CN106675795A - Cleaning agent for removing residual film glue from car glass and preparation method of cleaning agent - Google Patents
Cleaning agent for removing residual film glue from car glass and preparation method of cleaning agent Download PDFInfo
- Publication number
- CN106675795A CN106675795A CN201611110900.7A CN201611110900A CN106675795A CN 106675795 A CN106675795 A CN 106675795A CN 201611110900 A CN201611110900 A CN 201611110900A CN 106675795 A CN106675795 A CN 106675795A
- Authority
- CN
- China
- Prior art keywords
- parts
- cleaning agent
- cull
- pad pasting
- vehicle glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of technical production of cleaning agents, and discloses a cleaning agent for removing residual film glue from car glass. The cleaning agent comprises the following components in parts by weight: 200-300 parts of isopropanol, 0.5-2 parts of sodium dodecyl sulfate, 5-15 parts of ethylene glycol n-butyl ether, 1-10 parts of acetic acid, 30-50 parts of hydrochloric acid and 600-700 parts of deionized water. The preparation method of the cleaning agent comprises the following steps: sequentially adding isopropanol, acetic acid, hydrochloric acid and the deionized water in parts by weight into a stirrer, mixing for 10-20min by stirring, then proportionally adding sodium dodecyl sulfate and ethylene glycol n-butyl ether, further mixing for 15-30min by stirring, and performing standing to obtain the cleaning agent for removing the residual film glue from car glass. The cleaning agent adopts a neutral organic solvent formula, can quickly clean the residual film glue on the car glass, can quicken the glue removing speed, and is small in car glass corrosion, low in using cost and mild in reaction conditions.
Description
Technical field
The present invention relates to cleaning agent production technical field, more particularly to a kind of cleaning agent for removing vehicle glass pad pasting cull
And preparation method thereof.
Background technology
As living standards of the people are improved, automobile becomes many people for the vehicles ridden instead of walk.For new car, paint
Face is more tender and lovely, is easily scratched, lacquer painting easily aging loss of gloss, and for in-use automotive, due to the irradiation of chronic sun ultraviolet,
Wind, sand, rain etc. corrode, and car washing liquid inferior, polishing maintenance lack of standardization, lacquer painting are scratched etc., can all make lacquer painting continue aging loss of gloss, firmly
Degree and brightness decline, and affect car body attractive in appearance.Therefore people can be to liking that car carries out pad pasting protection.When needing to change pad pasting, have
The cull of pad pasting is retained on vehicle glass, needs to remove cull.Existing cleaning method mainly passes through acid and alkali corrosion by automobile
Packaging plastic on glass is removed, and is not only difficult to remove totally, and this kind of chemical reagent also will be right while packaging plastic is removed
Glass structure produces corrosion, therefore life-time service can cause vehicle glass to be damaged, and the conventional detergents of vehicle glass at present, it is main
Dust, oil stain, animal wastes for being used for away on glass etc., it is poor for the removal ability of pad pasting cull, it would therefore be highly desirable to need
A kind of cleaning agent for removing vehicle glass pad pasting cull of exploitation.
The content of the invention
The technical problem to be solved in the present invention is to overcome drawbacks described above, there is provided a kind of removal vehicle glass pad pasting cull it is clear
Clean dose and preparation method thereof.
The purpose of the present invention is achieved through the following technical solutions:
The first object of the present invention is to provide a kind of cleaning agent for removing vehicle glass pad pasting cull, in parts by weight,
Including following component:200~300 parts of isopropanol, 0.5~2 part of dodecyl sodium sulfate, 5~15 parts of ethylene glycol n-butyl ether, acetic acid
1~10 part, 30~50 parts of hydrochloric acid, 600~700 parts of deionized water.
Preferably, the cleaning agent in parts by weight, including following component:250~300 parts of isopropanol, dodecyl sulphur
0.5~1.5 part of sour sodium, 5~10 parts of ethylene glycol n-butyl ether, 5~10 parts of acetic acid, 30~40 parts of hydrochloric acid, deionized water 650~700
Part.
