CN106637954A - Environment-friendly textile auxiliary and preparation method thereof - Google Patents
Environment-friendly textile auxiliary and preparation method thereof Download PDFInfo
- Publication number
- CN106637954A CN106637954A CN201611166414.7A CN201611166414A CN106637954A CN 106637954 A CN106637954 A CN 106637954A CN 201611166414 A CN201611166414 A CN 201611166414A CN 106637954 A CN106637954 A CN 106637954A
- Authority
- CN
- China
- Prior art keywords
- parts
- textile auxiliary
- environment
- mixed
- added
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly textile auxiliary and a preparation method thereof. The environment-friendly textile auxiliary is prepared with sodium diethylhexyl sulfosuccinate, ethylene diamine tetraacetic acid, methyl silicone resin and styrene maleic anhydride resin as main components, phthalic anhydride, polyethylene glycol monostearate, fatty alcohol-polyoxyethylene ether, cocomut oil diethanolamide, nonylphenol polyoxyethylene ether, lignin sulfate, activated carbon, barium chloride, organic acid, a cross-linking agent and deionzied water are added, and the technologies of ball milling, stirring, emulsifying, pH adjusting, heating, heat preservation, ultrasonic oscillation, high-speed shearing and the like are also used. Therefore, after the prepared textile auxiliary is used, textile fabrics are high in toughness and good in viscosity stability, and the textile auxiliary is environmentally friendly, free of toxins, capable of meeting industrial requirements and good in application prospect.
Description
Technical field
The present invention relates to technical field of textile auxiliary agent, more particularly to a kind of environment-friendly type textile auxiliary and preparation method thereof.
Background technology
Textile auxiliary is necessary chemicals in textile production process.Product of the textile auxiliary to raising textile
Quality and surcharge have indispensable important function, and it can not only give the various specific functions of textile and style, such as
Soft, wrinkle resistant, shrinkproof, waterproof, antibacterial, antistatic, fire-retardant etc., can also improve dyeing and finishing technology, play energy saving and reduction
The effect of processing cost.Textile auxiliary to lifted textile industry integral level and the effect in Textile Chain be to pass
Important.Whole world textile auxiliary has nearly 100 classes, produces nearly 1.6 ten thousand kinds, about 4,100,000 tons of annual production.It is wherein American-European
48 classes of textile auxiliary kind, more than 8000 kind;There are 5500 kinds in Japan.It is reported that, world textile auxiliary agent market pin
Sell sales volume of the volume considerably beyond Dyestuff Market.Existing textile auxiliary mainly has scouring agent, coloring agent, levelling agent, softness
Agent, capillary effect elevator, terylene low temperature dyeing carrier, substitute alkali, CT powder, preparation medium, efficiently move back boil powder, hydrogen peroxide stabilizer,
Desiliconizing agent, foaming agent, raising agent, color fixing agent etc..
Specific to China, the textile auxiliary kind that the current country can produce is nearly 2000, and the kind of Jing often productions has 800
Remaining, principal item has 200 or so.China's textile auxiliary yield is big, and the industry output value is high, with wide market prospects.But
Domestic textile auxiliary also larger difference compared with international most advanced level in kind and quality and in terms of synthesis and application technology
Still have to dependence on import away from, special and high-grade textile auxiliary.Also, textile industry is particularly dyeing and finishing industry by national supervisor portion
Door is defined as heavy polluted industry.Impact and make that textile auxiliary comes in the manufacturing and its application process to environment and zoology
Into pollution problem can not be ignored, it would be highly desirable to solve.
Therefore, Devoting Major Efforts To Developing meets the environmentally friendly textile auxiliary of ecodevelopment, the whole competitiveness to improving auxiliary industry, carries
Rise textile auxiliary product quality and technical merit is particularly important, be the key of industry value chain.Also, the weaving developed
Additives Products will not only meet the market demand of domestic dyeing and finishing industry, also reach every quality standard of textile exports, just
Seem particularly necessary.
