CN106674573A - Processing method for color printing packaging compound film - Google Patents
Processing method for color printing packaging compound film Download PDFInfo
- Publication number
- CN106674573A CN106674573A CN201611214752.3A CN201611214752A CN106674573A CN 106674573 A CN106674573 A CN 106674573A CN 201611214752 A CN201611214752 A CN 201611214752A CN 106674573 A CN106674573 A CN 106674573A
- Authority
- CN
- China
- Prior art keywords
- color printing
- printing packaging
- composite film
- processing method
- packaging composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing method for a color printing packaging compound film. The processing method for the color printing packaging compound film comprises the following steps of: selecting materials; purifying gel; preparing; spraying; and storing. The processing method disclosed by the invention has an obvious advantage in cost; the production technology is mature; the color printing packaging compound film has excellent properties, such as, air barrier property, toughness and water solubility; the application is more extensive; the color printing packaging compound film processed according to the invention has the advantages of bright color, difficulty in fading, excellent biological degradability, excellent mechanical property, and the like.
Description
Technical field
The present invention relates to a kind of plastics package print field, specifically a kind of color printing packaging composite film processing method.
Background technology
As China's expanding economy, packaging, printing industry development are swift and violent, the market demand is big.Emerging color printing printing skill
Art possesses prominent advantage in satisfaction personalization, small lot batch manufacture demand and at aspects such as reduces costs, and it is used as environmental protection print
Brush technology is increasingly becoming printing industry main direction.But traditional color printing operation is complex, is not suitable for the processing of composite membrane.
The content of the invention
It is an object of the invention to provide a kind of color printing packaging composite film processing method, to solve above-mentioned background technology in carry
The problem for going out.
For achieving the above object, the present invention provides following technical scheme：
A kind of color printing packaging composite film processing method, comprises the steps：
(1) sorting：Plastic raw materialss are screened according to GB/T 10004-2008 standards, ink raw materials are according to GB/
T14624.1-2009 and GB/T 18724-2008 standards are screened；
(2) purification gel：Deionized water cleans gel, and gel is soaked in the boric acid solution of 0.6-0.8mol/L
12-24 hours, soaking temperature is 40-60 DEG C, then deionized water cyclic washing gel 3-5 time is to neutrality；
(3) prepare：Gel, polyethylene, polyurethane, phenolic resin and polyphenylene oxide are placed in a kettle., pressure is arranged
For 2-6MPa, temperature setting is 62-82 DEG C, and set of time is 1-2h, and reaction is transferred in double screw extruder after terminating, and is carried out
Blow molding, is obtained packaging film semi-finished product；
(4) spray：The packaging film semi-finished product of blow molding are placed into working region in flush coater, deionized water cleaning table
Behind face, then soak 15-20 minutes in mass concentration is for the glycerite of 30-40%, cold drying after taking-up, baking temperature is
40-60 DEG C, subsequent start-up flush coater adds ink raw materials to be sprayed according to required spraying effect, places ultraviolet roasting after spraying
Dried in case, drying temperature is 20-30 DEG C, and drying time is 1-2h, color printing packaging composite film is obtained.
(5) store：Color printing packaging composite film is cut, deburring and bonding, be subsequently placed at warehouse, MW temperature is
10 DEG C, warehouse humidity is 20%.
As further scheme of the invention：Gel soaks 18 hours in the boric acid solution of 0.7mol/L in step (2),
Soaking temperature is 50 DEG C.
As further scheme of the invention：The quality of polyethylene, polyurethane, phenolic resin and polyphenylene oxide in step (3)
Than for 2-4:3-5:1:2.
As further scheme of the invention：Pressure is set to 4MPa in step (3), and temperature setting is 72 DEG C, and the time sets
It is set to 1.5h.
As further scheme of the invention：Baking temperature is 50 DEG C in step (4).
As further scheme of the invention：Drying temperature is 25 DEG C in step (4), and drying time is 1.5h.
Color printing packaging composite film obtained in described color printing packaging composite film processing method.
