CN106700688A - 一种免打底uv光油及其制备方法 - Google Patents
一种免打底uv光油及其制备方法 Download PDFInfo
- Publication number
- CN106700688A CN106700688A CN201510793646.4A CN201510793646A CN106700688A CN 106700688 A CN106700688 A CN 106700688A CN 201510793646 A CN201510793646 A CN 201510793646A CN 106700688 A CN106700688 A CN 106700688A
- Authority
- CN
- China
- Prior art keywords
- gloss oil
- free
- priming
- added
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种免打底UV光油及其制备方法,所述免打底UV光油,按重量百分比计,包括以下组分:二缩三丙二醇二丙30~45%;热塑性丙烯酸树脂10~15%;三羟甲基丙烷三丙烯酸酯5~10%;消泡剂0.05~1%;环氧树脂8~15%;阻聚剂0.02~0.08%;二苯甲酮5~10%;光引发剂0.6~1流平剂0.4~1.3%;活性胺10~15%;溶剂5~10%。本发明提供的免打底UV光油主要具有以下几点优势:(1)UV光油的各项性能优异,具有光泽度高,流平性好,气味小,耐磨性好的特性;(2)具有高附着力、不变黄、耐磨、干燥速度快的特性;(3)具有优良的耐水性,粘结性、韧性及优异的阻燃性能。
Description
技术领域
本发明涉及一种UV光油,具体涉及一种免打底UV光油及其制备方法。
背景技术
UV技术在印铁制罐行业中的应用日益广泛,它是利用特殊油墨在一定波长范围内的紫外光线照射下快速形成大分子立体网状且理化性能稳定、表面亮度高墨层的技术。目前UV技术的应用主要是通过改进油墨涂布层,采用UV油墨来实现的。UV油墨的成分主要采用大分子聚酯丙烯酸酯、聚酯丙烯酸低聚物、改性环氧丙烯酸酯、活性单体、颜料、光引发剂等。
随着市场经济的发展,UV油墨具有固化速度快、节能、常温固化、性能优越、绿色环保等优点,其上光速度快,膜层光亮度高,干燥后膜面坚固耐热,折光效果好,使底材产生强烈的主体感,已广泛应用于化工、机械、电子轻工、通信等领域。由于其环保优势,UV固化已获得了相关的强有力支持和工业界的密切关注,UV辐射固化材料在市场需求高速增长的同时,UV辐射固化体系正同多种技术结合,以克服某些缺陷,满足实际的应用。现在印刷行业中,UV能使包装取得一些特殊的效果:高光泽度、良好的油墨保护特性、可加控制的滑爽性和耐摩擦性、低气味或没有气味、低萃取物或无法检出萃取物,以及对油墨的保护作用。
目前的UV固化材料各种各样,但是还是不同程度的存在着一些问题,例如:有机物污染,变黄,易爆色、不耐低温、成本高、耐腐蚀性差等一系列问题,都需要针对不同的用途继续改良,降低生产成本,扩大用途。
发明内容
针对以上现有技术中存在的缺陷,本发明的目的在于提供一种免打底UV光油及其制备方法。
本发明所采用的技术方案是:一种免打底UV光油,按重量百分比计,包括以下组分:
进一步的,所述免打底UV光油,按重量百分比计,包括以下组分:
进一步的,所述光引发剂为1-羟基环己基苯基甲酮。
本发明还提供一种免打底UV光油的制备方法,包括如下步骤:
(1)向二缩三丙二醇二丙烯酸酯中边搅拌边加入热塑性丙烯酸树脂,加完后高速搅拌至热塑性丙烯酸树脂完全溶解;
(2)将三羟甲基丙烷三丙烯酸酯在反应釜内加热溶解,控温50-70度,加入步骤(1);
(3)边搅拌边将消泡剂加入步骤(2),直至搅拌均匀;
(4)依次将环氧树脂、阻聚剂、二苯甲酮、光引发剂、流平剂、活性胺加入步骤(3);
(5)向步骤(4)中加入溶剂,调节粘度合格为止,搅拌3-7分钟后停机包装。
本发明的有益效果是:与现有技术相比,本发明提供的免打底UV光油主要具有以下几点优势:(1)UV光油的各项性能优异,与油墨的结合性能优异,具有光泽度高,流平性好,气味小,耐磨性好的特性;(2)具有高附着力、不变黄、耐磨、干燥速度快的特性;(3)本发明UV光油用于UV上光只需一道工序,免去了打底步骤,节约了作业成本,增加了工作效率;(4)具有优良的耐水性,粘结性、韧性及优异的阻燃性能;(5)所述免打底UV的制备方法具有简单、环保等优点。
