CN106675256A - Antibacterial paint - Google Patents
Antibacterial paint Download PDFInfo
- Publication number
- CN106675256A CN106675256A CN201611119379.3A CN201611119379A CN106675256A CN 106675256 A CN106675256 A CN 106675256A CN 201611119379 A CN201611119379 A CN 201611119379A CN 106675256 A CN106675256 A CN 106675256A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixed material
- paint
- antibiotic paint
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antibacterial paint and a preparation method thereof, belonging to the field of building raw materials. The antibacterial paint is prepared from an acrylic polylol emulsion, a polyurethane emulsion, a sodium carboxymethyl cellulose solution, titanium white, a sulfonate defoaming agent, a thickener, a film former and deionized water. The antioxidation paint is prepared by the following steps: mixing, dispersing, heating, reacting and standing. The antioxidation paint has the advantages of accessible raw material sources and simple preparation method, and is a novel paint product.
Description
Technical field
The invention belongs to building material field, and in particular to a kind of antibiotic paint and preparation method thereof.
Background technology
Coating is to be coated in be protected or decorated body surface, and can form the continuous thin of firm attachment with coated article
Film, generally based on resin, oily, emulsion form, can add the auxiliary agents such as pigment, filler, be commonly divided into water paint and oiliness
Coating.Coating belongs to fine chemical product, with multiple efficacies such as decoration, anti-corrosion and waterproofs, is widely used in building decoration work
Journey.
Water paint as species important in coating, with extensive market range of application.Every use water as solvent or
Person makees the coating of disperse medium, all can be described as water paint.Water paint includes water soluble paint, water-reducible coating, moisture
Scattered property coating（Latex paint）3 kinds.Water soluble paint is with water-soluble resin as film forming matter, with polyvinyl alcohol and its various modified
Thing is representative, in addition also water-soluble alkyd resin, water-soluble epoxy resin and inorganic polymer water-base resin etc..Water paint
Coating without organic solvent, without toxic heavy metals such as benzene,toluene,xylene, formaldehyde, free TDIs, has no irritating odor,
And have that paint film is plentiful, smooth, various colors, it is durable, environmentally friendly many advantages, such as.With the enforcement of environmental protection policy, consumer's ring
The continuous lifting of consciousness is protected, provinces and cities especially in all parts of the country have put into effect VOC emission limit standard, encourage using non-solvent coating,
The undoubtedly development to environmental protection coating materials such as water paints brings opportunity.
As the range of application of coating type gradually increases, the coating with difference in functionality there is also large market and need
Ask.Sapecial coating refers to the new coating for having essential distinction with traditional coating, and different sapecial coatings have different qualities.It is anti-
Bacterium coating is exactly the one kind in sapecial coating.Antibiotic paint has biocidal efficacies, can protect coated thing breed bacteria, while
Also the service life of coating is extended accordingly.
The content of the invention
It is an object of the invention to provide a kind of antibiotic paint, to lift the antibiotic property of coating.
In order to solve above technical problem, the present invention is employed the following technical solutions：A kind of antibiotic paint, with weight portion as list
Position, comprising following raw material：300 ~ 600 parts of acrylic polyol emulsion, 150 ~ 350 parts of polyaminoester emulsion, sodium carboxymethyl cellulose
35 ~ 105 parts of solution, 15 ~ 45 parts of titanium dioxide, 10 ~ 20 parts of Sulfonateses defoamer, 8 ~ 24 parts of thickening agent, 11 ~ 30 parts of film former,
120 ~ 280 parts of deionized water.
The present invention also provides a kind of preparation method of antibiotic paint, comprises the following steps：
S1：Will be deionized water, Sulfonateses defoamer, acrylic polyol emulsion, polyaminoester emulsion, sodium carboxymethyl cellulose molten
Liquid sequentially adds dispersion cylinder uniform stirring；
S2：Titanium dioxide, thickening agent, film former are sequentially added into mixed material uniform stirring obtained by step S1；
S3：Stirring reaction after mixed material obtained by step S2 is heated up；
S4：After mixed material obtained by step S3 stands, that is, antibiotic paint is obtained.
Preferably, in step S1, the mixing time of mixed material is 15 ~ 30min, and rotating speed is 300 ~ 500r/min.
Preferably, in step S2, mixed material mixing time is 40 ~ 70min, and rotating speed is 800 ~ 1200r/min.
Preferably, in step S3, the reaction temperature of mixed material is 40 ~ 60 DEG C, and the response time is 30 ~ 60min, stirs and turns
Speed is 400 ~ 600r/min.
Beneficial effects of the present invention：The antibiotic paint constituent wide material sources of the present invention, manufacturing process are simple, using this
The coating that inventive method is prepared from not only remains with the good characteristic of water paint, also because having containing sodium carboxymethyl cellulose
There are antibacterial characteristics.
Specific embodiment
1 a kind of antibiotic paint of embodiment, in units of weight portion, comprising following raw material：Acrylic polyol emulsion 300
Part, 150 parts of polyaminoester emulsion, 35 parts of carboxymethylcellulose sodium solution, 15 parts of titanium dioxide, 10 parts of Sulfonateses defoamer, thickening
8 parts of agent, 11 parts of film former, 120 parts of deionized water.