The content of the invention
To solve above-mentioned technical problem, the present invention provides a kind of environment-friendly type textile auxiliary, by being entered using specific raw material
Row combination, coordinates specific production technology so that the textile auxiliary being prepared from makes that yarn fabric toughness is strong, viscosity stabilization using after
Property is good, and textile auxiliary itself environment-protecting asepsis, the requirement of industry is disclosure satisfy that, with preferable application prospect.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of environment-friendly type textile auxiliary, is prepared by the raw materials in:Dioctyl sodium sulfosuccinate 35-45 parts, second two
Amine tetraacethyl disodium 30-36 parts, poly- methyl silicon resin 28-32 parts, styrene maleic resin 22-26 parts, phthalic acid
Acid anhydride 12-16 parts, polyethylene glycol mono stearate 10-14 parts, AEO 8-10 parts, cocounut oil diglycollic amide 6-8
Part, NPE 4-6 parts, ligninsulfonate 4-6 parts, activated carbon 2-4 parts, barium chloride 1-3 parts, organic acid 3-5 parts,
100 parts of crosslinking agent 3-5 parts, deionized water.
Preferably, any one of the organic acid in palmitic acid, citric acid, linoleic acid.
Preferably, the crosslinking agent is selected from methylene diacrylamine, PEGDMA-400, ethylene glycol two
Any one in glycidol ether.
The preparation method of described environment-friendly type textile auxiliary, comprises the following steps:
(1)Each raw material is accurately weighed by the weight portion;
(2)Cocounut oil diglycollic amide, NPE, ligninsulfonate, activated carbon, barium chloride are added into ball mill
In, ball milling 1-2 hours, then deionized water is added to the mixture after ball milling, stir under the stir speed (S.S.) of 1000-2000 rpm
2-3 hours, obtain preliminary mixed liquor;
(3)Preliminary mixed liquor is sent into reactor, poly- methyl silicon resin, styrene maleic resin, O-phthalic is added
Acid anhydrides, polyethylene glycol mono stearate, uniform rear emulsification 40-50 minutes at a high speed to be mixed, obtain emulsion mixture, are subsequently added
The HCl solution of 0.5 mol/L adjusts pH of mixed to 5.5, is heated to 90 DEG C, is incubated 25-35 minutes;
(4)Liquid to be mixed is cooled to after room temperature, adds dioctyl sodium sulfosuccinate, disodium ethylene diamine tetraacetate, poly alkyl alcohol
Oxygen vinethene, ultrasonically treated 2-3 hours, are subsequently added organic acid, crosslinking agent in ultrasonator, and Jing is high at 60-70 DEG C
Fast shear-mixed obtains finished product.
Preferably, the step(4)In, the power of ultrasonic vibration is 500W, and the time of ultrasonic vibration is 2 hours.
Preferably, the step(4)In, shear rate is 9000-15000 rpm, and shear time is 30 minutes.
Compared with prior art, its advantage is the present invention:
(1)The environment-friendly type textile auxiliary of the present invention is with dioctyl sodium sulfosuccinate, disodium ethylene diamine tetraacetate, poly- methyl silicon tree
Fat, styrene maleic resin are main component, by adding phthalic anhydride, polyethylene glycol mono stearate, fat
Alcohol APEO, cocounut oil diglycollic amide, NPE, ligninsulfonate, activated carbon, barium chloride, organic acid,
Crosslinking agent, deionized water, are aided with the techniques such as ball milling, stirring, emulsification, regulation pH, heating, insulation, ultrasonic vibration, high speed shear,
So that the textile auxiliary being prepared from can make after use, and yarn fabric toughness is strong, viscosity stability is good, and textile auxiliary self loop
Protect nontoxic, the requirement of industry is disclosure satisfy that, with preferable application prospect.
(2)The environment-friendly type textile auxiliary raw material of the present invention is cheap, process is simple, is suitable to heavy industrialization utilization, practical
Property is strong.
Specific embodiment
The technical scheme invented is described in detail with reference to specific embodiment.
