CN106700766A - Weather-resistant coating and preparation method thereof - Google Patents
Weather-resistant coating and preparation method thereof Download PDFInfo
- Publication number
- CN106700766A CN106700766A CN201710007154.7A CN201710007154A CN106700766A CN 106700766 A CN106700766 A CN 106700766A CN 201710007154 A CN201710007154 A CN 201710007154A CN 106700766 A CN106700766 A CN 106700766A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- mixture
- weathering resistance
- revs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a weather-resistant coating and a preparation method thereof. The weather-resistant coating comprises the following components in parts by weight: 10-40 parts of water, 10-50 parts of an acrylic acid emulsion, 20-70 parts of packing, 0.1-1 part of an ultraviolet absorbent, 1-30 parts of nano zinc oxide, 0.1-5 parts of a dispersing agent, 0.1-5 parts of a wetting agent, 0.5-5 parts of a defoaming agent, 0.1-5 parts of a leveling agent, 0.1-5 parts of a thickening agent and 0.1-5 parts of a preservative. The invention further discloses a preparation method of the weather-resistant coating. By adopting the weather-resistant coating, the ultraviolet light shielding property of a coated layer can be protected, meanwhile, the density of the coated layer can be greatly increased, the water resistance property of the coated layer can be improved, and thus the water movement prevention property of a pre-installed and inverted adhered waterproof roll can be improved; and in addition, the tensile strength and break elongation of the coated layer can be remarkably improved, and thus the waterproof property of the pre-installed and inverted adhered waterproof roll can be improved.
Description
Technical field
The present invention relates to a kind of weathering resistance coatings coating and preparation method thereof, and in particular to a kind of for pre-installed and inverted adhered waterproof volume
Weathering resistance coatings coating of material protective layer and preparation method thereof.
Background technology
After pre-installed and inverted adhered waterproof roll introduces Chinese market from the nineties in 20th century, by its excellent leakage-proof performance,
Quickly grow at home, be widely used in underground engineering, cut and cover method Tunnel Engineering, subsurface excavation method Tunnel Engineering, underground pipe gallery is prevented
The major projects such as Hydraulic Projects.Pre-installed and inverted adhered waterproof roll typical construction includes main water barrier, adhesive layer and protective layer, its
The Main Function of middle protective layer is Protection glue adhensive layer from outside contamination, isolation ultraviolet and oxygen environment, protection adhesive
There is no chain rupture disability by ultraviolet ray ageing in layer.Therefore, the shielding ultraviolet rays performance of protective layer is for pre-installed and inverted adhered waterproof roll
UV resistance influence it is very big.
Typically using empty laid process construction, be laid on for pre-installed and inverted adhered waterproof roll in advance anti-by pre-installed and inverted adhered waterproof coiled material construction
Water position, then assembling reinforcement, last casting concrete treats after the completion of concrete hydrating that protective layer is together with main water barrier and glue
Adhensive layer forms permanent adhesive layer with rear pouring concrete, reaches the effect of " skin-type " waterproof.But, some underground engineerings,
In the work progress of cut and cover method Tunnel Engineering, after laying pre-installed and inverted adhered waterproof roll, in addition it is also necessary to assembling reinforcement, coagulation can be just poured
Soil, pre-installed and inverted adhered waterproof roll will be fully exposed to be exposed to the sun under the ultraviolet of sunlight during this, particularly be shone in some ultraviolets
Strong area and low latitudes high temperature area is penetrated, ultraviolet irradiation is stronger.If running into special circumstances, project progress progress
In the case of slow, pre-installed and inverted adhered waterproof roll can expose and be exposed to the sun in the sun 2 months, even more long.Such as run into more than 2 months
Open air be exposed to the sun, pre-installed and inverted adhered waterproof roll is easy to the aging disability of adhesive layer, so as to influence pre-installed and inverted adhered effect,
It is difficult to reach good " skin-type " leakage-proof effect.
