CN106637497A - Negative ion polyester fiber - Google Patents
Negative ion polyester fiber Download PDFInfo
- Publication number
- CN106637497A CN106637497A CN201510486180.3A CN201510486180A CN106637497A CN 106637497 A CN106637497 A CN 106637497A CN 201510486180 A CN201510486180 A CN 201510486180A CN 106637497 A CN106637497 A CN 106637497A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyester fiber
- negative ion
- anion
- far infrared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the technical field of polyester fibers, particularly to negative ion polyester fibers, which comprise, by mass, 20-30 parts of polyester fiber slices, 5-12 parts of negative ion masterbatch, 5-10 parts of a polyamide resin, 3-8 parts of a silane coupling agent, 10-15 parts of super-dispersed negative ion powder, 20-35 parts of a nanometer antibacterial agent, 8-13 parts of a far infrared ray emitter, and 4-10 parts of phosphite. According to the present invention, by using the formula, the negative ion polyester fibers have characteristics of good use performance, high negative ion generation and wide application range, and the preparation method has characteristics of simple operation and easy promotion and application.
Description
Technical field
The present invention relates to polyester fiber technical field, particularly a kind of anion polyester fiber.
Background technology
Synthetic fibers of the polyester fiber by obtained by the polyester Jing spinning of organic dibasic acid and dihydroxylic alcohols polycondensation.Work
In a large number the polyester fiber of production is used made by polyethylene terephthalate to industryization, China's trade name
Terylene.It is the first big kind of current synthetic fibers.The production process of terylene includes polycondensation and melt spinning two
Part.Raw material is mainly obtained from petroleum cracking, also can be obtained from coal and natural gas.Petroleum cracking is obtained
Toluene, dimethylbenzene and ethene etc., terephthalic acid (TPA) or dimethyl terephthalate (DMT) are obtained Jing after chemical process
And ethylene glycol.Because terephthalic acid (TPA) is difficult to refine in early stage PET production, terephthalic acid (TPA) diformazan is once used
Ester and ethylene glycol are raw material.
The content of the invention
The technical problem to be solved in the invention is to provide a kind of anion polyester fiber.
To solve above-mentioned technical problem, a kind of anion polyester fiber of the present invention, according to mass fraction meter bag
Include following components：Polyester fiber section 20-30 parts, anion master batch 5-12 part, polyamide 5-10
Part, silane coupler 3-8 parts, ultra-dispersed negative ion powder 10-15 parts, nano antibacterial agent 20-35 parts, far
Infrared emitting agent 8-13 parts, phosphite ester 4-10 parts.
Further, following components is included according to mass fraction meter：Polyester fiber is cut into slices 20 parts, and anion is female
5 parts of grain, 5 parts of polyamide, 3 parts of silane coupler, 10 parts of ultra-dispersed negative ion powder, nano-antibacterial
20 parts of agent, 8 parts of far infrared cast charge, 4 parts of phosphite ester.
Further, following components is included according to mass fraction meter：Polyester fiber is cut into slices 30 parts, and anion is female
12 parts of grain, 10 parts of polyamide, 8 parts of silane coupler, 15 parts of ultra-dispersed negative ion powder, nanometer resists
35 parts of microbial inoculum, 13 parts of far infrared cast charge, 10 parts of phosphite ester.
Further, following components is included according to mass fraction meter：Polyester fiber is cut into slices 23 parts, and anion is female
9 parts of grain, 6 parts of polyamide, 5 parts of silane coupler, 12 parts of ultra-dispersed negative ion powder, nano-antibacterial
25 parts of agent, 9 parts of far infrared cast charge, 5 parts of phosphite ester.
Further, following components is included according to mass fraction meter：Polyester fiber is cut into slices 27 parts, and anion is female
10 parts of grain, 8 parts of polyamide, 6 parts of silane coupler, 14 parts of ultra-dispersed negative ion powder, nanometer resists
30 parts of microbial inoculum, 11 parts of far infrared cast charge, 8 parts of phosphite ester.
After above-mentioned formula, the anion polyester fiber of the present invention, performance is good, and anion-generating capacity is high,
Applied range；In addition, the preparation method of the anion polyester fiber of the present invention, simple to operate, it is easy to push away
Wide application.
