CN106637999A - Wool blending antiwrinkling suit fabric and preparation method thereof - Google Patents
Wool blending antiwrinkling suit fabric and preparation method thereof Download PDFInfo
- Publication number
- CN106637999A CN106637999A CN201611115204.5A CN201611115204A CN106637999A CN 106637999 A CN106637999 A CN 106637999A CN 201611115204 A CN201611115204 A CN 201611115204A CN 106637999 A CN106637999 A CN 106637999A
- Authority
- CN
- China
- Prior art keywords
- wool
- fabric
- suiting
- preparation
- wrinkle resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wool blending antiwrinkling suit fabric. The wool blending antiwrinkling suit fabric has the advantages that the fabric is blended by superfine polyester fiber, ramie fiber and wool together, so that the fabric has a drape feeling of polyster, and a good hand feeling of ramine fabric, and the grade of fabric is improved; by pretreating wool fibers, the felting shrinkage of wools is prevented, and the size stability of the wool fabric is improved; the vacuum enzyme treatment and polyurethane shaping combining mode is adopted in the pretreatment process of the wool fibers, the scale stripping effect is good, the later shaping effect is good, the antiwrinkling effect is good, and the ironing is basically not needed after airing; the halogen is not added in the treatment technology of the wool fibers, the environment-friendly effect is realized, and the environment-protection requirement of China on textile industry is met.
Description
Technical field
The present invention relates to a kind of preparation method of fabric, belongs to field of textile, more particularly to it is a kind of wool blended anti-
Wrinkle suiting and preparation method thereof.
Background technology
Modern more and more focuses on improving quality of the life, and wool has many good characteristics, such as elastic good, hygroscopicity
By force, it is difficult to stain, warmth retention property is good, gloss is soft etc., these characteristics cause wool fabric to have various individual styles, deep to receive people
Favor.But wool is susceptible to felting, the felting of wool fabric is mainly caused by the surface scale feature of wool, in washing
Under effect, wool is susceptible to " displacement " effect, so as to cause " gathering " effect of wool fiber, i.e. wool fiber to lose
Elasticity is simultaneously crimped, and tightens wool fabric, and then causes the dimensional stability of wool fabric to be deteriorated, and is had a strong impact on wool and is knitted
The outward appearance of thing and wear performance.Therefore wool fabric need to generally carry out corresponding chemistry dry-cleaning, or carry out slightly washing for very careful
Wash, and " can not machine-wash ", this is not suitable with modern lifestyle.
Research of the industry personnel to wool fabric felt proofing lasts for a long time.At present, shrinkproofing treatment side main both at home and abroad
Method has:Divest scale and prevent the relative movement of wool.General divesting adopt chloridising scale more, but it has following asking
Topic:One be in order to reach the stripping squama of yarn interior fiber, certainly will be overweight to the process of yam surface fiber, cause the inside and outside stripping of fiber
Squama is uneven, so as to damage yarn fibers, has had a strong impact on the performances such as strength, the color of wool fabric;Two is that its needs is adopted
Processed with heavy dose of stripping squama agent, but pollution of the stripping squama agent of heavy dose to environment is very big, is unfavorable for environmental protection,
There are some new techniques and process combination to be used for the shrinkproofing treatment of wool fabric, although these new technologies can reach wool and knit
The anti-felting effect of thing, but most effect stability and repeatability are poor.
The content of the invention
Based on the technical problem that background technology is present, the present invention proposes a kind of wool blended wrinkle resistant suiting and its system
Preparation Method.
Technical scheme is as follows:
A kind of wool blended wrinkle resistant suiting, including the composition of following percentage by weight:
Wool fiber 60-70%
Ultra-fine polyester fiber 18-25%
Ramee surplus.
A kind of preparation method of wool blended wrinkle resistant suiting, comprises the following steps:
A, wool fiber is pre-processed using vacuum enzyme treatment process;
B, pretreated wool fiber is heated into 8-15min under the conditions of 90-100 DEG C, inactivate enzyme, be then placed in 2-
20-30min is processed in 5% aqueous polyurethane solution, is dried, it is standby;
C, weave cotton cloth:Adopt ultra-fine polyester fiber, wool fiber and ramee for raw material, using water-jet loom base is made
Cloth;
D, dyeing:Fabric is dyeed using natural dyeing agent;
E, further carry out desizing refining, Alkali reduction, drying, postfinishing process and obtain wool blended wrinkle resistant suiting.
