CN106633986A - 一种木粉工艺品及其制备方法 - Google Patents
一种木粉工艺品及其制备方法 Download PDFInfo
- Publication number
- CN106633986A CN106633986A CN201611196340.1A CN201611196340A CN106633986A CN 106633986 A CN106633986 A CN 106633986A CN 201611196340 A CN201611196340 A CN 201611196340A CN 106633986 A CN106633986 A CN 106633986A
- Authority
- CN
- China
- Prior art keywords
- parts
- wood powder
- handicraft
- gum
- latex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种木粉工艺品及其制备方法。包括如下重量份数的原料：木粉300‑600份，树脂30‑100份，树胶30‑50份，增韧剂50‑100份，凹凸棒土20‑50份，乳胶50‑200份。本发明制备的工艺品，防水和防火性能高，抗拉和抗压强度高，塑形较好，塑形后不容易变形，制备方法简单，适合大规模工业化生产。
Description
技术领域
本发明涉及工艺品技术开发领域，特别涉及一种木粉工艺品及其制备方法。
背景技术
工艺品是生活中必不可少的用品。现代工艺品的种类繁多，有陶瓷工艺品，塑料工艺品，藤蔓工艺品，金属工艺品等，各种工艺品的制备方法多种多样，金属工艺品造价高，制备方法复杂，制备的能耗较高，藤蔓工艺品一般需要手工编织，人工成本高，塑料工艺品产生令人不愉快的气味，对人体健康不利，陶瓷工艺品制备困难，且成品率低，需要烧制，能耗较高。
专利201310001678.7公开了一种工艺品及其制备方法。，包括以下重量份的原料：树脂1000份，促进剂2～7份，固化剂3～10份。该技术克服了温度和湿度对工艺品成型的影响，避免了因湿度带来的工艺品中易产生水泡，因温度带来的工艺品易断裂分层，或不易成型的问题。制得的工艺品平整顺滑、色彩均匀、透明，可体现各种花纹的原有的美感，给人视觉上的享受。但是，该工艺品的质量依赖于天然桃壳的质量，制备的产品质量不均一。专利201110419590.8公开了一种高硬度石膏香薰工艺品及其制备方法，由以下重量比的原料制成：石膏粉CaSO4-2H2O 74.5％，水20.5-21％，烧结高岭土3％，硅氧烷水性分散剂1％，DH高分子改性树脂0.5-1％。该工艺品的应用范围比较窄。
发明内容
本发明是为了克服上述现有技术中缺陷，提出一种木粉工艺品及其制备方法。
一种木粉工艺品，包括如下重量份数的原料：木粉300-600份，树脂30-100份，树胶30-50份，增韧剂50-100份，凹凸棒土20-50份，乳胶50-200份。
所述树胶为桃胶，黄蓍胶，茄替胶，卡拉雅胶，罗望子胶中的一种或一种以上。
所述树脂为环氧树脂，丙烯酸树脂，苯乙烯-丁二烯-苯乙烯嵌段共聚物，苯乙烯-异戊二烯-苯乙烯嵌段共聚物，苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物中的一种或一种以上。
所述增韧剂为聚丙烯纤维，石棉段，甲基丙烯酸甲酯一丁二烯一苯乙烯共聚物，4-叔丁基苯硼酸，苯甲酰中乌头胺盐酸盐中的一种或一种以上。
所述乳胶为天然乳胶，聚丁二烯乳胶，丁苯乳胶，羧基丁腈胶乳胶中的一种或一种以上。
所述工艺品中还含有1-3份亚硫酸金钠。
上述的工艺品的制备方法，按照如下步骤进行：
(1)按照重量份数，取树胶30-50份，加热至60-80℃，加入木粉300-600份，凹凸棒土20-50份，搅拌均匀；
(2)将温度升至80-90℃，加入树脂30-100份，增韧剂50-100份，搅拌均匀；
(3)将温度降至室温，加入乳胶50-200份，搅拌均匀，倾倒在模具中成型，自然晾干或者烘干制成。
