CN106699073A - Waterproof structural steel for building roof - Google Patents
Waterproof structural steel for building roof Download PDFInfo
- Publication number
- CN106699073A CN106699073A CN201611042045.0A CN201611042045A CN106699073A CN 106699073 A CN106699073 A CN 106699073A CN 201611042045 A CN201611042045 A CN 201611042045A CN 106699073 A CN106699073 A CN 106699073A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- steel
- steel body
- oil reservoir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses waterproof structural steel for a building roof. The waterproof structural steel comprises a steel body, wherein the steel body comprises a cement oil layer and bricks located in the cement oil layer; a drainage trough is formed in the left end of the steel body, a connecting layer is arranged in the drainage trough, more than one connecting bar is arranged at the upper end of the connecting layer, the connecting layer comprises an asphalt layer and factice applied to the upper surface of the asphalt layer, two clamp plates are arranged at the lower end of the steel body and fixed with the steel body, and a cross beam is arranged between the clamp plates and fixed with the steel body. The waterproof structural steel for the building roof has the advantages of being simple in structure, convenient to construct and good in waterproofing, and the cement oil layer of the steel has the advantages of being high in hardness, difficult to crack, water-resistant and waterproof.
Description
Technical field
Present invention relates particularly to one kind building roof waterproof construction steel.
Background technology
Steel, is the general designation of the iron-carbon alloy to phosphorus content mass percent between 0.02% to 2.11%.The chemistry of steel
Composition can be so that great changes have taken place, and the steel containing only carbon is referred to as carbon steel(Carbon steel)Or ordinary steel;In actual production, steel is often
Difference according to purposes contains different alloying elements, such as:Manganese, nickel, vanadium etc..Application and research history phase of the mankind to steel
When long, but before the Bessemerizing invention of 19th century, producing for steel is all the inefficient work of a high cost.Such as
The present, steel is turned into the world one of using most materials with its cheap price, reliable performance, be construction industry, manufacturing industry and
Indispensable composition in people's daily life.It may be said that steel is the material base of modern society.Country of the People's Republic of China (PRC)
Standard GB/T 13304-91《Steel is classified》Description:" with iron as essential element, phosphorus content contain other typically below 2%
The material of element." other steel grades generally referred in addition to chromium steel therein, the phosphorus content of part chromium steel allowed more than 2%.It is carbon containing
Ferroalloy of the amount more than 2% is cast iron.In other international standards such as ISO 4948 or EN 10020 to the definition of steel also with it is such
Seemingly, AISI is the malleable stainless steel that various standard level are indicated with three bit digitals.Wherein:1. Austenitic is stainless
The steel numeral sign of 200 and 300 series, for example, some more common austenitic stainless steels be with 201,304,316 and
310 is mark.Strictly speaking, steel is phosphorus content in the 0.0218%-2.11 [iron-carbon alloys between 1%.We are generally by itself and iron
Steel is collectively referred to as, in order to ensure its toughness and plasticity, phosphorus content is usually no more than 1.7%.The essential element of steel is gone back in addition to iron, carbon
There are silicon, manganese, sulphur, phosphorus etc..Other compositions are in order that steel performance is otherwise varied.Hereinafter important steel is alphabetically listed
Material, therefore, regarding to the issue above, it is necessary to propose further solution, the present invention provides a kind of novel high speed steel construction
Material and its preparation technology, a kind of performance of novel high speed steel structure material of the invention are suitable with M42 steel, can be in mould steel
Field replaces import and domestic M42 comprehensively, and tool steel field replaces import M35 and domestic M42 comprehensively.The present invention is solved simultaneously
Traditional M42 steel of having determined need a large amount of Co elements and the interval narrow problem of heat treatment temperature, improve forging and heat treatment life
Lumber recovery in product, Co constituent contents drop to 3% from 8%, i.e., reduces cost while the country of guarantor beneficial to to(for) Precious Metals Resources
Shield.Carbide particle present invention improves over traditional M42 is difficult to the easily thick defect of broken and grain size number, namely has refined crystalline substance
Grain and carbide.