Embodiment 1
(1)35 parts of dioctyl sodium sulfosuccinate, 30 parts of disodium ethylene diamine tetraacetate, poly- methyl are accurately weighed by the weight portion
28 parts of silicones, 22 parts of styrene maleic resin, 12 parts of phthalic anhydride, 10 parts of polyethylene glycol mono stearate, fat
8 parts of fat alcohol APEO, 6 parts of cocounut oil diglycollic amide, 4 parts of NPE, 4 parts of ligninsulfonate, activated carbon 2
Part, 1 part of barium chloride, 3 parts of palmitic acid, 3 parts of methylene diacrylamine, 100 parts of deionized water;
(2)Cocounut oil diglycollic amide, NPE, ligninsulfonate, activated carbon, barium chloride are added into ball mill
In, ball milling 1 hour, then deionized water is added to the mixture after ball milling, stir 2 hours under the stir speed (S.S.) of 1000rpm, obtain
Preliminary mixed liquor;
(3)Preliminary mixed liquor is sent into reactor, poly- methyl silicon resin, styrene maleic resin, O-phthalic is added
Acid anhydrides, polyethylene glycol mono stearate, uniform rear emulsification 40 minutes at a high speed to be mixed, obtain emulsion mixture, are subsequently added 0.5
The HCl solution of mol/L adjusts pH of mixed to 5.5, is heated to 90 DEG C, is incubated 25 minutes;
(4)Liquid to be mixed is cooled to after room temperature, adds dioctyl sodium sulfosuccinate, disodium ethylene diamine tetraacetate, poly alkyl alcohol
Oxygen vinethene, ultrasonically treated in ultrasonator, the power of ultrasonic vibration is 500W, and the time of ultrasonic vibration is 2 hours, with
Palmitic acid, methylene diacrylamine are added afterwards, and Jing high speed shears are mixed to get finished product at 60 DEG C, and its medium shear rate is
9000 rpm, shear time is 30 minutes.
The performance test results of obtained environment-friendly type textile auxiliary are as shown in table 1.
Embodiment 2
(1)40 parts of dioctyl sodium sulfosuccinate, 33 parts of disodium ethylene diamine tetraacetate, poly- methyl are accurately weighed by the weight portion
30 parts of silicones, 24 parts of styrene maleic resin, 14 parts of phthalic anhydride, 12 parts of polyethylene glycol mono stearate, fat
9 parts of fat alcohol APEO, 7 parts of cocounut oil diglycollic amide, 5 parts of NPE, 5 parts of ligninsulfonate, activated carbon 3
Part, 2 parts of barium chloride, 4 parts of citric acid, 4 parts of PEGDMA-400,100 parts of deionized water;
(2)Cocounut oil diglycollic amide, NPE, ligninsulfonate, activated carbon, barium chloride are added into ball mill
In, ball milling 1.5 hours, then deionized water is added to the mixture after ball milling, stirring 2.5 is little under the stir speed (S.S.) of 1500 rpm
When, obtain preliminary mixed liquor;
(3)Preliminary mixed liquor is sent into reactor, poly- methyl silicon resin, styrene maleic resin, O-phthalic is added
Acid anhydrides, polyethylene glycol mono stearate, uniform rear emulsification 45 minutes at a high speed to be mixed, obtain emulsion mixture, are subsequently added 0.5
The HCl solution of mol/L adjusts pH of mixed to 5.5, is heated to 90 DEG C, is incubated 30 minutes;
(4)Liquid to be mixed is cooled to after room temperature, adds dioctyl sodium sulfosuccinate, disodium ethylene diamine tetraacetate, poly alkyl alcohol
Oxygen vinethene, ultrasonically treated in ultrasonator, the power of ultrasonic vibration is 500W, and the time of ultrasonic vibration is 2 hours, with
Citric acid, PEGDMA-400 are added afterwards, Jing high speed shears are mixed to get finished product at 65 DEG C, wherein shearing speed
Rate is 12000 rpm, and shear time is 30 minutes.
The performance test results of obtained environment-friendly type textile auxiliary are as shown in table 1.