Preferably, the cleaning agent in parts by weight, including following component:260 parts of isopropanol, dodecyl sodium sulfate
0.8 part, 8 parts of ethylene glycol n-butyl ether, 5 parts of acetic acid, 40 parts of hydrochloric acid, 680 parts of deionized water.
Preferably, the cleaning agent in parts by weight, including following component:260 parts of isopropanol, dodecyl sodium sulfate
0.7 part, 8 parts of ethylene glycol n-butyl ether, 5 parts of acetic acid, 40 parts of hydrochloric acid, 700 parts of deionized water.
Preferably, the volume fraction of acetic acid described above is 20~30%.
The second object of the present invention is to provide a kind of preparation side for removing the cleaning agent of vehicle glass pad pasting cull
Method, comprises the steps:Isopropanol, acetic acid, hydrochloric acid, deionized water are sequentially placed in agitator according to weight proportion are mixed,
Stirring mixing 10~20min, then be proportionally added into dodecyl sodium sulfate, ethylene glycol n-butyl ether continue stir mixing 15~
30min, stands and the cleaning agent for removing vehicle glass pad pasting cull is obtained.
Preferably, the mixing speed is 300~1000rpm.
Preferably, the whipping temp is 20~30 DEG C.
Compared with prior art the invention has the beneficial effects as follows:
1st, cleaning agent of the present invention be neutral organic solvent formula, can with the pad pasting cull on Rapid Cleaning vehicle glass, plus
Speed is removed photoresist speed, and the corrosion to vehicle glass is little, and use cost is low, and reaction condition is gentle.
2nd, cleaning agent of the present invention can be used in combination with simple glass cleaning agent, first remove glass of automobile with cleaning agent of the present invention
Cull on glass, then cleans with Common detergents again glass, the cleaning speed of vehicle glass is improved, while cleaning can be reduced
The usage amount of agent, reduces cost.
3rd, rationally, environmental protection is free from environmental pollution without harmful material, has for present invention cleaning agent prescription
Good spatter property.
Specific embodiment
The specific embodiment of the present invention is described further below.Here is it should be noted that for these enforcements
The explanation of mode is used to help understand the present invention, but does not constitute limitation of the invention.Additionally, invention described below
As long as involved technical characteristic does not constitute each other conflict and just can be mutually combined in each embodiment.
Embodiment 1
The weight portion of isopropanol 200, the weight portion of acetic acid 8, the weight portion of hydrochloric acid 30, the weight portion of deionized water 650 are sequentially placed into
Mixing in agitator, stirring mixing 10min, then it is proportionally added into the weight portion of dodecyl sodium sulfate 0.5, ethylene glycol n-butyl ether 5
Weight portion continues to stir mixing 30min, stands and the cleaning agent for removing vehicle glass pad pasting cull is obtained.
Embodiment 2
The weight portion of isopropanol 260, the weight portion of acetic acid 5, the weight portion of hydrochloric acid 40, the weight portion of deionized water 680 are sequentially placed into
Mixing in agitator, stirring mixing 10min, then it is proportionally added into the weight portion of dodecyl sodium sulfate 0.8, ethylene glycol n-butyl ether 8
Weight portion continues to stir mixing 30min, stands and the cleaning agent for removing vehicle glass pad pasting cull is obtained.
Embodiment 3
The weight portion of isopropanol 260, the weight portion of acetic acid 5, the weight portion of hydrochloric acid 40, the weight portion of deionized water 700 are sequentially placed into
Mixing in agitator, stirring mixing 15min, then it is proportionally added into the weight portion of dodecyl sodium sulfate 0.7, ethylene glycol n-butyl ether 8
Weight portion continues to stir mixing 25min, stands and the cleaning agent for removing vehicle glass pad pasting cull is obtained.
