CN106637940A - Recycled cotton yarn textile material having skin-protecting and skin-moistening effects and used for gloves and preparation method thereof - Google Patents
Recycled cotton yarn textile material having skin-protecting and skin-moistening effects and used for gloves and preparation method thereof Download PDFInfo
- Publication number
- CN106637940A CN106637940A CN201610998095.XA CN201610998095A CN106637940A CN 106637940 A CN106637940 A CN 106637940A CN 201610998095 A CN201610998095 A CN 201610998095A CN 106637940 A CN106637940 A CN 106637940A
- Authority
- CN
- China
- Prior art keywords
- skin
- textile material
- gloves
- cotton
- cotton yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a recycled cotton yarn textile material having skin-protecting and skin-moistening effects and used for gloves. The recycled cotton yarn textile material is prepared from the following raw materials in parts by weight: 80-100 parts of polyester cotton cloth strips with the cotton content of 40%-60%, 5-10 parts of soybean protein fibers, 0.5-1 part of avocado oil, 0.3-0.5 part of cetyl alcohol, 0.5-1 part of tetrabutyl titanate, 3-5 parts of liquid paraffin, 0.3-0.5 part of nonylphenol ethoxylates, 0.5-1 part of polysorbate-80, 0.2-0.4 part of rosin glycerin ester and 0.5-1 part of allantoin. The recycled cotton yarn textile material disclosed by the invention not only has good strength and wear-resisting performance, but also has skin-protecting and skin-moistening health-care effects, relatively high durability and relatively long service life; and meanwhile, the environment-friendly performance is good.
Description
Technical field
The present invention relates to textile material technical field, more particularly to a kind of gloves regeneration cotton with skin care soothing effect
Yarn textile material and preparation method thereof.
Background technology
China is that fabric clothing maximum in the world is produced and exported country.With economic level and people's living standard
Improve, textile waste is in increase trend, not only waste of resource but also has caused environmental pollution.Regeneration cotton yarn is by process of textile production, clothes
The particle pieces of cloth produced during dress cutting and the waste material such as textile fabric abandoned in daily routines re-work made by yarn
Line.By the way that textile waste cycling and reutilization is made into regeneration cotton yarn, to enterprise considerable economic benefit can be brought, and for ring
Border is administered and is contributed.
The of many uses of cotton yarn is regenerated, is usually used in making mop, gloves, towel, bedding, clothing item etc..Gloves
As conventional articles for labour protection, need with good mechanical performance, anti-wear performance and stability.However, regeneration cotton yarn
It is, using the cotton yarn that re-works of textile raw material for reclaiming, there is that fiber is short, the low problem of strength, mechanical performance and wear-resisting
Property is poor, and durability is low, has had a strong impact on its service life and barrier propterty.CN201410511382 utilizes bisphenol a resin pair
Cotton is processed, and can effectively improve the intensity of cotton.However, the environmental-protecting performance of bisphenol a resin is poor, and it is not suitable for using
In for a long time with the glove product of human contact.To meet the requirement of gloves textile material, in addition it is also necessary to the performance to regenerating cotton yarn
Improved.
The content of the invention
The object of the invention is exactly to make up the defect of prior art, there is provided a kind of intensity is high, anti-wear performance is good, durability
By force, the gloves with skin care soothing effect of good environmental protection regeneration cotton yarn textile material and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of gloves with skin care soothing effect regeneration cotton yarn textile material, it is obtained by the raw material of following weight parts:
Cotton content is the polyester-cotton blend cloth 80-100, soybean fiber 5-10, avocado oil 0.5-1, cetanol 0.3- of 40-60%
0.5, butyl titanate 0.5-1, atoleine 3-5, NPE 0.3-0.5, Tween-80 0.5-1, pine
Fragrant glyceride 0.2-0.4, allantoin 0.5-1.
A kind of preparation method of regeneration cotton yarn textile material of the gloves with skin care soothing effect, comprises the following steps:
(1)Regeneration cotton is split into after polyester-cotton blend cloth is bleached, through clearing up impurity, combing sliver and combing fiber is obtained
Sliver;
(2)By step(1)The fiber sliver for obtaining merges to form sliver with soybean fiber, then through spinning processing
Technique obtains yarn fabric;
(3)First avocado oil, cetanol, butyl titanate, ester gum are mixed with atoleine and stirs 2- after 80-90 DEG C
4h, is subsequently adding Tween-80 and obtains oil phase in 200-400r/min stirring 0.5-1h, and NPE is added
Dispersed with stirring is uniform in the water of 30-40 times of weight obtains water phase, and then oil phase is slowly added dropwise in water phase and in 1200-1500r/
Min stirs 0.5-1h, is eventually adding remaining raw material and stirs, and obtains complex emulsions;
(4)By step(3)The complex emulsions for obtaining are coated uniformly on step(2)On the yarn fabric for obtaining, then in 60-80 DEG C of baking
It is dry, obtain final product the regeneration cotton yarn textile material of the gloves with skin care soothing effect.