Embodiment 3
(1)45 parts of dioctyl sodium sulfosuccinate, 36 parts of disodium ethylene diamine tetraacetate, poly- methyl are accurately weighed by the weight portion
32 parts of silicones, 26 parts of styrene maleic resin, 16 parts of phthalic anhydride, 14 parts of polyethylene glycol mono stearate, fat
10 parts of fat alcohol APEO, 8 parts of cocounut oil diglycollic amide, 6 parts of NPE, 6 parts of ligninsulfonate, activated carbon
4 parts, 3 parts of barium chloride, 5 parts of linoleic acid, 5 parts of ethylene glycol diglycidylether, 100 parts of deionized water;
(2)Cocounut oil diglycollic amide, NPE, ligninsulfonate, activated carbon, barium chloride are added into ball mill
In, ball milling 2 hours, then deionized water is added to the mixture after ball milling, stir 3 hours under the stir speed (S.S.) of 2000 rpm,
Obtain preliminary mixed liquor;
(3)Preliminary mixed liquor is sent into reactor, poly- methyl silicon resin, styrene maleic resin, O-phthalic is added
Acid anhydrides, polyethylene glycol mono stearate, uniform rear emulsification 50 minutes at a high speed to be mixed, obtain emulsion mixture, are subsequently added 0.5
The HCl solution of mol/L adjusts pH of mixed to 5.5, is heated to 90 DEG C, is incubated 35 minutes;
(4)Liquid to be mixed is cooled to after room temperature, adds dioctyl sodium sulfosuccinate, disodium ethylene diamine tetraacetate, poly alkyl alcohol
Oxygen vinethene, ultrasonically treated in ultrasonator, the power of ultrasonic vibration is 500W, and the time of ultrasonic vibration is 2 hours, with
Linoleic acid, ethylene glycol diglycidylether are added afterwards, and Jing high speed shears are mixed to get finished product at 70 DEG C, and its medium shear rate is
15000 rpm, shear time is 30 minutes.
The performance test results of obtained environment-friendly type textile auxiliary are as shown in table 1.
Embodiment 4
(1)45 parts of dioctyl sodium sulfosuccinate, 30 parts of disodium ethylene diamine tetraacetate, poly- methyl are accurately weighed by the weight portion
32 parts of silicones, 22 parts of styrene maleic resin, 16 parts of phthalic anhydride, 10 parts of polyethylene glycol mono stearate, fat
10 parts of fat alcohol APEO, 6 parts of cocounut oil diglycollic amide, 6 parts of NPE, 4 parts of ligninsulfonate, activated carbon
4 parts, 1 part of barium chloride, 3 parts of palmitic acid, 5 parts of PEGDMA-400,100 parts of deionized water;
(2)Cocounut oil diglycollic amide, NPE, ligninsulfonate, activated carbon, barium chloride are added into ball mill
In, ball milling 2 hours, then deionized water is added to the mixture after ball milling, stir 3 hours under the stir speed (S.S.) of 1000 rpm,
Obtain preliminary mixed liquor;
(3)Preliminary mixed liquor is sent into reactor, poly- methyl silicon resin, styrene maleic resin, O-phthalic is added
Acid anhydrides, polyethylene glycol mono stearate, uniform rear emulsification 40 minutes at a high speed to be mixed, obtain emulsion mixture, are subsequently added 0.5
The HCl solution of mol/L adjusts pH of mixed to 5.5, is heated to 90 DEG C, is incubated 35 minutes;
(4)Liquid to be mixed is cooled to after room temperature, adds dioctyl sodium sulfosuccinate, disodium ethylene diamine tetraacetate, poly alkyl alcohol
Oxygen vinethene, ultrasonically treated in ultrasonator, the power of ultrasonic vibration is 500W, and the time of ultrasonic vibration is 2 hours, with
Palmitic acid, PEGDMA-400 are added afterwards, Jing high speed shears are mixed to get finished product at 70 DEG C, wherein shearing speed
Rate is 9000 rpm, and shear time is 30 minutes.
The performance test results of obtained environment-friendly type textile auxiliary are as shown in table 1.