Therefore, existing building roof waterproof construction steel construction complexity, constructional difficulties and waterproof effect are poor at present, build building
Top waterproof construction steel surface is simple cement layer, and its water-impervious and etch-proof effect are small, and hardness is small, easily cracking.
The content of the invention
The technical problem to be solved in the present invention is to provide the good building roof of a kind of simple structure, easy construction and waterproof and prevents
Water-bound steel, and hardness is big, the cement oil reservoir of waterproof not easy to crack and water-fast.
To solve the above problems, the present invention is adopted the following technical scheme that:
One kind building roof waterproof construction steel, including steel body, the steel body are made up of cement oil reservoir and masonry, and the masonry is located at
In cement oil reservoir, the left end of the steel body is provided with rhone, is provided with articulamentum in the rhone, the articulamentum it is upper
End is provided with connection strap, and the connection strap is provided with one or more, and the articulamentum includes bitumen layer and ointment, and the ointment is applied
The upper surface of bitumen layer is put on, the lower end of the steel body is provided with clamping plate, and the clamping plate is mutually fixed with steel body, the clamping plate is set
There are two pieces, crossbeam is provided with the clamping plate, the crossbeam is mutually fixed with steel body.
Further, the cement oil reservoir is made up of the material that following parts by weight are matched, including portland cement 30-50
Part, aluminate cement 30-50 parts, sulfate cement 30-50 parts, latex powder 11-23 parts, water-base resin 20-30 parts, ceramic aggregate
10-16 parts, silicon ash 6-10 parts, asbestos fibre 20-30 parts, water reducer 4-6 parts, early strength agent 4-6 parts, nano oxidized zinc solution 10-
14 parts, 7-9 parts, double thioether 2-4 parts, stabilizer 3-5 parts and water 70-90 parts of propyl benzene emulsion.
Further, the steel body is docking setting, is conducive to steel body 1 that roof is laid on by way of docking, can
Increase operation rate.
Further, set for raised at the docking of the steel body, be conducive to preventing occurring ponding at docking, and then occurred
Infiltration phenomenon.
Further, the connection strap is provided with two, is conducive to preventing steel body to be broken.
Further, the ointment covering steel body, is conducive to improving percolation-proof effect.
Further, the crossbeam is detachable setting, after being conducive to dismantling on crossbeam, steel body directly is fixed on into flooring
On.
A kind of preparation method of cement oil reservoir, comprises the following steps:
1)Take portland cement 30-50 parts, aluminate cement 30-50 parts and sulfate cement 30-50 parts and pour into mixer successively
It is interior so that portland cement, aluminate cement and sulfate cement are well mixed under the high-speed stirred of mixer, mixing is obtained
Cement, it is standby;
2)Take latex powder 11-23 parts, ceramic aggregate 10-16 parts and silicon ash 6-10 parts to pour into mixer, stirred by mixer
Uniformly, filler is obtained, it is standby;
3)By step 2)Obtained filler is ground repeatedly by ball mill, by filling material grinding into 50 mesh powder, it is standby;
4)By step 1)Blended cement and step 3)Obtained filler powder mixing, and water 70-90 parts is added, then by water
Mud mixer stirs into cement oil, standby;
5)Aqueous resin 20-30 parts, water reducer 4-6 parts, early strength agent 4-6 parts, nano oxidized zinc solution 10-14 parts, propyl benzene breast
Liquid 7-9 parts, double thioether 2-4 parts and stabilizer 3-5 parts mixing, and stirred by stirring rod so that above-mentioned material is mutually reciprocal
Should, addition solution is obtained, it is standby;
6)By step 5)Obtained addition solution is added to step 4)In obtained cement oil, asbestos fibre 20-30 is then added
Part, it is again started up cement mixer so that addition solution and cement oil hybrid reaction, cement slurry oil is obtained, it is standby;
7)By step 6)Obtained cement slurry oil uniform application forms cement oil reservoir on masonry, and stands solidification, cement oil reservoir
Surface condenses one layer of glued membrane, standby;
8)Cement oil reservoir is sprayed every six hours so that cement oil reservoir surface keeps moistening, accelerates the solidification of cement oil reservoir,
Obtain final product.
