CN106636782A - 适用于汽车结构件的铸造铝硅合金 - Google Patents

适用于汽车结构件的铸造铝硅合金 Download PDF

Info

Publication number
CN106636782A
CN106636782A CN201510713387.XA CN201510713387A CN106636782A CN 106636782 A CN106636782 A CN 106636782A CN 201510713387 A CN201510713387 A CN 201510713387A CN 106636782 A CN106636782 A CN 106636782A
Authority
CN
China
Prior art keywords
cast
mass percent
aluminum alloy
automobile structure
casting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510713387.XA
Other languages
English (en)
Inventor
李道源
章玲敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Yongmao Thai Beijing Great Automotive Components Company Limited
Original Assignee
SHANGHAI WANTAI AUTO PARTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI WANTAI AUTO PARTS CO Ltd filed Critical SHANGHAI WANTAI AUTO PARTS CO Ltd
Priority to CN201510713387.XA priority Critical patent/CN106636782A/zh
Publication of CN106636782A publication Critical patent/CN106636782A/zh
Pending legal-status Critical Current

Abstract

本发明涉及硅作次主要成分的铝基合金领域，具体为一种适用于汽车结构件的铸造铝硅合金。一种适用于汽车结构件的铸造铝硅合金，包括Al和Si，Si的质量百分比为10%～11%，其特征是：还包括Sr、Ti、Mg和Mn，各元素的质量百分比分别为：Sr：0.015%～0.025%；Ti：0.05%～0.15%；Mg：0.25%～0.33；Mn：0.55%～0.85；余量为Al。本发明机械性能高，铸造性能好。

