CN106696433A - Method for making noble metal paper part - Google Patents
Method for making noble metal paper part Download PDFInfo
- Publication number
- CN106696433A CN106696433A CN201510780390.3A CN201510780390A CN106696433A CN 106696433 A CN106696433 A CN 106696433A CN 201510780390 A CN201510780390 A CN 201510780390A CN 106696433 A CN106696433 A CN 106696433A
- Authority
- CN
- China
- Prior art keywords
- paper
- noble metal
- thin slice
- part preparation
- method made
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a method for making a noble metal paper part. The method comprises the following steps: a noble metal preliminary processing step used for making a noble metal blank material into slices with patterns; and a bonding step for attaching the noble metal slices to a paper part as a substrate by an adhesive. The noble metal preliminary processing step comprises the following steps: rolling the noble metal blank material into the slices with the thickness of 5 microns to 0.5 mm; using a cutting punching machine to cut and punch the rolled slices into a preset shape; and carving out the set patterns on the cut and punched slices. Compared with the prior art, the beneficial effect are that: the paper part as the substrate is attached with the noble metal slices, the process is simple and easy to implement, the cost is not high, the combining application range of the paper part and the noble metal is improved, and collection value and practicability of the paper part are improved.
Description
Technical field
The present invention relates to application of the noble metal on part made of paper, more particularly to a kind of noble metal part system made of paper
Make method.
Background technology
Common part made of paper has stamp, greeting card, stamp folder and mail cover etc..In the market these are made of paper
Part is generally paper substrates, and noble metal impressing product can only also be realized being imprinted in the aspect of noble metal,
Noble metal of being fitted on the basis of paper substrates can not be realized, part made of paper is limited and is led in noble metal application
The application in domain.
The content of the invention
It is an object of the invention to overcome the defect of prior art, and provide a kind of noble metal part made of paper
Preparation method, to improve the connected applications scope of part made of paper and noble metal.
To achieve the above object, the present invention uses following technical scheme:
A kind of noble metal part preparation method made of paper is comprised the following steps:
Noble metal preliminary working step, for noble metal blank to be made with figuratum thin slice;
Laminating step, the paper for noble metal thin slice to be fitted in substrate by adhesive.
Further, noble metal preliminary working step includes:
Noble metal blank is rolled into the thin slice that thickness is 5 microns to 0.5 millimeter;
Using cutting the thin slice punching that will roll of punch press into the shape for setting;
The pattern for setting is carved out on the good thin slice of punching.
Further, in noble metal preliminary working step, the engraving to thin slice uses laser holographic relief
Machine is carried out.
Further, laminating step includes:
Paper is placed on punching block, and by adhesive spots in paper;
Thin slice is placed in one side of the paper with adhesive, thin slice is entered with paper with hot melt hydraulic press
Row hot pressing is fitted.
Further, in laminating step, hot melt hydraulic press is 300t to the pressure that thin slice and paper apply
To 3500t.
Further, in laminating step, hot melt hydraulic press carries out the temperature of hot pressing to thin slice and paper
It is 120 DEG C.
Further, in laminating step, hot melt hydraulic press carries out the time of hot pressing to thin slice and paper
It is 30 seconds.
Further, adhesive is environment-friendly resin adhesive.
Further, part made of paper is stamp dedicated paper, greeting card dedicated paper, stamp folder dedicated paper or mail cover
Dedicated paper.
Further, the noble metal for using is gold, platinum, porpezite or silver.
Compared with the prior art, the invention has the advantages that:The present invention is realized using part made of paper as base
Bottom, noble metal thin slice in laminating, process is simple is easily realized, and cost is not high, improves part made of paper
With the connected applications scope of noble metal, the reserve value and practicality of part made of paper are also improved.
Specific embodiment
In order to more fully understand technology contents of the invention, with reference to specific embodiment to of the invention
Technical scheme is described further and illustrates.
In the noble metal part preparation method made of paper of the embodiment of the present invention, noble metal is gold, and part made of paper is
Stamp dedicated paper.In other embodiments, noble metal can also be platinum, porpezite or silver, paper
Product can also be greeting card dedicated paper, stamp folder dedicated paper or mail cover dedicated paper.