Preferably, described vacuum enzyme treatment process, using neutral protein ferment treatment.
Preferably, described vacuum enzyme treatment process, comprises the following steps:After wool is broken up, vacuum laboratory box is put into
It is interior, vacuumize, neutral protein enzyme solutions are then injected into, 40-60 DEG C is maintained the temperature at, process time is 16-20h.
Preferably, the described vacuum for vacuumizing is -0.5MPa.
Preferably, the concentration of described neutral protein enzyme solutions is 2-5%, and enzyme activity of the neutral proteinase after dilution is
300-500IU/ml。
Preferably, described postfinishing process is arranged using Aroma finishing agent and pilling fluffing resistant finishing agent.
The invention has benefit that:
1st, fabric possesses the pendency of terylene using ultra-fine polyester fiber and ramee and wool blending together, not only fabric
Sense, and the also excellent handle of flax fabric, lift fabric class;
2nd, pre-treatment is carried out to wool fiber, prevents wool from producing felting, lift the dimensional stability of wool fabric;
3rd, to the pre-treatment of wool fiber during using vacuum ferment treatment and polyurethane sizing combination, not only may be used
It is good to shell squama effect, and later stage fixed effect is good, and wrinkle-proof effect is good, need not press substantially after drying;
4th, in the handling process of wool fiber without halogen, it is environmentally friendly, meet ring of the country to textile industry
Guaranteed request.
Specific embodiment
Embodiment 1:
A kind of wool blended wrinkle resistant suiting, including the composition of following percentage by weight:
Wool fiber 65%
Ultra-fine polyester fiber 20%
Ramee surplus.
A kind of preparation method of wool blended wrinkle resistant suiting, comprises the following steps:
A, wool fiber is pre-processed using vacuum enzyme treatment process;
B, pretreated wool fiber is heated into 10min under the conditions of 95 DEG C, inactivate enzyme, be then placed in 3% aqueous
25min is processed in polyurethane solutions, is dried, it is standby;
C, weave cotton cloth:Adopt ultra-fine polyester fiber, wool fiber and ramee for raw material, using water-jet loom base is made
Cloth;
D, dyeing:Fabric is dyeed using natural dyeing agent;
E, further carry out desizing refining, Alkali reduction, drying, postfinishing process and obtain wool blended wrinkle resistant suiting.
Described vacuum enzyme treatment process, comprises the following steps:After wool is broken up, it is put in vacuum laboratory box, takes out true
Sky, is then injected into neutral protein enzyme solutions, maintains the temperature at 45 DEG C, and process time is 18h.
The described vacuum for vacuumizing is -0.5MPa.
The concentration of described neutral protein enzyme solutions is 3%, and enzyme activity of the neutral proteinase after dilution is 450IU/ml.
Described postfinishing process is arranged using Aroma finishing agent and pilling fluffing resistant finishing agent.
Embodiment 2:
A kind of wool blended wrinkle resistant suiting, including the composition of following percentage by weight:
Wool fiber 70%
Ultra-fine polyester fiber 18%
Ramee surplus.
A kind of preparation method of wool blended wrinkle resistant suiting, comprises the following steps:
A, wool fiber is pre-processed using vacuum enzyme treatment process;
B, pretreated wool fiber is heated into 8min under the conditions of 100 DEG C, inactivate enzyme, be then placed in 5% aqueous
20min is processed in polyurethane solutions, is dried, it is standby;
C, weave cotton cloth:Adopt ultra-fine polyester fiber, wool fiber and ramee for raw material, using water-jet loom base is made
Cloth;
D, dyeing:Fabric is dyeed using natural dyeing agent;
E, further carry out desizing refining, Alkali reduction, drying, postfinishing process and obtain wool blended wrinkle resistant suiting.
Described vacuum enzyme treatment process, comprises the following steps:After wool is broken up, it is put in vacuum laboratory box, takes out true
Sky, is then injected into neutral protein enzyme solutions, maintains the temperature at 60 DEG C, and process time is 16h.
