facilitated.
Description
Technical field
The present invention relates to building coating technical field, particularly a kind of heat resistant paint.
Background technology
Reflective heat-insulation paint is made up of base-material, heat reflection pigment, filler and auxiliary agent etc..By high-efficiency reflective too
Sunlight reaches heat-insulated purpose.Thin layer heat insulating reflecting coating is the representative of this kind of coating.Country put into effect reflection every
Hot coating standard (JC/T1040-2007) requires：Sun reflectivity is not less than 85%, and hemispherical emissivity is not small
In 83%.Reflective heat-insulation paint is that collection reflects, radiates the new High tailored coating with one heat-insulated with cenosphere,
Coating can carry out high reflection to the solar infrared of 400nm--2500nm scopes and ultraviolet.
The content of the invention
The technical problem to be solved in the invention is to provide a kind of heat resistant paint.
Be to solve above-mentioned technical problem, a kind of heat resistant paint of the invention, according to mass fraction meter include with
Lower component：Calcium silicates 2.3-4.5 parts, neopelex 3-9 parts, sodium tripolyphosphate 1.8-3.3
Part, methyl-silicone oil 4-10 parts, hollow glass micropearl 3.5-5.6 parts, water-based acrylic resin 20-35 parts,
8-15 parts, diatomite 12-18 parts, silica 5-11 parts of ethylenediamine methylene phosphate.
Further, following component is included according to mass fraction meter：2.3 parts of calcium silicates, DBSA
3 parts of sodium, 1.8 parts of sodium tripolyphosphate, 4 parts of methyl-silicone oil, 3.5 parts of hollow glass micropearl, aqueous acrylamide
20 parts of acid resin, 8 parts of ethylenediamine methylene phosphate, 12 parts of diatomite, 5 parts of silica.
Further, following component is included according to mass fraction meter：4.5 parts of calcium silicates, DBSA
9 parts of sodium, 3.3 parts of sodium tripolyphosphate, 10 parts of methyl-silicone oil, 5.6 parts of hollow glass micropearl, aqueous acrylamide
35 parts of acid resin, 15 parts of ethylenediamine methylene phosphate, 18 parts of diatomite, 1 part of silica 1.
Further, following component is included according to mass fraction meter：3.1 parts of calcium silicates, DBSA
5 parts of sodium, 2.2 parts of sodium tripolyphosphate, 6 parts of methyl-silicone oil, 4.2 parts of hollow glass micropearl, aqueous acrylamide
25 parts of acid resin, 10 parts of ethylenediamine methylene phosphate, 13 parts of diatomite, 8 parts of silica.
Further, following component is included according to mass fraction meter：3.9 parts of calcium silicates, DBSA
6 parts of sodium, 2.8 parts of sodium tripolyphosphate, 9 parts of methyl-silicone oil, 5.3 parts of hollow glass micropearl, aqueous acrylamide
30 parts of acid resin, 12 parts of ethylenediamine methylene phosphate, 16 parts of diatomite, 0 part of silica 1.
After using above-mentioned formula, heat resistant paint of the invention, using the low material of thermal conductivity factor as thermal resistance material
Material, thermal resistance effect is good；In addition, composition low cost of the invention, it is easy to obtain, process is simple is convenient, just
In popularization and application.
Specific embodiment
A kind of heat resistant paint of the invention, following component is included according to mass fraction meter：Calcium silicates 2.3-4.5
Part, it is neopelex 3-9 parts, sodium tripolyphosphate 1.8-3.3 parts, methyl-silicone oil 4-10 parts, empty
3.5-5.6 parts of heart glass microballoon, water-based acrylic resin 20-35 parts, 8-15 parts of ethylenediamine methylene phosphate,
Diatomite 12-18 parts, silica 5-11 parts.
Implementation method one：
Include following component according to mass fraction meter：2.3 parts of calcium silicates, 3 parts of neopelex, three
1.8 parts of polyphosphate sodium, 4 parts of methyl-silicone oil, 3.5 parts of hollow glass micropearl, 20 parts of water-based acrylic resin,
8 parts of ethylenediamine methylene phosphate, 12 parts of diatomite, 5 parts of silica.
