CN106674758A - Novel rubber material - Google Patents
Novel rubber material Download PDFInfo
- Publication number
- CN106674758A CN106674758A CN201611119105.4A CN201611119105A CN106674758A CN 106674758 A CN106674758 A CN 106674758A CN 201611119105 A CN201611119105 A CN 201611119105A CN 106674758 A CN106674758 A CN 106674758A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber material
- prepared
- novel rubber
- novel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel rubber material, which is prepared from the following ingredients including EPDM (ethylene-propylene-diene monomer), vinyl resin, wood fiber, calcium carbonate, coumarone, plasticizers, dioctyl phthalate, crack preventing agents, white oil, liquid softening agents, anti-aging agents and the like. The novel rubber material prepared by the formula has the advantages that the formula is reasonable; simplicity is realized; the acquisition is easy; the raw material cost is lower, so that the cost of the prepared rubber materials is lower than that of the rubber material in the prior art. In addition, toxic and harmful substances such as sulphur are not added, so that the rubber material cannot release toxic and harmful substances in the use process; the rubber material has the high-temperature-resistant characteristics, and is particularly suitable for being used for producing tire products for automobiles, motorcycles and the like.
Description
Technical field
The present invention relates to Material Field, and in particular to a kind of Novel rubber material.
Background technology
In high temperature season, automobile tire is directly contacted with ground, and automobile long-time is travelled in hot weather, due to temperature
Height is spent, the aging and exhaustion of tire can be accelerated；Due to operating at a high speed and for a long time, can also cause to produce on elastomeric material surface
Raw high temperature, accelerates the aging of rubber.Tire is easy to absorb the heat in sunlight, and the air in tire is thermal coefficient of expansion again
Very high medium；Along with the heat produced with high temperature pavement friction, tire subjects powerful high temperature test.
Elastomeric material of the prior art due to adding the mode such as sulfur to produce using sulfur, therefore, the rubber of finished product
Material can contain the harmful substances such as various poisonous and harmful substances, such as halogen-containing, sulfur-bearing, and then affect the application quality of rubber.
The content of the invention
Present invention aim at a kind of Novel rubber material is provided, the no added sulfur-bearing noxious substance of the elastomeric material, and
With resistant to elevated temperatures characteristic.
The present invention is achieved by the following technical programs：A kind of Novel rubber material, by the former material of following parts by weight
Material is prepared from：Ethylene propylene diene rubber 8-9 parts, vinylite 5-6 parts, wood fibre 1-2 parts, Calcium Carbonate 6-7 part, coumarone
2.0-3.6 parts, plasticizer 3.5-4.6 parts, dioctyl ester 2.3-5.3 parts, cracking preventing agent 2.3-6.3 part, white oil 2.1-3.5 parts,
Liquid softener 2-9 parts, age resistor 0.5-0.9 parts.
Preferably, the Novel rubber material, is prepared from by the raw material of following parts by weight：Ethylene propylene diene rubber
8.5 parts, it is 5.5 parts of vinylite, 1.5 parts of wood fibre, 6.5 parts of Calcium Carbonate, 3.0 parts of coumarone, 4.0 parts of plasticizer, two pungent
3.2 parts of ester, 3.0 parts of preventing agent of cracking, 3.0 parts of white oil, 5 parts of liquid softener, 0.55 part of age resistor.
Preferably, the lignocellulose can also use polypropylene fibre or polyester fiber to replace.
Preferably, the age resistor be 6- ethyoxyl -2,2,4- trimethyl -1,2- dihyaroquinolines.
Vinyl polysiloxane or vinyl MQ resin of the vinylite for liquid.
The product that the cracking preventing agent, liquid softener are adopted using this area.
Compared to prior art, beneficial effects of the present invention：Closed using Novel rubber material formula made by above-mentioned formula
Reason and simple and easy to get, as cost of material is relatively low, therefore obtained elastomeric material cost elastomeric material more of the prior art is low；
Due to not adding the poisonous and hazardous material such as sulfur, therefore make the elastomeric material not discharge poisonous and harmful in use
Material, reduces the harm to environment；The elastomeric material has high-temperature stability, is particularly suited for producing the wheel such as automobile, motorcycle
Tire product.
Specific embodiment
The invention will be further described with the following Examples.