At present, pre-installed and inverted adhered waterproof roll protective layer carries out protection adhesive using mineral grain or artificial synthesized particle
The method of layer.For example, prior art CN104057686A is disclosed with the weather-proof mineral grain function with cement reactivity
Layer with the materials such as alumine, aluminum oxide it is size-reduced, fire, cooling, crush, screening, washing, drying etc. technique it is artificial synthesized
Mineral grain.Can be with shield portions shielding ultraviolet rays, because its mineral grain is covered in although the method is made protective layer
Adhesive layer surface is unable to reach 100% continuous covering, therefore is unable to reach the effect of complete shielding ultraviolet rays.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of weather-proof painting for pre-installed and inverted adhered waterproof roll protective layer
Coating and preparation method thereof, the weathering resistance coatings coating mainly solves to irradiate strong area and low latitudes high temperature ground in ultraviolet
Area, pre-installed and inverted adhered waterproof roll was exposed to the sun more than 2 months in the sun, it is even more prolonged in the case of, still can effectively shield purple
Outside line, protects adhesive layer not irradiated by ultraviolet and destroys.
The present invention solve its technical problem use technical scheme be, a kind of weathering resistance coatings coating, in parts by weight, including
Following components:10~40 parts of water, 10~50 parts of acrylic emulsions, 20~70 parts of filler, 0.1~1 part of ultraviolet absorber, nanometer
1~30 part of zinc oxide, 0.1~5 part of dispersant, 0.1~5 part of wetting agent, 0.5~5 part of defoamer, 0.1~5 part of levelling agent increases
Thick dose 0.1~5 part.
Further, the nano zine oxide is zinc oxide content >=98%, Electronic Speculum average grain diameter≤50nm commercially available prod.
Further, the water is deionized water, the running water of pure water, distilled water or soft.
Further, the acrylic emulsion is vinegar-acrylic emulsion, styryl acrylic emulsion, pure-acrylic emulsion, silicon-acralyte latex uncle and carbonic acid
One or more mixture in ester emulsion.
Further, described filler is the one kind in powdered whiting, precipitated calcium carbonate, titanium dioxide, kaolin and wollastonite
Or two or more mixtures.
Further, the ultraviolet absorber is salicylic acid esters, benzophenone class, benzotriazole, group-substituted acrylonitrile and three
One or more mixture in piperazine class and hindered amines.
Further, the dispersant is selected from the mixed of one or more in polyacrylic acid sodium salt, ammonium polyacrylate salt
Compound, such as DP270, DA40 and 5040 etc., the wetting agent is selected from APES class, alkylsurfuric acid salt, sulphur
One or more mixture in Barbiturates, such as DM-410, NP10 and X405 etc., the defoamer are selected from mineral oil
One or more mixture in class, organic silicon, paraffin class, such as 7010, NXZ and F-111 etc., the levelling agent
Selected from one or more mixed in pure acrylic acid class levelling agent, modified acrylic acid levelling agent, silicone levelling agent
Compound, such as ASE-60, Polyflow S, NO.90 and KL-700 etc., the thickener are selected from swelling great soil group thickener, fiber
One or more mixture in plain ethers thickener, polyacrylamide thickener, such as TT-935, RM-8W,
HEC440 and D105 etc..
The present invention further solve its technical problem use technical scheme be, a kind of preparation side of weathering resistance coatings coating
Method, comprises the following steps:
(1) by the accurate water weighed with nano zinc oxide powder phase homogenous quantities of formula, add the dispersant of gross mass half with
Nano zinc oxide powder is premixed, and activation process is carried out through ultrasonic cumulative reactor, is taken out standby;
(2) remaining water is accurately weighed by formula, is added in dispersion cylinder, stirred with 100 revs/min;Then accurately weigh
The dispersant of gross mass half, wetting agent and defoamer, add in dispersion cylinder, are stirred 2~3 minutes with 100 revs/min, and stirring is equal
It is even;Then mixing speed is improved to 200 revs/min, the filler for accurately having weighed is slowly uniformly added into, and has been added within 10~15 minutes
Finish, be evenly stirred until that fineness is less than 50 μm;
(3) acrylic emulsions are accurately weighed, dispersion cylinder is slowly uniformly added into, charging in 5~8 minutes are finished, with 200 turns/
Dispersion 4~5 minutes, stirs;Then levelling agent, thickener, ultraviolet absorber, preservative are accurately weighed, dispersion is added
Cylinder, is disperseed 4~5 minutes with 200 revs/min, is stirred;It is last accurately to weigh nano zine oxide after activation process, add dispersion
Cylinder, is disperseed 4~5 minutes with 200 revs/min, is stirred, and is weighed filling.