The beneficial effects of the invention are as follows:Due to being provided with steel body, can mutually be fixed with the top in house, due to being provided with water
Mud oil reservoir, can cover masonry, and can play a part of to bond masonry, due to being provided with rhone, can by rain drainage,
Prevent roofing from ponding occur, due to being provided with articulamentum, enable to be sealed at the docking between steel body and steel body, be conducive to preventing
Only seep water, due to being provided with ointment, it is possible to increase the effect of water-impervious, due to being provided with clamping plate, be conducive to steel body with roof phase
It is fixed, meanwhile, cement oil reservoir is made of material of the invention, can be increased hardness, be prevented cracking from improving the effect of water-fast waterproof
Really.
Brief description of the drawings
Fig. 1 is a kind of structural representation for building roof waterproof construction steel of the present invention;
Fig. 2 is a kind of articulamentum structural representation for building roof waterproof construction steel of the present invention.
Specific embodiment
Embodiment one:
Refering to shown in Fig. 1-2, one kind builds roof waterproof construction steel, including steel body 1, and the steel body 1 is by cement oil reservoir 2 and masonry
3 compositions, the masonry 3 is located in cement oil reservoir 2, and the left end of the steel body 1 is provided with rhone 4, the rhone 4 and sets
The upper end for having articulamentum 5, the articulamentum 5 is provided with connection strap 6, and the connection strap 6 is provided with one or more, the articulamentum
5 include bitumen layer 7 and ointment 8, and the ointment 8 is applied to the upper surface of bitumen layer 7, and the lower end of the steel body 1 is provided with clamping plate
9, the clamping plate 9 is mutually fixed with steel body 1, and the clamping plate 9 is provided with two pieces, the clamping plate 9 and is provided with crossbeam 10, the crossbeam
10 mutually fix with steel body 1.
The cement oil reservoir is made up of the material that following parts by weight are matched, including 50 parts of portland cement, aluminic acid salt solution
30 parts of mud, 30 parts of sulfate cement, 11 parts of latex powder, 20 parts of water-base resin, 10 parts of ceramic aggregate, 6 parts of silicon ash, asbestos fibre 20
Part, 4 parts of water reducer, 4 parts of early strength agent, 10 parts of nano oxidized zinc solution, 7 parts of propyl benzene emulsion, 2 parts of double thioether, 3 parts of stabilizer and water
70 parts.
The steel body 1 is set for docking, is conducive to steel body 1 that roof is laid on by way of docking, it is possible to increase utilize
Rate.
Set for raised at the docking of the steel body 1, be conducive to preventing occurring ponding at docking, and then it is existing infiltration occur
As.
The connection strap 6 is provided with two, is conducive to preventing steel body 1 to be broken.
The ointment 8 covers steel body 1, is conducive to improving percolation-proof effect.
The crossbeam 10 is detachable setting, after being conducive to dismantling on crossbeam 10, directly steel body 1 is fixed on flooring.