Implementation method two：
Include following component according to mass fraction meter：4.5 parts of calcium silicates, 9 parts of neopelex, three
3.3 parts of polyphosphate sodium, 10 parts of methyl-silicone oil, 5.6 parts of hollow glass micropearl, water-based acrylic resin 35
Part, 15 parts of ethylenediamine methylene phosphate, 18 parts of diatomite, 1 part of silica 1.
Implementation method three：
Include following component according to mass fraction meter：3.1 parts of calcium silicates, 5 parts of neopelex, three
2.2 parts of polyphosphate sodium, 6 parts of methyl-silicone oil, 4.2 parts of hollow glass micropearl, 25 parts of water-based acrylic resin,
10 parts of ethylenediamine methylene phosphate, 13 parts of diatomite, 8 parts of silica.
Implementation method four：
Include following component according to mass fraction meter：3.9 parts of calcium silicates, 6 parts of neopelex, three
2.8 parts of polyphosphate sodium, 9 parts of methyl-silicone oil, 5.3 parts of hollow glass micropearl, 30 parts of water-based acrylic resin,
12 parts of ethylenediamine methylene phosphate, 16 parts of diatomite, 0 part of silica 1.
Although the foregoing describing specific embodiment of the invention, those skilled in the art should manage
Solution, these are merely illustrative of, and various changes or modifications can be made to present embodiment, without departing from hair
Bright principle and essence, protection scope of the present invention is only limited by the claims that follow.
Claims (5)
1. a kind of heat resistant paint, it is characterised in that include following component according to mass fraction meter：Calcium silicates 2.3-4.5
Part, it is neopelex 3-9 parts, sodium tripolyphosphate 1.8-3.3 parts, methyl-silicone oil 4-10 parts, empty
3.5-5.6 parts of heart glass microballoon, water-based acrylic resin 20-35 parts, 8-15 parts of ethylenediamine methylene phosphate,
Diatomite 12-18 parts, silica 5-11 parts.
2. according to a kind of heat resistant paint described in claim 1, it is characterised in that include according to mass fraction meter
Following component：2.3 parts of calcium silicates, 3 parts of neopelex, 1.8 parts of sodium tripolyphosphate, methyl
4 parts of silicone oil, 3.5 parts of hollow glass micropearl, 20 parts of water-based acrylic resin, ethylenediamine methylene phosphate 8
Part, 12 parts of diatomite, 5 parts of silica.
3. according to a kind of heat resistant paint described in claim 1, it is characterised in that include according to mass fraction meter
Following component：4.5 parts of calcium silicates, 9 parts of neopelex, 3.3 parts of sodium tripolyphosphate, methyl
10 parts of silicone oil, 5.6 parts of hollow glass micropearl, 35 parts of water-based acrylic resin, ethylenediamine methylene phosphate
15 parts, 18 parts of diatomite, 1 part of silica 1.
4. according to a kind of heat resistant paint described in claim 1, it is characterised in that include according to mass fraction meter
Following component：3.1 parts of calcium silicates, 5 parts of neopelex, 2.2 parts of sodium tripolyphosphate, methyl
6 parts of silicone oil, 4.2 parts of hollow glass micropearl, 25 parts of water-based acrylic resin, ethylenediamine methylene phosphate 10
Part, 13 parts of diatomite, 8 parts of silica.
5. according to a kind of heat resistant paint described in claim 1, it is characterised in that include according to mass fraction meter
Following component：3.9 parts of calcium silicates, 6 parts of neopelex, 2.8 parts of sodium tripolyphosphate, methyl
9 parts of silicone oil, 5.3 parts of hollow glass micropearl, 30 parts of water-based acrylic resin, ethylenediamine methylene phosphate 12
Part, 16 parts of diatomite, 0 part of silica 1.