CN106698942A - Painted pottery glaze - Google Patents
Painted pottery glaze Download PDFInfo
- Publication number
- CN106698942A CN106698942A CN201611158095.5A CN201611158095A CN106698942A CN 106698942 A CN106698942 A CN 106698942A CN 201611158095 A CN201611158095 A CN 201611158095A CN 106698942 A CN106698942 A CN 106698942A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- painted pottery
- quartz
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses painted pottery glaze. The glaze is prepared from, by weight, 30-50 parts of kaolin, 20-30 parts of quartz, 1-5 parts of zinc oxide, 1-5 parts of stearic acid and 1-2 parts of white carbon black. Compared with the traditional technology, the color of the glaze is quaint and soft, the binding force between the glaze and potteries is high, and the glaze is attractive and has a protective effect.
Description
Technical field
The invention belongs to electrothermal dark-red pottery field, and in particular to a kind of ancient painted pottery glaze.
Background technology
Early in away from modern 7,000 years or so half way up the mountain culture period, earliest colored drawing is just occurred in that on pottery.And make condition on porcelain
Tension force is had more to hard copy, artistical various creative ideas, style, language have been merged in ancient painted pottery art, create different style
And a colourful gem of art, it is the rare culture rarity of China.The glaze that traditional ancient painted pottery is used is more dull,
And because ancient painted pottery surface may not enough fully by being combined with glaze after engraving, the influence later stage fires.
The content of the invention
Goal of the invention：The purpose of the present invention is to solve the shortcomings of the prior art, there is provided a kind of ancient painted pottery glaze.
Technical scheme：In order to reach foregoing invention purpose, the present invention is specifically achieved like this：A kind of ancient painted pottery glaze, bag
Include the component of following parts by weight：30 ~ 50 parts of kaolin, 20 ~ 30 parts of quartz, 1 ~ 5 part of zinc oxide, 1 ~ 5 part of tristearin
Acid, 1 ~ 2 part of white carbon.
Wherein, the fineness of each raw material is respectively less than 100 mesh.
A kind of preferred scheme, is made up of the component of following parts by weight：40 parts of kaolin, 20 parts of quartz, 4 parts
Zinc oxide, 3 parts of stearic acid, 1 part of white carbon.
Beneficial effect：The present invention is compared with conventional art, and glaze colours is simple and unsophisticated soft, strong with pottery adhesion, not only attractive in appearance but also tool
There is protecting effect.
Specific embodiment
Embodiment 1：
A kind of ancient painted pottery glaze, is made up of the component of following parts by weight：30 parts of kaolin, 20 parts of quartz, 1 part of zinc oxide,
1 part of stearic acid, 1 part of white carbon.
Embodiment 2：
A kind of ancient painted pottery glaze, is made up of the component of following parts by weight：50 parts of kaolin, 30 parts of quartz, 5 parts of oxidation
Zinc, 5 parts of stearic acid, 2 parts of white carbon.
Embodiment 3：
A kind of ancient painted pottery glaze, is made up of the component of following parts by weight：40 parts of kaolin, 25 parts of quartz, 4 parts of zinc oxide,
3 parts of stearic acid, 2 parts of white carbon.
Embodiment 4：
A kind of ancient painted pottery glaze, is made up of the component of following parts by weight：The quartz of 35 parts of 28 parts of kaolin, 3 parts of zinc oxide, 2
The stearic acid of part, 1 part of white carbon.
Claims (3)
1. a kind of ancient painted pottery glaze, it is characterised in that the component including following parts by weight：30 ~ 50 parts of kaolin, 20 ~ 30 parts
Quartz, 1 ~ 5 part of zinc oxide, 1 ~ 5 part of stearic acid, 1 ~ 2 part of white carbon.
2. equal bristol glaze according to claim 1, it is characterised in that the fineness of each raw material is respectively less than 100 mesh.
3. ancient painted pottery glaze according to claim 1, it is characterised in that be made up of the component of following parts by weight：40 parts of height
Age soil, 20 parts of quartz, 4 parts of zinc oxide, 3 parts of stearic acid, 1 part of white carbon.