A kind of preparation method of cement oil reservoir, comprises the following steps:
1)Take 30 parts of 50 parts of portland cement, 30 parts of aluminate cement and sulfate cement to pour into mixer successively so that silicon
Acid salt cement, aluminate cement and sulfate cement are well mixed under the high-speed stirred of mixer, and blended cement is obtained, standby
With;
2)Take 6 parts of 11 parts of latex powder, 10 parts of ceramic aggregate and silicon ash to pour into mixer, stirred by mixer, be obtained
Filler, it is standby;
3)By step 2)Obtained filler is ground repeatedly by ball mill, by filling material grinding into 50 mesh powder, it is standby;
4)By step 1)Blended cement and step 3)Obtained filler powder mixing, and 70 parts of water is added, then by cement
Mixer stirs into cement oil, standby;
5)20 parts of aqueous resin, 4 parts of water reducer, 4 parts of early strength agent, 10 parts of nano oxidized zinc solution, 7 parts of propyl benzene emulsion, double sulphur
The 3 parts of mixing of 2 parts of ether and stabilizer, and stirred by stirring rod so that above-mentioned material reacts to each other, and addition solution is obtained,
It is standby;
6)By step 5)Obtained addition solution is added to step 4)In obtained cement oil, asbestos fibre 20-30 is then added
Part, it is again started up cement mixer so that addition solution and cement oil hybrid reaction, cement slurry oil is obtained, it is standby;
7)By step 6)Obtained cement slurry oil uniform application forms cement oil reservoir on masonry, and stands solidification, cement oil reservoir
Surface condenses one layer of glued membrane, standby;
8)Cement oil reservoir is sprayed every six hours so that cement oil reservoir surface keeps moistening, accelerates the solidification of cement oil reservoir,
Obtain final product.
Embodiment two:
Refering to shown in Fig. 1-2, one kind builds roof waterproof construction steel, including steel body 1, and the steel body 1 is by cement oil reservoir 2 and masonry
3 compositions, the masonry 3 is located in cement oil reservoir 2, and the left end of the steel body 1 is provided with rhone 4, the rhone 4 and sets
The upper end for having articulamentum 5, the articulamentum 5 is provided with connection strap 6, and the connection strap 6 is provided with one or more, the articulamentum
5 include bitumen layer 7 and ointment 8, and the ointment 8 is applied to the upper surface of bitumen layer 7, and the lower end of the steel body 1 is provided with clamping plate
9, the clamping plate 9 is mutually fixed with steel body 1, and the clamping plate 9 is provided with two pieces, the clamping plate 9 and is provided with crossbeam 10, the crossbeam
10 mutually fix with steel body 1.
The cement oil reservoir is made up of the material that following parts by weight are matched, including portland cement 30-50 parts, aluminate
30 parts of cement, 50 parts of sulfate cement, 23 parts of latex powder, 30 parts of water-base resin, 16 parts of ceramic aggregate, 10 parts of silicon ash, asbestos are fine
30 parts of dimension, 6 parts of water reducer, 6 parts of early strength agent, 14 parts of nano oxidized zinc solution, 9 parts of propyl benzene emulsion, 4 parts of double thioether, 5 parts of stabilizer
With 90 parts of water.
The steel body 1 is set for docking, is conducive to steel body 1 that roof is laid on by way of docking, it is possible to increase utilize
Rate.
Set for raised at the docking of the steel body 1, be conducive to preventing occurring ponding at docking, and then it is existing infiltration occur
As.
The connection strap 6 is provided with two, is conducive to preventing steel body 1 to be broken.
The ointment 8 covers steel body 1, is conducive to improving percolation-proof effect.
The crossbeam 10 is detachable setting, after being conducive to dismantling on crossbeam 10, directly steel body 1 is fixed on flooring.
A kind of preparation method of cement oil reservoir, comprises the following steps:
1)Take 50 parts of 30 parts of portland cement, 50 parts of aluminate cement and sulfate cement to pour into mixer successively so that silicon
Acid salt cement, aluminate cement and sulfate cement are well mixed under the high-speed stirred of mixer, and blended cement is obtained, standby
With;
2)Take 10 parts of 23 parts of latex powder, 16 parts of ceramic aggregate and silicon ash to pour into mixer, stirred by mixer, be obtained
Filler, it is standby;
3)By step 2)Obtained filler is ground repeatedly by ball mill, by filling material grinding into 50 mesh powder, it is standby;
4)By step 1)Blended cement and step 3)Obtained filler powder mixing, and water 70-90 parts is added, then by water
Mud mixer stirs into cement oil, standby;
5)30 parts of aqueous resin, 6 parts of water reducer, 6 parts of early strength agent, 14 parts of nano oxidized zinc solution, 9 parts of propyl benzene emulsion, double sulphur
The 5 parts of mixing of 4 parts of ether and stabilizer, and stirred by stirring rod so that above-mentioned material reacts to each other, and addition solution is obtained,
It is standby;
6)By step 5)Obtained addition solution is added to step 4)In obtained cement oil, asbestos fibre 20-30 is then added
Part, it is again started up cement mixer so that addition solution and cement oil hybrid reaction, cement slurry oil is obtained, it is standby;
7)By step 6)Obtained cement slurry oil uniform application forms cement oil reservoir on masonry, and stands solidification, cement oil reservoir
Surface condenses one layer of glued membrane, standby;
8)Cement oil reservoir is sprayed every six hours so that cement oil reservoir surface keeps moistening, accelerates the solidification of cement oil reservoir,
Obtain final product.