Comparative example 1
(1)40 parts of dioctyl sodium sulfosuccinate, 33 parts of disodium ethylene diamine tetraacetate, poly- methyl are accurately weighed by the weight portion
30 parts of silicones, 24 parts of styrene maleic resin, 14 parts of phthalic anhydride, 12 parts of polyethylene glycol mono stearate, fat
9 parts of fat alcohol APEO, 7 parts of cocounut oil diglycollic amide, 5 parts of ligninsulfonate, 3 parts of activated carbon, 4 parts of citric acid, dimethyl
4 parts of polyalkylene glycol acrylate ester, 100 parts of deionized water;
(2)Cocounut oil diglycollic amide, ligninsulfonate, activated carbon are added in ball mill, ball milling 1.5 hours, then to after ball milling
Mixture add deionized water, under the stir speed (S.S.) of 1500 rpm stir 2.5 hours, obtain preliminary mixed liquor;
(3)Preliminary mixed liquor is sent into reactor, poly- methyl silicon resin, styrene maleic resin, O-phthalic is added
Acid anhydrides, polyethylene glycol mono stearate, uniform rear emulsification 45 minutes at a high speed to be mixed, obtain emulsion mixture, are subsequently added 0.5
The HCl solution of mol/L adjusts pH of mixed to 5.5, is heated to 90 DEG C, is incubated 30 minutes;
(4)Liquid to be mixed is cooled to after room temperature, adds dioctyl sodium sulfosuccinate, disodium ethylene diamine tetraacetate, poly alkyl alcohol
Oxygen vinethene, ultrasonically treated in ultrasonator, the power of ultrasonic vibration is 500W, and the time of ultrasonic vibration is 2 hours, with
Citric acid, PEGDMA-400 are added afterwards, Jing high speed shears are mixed to get finished product at 65 DEG C, wherein shearing speed
Rate is 12000 rpm, and shear time is 30 minutes.
The performance test results of obtained environment-friendly type textile auxiliary are as shown in table 1.
Comparative example 2
(1)45 parts of dioctyl sodium sulfosuccinate, 30 parts of disodium ethylene diamine tetraacetate, poly- methyl are accurately weighed by the weight portion
32 parts of silicones, 22 parts of styrene maleic resin, 16 parts of phthalic anhydride, 10 parts of polyethylene glycol mono stearate, fat
10 parts of fat alcohol APEO, 6 parts of NPE, 4 parts of ligninsulfonate, 1 part of barium chloride, 3 parts of palmitic acid, diformazan
5 parts of base polyalkylene glycol acrylate ester, 100 parts of deionized water;
(2)NPE, ligninsulfonate, barium chloride are added in ball mill, ball milling 2 hours, then to after ball milling
Mixture add deionized water, under the stir speed (S.S.) of 1000 rpm stir 3 hours, obtain preliminary mixed liquor;
(3)Preliminary mixed liquor is sent into reactor, poly- methyl silicon resin, styrene maleic resin, O-phthalic is added
Acid anhydrides, polyethylene glycol mono stearate, uniform rear emulsification 40 minutes at a high speed to be mixed, obtain emulsion mixture, are subsequently added 0.5
The HCl solution of mol/L adjusts pH of mixed to 5.5, is heated to 90 DEG C, is incubated 35 minutes;
(4)Liquid to be mixed is cooled to after room temperature, adds dioctyl sodium sulfosuccinate, disodium ethylene diamine tetraacetate, poly alkyl alcohol
Oxygen vinethene, ultrasonically treated in ultrasonator, the power of ultrasonic vibration is 500W, and the time of ultrasonic vibration is 2 hours, with
Palmitic acid, PEGDMA-400 are added afterwards, Jing high speed shears are mixed to get finished product at 70 DEG C, wherein shearing speed
Rate is 9000 rpm, and shear time is 30 minutes.
The performance test results of obtained environment-friendly type textile auxiliary are as shown in table 1.
The environment-friendly type textile auxiliary of embodiment 1-4 and comparative example 1-2 is applied to respectively after yarn fabric carries out extension at break
Rate, viscosity thermal stability, this several tests of toxotest.