It is an advantage of the invention that:
The present invention is composite modified as raw material using atoleine, butyl titanate and ester gum, and Tween-80 is used as table
Face activating agent, oil phase is obtained using avocado oil, cetanol as additive, then carries out emulsifying by NPE
To complex emulsions, textile surfaces and inside can be securely attached to, be effectively improved intensity, the anti-wear performance of yarn fabric, and
Effect of yarn fabric skin care moisturizing is given, by textile waste polyester-cotton blend cloth as raw material, obtaining with soybean fiber blended
To yarn fabric be coated and process and dry, so as to get regeneration cotton yarn textile material not only there is good intensity and wear-resisting
Performance, the also health-care effect of skin care moisturizing, durability and service life it is higher, while good environmental protection.
Specific embodiment
A kind of gloves with skin care soothing effect regeneration cotton yarn textile material, by the component raw material of following weight (kg)
It is prepared from:
Cotton content is 40% polyester-cotton blend cloth 80, soybean fiber 5, avocado oil 0.5, cetanol 0.3, butyl titanate 0.5,
Atoleine 3, NPE 0.3, Tween-80 0.5, ester gum 0.2, allantoin 0.5.
A kind of preparation method of regeneration cotton yarn textile material of the gloves with skin care soothing effect, comprises the following steps:
(1)Regeneration cotton is split into after polyester-cotton blend cloth is bleached, through clearing up impurity, combing sliver and combing fiber is obtained
Sliver;
(2)By step(1)The fiber sliver for obtaining merges to form sliver with soybean fiber, then through spinning processing
Technique obtains yarn fabric;
(3)First avocado oil, cetanol, butyl titanate, ester gum are mixed with atoleine and stirs 2h after 80 DEG C, so
Tween-80 is added afterwards and oil phase is obtained in 200r/min stirring 0.5h, by NPE 30 times of weight of addition
Dispersed with stirring is uniform in water obtains water phase, and then oil phase is slowly added dropwise in water phase and 0.5h is stirred in 1200r/min, finally adds
Enter remaining raw material to stir, obtain complex emulsions;
(4)By step(3)The complex emulsions for obtaining are coated uniformly on step(2)On the yarn fabric for obtaining, then dry in 60 DEG C,
Obtain final product the regeneration cotton yarn textile material of the gloves with skin care soothing effect.
Regeneration cotton yarn textile material obtained above tears strong compared with the textile material that common cotton Jing weavings are obtained
Power improves 34%.
Claims (2)
1. a kind of gloves with skin care soothing effect are used and regenerate cotton yarn textile material, it is characterised in that it is by following weight
The raw material of part is obtained:
Cotton content is the polyester-cotton blend cloth 80-100, soybean fiber 5-10, avocado oil 0.5-1, cetanol 0.3- of 40-60%
0.5, butyl titanate 0.5-1, atoleine 3-5, NPE 0.3-0.5, Tween-80 0.5-1, pine
Fragrant glyceride 0.2-0.4, allantoin 0.5-1.
2. a kind of use of the gloves with skin care soothing effect according to claim 1 regenerates the preparation side of cotton yarn textile material
Method, it is characterised in that comprise the following steps:
(1)Regeneration cotton is split into after polyester-cotton blend cloth is bleached, through clearing up impurity, combing sliver and combing fiber is obtained
Sliver;
(2)By step(1)The fiber sliver for obtaining merges to form sliver with soybean fiber, then through spinning processing
Technique obtains yarn fabric;
(3)First avocado oil, cetanol, butyl titanate, ester gum are mixed with atoleine and stirs 2- after 80-90 DEG C
4h, is subsequently adding Tween-80 and obtains oil phase in 200-400r/min stirring 0.5-1h, and NPE is added
Dispersed with stirring is uniform in the water of 30-40 times of weight obtains water phase, and then oil phase is slowly added dropwise in water phase and in 1200-1500r/
Min stirs 0.5-1h, is eventually adding remaining raw material and stirs, and obtains complex emulsions;
(4)By step(3)The complex emulsions for obtaining are coated uniformly on step(2)On the yarn fabric for obtaining, then in 60-80 DEG C of baking
It is dry, obtain final product the regeneration cotton yarn textile material of the gloves with skin care soothing effect.