Embodiment three:
Refering to shown in Fig. 1-2, one kind builds roof waterproof construction steel, including steel body 1, and the steel body 1 is by cement oil reservoir 2 and masonry
3 compositions, the masonry 3 is located in cement oil reservoir 2, and the left end of the steel body 1 is provided with rhone 4, the rhone 4 and sets
The upper end for having articulamentum 5, the articulamentum 5 is provided with connection strap 6, and the connection strap 6 is provided with one or more, the articulamentum
5 include bitumen layer 7 and ointment 8, and the ointment 8 is applied to the upper surface of bitumen layer 7, and the lower end of the steel body 1 is provided with clamping plate
9, the clamping plate 9 is mutually fixed with steel body 1, and the clamping plate 9 is provided with two pieces, the clamping plate 9 and is provided with crossbeam 10, the crossbeam
10 mutually fix with steel body 1.
The cement oil reservoir is made up of the material that following parts by weight are matched, including 40 parts of portland cement, aluminic acid salt solution
40 parts of mud, 40 parts of sulfate cement, 17 parts of latex powder, 25 parts of water-base resin, 13 parts of ceramic aggregate, 8 parts of silicon ash, asbestos fibre 25
Part, 5 parts of water reducer, 5 parts of early strength agent, 12 parts of nano oxidized zinc solution, 8 parts of propyl benzene emulsion, 3 parts of double thioether, 4 parts of stabilizer and water
80 parts.
The steel body 1 is set for docking, is conducive to steel body 1 that roof is laid on by way of docking, it is possible to increase utilize
Rate.
Set for raised at the docking of the steel body 1, be conducive to preventing occurring ponding at docking, and then it is existing infiltration occur
As.
The connection strap 6 is provided with two, is conducive to preventing steel body 1 to be broken.
The ointment 8 covers steel body 1, is conducive to improving percolation-proof effect.
The crossbeam 10 is detachable setting, after being conducive to dismantling on crossbeam 10, directly steel body 1 is fixed on flooring.
A kind of preparation method of cement oil reservoir, comprises the following steps:
1)Take 40 parts of 40 parts of portland cement, 40 parts of aluminate cement and sulfate cement to pour into mixer successively so that silicon
Acid salt cement, aluminate cement and sulfate cement are well mixed under the high-speed stirred of mixer, and blended cement is obtained, standby
With;
2)Take 8 parts of 17 parts of latex powder, 13 parts of ceramic aggregate and silicon ash to pour into mixer, stirred by mixer, be obtained
Filler, it is standby;
3)By step 2)Obtained filler is ground repeatedly by ball mill, by filling material grinding into 50 mesh powder, it is standby;
4)By step 1)Blended cement and step 3)Obtained filler powder mixing, and 80 parts of water is added, then by cement
Mixer stirs into cement oil, standby;
5)25 parts of aqueous resin, 5 parts of water reducer, 5 parts of early strength agent, 12 parts of nano oxidized zinc solution, 8 parts of propyl benzene emulsion, double sulphur
The 4 parts of mixing of 3 parts of ether and stabilizer, and stirred by stirring rod so that above-mentioned material reacts to each other, and addition solution is obtained,
It is standby;
6)By step 5)Obtained addition solution is added to step 4)In obtained cement oil, asbestos fibre 20-30 is then added
Part, it is again started up cement mixer so that addition solution and cement oil hybrid reaction, cement slurry oil is obtained, it is standby;
7)By step 6)Obtained cement slurry oil uniform application forms cement oil reservoir on masonry, and stands solidification, cement oil reservoir
Surface condenses one layer of glued membrane, standby;
8)Cement oil reservoir is sprayed every six hours so that cement oil reservoir surface keeps moistening, accelerates the solidification of cement oil reservoir,
Obtain final product.
