CN103214710A - Environmental-friendly flame retardation plastic pallet - Google Patents
Environmental-friendly flame retardation plastic pallet Download PDFInfo
- Publication number
- CN103214710A CN103214710A CN 201310094126 CN201310094126A CN103214710A CN 103214710 A CN103214710 A CN 103214710A CN 201310094126 CN201310094126 CN 201310094126 CN 201310094126 A CN201310094126 A CN 201310094126A CN 103214710 A CN103214710 A CN 103214710A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic pallet
- friendly flame
- environmental
- wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses an environmental-friendly flame retardation plastic pallet, including the following components by weight: 30-50 parts of PE, 20-30 parts of PP, 10-15 parts of calcium carbonate, 2-5 parts of an antimony-based environmental-friendly flame retardation agent, 3-5 parts of pentaerythritol, 8-12 parts of zinc borate, 7-10 parts of ammonium polyphosphate, 1.5-2 parts of a polyolefin elastomer, 0.5-1 part of stearic acid, 0.5-1 parts of a silane coupling agent, and 0.5-1 part of PE wax. The plastic pallet of the present invention has good flame retardant properties and environmental durability.
Description
Technical field
The present invention relates to a kind of plastic pallet, be specifically related to a kind of environment friendly flame-retardant plastic pallet.
Background technology
The pallet that is made of plastics, light weight, inexpensive is liked by the human consumer deeply, but plastics should not degrade, and easily cause environmental pollution, and very easily burning discharges toxic gas, therefore can raise the cost in production, transportation, use.Fire retardant is also arranged in the market, and flame retardant effect is undesirable, and price is higher.
Summary of the invention
The objective of the invention is at the deficiencies in the prior art, a kind of environment friendly flame-retardant plastic pallet is provided.
For achieving the above object, the technical solution used in the present invention is as follows: a kind of prescription of environment friendly flame-retardant plastic pallet, raw material is made up of following compositions in portion by weight: PE30-50 part, PP20-30 part, lime carbonate 10-15 part, the nano combined environmental protection fire retarding agent 5-10 of antimony base part, zinc borate 8-12 part, ammonium polyphosphate 7-10 part, polyolefin elastomer 1.5-2 part, stearic acid 0.5-1 part, silane coupling agent 0.5-1 part, PE wax 0.5-1 part.。
Its production technique may further comprise the steps:
(a) with the nano combined environmental protection fire retarding agent 5-10 of antimony base part, zinc borate 8-12 part, silane coupling agent 0.5-1 part 120 ℃ of following high-speed mixing;
(b) with (a) mixture and PE30-50 part, PP20-30 part, lime carbonate 10-15 part, ammonium polyphosphate 7-10 part, polyolefin elastomer 1.5-2 part, stearic acid 0.5-1 part, PE wax 0.5-1 part high-speed mixing, granulation, injecting products.
Beneficial effect of the present invention: plastic pallet of the present invention, have good flame retardancy, and environmental protection, easily degraded, mechanical property is strong, and production cost is low.
Embodiment
The present invention is further illustrated below in conjunction with specific embodiment.
Embodiment 1
A kind of prescription of environment friendly flame-retardant plastic pallet, raw material is made up of following compositions in portion by weight: PE50 part, PP20 part, 10 parts in lime carbonate, 10 parts of the nano combined environmental protection fire retarding agents of antimony base, 12 parts of zinc borates, 7 parts of ammonium polyphosphates, 1.5 parts of polyolefin elastomers, 1 part of stearic acid, 0.5 part of silane coupling agent, 1 part in PE wax.
Its production technique may further comprise the steps:
(a) with 0.5 part of 10 parts of the nano combined environmental protection fire retarding agent of antimony base, 12 parts of zinc borates, silane coupling agent 120 ℃ of following high-speed mixing;
(b) with (a) mixture and PE50 part, PP20 part, 10 parts in lime carbonate, 7 parts of ammonium polyphosphates, 1.5 parts of polyolefin elastomers, 1 part of stearic acid, 1 part of high-speed mixing of PE wax, granulation, injecting products.
Embodiment 2
A kind of prescription of environment friendly flame-retardant plastic pallet, raw material is made up of following compositions in portion by weight: PE30 part, PP30 part, 15 parts in lime carbonate, 5 parts of the nano combined environmental protection fire retarding agents of antimony base, 8 parts of zinc borates, 10 parts of ammonium polyphosphates, 2 parts of polyolefin elastomers, 0.5 part of stearic acid, 1 part of silane coupling agent, 0.5 part in PE wax.
Its production technique may further comprise the steps:
(a) with 1 part of 5 parts of the nano combined environmental protection fire retarding agent of antimony base, 8 parts of zinc borates, silane coupling agent 120 ℃ of following high-speed mixing;
(b) with (a) mixture and PE30 part, PP30 part, 15 parts in lime carbonate, 10 parts of ammonium polyphosphates, 2 parts of polyolefin elastomers, 0.5 part of stearic acid, 1 part of high-speed mixing of PE wax, granulation, injecting products.
Claims (2)
1. environment friendly flame-retardant plastic pallet, it is characterized in that: raw material is grouped into by the one-tenth of following weight part: PE30-50 part, PP20-30 part, lime carbonate 10-15 part, the nano combined environmental protection fire retarding agent 5-10 of antimony base part, zinc borate 8-12 part, ammonium polyphosphate 7-10 part, polyolefin elastomer 1.5-2 part, stearic acid 0.5-1 part, silane coupling agent 0.5-1 part, PE wax 0.5-1 part.
2. a kind of environment friendly flame-retardant plastic pallet according to claim 1, it is characterized in that: the making processes of described plastic pallet is:
(a) with the nano combined environmental protection fire retarding agent 5-10 of antimony base part, zinc borate 8-12 part, silane coupling agent 0.5-1 part 120 ℃ of following high-speed mixing;
(b) with (a) mixture and PE30-50 part, PP20-30 part, lime carbonate 10-15 part, ammonium polyphosphate 7-10 part, polyolefin elastomer 1.5-2 part, stearic acid 0.5-1 part, PE wax 0.5-1 part high-speed mixing, granulation, injecting products.