Noble metal part preparation method made of paper is comprised the following steps:
Noble metal preliminary working step, for noble metal blank to be made with figuratum thin slice;
Laminating step, the paper for noble metal thin slice to be fitted in substrate by adhesive.
Wherein, noble metal preliminary working step, laminating step are successively carried out successively.
Specifically, noble metal preliminary working step includes:
Noble metal blank is rolled into the thin slice that thickness is 5 microns to 0.5 millimeter using flaking machine;
Using cutting the thin slice punching that will roll of punch press into the shape for setting;
The pattern for setting is carved out on the good thin slice of punching.
Three steps in noble metal preliminary working step are that order is performed successively.
In noble metal preliminary working step, the engraving to thin slice is carried out using laser holographic relief machine.
Specifically, laminating step includes:
Paper is placed on punching block, and by adhesive spots in paper, adhesive is viscous for environment-friendly resin
Mixture;
Thin slice is placed in one side of the paper with adhesive, thin slice is entered with paper with hot melt hydraulic press
Row hot pressing is fitted.
In laminating step, hot melt hydraulic press is 300t to 3500t to the pressure that thin slice and paper apply.
Depending on the pressure of applying is needed according to the thickness of thin slice, thin slice, can be with a little bit smaller in itself than relatively thin
Pressure, and thin slice is thicker, can use bigger pressure.
In laminating step, the temperature that hot melt hydraulic press carries out hot pressing to thin slice and paper is 120 DEG C.
In laminating step, the time that hot melt hydraulic press carries out hot pressing to thin slice and paper is 30 seconds.
It is set forth above that technology contents of the invention are only further illustrated with embodiment, in order to reader more
It is readily appreciated that, but does not represent embodiments of the present invention and is only limitted to this, any skill done according to the present invention
Art extends or recreates, by protection of the invention.
Claims (10)
1. a kind of noble metal part preparation method made of paper, it is characterised in that it is comprised the following steps:
Noble metal preliminary working step, for noble metal blank to be made with figuratum thin slice;
Laminating step, the paper for noble metal thin slice to be fitted in substrate by adhesive.
2. noble metal as claimed in claim 1 part preparation method made of paper, it is characterised in that described expensive
Metal preliminary working step includes:
Noble metal blank is rolled into the thin slice that thickness is 5 microns to 0.5 millimeter;
Using cutting the thin slice punching that will roll of punch press into the shape for setting;
The pattern for setting is carved out on the good thin slice of punching.
3. noble metal as claimed in claim 2 part preparation method made of paper, it is characterised in that described
In noble metal preliminary working step, the engraving to thin slice is carried out using laser holographic relief machine.
4. noble metal as claimed in claim 1 part preparation method made of paper, it is characterised in that the patch
Closing step includes:
Paper is placed on punching block, and by adhesive spots in paper;
Thin slice is placed in one side of the paper with adhesive, thin slice is entered with paper with hot melt hydraulic press
Row hot pressing is fitted.
5. noble metal as claimed in claim 4 part preparation method made of paper, it is characterised in that described
In laminating step, hot melt hydraulic press is 300t to 3500t to the pressure that thin slice and paper apply.
6. noble metal as claimed in claim 4 part preparation method made of paper, it is characterised in that described
In laminating step, the temperature that hot melt hydraulic press carries out hot pressing to thin slice and paper is 120 DEG C.
7. noble metal as claimed in claim 4 part preparation method made of paper, it is characterised in that described
In laminating step, the time that hot melt hydraulic press carries out hot pressing to thin slice and paper is 30 seconds.
8. noble metal as claimed in claim 4 part preparation method made of paper, it is characterised in that described viscous
Mixture is environment-friendly resin adhesive.
9. the noble metal part preparation method made of paper as described in any one of claim 1 to 8, it is characterised in that
The part made of paper is stamp dedicated paper, greeting card dedicated paper, stamp folder dedicated paper or mail cover dedicated paper.
10. the noble metal part preparation method made of paper as described in any one of claim 1 to 8, its feature exists
In the noble metal for using is gold, platinum, porpezite or silver.