Description

适用于汽车结构件的铸造铝硅合金
技术领域
本发明涉及硅作次主要成分的铝基合金领域，具体为一种适用于汽车结构件的铸造铝硅合金。
背景技术
在航空、汽车制造领域，由于需要尽可能降低零部件重量以省油减耗，密度低、热传导性佳铝合金因而获得广泛应用。汽车结构件多数结构复杂，对机械性能要求高，如箱体类零件壁薄而形状复杂，目前多采用高压铸造，但由于受铝合金性能的限制，很难达到有高延展性的要求，抗拉强度、屈服强度、延伸率等指标都不理想，铸造时废品率高。
发明内容
为了克服现有技术的缺陷，提供一种机械性能高的铝合金，本发明公开了一种适用于汽车结构件的铸造铝硅合金。
本发明通过如下技术方案达到发明目的：
一种适用于汽车结构件的铸造铝硅合金，包括Al和Si，Si的质量百分比为10%～11%，其特征是：还包括Sr、Ti、Mg和Mn，各元素的质量百分比分别为：Sr：0.015%～0.025%；Ti：0.05%～0.15%；Mg：0.25%～0.33；Mn：0.55%～0.85；余量为Al。
所述的适用于汽车结构件的铸造铝硅合金，其特征是：还包括Cu、Pb、Sn、Zn和Fe，各元素的质量百分比分别为：Cu≤0.05%；Pb≤0.05%；Sn≤0.05%；Zn≤0.1%；Fe≤0.15%；其他杂质的质量百分比单列不大于0.05%且总计不大于0.15%。
本发明在压铸时的各项机械性能指标如下：抗拉强度σb为318MPa；屈服强度σ0.2为176MPa，延伸率δS为8.5%。本发明的材料铸造性能好，铸造时废品率低，是取代灰铸铁或合金铸铁的新型材料。
本发明的有益效果是：机械性能高，铸造性能好。
具体实施方式
以下通过具体实施例进一步说明本发明。
实施例1
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg和Mn，各元素的质量百分比分别为：
Sr：0.015%；Ti：0.05%；Mg：0.25%；Mn：0.55%；Si：10%；Al：余量。
本实施例压铸时的各项机械性能指标如下：抗拉强度σb为318MPa；屈服强度σ0.2为176MPa，延伸率δS为8.5%。
实施例2
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg和Mn，各元素的质量百分比分别为：
Sr：0.017%；Ti：0.07%；Mg：0.27%；Mn：0.6%；Si：10.2%；Al：余量。
实施例3
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg和Mn，各元素的质量百分比分别为：
Sr：0.019%；Ti：0.09%；Mg：0.29%；Mn：0.65%；Si：10.4%；Al：余量。
实施例4
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg和Mn，各元素的质量百分比分别为：
Sr：0.021%；Ti：0.11%；Mg：0.31%；Mn：0.7%；Si：10.6%；Al：余量。
实施例5
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg和Mn，各元素的质量百分比分别为：
Sr：0.023%；Ti：0.13%；Mg：0.33%；Mn：0.75%；Si：10.8%；Al：余量。
实施例6
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg和Mn，各元素的质量百分比分别为：
Sr：0.025%；Ti：0.15%；Mg：0.33%；Mn0.8：%；Si：11%；Al：余量。
实施例7
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg和Mn，各元素的质量百分比分别为：
Sr：0.025%；Ti：0.15%；Mg：0.33%；Mn：0.85%；Si：11%；Al：余量。
实施例8
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg、Mn、Cu、Pb、Sn、Zn和Fe，各元素的质量百分比分别为：
Sr：0.015%；Ti：0.05%；Mg：0.25%；Mn：0.55%；Si：10%；Cu：0.01%；Pb：0.01%；Sn：0.01%；Zn：0.02%；Fe：0.03；Al：余量。
实施例9
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg、Mn、Cu、Pb、Sn、Zn和Fe，各元素的质量百分比分别为：
Sr：0.017%；Ti：0.07%；Mg：0.27%；Mn：0.6%；Si：10.2%；Cu：0.01%；Pb：0.01%；Sn：0.01%；Zn：0.02%；Fe：0.03；Al：余量。
实施例10
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg、Mn、Cu、Pb、Sn、Zn和Fe，各元素的质量百分比分别为：
Sr：0.019%；Ti：0.09%；Mg：0.29%；Mn：0.65%；Si：10.4%；Cu：0.02%；Pb：0.02%；Sn：0.02%；Zn：0.04%；Fe：0.06；Al：余量。
实施例11
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg、Mn、Cu、Pb、Sn、Zn和Fe，各元素的质量百分比分别为：
Sr：0.021%；Ti：0.11%；Mg：0.31%；Mn：0.7%；Si：10.6%；Cu：0.03%；Pb：0.03%；Sn：0.03%；Zn：0.06%；Fe：0.09；Al：余量。
实施例12
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg、Mn、Cu、Pb、Sn、Zn和Fe，各元素的质量百分比分别为：
Sr：0.023%；Ti：0.13%；Mg：0.33%；Mn：0.75%；Si：10.8%；Cu：0.04%；Pb：0.04%；Sn：0.04%；Zn：0.08%；Fe：0.12；Al：余量。
实施例13
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg、Mn、Cu、Pb、Sn、Zn和Fe，各元素的质量百分比分别为：
Sr：0.025%；Ti：0.15%；Mg：0.33%；Mn：0.8%；Si：11%；Cu：0.05%；Pb：0.05%；Sn：0.05%；Zn：0.1%；Fe：0.15；Al：余量。
实施例14
一种适用于汽车结构件的铸造铝硅合金，包括Al、Si、Sr、Ti、Mg、Mn、Cu、Pb、Sn、Zn和Fe，各元素的质量百分比分别为：
Sr：0.025%；Ti：0.15%；Mg：0.33%；Mn：0.85%；Si：11%；Cu：0.05%；Pb：0.05%；Sn：0.05%；Zn：0.1%；Fe：0.15；Al：余量。

Claims (2)

1. 一种适用于汽车结构件的铸造铝硅合金，包括Al和Si，Si的质量百分比为10%～11%，其特征是：还包括Sr、Ti、Mg和Mn，各元素的质量百分比分别为：Sr：0.015%～0.025%；Ti：0.05%～0.15%；Mg：0.25%～0.33；Mn：0.55%～0.85；余量为Al。
2. 如权利要求1所述的适用于汽车结构件的铸造铝硅合金，其特征是：还包括Cu、Pb、Sn、Zn和Fe，各元素的质量百分比分别为：Cu≤0.05%；Pb≤0.05%；Sn≤0.05%；Zn≤0.1%；Fe≤0.15%；其他杂质的质量百分比单列不大于0.05%且总计不大于0.15%。
CN201510713387.XA 2015-10-28 2015-10-28 适用于汽车结构件的铸造铝硅合金 Pending CN106636782A (zh)