Compared with prior art, the invention has the beneficial effects as follows：
Processing method of the present invention has obvious price advantage, and production technology is more ripe, and it is also equipped with preferable gas
The premium properties such as body barrier, obdurability, water solublity so as to be more widely applied；The obtained color printing packaging of present invention processing is multiple
Close film and also there is not fugitive color bright in luster, good biological degradability and excellent mechanical property.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than the embodiment of whole.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment 1
A kind of color printing packaging composite film processing method, comprises the steps：
(1) sorting：Plastic raw materialss are screened according to GB/T 10004-2008 standards, ink raw materials are according to GB/
T14624.1-2009 and GB/T 18724-2008 standards are screened；
(2) purification gel：Deionized water cleans gel, gel is soaked in the boric acid solution of 0.6mol/L 12 little
When, soaking temperature is 40 DEG C, then deionized water cyclic washing gel 3 times is to neutral；
(3) prepare：Gel, polyethylene, polyurethane, phenolic resin and polyphenylene oxide are placed in a kettle., pressure is arranged
For 2MPa, temperature setting is 62 DEG C, and set of time is 1h, and reaction is transferred in double screw extruder after terminating, and is blow molded into
Type, is obtained packaging film semi-finished product；
(4) spray：The packaging film semi-finished product of blow molding are placed into working region in flush coater, deionized water cleaning table
Behind face, then soak 15 minutes in the glycerite that mass concentration is 30%, cold drying after taking-up, baking temperature is 40 DEG C,
Subsequent start-up flush coater, adds ink raw materials to be sprayed according to required spraying effect, and placing after spraying in ultraviolet baking box is carried out
Drying, drying temperature is 20 DEG C, and drying time is 1h, and color printing packaging composite film is obtained.
(5) store：Color printing packaging composite film is cut, deburring and bonding, be subsequently placed at warehouse, MW temperature is
10 DEG C, warehouse humidity is 20%.
Wherein：
The mass ratio of polyethylene, polyurethane, phenolic resin and polyphenylene oxide is 2 in step (3):3:1:2.
Color printing packaging composite film obtained in described color printing packaging composite film processing method.
Embodiment 2
A kind of color printing packaging composite film processing method, comprises the steps：
(1) sorting：Plastic raw materialss are screened according to GB/T 10004-2008 standards, ink raw materials are according to GB/
T14624.1-2009 and GB/T 18724-2008 standards are screened；
(2) purification gel：Deionized water cleans gel, gel is soaked in the boric acid solution of 0.7mol/L 18 little
When, soaking temperature is 50 DEG C, then deionized water cyclic washing gel 3-5 time is to neutrality；
(3) prepare：Gel, polyethylene, polyurethane, phenolic resin and polyphenylene oxide are placed in a kettle., pressure is arranged
For 4MPa, temperature setting is 72 DEG C, and set of time is 1.5h, and reaction is transferred in double screw extruder after terminating, and is blow molded
Molding, is obtained packaging film semi-finished product；
(4) spray：The packaging film semi-finished product of blow molding are placed into working region in flush coater, deionized water cleaning table
Behind face, then soak 18 minutes in the glycerite that mass concentration is 35%, cold drying after taking-up, baking temperature is 50 DEG C,
Subsequent start-up flush coater, adds ink raw materials to be sprayed according to required spraying effect, and placing after spraying in ultraviolet baking box is carried out
Drying, drying temperature is 25 DEG C, and drying time is 1.5h, and color printing packaging composite film is obtained.
(5) store：Color printing packaging composite film is cut, deburring and bonding, be subsequently placed at warehouse, MW temperature is
10 DEG C, warehouse humidity is 20%.
Color printing packaging composite film obtained in described color printing packaging composite film processing method.
Wherein：
The mass ratio of polyethylene, polyurethane, phenolic resin and polyphenylene oxide is 3 in step (3):4:1:2.
Embodiment 3
A kind of color printing packaging composite film processing method, comprises the steps：
(1) sorting：Plastic raw materialss are screened according to GB/T 10004-2008 standards, ink raw materials are according to GB/
T14624.1-2009 and GB/T 18724-2008 standards are screened；
(2) purification gel：Deionized water cleans gel, gel is soaked in the boric acid solution of 0.8mol/L 24 little
When, soaking temperature is 60 DEG C, then deionized water cyclic washing gel 5 times is to neutral；
(3) prepare：Gel, polyethylene, polyurethane, phenolic resin and polyphenylene oxide are placed in a kettle., pressure is arranged
For 6MPa, temperature setting is 82 DEG C, and set of time is 2h, and reaction is transferred in double screw extruder after terminating, and is blow molded into
Type, is obtained packaging film semi-finished product；
(4) spray：The packaging film semi-finished product of blow molding are placed into working region in flush coater, deionized water cleaning table
Behind face, then soak 20 minutes in the glycerite that mass concentration is 40%, cold drying after taking-up, baking temperature is 60 DEG C,
Subsequent start-up flush coater, adds ink raw materials to be sprayed according to required spraying effect, and placing after spraying in ultraviolet baking box is carried out
Drying, drying temperature is 30 DEG C, and drying time is 2h, and color printing packaging composite film is obtained.