A kind of 1 Novel rubber material of embodiment, is prepared from by the raw material of following parts by weight：Ethylene propylene diene rubber
8.5 parts, 5.5 parts of liquid ethylene base silicones, 1.5 parts of wood fibre, 6.5 parts of Calcium Carbonate, 3.0 parts of coumarone, plasticizer 4.0
Part, 3.2 parts of dioctyl ester, cracking preventing agent B-103.0 part, 3.0 parts of white oil, 5 parts of liquid softener, age resistor 6- ethyoxyl -2,
0.55 part of 2,4- trimethyl -1,2- dihyaroquinolines.
A kind of 2 Novel rubber material of embodiment, is prepared from by the raw material of following parts by weight：Ethylene propylene diene rubber 8-
9 parts, 5 parts of vinyl MQ resin, 1.7 parts of polypropylene fibre, 6 parts of Calcium Carbonate, 2.0 parts of coumarone, 4.3 parts of plasticizer, dioctyl ester
2.3-5.3 parts, cracking preventing agent LSB202.3-6.3 part, white oil 2.1-3.5 parts, liquid softener 2-9 parts, GM age resistor 0.5-
0.9 part.
A kind of 3 Novel rubber material of embodiment, is prepared from by the raw material of following parts by weight：Ethylene propylene diene rubber 8-
9 parts, 6 parts of vinyl polysiloxane, 1 part of polyester fiber, 7 parts of Calcium Carbonate, 2.5 parts of coumarone, 3.9 parts of plasticizer, dioctyl ester 2.3-
5.3 parts, cracking preventing agent LSB202.3-6.3 part, white oil 2.1-3.5 parts, liquid softener 2-9 parts, age resistor 6- ethyoxyls-
2,2,4- trimethyl -1,2- dihyaroquinoline 0.5-0.9 parts.
A kind of 4 Novel rubber material of embodiment, is prepared from by the raw material of following parts by weight：Ethylene propylene diene rubber 8-
9 parts, it is 5.2 parts of vinyl MQ resin, 2 parts of polypropylene fibre, 6.4 parts of Calcium Carbonate, 3.6 parts of coumarone, 4.6 parts of plasticizer, two pungent
Ester 2.3-5.3 parts, cracking preventing agent LSB202.3-6.3 part, white oil 2.1-3.5 parts, liquid softener 2-9 parts, age resistor
RD0.5-0.9 parts.
A kind of 5 Novel rubber material of embodiment, is prepared from by the raw material of following parts by weight：Ethylene propylene diene rubber 8-
9 parts, 5.8 parts of vinyl polysiloxane, 1.3 parts of wood fibre, 7 parts of Calcium Carbonate, 2.8 parts of coumarone, 3.5 parts of plasticizer, dioctyl ester
2.3-5.3 parts, cracking preventing agent LSB202.3-6.3 part, white oil 2.1-3.5 parts, liquid softener 2-9 parts, age resistor 0.5-
0.9 part.
Claims (4)
1. a kind of Novel rubber material, it is characterised in that：It is prepared from by the raw material of following parts by weight：Ethylene propylene diene rubber
8-9 parts, vinylite 5-6 parts, wood fibre 1-2 parts, Calcium Carbonate 6-7 part, coumarone 2.0-3.6 parts, plasticizer 3.5-4.6
Part, dioctyl ester 2.3-5.3 parts, cracking preventing agent 2.3-6.3 part, white oil 2.1-3.5 parts, liquid softener 2-9 parts, age resistor
0.5-0.9 parts.
2. a kind of Novel rubber material according to claim 1, it is characterised in that 8.5 parts of ethylene propylene diene rubber, vinyl
5.5 parts of resin, 1.5 parts of wood fibre, 6.5 parts of Calcium Carbonate, 3.0 parts of coumarone, 4.0 parts of plasticizer, 3.2 parts of dioctyl ester, cracking
3.0 parts of preventing agent, 3.0 parts of white oil, 5 parts of liquid softener, 0.55 part of age resistor.
3. according to the arbitrary described a kind of Novel rubber material of claim 1 or 2, it is characterised in that the lignocellulose
Replaced with polypropylene fibre or polyester fiber.
4. a kind of Novel rubber material according to claim 1 and 2, it is characterised in that the age resistor be 6- ethyoxyls-
2,2,4- trimethyl -1,2- dihyaroquinolines.