The preparation method of the antibiotic paint, comprises the following steps：
S1：Will be deionized water, Sulfonateses defoamer, acrylic polyol emulsion, polyaminoester emulsion, sodium carboxymethyl cellulose molten
Liquid sequentially adds dispersion cylinder and stirs 30min under the conditions of rotating speed 300r/min；
S2：Titanium dioxide, thickening agent, film former are sequentially added mixed material obtained by step S1 to stir under the conditions of rotating speed 800r/min
Mix 70min；
S3：Mixed material obtained by step S2 is warming up to into 40 DEG C, stirring reaction 60min under the conditions of 400r/min；
S4：After mixed material obtained by step S3 stands, that is, antibiotic paint is obtained.
2 a kind of antibiotic paint of embodiment, in units of weight portion, comprising following raw material：Acrylic polyol emulsion 600
Part, 350 parts of polyaminoester emulsion, 60 parts of carboxymethylcellulose sodium solution, 45 parts of titanium dioxide, 20 parts of Sulfonateses defoamer, thickening
24 parts of agent, 30 parts of film former, 280 parts of deionized water.
The preparation method of the antibiotic paint, comprises the following steps：
S1：Will be deionized water, Sulfonateses defoamer, acrylic polyol emulsion, polyaminoester emulsion, sodium carboxymethyl cellulose molten
Liquid sequentially adds dispersion cylinder and stirs 15min under the conditions of rotating speed 500r/min；
S2：Titanium dioxide, thickening agent, film former are sequentially added into mixed material obtained by step S1 under the conditions of rotating speed 1200r/min
Stirring 40min；
S3：Mixed material obtained by step S2 is warming up to into 60 DEG C, stirring reaction 30min under the conditions of 600r/min；
S4：After mixed material obtained by step S3 stands, that is, antibiotic paint is obtained.
3 a kind of antibiotic paint of embodiment, in units of weight portion, comprising following raw material：Acrylic polyol emulsion 450
Part, 230 parts of polyaminoester emulsion, 105 parts of carboxymethylcellulose sodium solution, 30 parts of titanium dioxide, 15 parts of Sulfonateses defoamer, thickening
12 parts of agent, 21 parts of film former, 210 parts of deionized water.
The preparation method of the antibiotic paint, comprises the following steps：
S1：Will be deionized water, Sulfonateses defoamer, acrylic polyol emulsion, polyaminoester emulsion, sodium carboxymethyl cellulose molten
Liquid sequentially adds dispersion cylinder and stirs 20min under the conditions of rotating speed 400r/min；
S2：Titanium dioxide, thickening agent, film former are sequentially added into mixed material obtained by step S1 under the conditions of rotating speed 1000r/min
Stirring 50min；
S3：Mixed material obtained by step S2 is warming up to into 50 DEG C, stirring reaction 45min under the conditions of 500r/min；
S4：After mixed material obtained by step S3 stands, that is, antibiotic paint is obtained.
Above content it cannot be assumed that the present invention be embodied as be confined to these explanation, for belonging to the present invention technology neck
For the those of ordinary skill in domain, without departing from the inventive concept of the premise, some simple deduction or replace can also be made,
The scope of patent protection that the present invention is determined by the claims submitted to should be all considered as belonging to.
Claims (5)
1. a kind of antibiotic paint, it is characterised in that in units of weight portion, comprising following raw material：Acrylic polyol emulsion 300
~ 600 parts, 150 ~ 350 parts of polyaminoester emulsion, 35 ~ 105 parts of carboxymethylcellulose sodium solution, 15 ~ 45 parts of titanium dioxide, Sulfonateses
10 ~ 20 parts of defoamer, 8 ~ 24 parts of thickening agent, 11 ~ 30 parts of film former, 120 ~ 280 parts of deionized water.
2. the preparation method of antibiotic paint according to claim 1, it is characterised in that comprise the following steps：
S1：Will be deionized water, Sulfonateses defoamer, acrylic polyol emulsion, polyaminoester emulsion, sodium carboxymethyl cellulose molten
Liquid sequentially adds dispersion cylinder uniform stirring；
S2：Titanium dioxide, thickening agent, film former are sequentially added into mixed material uniform stirring obtained by step S1；
S3：Stirring reaction after mixed material obtained by step S2 is heated up；
S4：After mixed material obtained by step S3 stands, that is, antibiotic paint is obtained.
3. the preparation method of antibiotic paint according to claim 2, it is characterised in that the stirring of mixed material in step S1
Time is 15 ~ 30min, and rotating speed is 300 ~ 500r/min.
4. the preparation method of antibiotic paint according to claim 2, it is characterised in that when mixed material is stirred in step S2
Between be 40 ~ 70min, rotating speed be 800 ~ 1200r/min.
5. the preparation method of antibiotic paint according to claim 2, it is characterised in that the reaction of mixed material in step S3
Temperature is 40 ~ 60 DEG C, and the response time is 30 ~ 60min, and speed of agitator is 400 ~ 600r/min.