Embodiment 4
The weight portion of isopropanol 300, the weight portion of acetic acid 10, the weight portion of hydrochloric acid 30, the weight portion of deionized water 686 are sequentially placed into
Mixing in agitator, stirring mixing 20min, then it is proportionally added into the weight portion of dodecyl sodium sulfate 1.5, ethylene glycol n-butyl ether 10
Weight portion continues to stir mixing 15min, stands and the cleaning agent for removing vehicle glass pad pasting cull is obtained.
Test effect
The abluent of table 1 removes packaging plastic effect assessment table
Evaluating | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 |
Remove photoresist degree | More than 99.9% | More than 99.9% | More than 99.9% | More than 99.9% |
Glass corrosion degree | Corrosion-free point | Corrosion-free point | Corrosion-free point | Corrosion-free point |
Result of the test shows that the cleaning agent of embodiment of the present invention 1-4 can completely remove vehicle glass cull, remove speed
Hurry up, efficiency high, and cleaning agent is to the completely no corrosiveness of vehicle glass.
Ultimate principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel it should be appreciated that the present invention is not restricted to the described embodiments, the simply explanation described in above-described embodiment and description this
The principle of invention, of the invention without departing from the spirit and scope of the present invention also to have various changes and modifications, these changes
Change and improvement is both fallen within scope of the claimed invention.The claimed scope of the invention by appending claims and its
Equivalent is defined.
Claims (8)
1. a kind of cleaning agent for removing vehicle glass pad pasting cull, it is characterised in that:In parts by weight, including following component:It is different
200~300 parts of propanol, 0.5~2 part of dodecyl sodium sulfate, 5~15 parts of ethylene glycol n-butyl ether, 1~10 part of acetic acid, hydrochloric acid 30
~50 parts, 600~700 parts of deionized water.
2. the cleaning agent for removing vehicle glass pad pasting cull according to claim 1, it is characterised in that:In parts by weight,
Including following component:250~300 parts of isopropanol, 0.5~1.5 part of dodecyl sodium sulfate, 5~10 parts of ethylene glycol n-butyl ether, second
5~10 parts of acid, 30~40 parts of hydrochloric acid, 650~700 parts of deionized water.
3. the cleaning agent for removing vehicle glass pad pasting cull according to claim 1, it is characterised in that:In parts by weight,
Including following component:260 parts of isopropanol, 0.8 part of dodecyl sodium sulfate, 8 parts of ethylene glycol n-butyl ether, 5 parts of acetic acid, hydrochloric acid 40
Part, 680 parts of deionized water.
4. the cleaning agent for removing vehicle glass pad pasting cull according to claim 1, it is characterised in that:In parts by weight,
Including following component:260 parts of isopropanol, 0.7 part of dodecyl sodium sulfate, 8 parts of ethylene glycol n-butyl ether, 5 parts of acetic acid, hydrochloric acid 40
Part, 700 parts of deionized water.
5. the cleaning agent of the removal vehicle glass pad pasting cull according to any one of claim 1-4, it is characterised in that:It is described
The volume fraction of acetic acid is 20~30%.
6. the preparation method of the cleaning agent of the removal vehicle glass pad pasting cull described in a kind of any one of claim 1-4, it is special
Levy and be:Comprise the steps:Isopropanol, acetic acid, hydrochloric acid, deionized water are sequentially placed in agitator according to weight proportion are mixed
Close, stirring mixing 10~20min, then be proportionally added into dodecyl sodium sulfate, ethylene glycol n-butyl ether continue stir mixing 15~
30min, stands and the cleaning agent for removing vehicle glass pad pasting cull is obtained.
7. it is according to claim 6 remove vehicle glass pad pasting cull cleaning agent preparation method, it is characterised in that:Institute
Mixing speed is stated for 300~1000rpm.
8. it is according to claim 6 remove vehicle glass pad pasting cull cleaning agent preparation method, it is characterised in that:Institute
Whipping temp is stated for 20~30 DEG C.