(5) store：Color printing packaging composite film is cut, deburring and bonding, be subsequently placed at warehouse, MW temperature is
10 DEG C, warehouse humidity is 20%.
Color printing packaging composite film obtained in described color printing packaging composite film processing method.
Wherein：
As further scheme of the invention：The quality of polyethylene, polyurethane, phenolic resin and polyphenylene oxide in step (3)
Than for 4:5:1:2.
Comparative example 1
A kind of color printing packaging composite film processing method, comprises the steps：
(1) sorting：Plastic raw materialss are screened according to GB/T 10004-2008 standards, ink raw materials are according to GB/
T14624.1-2009 and GB/T 18724-2008 standards are screened；
(2) purification gel：Deionized water cleans gel, and gel is soaked in clear water 12-24 hours, and soaking temperature is
50 DEG C, then deionized water cyclic washing gel 4 times；
(3) prepare：Gel, polyethylene, polyurethane, phenolic resin and polyphenylene oxide are placed in a kettle., pressure is arranged
For 2MPa, temperature setting is 62 DEG C, and set of time is 1h, and reaction is transferred in double screw extruder after terminating, and is blow molded into
Type, is obtained packaging film semi-finished product；
(4) spray：The packaging film semi-finished product of blow molding are placed into working region in flush coater, deionized water cleaning table
Behind face, then soak 20 minutes in the glycerite that mass concentration is 30%, cold drying after taking-up, baking temperature is 40 DEG C,
Subsequent start-up flush coater, adds ink raw materials to be sprayed according to required spraying effect, and placing after spraying in ultraviolet baking box is carried out
Drying, drying temperature is 20 DEG C, and drying time is 1h, and color printing packaging composite film is obtained.
(5) store：Color printing packaging composite film is cut, deburring and bonding, be subsequently placed at warehouse, MW temperature is
10 DEG C, warehouse humidity is 20%.
Color printing packaging composite film obtained in described color printing packaging composite film processing method.
Wherein：
The mass ratio of polyethylene, polyurethane, phenolic resin and polyphenylene oxide is 2 in step (3):3:1:2.
Color printing packaging composite film obtained in described color printing packaging composite film processing method.
Comparative example 2
A kind of color printing packaging composite film processing method, comprises the steps：
(1) sorting：Plastic raw materialss are screened according to GB/T 10004-2008 standards, ink raw materials are according to GB/
T14624.1-2009 and GB/T 18724-2008 standards are screened；
(2) purification gel：Deionized water cleans gel, gel is soaked in the boric acid solution of 0.8mol/L 24 little
When, soaking temperature is 60 DEG C, then deionized water cyclic washing gel 3-5 time is to neutrality；
(3) prepare：Gel, polyethylene, polyurethane, phenolic resin and polyphenylene oxide are placed in a kettle., pressure is arranged
For 6MPa, temperature setting is 82 DEG C, and set of time is 2h, and reaction is transferred in double screw extruder after terminating, and is blow molded into
Type, is obtained packaging film semi-finished product；
(4) spray：The packaging film semi-finished product of blow molding are placed into working region in flush coater, starts flush coater, according to
Required spraying effect adds ink raw materials to be sprayed, and places after spraying and is dried in ultraviolet baking box, and drying temperature is 30 DEG C,
Drying time is 2h, and color printing packaging composite film is obtained.
(5) store：Color printing packaging composite film is cut, deburring and bonding, be subsequently placed at warehouse, MW temperature is
10 DEG C, warehouse humidity is 20%.
Color printing packaging composite film obtained in described color printing packaging composite film processing method.
Wherein：
The mass ratio of polyethylene, polyurethane, phenolic resin and polyphenylene oxide is 3 in step (3):4:1:2.
Color printing packaging composite film obtained in described color printing packaging composite film processing method.