The technology of the present invention principle is premixed with chemical assistant and nano zinc oxide powder, and ultrasonic activation is carried out in water, is made
Itself turns into a kind of stabilising system;The know-why of nano zine oxide shielding ultraviolet rays is to absorb and scatters ultraviolet, nanometer
Zinc oxide belongs to N-type semiconductor, and the energy gap of ZnO is 312eV, when nano zine oxide is subject to ultraviolet irradiation, nanometer
The electronics that zinc oxide Jie takes can absorb ultraviolet and is excited on conduction band, while hole-electron pair is produced, so that ZnO
Function with excellent absorption ultraviolet.Further, since size itself is much smaller than the wavelength of ultraviolet, nano-particle will can be made
Scattered to all directions with ultraviolet thereon, so as to reduce the uitraviolet intensity of direction of illumination.Therefore, it is follow-up to add protection
Coated coating is formulated, the final high-performance protective coating coating for providing shielding ultraviolet rays excellent performance, protect adhesive layer not by
Ultraviolet irradiation destruction.
The present invention substantially increases the shielding ultraviolet rays performance of protective coating using nano zine oxide, when being received in protective coating
Rice zinc oxide content is when being added to 5 weight portion, after its outdoor placement 6 months, pre-installed and inverted adhered waterproof roll and concrete
Peel strength can reach more than 2.0N/mm.Meanwhile, nano zine oxide is added in protective coating coating, protection can be greatly improved
The consistency of coating, strengthens the water resistance of protective coating, so as to improve the leakage-proof performance of pre-installed and inverted adhered waterproof roll;And
The addition of nano zine oxide can play enhanced effect, significantly improve the tensile strength of protective coating and the extension at break of coating
Rate, so as to improve pre-installed and inverted adhered waterproof roll water resistance.
Specific embodiment
The present invention is further illustrated with reference to embodiment.
Embodiment 1:The preparation of UV resistance coiled material protective coating
UV resistance coiled material protective coating high, contains following component in parts by weight:
Water | Deionized water | 25 parts |
Acrylic emulsions | ROHM AND HAAS AC-261P | 35 parts |
Filler | Coarse whiting Jiangxi Guang Yuan CC800 | 30 parts |
Ultraviolet absorber | Vapour bar ultra-violet absorber 326 | 1.0 parts |
Nano zine oxide | Shanghai is then into ZEC Slurral ZNO30W | 5.0 parts |
Dispersant | DP270 | 1.0 parts |
Wetting agent | CF10 | 0.5 part |
Defoamer | NXZ | 0.5 part |
Levelling agent | ASE-60 | 0.5 part |
Thickener | RM-8W | 1.0 parts |
Preservative | MV | 0.5 part |
The preparation method of UV resistance coiled material protective coating high, comprises the following steps:
(1) by the accurate water weighed with nano zinc oxide powder phase homogenous quantities of formula, add the dispersant of gross mass half with
Nano zinc oxide powder is premixed, and activation process is carried out through ultrasonic cumulative reactor, is taken out standby;
(2) remaining water is accurately weighed by formula, is added in dispersion cylinder, stirred with 100 revs/min;Then accurately weigh
The dispersant of gross mass half, wetting agent and defoamer, add in dispersion cylinder, are stirred 2~3 minutes with 100 revs/min, and stirring is equal
It is even;Then mixing speed is improved to 200 revs/min, the filler for accurately having weighed is slowly uniformly added into, and has been added within 10~15 minutes
Finish, be evenly stirred until that fineness is less than 50 μm;
(3) acrylic emulsions are accurately weighed, dispersion cylinder is slowly uniformly added into, charging in 5~8 minutes are finished, with 200 turns/
Dispersion 4~5 minutes, stirs;Then levelling agent, thickener, ultraviolet absorber, preservative are accurately weighed, dispersion is added
Cylinder, is disperseed 4~5 minutes with 200 revs/min, is stirred;It is last accurately to weigh nano zine oxide after activation process, add dispersion
Cylinder, is disperseed 4~5 minutes with 200 revs/min, is stirred, and is weighed filling.
Embodiment 2:UV resistance coiled material protective coating high
UV resistance coiled material protective coating high contains following component in parts by weight:
The preparation method of UV resistance coiled material protective coating high, with embodiment 1.