The described vacuum for vacuumizing is -0.5MPa.
The concentration of described neutral protein enzyme solutions is 5%, and enzyme activity of the neutral proteinase after dilution is 300IU/ml.
Described postfinishing process is arranged using Aroma finishing agent and pilling fluffing resistant finishing agent.
Embodiment 3:
A kind of wool blended wrinkle resistant suiting, including the composition of following percentage by weight:
Wool fiber 60%
Ultra-fine polyester fiber 25%
Ramee surplus.
A kind of preparation method of wool blended wrinkle resistant suiting, comprises the following steps:
A, wool fiber is pre-processed using vacuum enzyme treatment process;
B, pretreated wool fiber is heated into 15min under the conditions of 90 DEG C, inactivate enzyme, be then placed in 2% aqueous
30min is processed in polyurethane solutions, is dried, it is standby;
C, weave cotton cloth:Adopt ultra-fine polyester fiber, wool fiber and ramee for raw material, using water-jet loom base is made
Cloth;
D, dyeing:Fabric is dyeed using natural dyeing agent;
E, further carry out desizing refining, Alkali reduction, drying, postfinishing process and obtain wool blended wrinkle resistant suiting.
Described vacuum enzyme treatment process, comprises the following steps:After wool is broken up, it is put in vacuum laboratory box, takes out true
Sky, is then injected into neutral protein enzyme solutions, maintains the temperature at 40 DEG C, and process time is 20h.
The described vacuum for vacuumizing is -0.5MPa.
The concentration of described neutral protein enzyme solutions is 2%, and enzyme activity of the neutral proteinase after dilution is 500IU/ml.
Described postfinishing process is arranged using Aroma finishing agent and pilling fluffing resistant finishing agent.
Below properties test is carried out to fabric prepared by embodiment 1-3:
This detection data is just for above-mentioned detection sample.
The above, the only present invention preferably specific embodiment, but protection scope of the present invention is not limited thereto,
Any those familiar with the art the invention discloses technical scope in, technology according to the present invention scheme and its
Inventive concept equivalent or change in addition, all should be included within the scope of the present invention.
Claims (7)
1. a kind of wool blended wrinkle resistant suiting, it is characterised in that including the composition of following percentage by weight:
Wool fiber 60-70%
Ultra-fine polyester fiber 18-25%
Ramee surplus.
2. a kind of preparation method of wool blended wrinkle resistant suiting, it is characterised in that comprise the following steps:
A, wool fiber is pre-processed using vacuum enzyme treatment process;
B, pretreated wool fiber is heated into 8-15min under the conditions of 90-100 DEG C, inactivate enzyme, be then placed in 2-5% water
Property polyurethane solutions in process 20-30min, dry, it is standby;
C, weave cotton cloth:Adopt ultra-fine polyester fiber, wool fiber and ramee for raw material, using water-jet loom fabric is made;
D, dyeing:Fabric is dyeed using natural dyeing agent;
E, further carry out desizing refining, Alkali reduction, drying, postfinishing process and obtain wool blended wrinkle resistant suiting.
3. the preparation method of wool blended wrinkle resistant suiting as claimed in claim 2, it is characterised in that described vacuum enzyme
Handling process, using neutral protein ferment treatment.
4. the preparation method of wool blended wrinkle resistant suiting as claimed in claim 3, it is characterised in that described vacuum enzyme
Handling process, comprises the following steps:After wool is broken up, it is put in vacuum laboratory box, vacuumizes, is then injected into neutral proteinase
Solution, maintains the temperature at 40-60 DEG C, and process time is 16-20h.
5. the preparation method of wool blended wrinkle resistant suiting as claimed in claim 4, it is characterised in that described vacuumizes
Vacuum be -0.5MPa.
6. the preparation method of wool blended wrinkle resistant suiting as claimed in claim 4, it is characterised in that described neutral egg
The concentration of white enzyme solutions is 2-5%, and enzyme activity of the neutral proteinase after dilution is 300-500IU/ml.
7. the preparation method of wool blended wrinkle resistant suiting as claimed in claim 2, it is characterised in that described Final finishing
Technique is arranged using Aroma finishing agent and pilling fluffing resistant finishing agent.