Table 1
Elongation at break(%) | Viscosity thermal stability(%) | Toxotest | |
Embodiment 1 | 172.8 | 97.2 | It is non-toxic |
Embodiment 2 | 185.3 | 98.3 | It is non-toxic |
Embodiment 3 | 184.1 | 97.9 | It is non-toxic |
Embodiment 4 | 176.3 | 97.5 | It is non-toxic |
Comparative example 1 | 130.9 | 92.2 | It is non-toxic |
Comparative example 2 | 131.6 | 91.6 | It is non-toxic |
The present invention environment-friendly type textile auxiliary with dioctyl sodium sulfosuccinate, disodium ethylene diamine tetraacetate, poly- methyl silicon resin,
Styrene maleic resin is main component, by adding phthalic anhydride, polyethylene glycol mono stearate, poly alkyl alcohol
Oxygen vinethene, cocounut oil diglycollic amide, NPE, ligninsulfonate, activated carbon, barium chloride, organic acid, crosslinking
Agent, deionized water, are aided with the techniques such as ball milling, stirring, emulsification, regulation pH, heating, insulation, ultrasonic vibration, high speed shear so that
The textile auxiliary being prepared from can make after use that yarn fabric toughness is strong, viscosity stability is good, and the environmentally friendly nothing of textile auxiliary itself
Poison, disclosure satisfy that the requirement of industry, with preferable application prospect.The environment-friendly type textile auxiliary raw material of the present invention is cheap, technique
Simply, heavy industrialization utilization is suitable to, it is practical.
Embodiments of the invention are the foregoing is only, the scope of the claims of the present invention is not thereby limited, it is every using this
Equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, is included within the scope of the present invention.
Claims (6)
1. a kind of environment-friendly type textile auxiliary, it is characterised in that:It is prepared by the raw materials in:Dioctyl sodium sulfosuccinate
35-45 parts, disodium ethylene diamine tetraacetate 30-36 parts, poly- methyl silicon resin 28-32 parts, styrene maleic resin 22-26
Part, phthalic anhydride 12-16 parts, polyethylene glycol mono stearate 10-14 parts, AEO 8-10 parts, cocounut oil
Diglycollic amide 6-8 parts, NPE 4-6 parts, ligninsulfonate 4-6 parts, activated carbon 2-4 parts, barium chloride 1-3
Part, organic acid 3-5 parts, crosslinking agent 3-5 parts, 100 parts of deionized water.
2. environment-friendly type textile auxiliary according to claim 1, it is characterised in that:The organic acid is selected from palmitic acid, lemon
Any one in acid, linoleic acid.
3. environment-friendly type textile auxiliary according to claim 1, it is characterised in that:The crosslinking agent is selected from the propylene of methylene two
Any one in acid amides, PEGDMA-400, ethylene glycol diglycidylether.
4. according to the preparation method of the arbitrary described environment-friendly type textile auxiliary of claim 1-3, it is characterised in that including following step
Suddenly:
(1)Each raw material is accurately weighed by the weight portion;
(2)Cocounut oil diglycollic amide, NPE, ligninsulfonate, activated carbon, barium chloride are added into ball mill
In, ball milling 1-2 hours, then deionized water is added to the mixture after ball milling, stir under the stir speed (S.S.) of 1000-2000 rpm
2-3 hours, obtain preliminary mixed liquor;
(3)Preliminary mixed liquor is sent into reactor, poly- methyl silicon resin, styrene maleic resin, O-phthalic is added
Acid anhydrides, polyethylene glycol mono stearate, uniform rear emulsification 40-50 minutes at a high speed to be mixed, obtain emulsion mixture, are subsequently added
The HCl solution of 0.5 mol/L adjusts pH of mixed to 5.5, is heated to 90 DEG C, is incubated 25-35 minutes;
(4)Liquid to be mixed is cooled to after room temperature, adds dioctyl sodium sulfosuccinate, disodium ethylene diamine tetraacetate, poly alkyl alcohol
Oxygen vinethene, ultrasonically treated 2-3 hours, are subsequently added organic acid, crosslinking agent in ultrasonator, and Jing is high at 60-70 DEG C
Fast shear-mixed obtains finished product.
5. the preparation method of environment-friendly type textile auxiliary according to claim 4, it is characterised in that the step(4)In, surpass
The power that acoustic shock is swung is 500W, and the time of ultrasonic vibration is 2 hours.
6. the preparation method of environment-friendly type textile auxiliary according to claim 4, it is characterised in that the step(4)In, cut
Cutting speed rate is 9000-15000rpm, and shear time is 30 minutes.