Specific embodiment
A kind of anion polyester fiber of the present invention, according to mass fraction meter following components is included：Polyester fiber is cut
Piece 20-30 parts, anion master batch 5-12 part, polyamide 5-10 parts, silane coupler 3-8 parts,
Ultra-dispersed negative ion powder 10-15 parts, nano antibacterial agent 20-35 parts, far infrared cast charge 8-13 parts are sub-
Phosphate 4-10 parts.
Embodiment one：
Include following components according to mass fraction meter：Polyester fiber is cut into slices 20 parts, 5 parts of anion master batch, is gathered
5 parts of amide resin, 3 parts of silane coupler, 10 parts of ultra-dispersed negative ion powder, 20 parts of nano antibacterial agent,
8 parts of far infrared cast charge, 4 parts of phosphite ester.
Embodiment two：
Include following components according to mass fraction meter：Polyester fiber is cut into slices 30 parts, 12 parts of anion master batch, is gathered
10 parts of amide resin, 8 parts of silane coupler, 15 parts of ultra-dispersed negative ion powder, 35 parts of nano antibacterial agent,
13 parts of far infrared cast charge, 10 parts of phosphite ester.
Embodiment three：
Include following components according to mass fraction meter：Polyester fiber is cut into slices 23 parts, 9 parts of anion master batch, is gathered
6 parts of amide resin, 5 parts of silane coupler, 12 parts of ultra-dispersed negative ion powder, 25 parts of nano antibacterial agent,
9 parts of far infrared cast charge, 5 parts of phosphite ester.
Embodiment four：
Include following components according to mass fraction meter：Polyester fiber is cut into slices 27 parts, 10 parts of anion master batch, is gathered
8 parts of amide resin, 6 parts of silane coupler, 14 parts of ultra-dispersed negative ion powder, 30 parts of nano antibacterial agent,
11 parts of far infrared cast charge, 8 parts of phosphite ester.
Although the foregoing describing the specific embodiment of the present invention, those skilled in the art should manage
Solution, these are merely illustrative of, and can make various changes or modifications to present embodiment, without departing from send out
Bright principle and essence, protection scope of the present invention is only limited by the claims that follow.
Claims (5)
1. a kind of anion polyester fiber, it is characterised in that include following components according to mass fraction meter：Polyester is fine
Dimension section 20-30 parts, anion master batch 5-12 part, polyamide 5-10 parts, silane coupler 3-8
Part, ultra-dispersed negative ion powder 10-15 parts, nano antibacterial agent 20-35 parts, far infrared cast charge 8-13 parts,
Phosphite ester 4-10 parts.
2. according to a kind of anion polyester fiber described in claim 1, it is characterised in that according to mass fraction meter
Including following components：Polyester fiber is cut into slices 20 parts, 5 parts of anion master batch, 5 parts of polyamide, silane
3 parts of coupling agent, 10 parts of ultra-dispersed negative ion powder, 20 parts of nano antibacterial agent, 8 parts of far infrared cast charge,
4 parts of phosphite ester.
3. according to a kind of anion polyester fiber described in claim 1, it is characterised in that according to mass fraction meter
Including following components：Polyester fiber is cut into slices 30 parts, 12 parts of anion master batch, 10 parts of polyamide, silicon
8 parts of alkane coupling agent, 15 parts of ultra-dispersed negative ion powder, 35 parts of nano antibacterial agent, far infrared cast charge 13
Part, 10 parts of phosphite ester.
4. according to a kind of anion polyester fiber described in claim 1, it is characterised in that according to mass fraction meter
Including following components：Polyester fiber is cut into slices 23 parts, 9 parts of anion master batch, 6 parts of polyamide, silane
5 parts of coupling agent, 12 parts of ultra-dispersed negative ion powder, 25 parts of nano antibacterial agent, 9 parts of far infrared cast charge,
5 parts of phosphite ester.
5. according to a kind of anion polyester fiber described in claim 1, it is characterised in that according to mass fraction meter
Including following components：Polyester fiber is cut into slices 27 parts, 10 parts of anion master batch, 8 parts of polyamide, silicon
6 parts of alkane coupling agent, 14 parts of ultra-dispersed negative ion powder, 30 parts of nano antibacterial agent, far infrared cast charge 11
Part, 8 parts of phosphite ester.