Experimental example:
Choosing common has cement oil reservoir and special cement oil reservoir compared with cement oil reservoir of the invention, and according to weather-proof effect
Really, waterproof effect and hardness foundation as a comparison, analyzes three groups of situations of cement polystyrene board, and draw best cement and polystyrene
Plate.
It is control group two and of the invention by control group one, special glue-line cement plate of the common cement plate for having a glue-line
Cement polystyrene board is control group three, and specific data are as shown in the table:
Three groups of materials are contrasted, cement oil reservoir effect of the invention is obtained preferably, be there is good weatherability compared with two groups of control groups, prevented
The advantage that water effect is good and hardness is big.
The beneficial effects of the invention are as follows:Due to being provided with steel body, can mutually be fixed with the top in house, due to being provided with water
Mud oil reservoir, can cover masonry, and can play a part of to bond masonry, due to being provided with rhone, can by rain drainage,
Prevent roofing from ponding occur, due to being provided with articulamentum, enable to be sealed at the docking between steel body and steel body, be conducive to preventing
Only seep water, due to being provided with ointment, it is possible to increase the effect of water-impervious, due to being provided with clamping plate, be conducive to steel body with roof phase
It is fixed, meanwhile, cement oil reservoir is made of material of the invention, can be increased hardness, be prevented cracking from improving the effect of water-fast waterproof
Really.
The above, specific embodiment only of the invention, but protection scope of the present invention is not limited thereto, and it is any
The change or replacement expected without creative work, should all cover and be defined in the scope of the present invention.
Claims (7)
- It is 1. a kind of to build roof waterproof construction steel, it is characterised in that:Including steel body, the steel body is by cement oil reservoir and masonry group Into the masonry is located in cement oil reservoir, and the left end of the steel body is provided with rhone, and connection is provided with the rhone Layer, the upper end of the articulamentum is provided with connection strap, and the connection strap is provided with one or more, and the articulamentum includes bitumen layer And ointment, the balm daubing is provided with clamping plate, the clamping plate and steel body phase in the upper surface of bitumen layer, the lower end of the steel body Fixed, the clamping plate is provided with two pieces, crossbeam is provided with the clamping plate, and the crossbeam is mutually fixed with steel body.
- It is 2. as claimed in claim 2 to build roof waterproof construction steel, it is characterised in that:The cement oil reservoir is by following weight portion The material of number proportioning is made, including portland cement 30-50 parts, aluminate cement 30-50 parts, sulfate cement 30-50 parts, breast Rubber powder 11-23 parts, water-base resin 20-30 parts, ceramic aggregate 10-16 parts, silicon ash 6-10 parts, asbestos fibre 20-30 parts, water reducer 4-6 parts, early strength agent 4-6 parts, nano oxidized zinc solution 10-14 parts, 7-9 parts, double thioether 2-4 parts, stabilizer 3-5 parts of propyl benzene emulsion With water 70-90 parts.
- It is 3. as claimed in claim 3 to build roof waterproof construction steel, it is characterised in that:The steel body is set for docking.
- It is 4. as claimed in claim 4 to build roof waterproof construction steel, it is characterised in that:For projection sets at the docking of the steel body Put.
- It is 5. as claimed in claim 5 to build roof waterproof construction steel, it is characterised in that:The connection strap is provided with two.
- It is 6. as claimed in claim 6 to build roof waterproof construction steel, it is characterised in that:The ointment covers steel body.
- It is 7. as claimed in claim 7 to build roof waterproof construction steel, it is characterised in that:The crossbeam is detachable setting.