Comparative example 3
A kind of color printing packaging composite film processing method, comprises the steps：
(1) sorting：Plastic raw materialss are screened according to GB/T 10004-2008 standards, ink raw materials are according to GB/
T14624.1-2009 and GB/T 18724-2008 standards are screened；
(2) purification gel：Deionized water cleans gel, gel is soaked in the boric acid solution of 0.6mol/L 12 little
When, soaking temperature is 40 DEG C, then deionized water cyclic washing gel 3-5 time is to neutrality；
(3) prepare：Gel, polyethylene, polyurethane, phenolic resin and polyphenylene oxide are placed in a kettle., pressure is arranged
For 2-6MPa, temperature setting is 62 DEG C, and set of time is 1h, and reaction is transferred in double screw extruder after terminating, and is blow molded
Molding, is obtained packaging film semi-finished product；
(4) spray：The packaging film semi-finished product of blow molding are placed into working region in flush coater, deionized water cleaning table
Behind face, then soak 20 minutes in the glycerite that mass concentration is 40%, cold drying after taking-up, baking temperature is 22 DEG C,
Subsequent start-up flush coater, adds ink raw materials to be sprayed according to required spraying effect, and placing after spraying in ultraviolet baking box is carried out
Drying, drying temperature is 15 DEG C, and drying time is 1h, and color printing packaging composite film is obtained.
(5) store：Color printing packaging composite film is cut, deburring and bonding, be subsequently placed at warehouse, MW temperature is
10 DEG C, warehouse humidity is 20%.
Color printing packaging composite film obtained in described color printing packaging composite film processing method.
Wherein：
As further scheme of the invention：Polyethylene, polyurethane, the mass ratio of phenolic resin are 2 in step (3):3:
1。
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of spirit or essential attributes without departing substantially from the present invention, the present invention can be in other specific forms realized.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit is required rather than described above is limited, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although this specification is been described by according to embodiment, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of description is only that for clarity those skilled in the art should
Using description as an entirety, the technical scheme in each embodiment can also Jing it is appropriately combined, form those skilled in the art
Understandable other embodiment.
Claims (7)
1. a kind of color printing packaging composite film processing method, it is characterised in that comprise the steps：
(1) sorting：Plastic raw materialss are screened according to GB/T 10004-2008 standards, ink raw materials are according to GB/
T14624.1-2009 and GB/T 18724-2008 standards are screened；
(2) purification gel：Deionized water cleans gel, and gel is soaked into 12-24 in the boric acid solution of 0.6-0.8mol/L
Hour, soaking temperature is 40-60 DEG C, then deionized water cyclic washing gel 3-5 time is to neutrality；
(3) prepare：Gel, polyethylene, polyurethane, phenolic resin and polyphenylene oxide are placed in a kettle., pressure is set to 2-
6MPa, temperature setting is 62-82 DEG C, and set of time is 1-2h, and reaction is transferred in double screw extruder after terminating, and is blow molded
Molding, is obtained packaging film semi-finished product；
(4) spray：The packaging film semi-finished product of blow molding are placed into working region in flush coater, deionized water cleaning surface
Afterwards, then in mass concentration is for the glycerite of 30-40% soak 15-20 minutes, cold drying after taking-up, baking temperature is
40-60 DEG C, subsequent start-up flush coater adds ink raw materials to be sprayed according to required spraying effect, places ultraviolet roasting after spraying
Dried in case, drying temperature is 20-30 DEG C, and drying time is 1-2h, color printing packaging composite film is obtained.
(5) store：Color printing packaging composite film is cut, deburring and bonding, be subsequently placed at warehouse, MW temperature is 10
DEG C, warehouse humidity is 20%.
2. color printing packaging composite film processing method according to claim 1, it is characterised in that gel exists in step (2)
Soak 18 hours in the boric acid solution of 0.7mol/L, soaking temperature is 50 DEG C.
3. color printing packaging composite film processing method according to claim 1, it is characterised in that polyethylene in step (3), poly-
The mass ratio of urethane, phenolic resin and polyphenylene oxide is 2-4:3-5:1:2.
4. color printing packaging composite film processing method according to claim 1, it is characterised in that pressure is arranged in step (3)
For 4MPa, temperature setting is 72 DEG C, and set of time is 1.5h.
5. color printing packaging composite film processing method according to claim 1, it is characterised in that baking temperature in step (4)
For 50 DEG C.
6. color printing packaging composite film processing method according to claim 1, it is characterised in that drying temperature in step (4)
For 25 DEG C, drying time is 1.5h.
7. color printing packaging composite film obtained in a kind of color printing packaging composite film processing method as described in claim 1-6 is arbitrary.