Embodiment 3:UV resistance coiled material protective coating high
UV resistance coiled material protective coating high contains following component in parts by weight:
Water | Deionized water | 15 parts |
Acrylic emulsions | ROHM AND HAAS AC-261P | 30 parts |
Filler | Coarse whiting Jiangxi Guang Yuan CC800 | 42 parts |
Ultraviolet absorber | Vapour bar ultra-violet absorber 326 | 2.0 parts |
Nano zine oxide | Shanghai is then into ZEC Slurral ZNO 30W | 7.0 parts |
Dispersant | DP270 | 0.5 part |
Wetting agent | CF10 | 0.5 part |
Defoamer | NXZ | 1.0 parts |
Levelling agent | ASE-60 | 0.5 part |
Thickener | RM-8W | 1.0 parts |
Preservative | MV | 0.5 part |
The preparation method of UV resistance coiled material protective coating high, with embodiment 1.
The corresponding the performance test results of various embodiments above, are shown in Table 1.
Each embodiment the performance test results of table 1-
With rear pouring concrete peel strength | Embodiment 1 | Embodiment 2 | Embodiment 3 |
Without treatment | 2.5N/mm | 2.5N/mm | 2.5N/mm |
Outdoor naturally quick-fried Sai 90d | 2.0N/mm | 1.9N/mm | 2.3N/mm |
Claims (8)
1. a kind of weathering resistance coatings coating, it is characterised in that in parts by weight, including following components:10~40 parts of water, acrylic compounds
10~50 parts of emulsion, 20~70 parts of filler, 0.1~1 part of ultraviolet absorber, 1~30 part of nano zine oxide, dispersant 0.1~5
Part, 0.1~5 part of wetting agent, 0.5~5 part of defoamer, 0.1~5 part of levelling agent, 0.1~5 part of thickener, preservative 0.1~5
Part.
2. weathering resistance coatings coating according to claim 1, it is characterised in that the nano zine oxide be zinc oxide content >=
98%, Electronic Speculum average grain diameter≤50nm commercially available prod.
3. weathering resistance coatings coating according to claim 1, it is characterised in that the water is deionized water, pure water, distillation
The running water of water or soft.
4. weathering resistance coatings coating according to claim 1, it is characterised in that the acrylic emulsion be vinegar-acrylic emulsion,
One or more mixture in styryl acrylic emulsion, pure-acrylic emulsion, silicon-acralyte latex uncle and carbonic ester emulsion.
5. weathering resistance coatings coating according to claim 1, it is characterised in that described filler is powdered whiting, lightweight carbon
One or more mixture in sour calcium, titanium dioxide, kaolin and wollastonite.
6. weathering resistance coatings coating according to claim 1, it is characterised in that the ultraviolet absorber be salicylic acid esters,
One or more mixture in benzophenone class, benzotriazole, group-substituted acrylonitrile and triazines and hindered amines.
7. weathering resistance coatings coating according to claim 1, it is characterised in that the dispersant be selected from DP270, DA40 and
One or more mixture in 5040, the wetting agent be selected from DM-410, NP10 and X405 in one or two
Mixture above, the defoamer is selected from one or more the mixture in 7010, NXZ and F-111, the levelling
Agent is selected from one or more the mixture in ASE-60, Polyflow S, NO.90 and KL-700, the thickener choosing
One or more mixture from TT-935, RM-8W, HEC440 and D105.
8. the preparation method of a kind of weathering resistance coatings coating as described in one of claim 1~8, it is characterised in that including following
Step:
(1) by the accurate water weighed with nano zinc oxide powder phase homogenous quantities of formula, the dispersant and nanometer of gross mass half are added
Oxide powder and zinc is premixed, and activation process is carried out through ultrasonic cumulative reactor, is taken out standby;
(2) remaining water is accurately weighed by formula, is added in dispersion cylinder, stirred with 100 revs/min;Then total matter is accurately weighed
Dispersant, wetting agent and the defoamer of half are measured, is added in dispersion cylinder, stirred 2~3 minutes with 100 revs/min, stirred;Connect
Raising mixing speed to 200 revs/min, the filler for accurately having weighed is slowly uniformly added into, addition in 10~15 minutes is finished, stirred
Uniformly 50 μm are less than to fineness;
(3) acrylic emulsions are accurately weighed, dispersion cylinder is slowly uniformly added into, charging in 5~8 minutes is finished, with 200 revs/min points
Dissipate 4~5 minutes, stir;Then levelling agent, thickener, ultraviolet absorber, preservative are accurately weighed, dispersion cylinder is added, with
200 revs/min are disperseed 4~5 minutes, are stirred;It is last accurately to weigh nano zine oxide after activation process, dispersion cylinder is added, with
200 revs/min are disperseed 4~5 minutes, are stirred, and are weighed filling.