具体实施方式
下述实施例详细说明本发明,但不限制本发明的范围。
实施例1
一种免打底UV光油及其制备方法:
所述免打底UV光油,按重量百分比计,包括以下组分:
所述免打底UV光油的制备方法,包括如下步骤:
(1)清洗搅拌缸,将二缩三丙二醇二丙烯酸酯放入搅拌缸;
(2)向二缩三丙二醇二丙烯酸酯中边搅拌边加入热塑性丙烯酸树脂,加完后高速搅拌至热塑性丙烯酸树脂完全溶解;取样检测细度合格;
(3)将三羟甲基丙烷三丙烯酸酯在反应釜内加热溶解,控温50-70度,加入步骤(2);
(4)边搅拌边将消泡剂加入步骤(3),直至搅拌均匀;取样检测
(5)依次将环氧树脂、阻聚剂、二苯甲酮、光引发剂、流平剂、活性胺加入步骤(4);取样检测粘度;
(6)向步骤(5)中加入溶剂,调节粘度合格为止,搅拌5分钟后停机包装。
实施例2
一种免打底UV光油及其制备方法:
所述免打底UV光油,按重量百分比计,包括以下组分:
所述免打底UV光油的制备方法,包括如下步骤:
(1)清洗搅拌缸,将二缩三丙二醇二丙烯酸酯放入搅拌缸;
(2)向二缩三丙二醇二丙烯酸酯中边搅拌边加入热塑性丙烯酸树脂,加完后高速搅拌至热塑性丙烯酸树脂完全溶解;取样检测细度合格;
(3)将三羟甲基丙烷三丙烯酸酯在反应釜内加热溶解,控温55-68度,加入步骤(2);
(4)边搅拌边将消泡剂加入步骤(3),直至搅拌均匀;取样检测
(5)依次将环氧树脂、阻聚剂、二苯甲酮、光引发剂、流平剂、活性胺加入步骤(4);取样检测粘度;
(6)向步骤(5)中加入溶剂,调节粘度合格为止,搅拌3-7分钟后停机包装。
实施例3
一种免打底UV光油及其制备方法:
所述免打底UV光油,按重量百分比计,包括以下组分:
所述免打底UV光油的制备方法,包括如下步骤:
(1)清洗搅拌缸,将二缩三丙二醇二丙烯酸酯放入搅拌缸;
(2)向二缩三丙二醇二丙烯酸酯中边搅拌边加入热塑性丙烯酸树脂,加完后高速搅拌至热塑性丙烯酸树脂完全溶解;取样检测细度合格;
(3)将三羟甲基丙烷三丙烯酸酯在反应釜内加热溶解,控温65度,加入步骤(2);(4)边搅拌边将消泡剂加入步骤(3),直至搅拌均匀;取样检测
(5)依次将环氧树脂、阻聚剂、二苯甲酮、光引发剂、流平剂、活性胺加入步骤(4);取样检测粘度;
(6)向步骤(5)中加入溶剂,调节粘度合格为止,搅拌6分钟后停机包装。
本发明免打底UV光油的性能检测情况如下表:
检测项目 | 品控指针 |
H-外观 | 1、淡黄色;2、半透明液 |
H-细度 | ≤30μm |
H-粘度 | 40±2s |
H-固化速度及干膜外观 | 干爽、不粘手、无油窝 |
H-涂层外观 | 无油窝、针孔、麻点、桔皮 |
H-光泽 | 光泽差小于3个点 |
H-附着力 | ≤1级 |
M-抗擦花性 | 符合标准 |
本发明提供的免打底UV光油主要具有以下几点优势:(1)UV光油的各项性能优异,与油墨的结合性能优异,具有光泽度高,流平性好,气味小,耐磨性好的特性;(2)具有高附着力、不变黄、耐磨、干燥速度快的特性;(3)本发明UV光油用于UV上光只需一道工序,免去了打底步骤,节约了作业成本,增加了工作效率;(4)具有优良的耐水性,粘结性、韧性及优异的阻燃性能;(5)所述免打底UV的制备方法具有简单、环保等优点。
Claims (4)
1.一种免打底UV光油,其特征在于,所述免打底UV光油,按重量百分比计,包括以下组分:
2.如权利要求1所述的一种免打底UV光油,其特征在于,所述免打底UV光油,按重量百分比计,包括以下组分:
3.如权利要求1所述的一种免打底UV光油,其特征在于,所述光引发剂为1-羟基环己基苯基甲酮。
4.一种如权利要求1-3任一所述的免打底UV光油的制备方法,其特征在于,所述制备方法包括如下步骤:
(1)向二缩三丙二醇二丙烯酸酯中边搅拌边加入热塑性丙烯酸树脂,加完后高速搅拌至热塑性丙烯酸树脂完全溶解;
(2)将三羟甲基丙烷三丙烯酸酯在反应釜内加热溶解,控温50-70度,加入步骤(1);
(3)边搅拌边将消泡剂加入步骤(2),直至搅拌均匀;
(4)依次将环氧树脂、阻聚剂、二苯甲酮、光引发剂、流平剂、活性胺加入步骤(3);
(5)向步骤(4)中加入溶剂,调节粘度合格为止,搅拌3-7分钟后停机包装。