与现有技术相比，本发明具有如下有益效果：本发明制备的木粉工艺品，防水和防火性能高，抗拉和抗压强度高，塑形较好，塑形后不容易变形，制备方法简单，适合大规模工业化生产。
具体实施方式
下面对本发明的具体实施方式进行详细描述，但应当理解本发明的保护范围并不受具体实施方式的限制。
实施例1
一种木粉工艺品，包括如下重量份数的原料：木粉450份，环氧树脂60份，桃胶40份，聚丙烯纤维60份，凹凸棒土30份，天然乳胶100份。
上述的工艺品的制备方法，按照如下步骤进行：
(1)按照重量份数，取桃胶40份，加热至70℃，加入木粉450份，凹凸棒土30份，搅拌均匀；
(2)将温度升至85℃，加入环氧树脂60份，聚丙烯纤维60份，搅拌均匀；
(3)将温度降至室温，加入天然乳胶100份，搅拌均匀，倾倒在模具中成型，自然晾干或者烘干制成。
实施例2
一种木粉工艺品，包括如下重量份数的原料：木粉300份，丙烯酸树脂30份，黄蓍胶30份，石棉段50份，凹凸棒土20份，聚丁二烯乳胶50份。
上述的工艺品的制备方法，按照如下步骤进行：
(1)按照重量份数，取黄蓍胶30份，加热至60℃，加入木粉300份，凹凸棒土20份，搅拌均匀；
(2)将温度升至80℃，加入丙烯酸树脂30份，石棉段50份，搅拌均匀；
(3)将温度降至室温，加入聚丁二烯乳胶50份，搅拌均匀，倾倒在模具中成型，自然晾干或者烘干制成。
实施例3
一种木粉工艺品，包括如下重量份数的原料：木粉600份，苯乙烯-丁二烯-苯乙烯嵌段共聚物100份，茄替胶50份，甲基丙烯酸甲酯一丁二烯一苯乙烯共聚物100份，凹凸棒土50份，羧基丁腈胶乳胶200份。
上述的工艺品的制备方法，按照如下步骤进行：
(1)按照重量份数，取茄替胶50份，加热至80℃，加入木粉600份，凹凸棒土50份，搅拌均匀；
(2)将温度升至90℃，加入苯乙烯-丁二烯-苯乙烯嵌段共聚物100份，甲基丙烯酸甲酯一丁二烯一苯乙烯共聚物100份，搅拌均匀；
(3)将温度降至室温，加入羧基丁腈胶乳胶200份，搅拌均匀，倾倒在模具中成型，自然晾干或者烘干制成。
实施例4
一种木粉工艺品，包括如下重量份数的原料：木粉455份，苯乙烯-异戊二烯-苯乙烯嵌段共聚物66份，卡拉雅胶33份，4-叔丁基苯硼酸77份，凹凸棒土25份，丁苯乳胶145份。
上述的工艺品的制备方法，按照如下步骤进行：
(1)按照重量份数，取卡拉雅胶33份，加热至65℃，加入木粉455份，凹凸棒土25份，搅拌均匀；
(2)将温度升至85℃，加入苯乙烯-异戊二烯-苯乙烯嵌段共聚物66份，4-叔丁基苯硼酸77份，搅拌均匀；
(3)将温度降至室温，加入丁苯乳胶145份，搅拌均匀，倾倒在模具中成型，自然晾干或者烘干制成。
实施例5
一种木粉工艺品，包括如下重量份数的原料：木粉333份，苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物45份，罗望子胶45份，苯甲酰中乌头胺盐酸钠76份，凹凸棒土22份，丁苯乳胶89份。
上述的工艺品的制备方法，按照如下步骤进行：
(1)按照重量份数，取树胶罗望子胶45份，加热至66℃，加入木粉333份，凹凸棒土22份，搅拌均匀；
(2)将温度升至88℃，加入苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物45份，苯甲酰中乌头胺盐酸钠76份，搅拌均匀；
(3)将温度降至室温，加入丁苯乳胶89份，搅拌均匀，倾倒在模具中成型，自然晾干或者烘干制成。
实施例6
一种木粉工艺品，包括如下重量份数的原料：木粉333份，苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物45份，罗望子胶45份，苯甲酰中乌头胺盐酸钠76份，凹凸棒土22份，丁苯乳胶89份，亚硫酸金钠2份。
上述的工艺品的制备方法，按照如下步骤进行：
(1)按照重量份数，取树胶罗望子胶45份，加热至66℃，加入木粉333份，凹凸棒土22份，亚硫酸金钠2份，搅拌均匀；
(2)将温度升至88℃，加入苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物45份，苯甲酰中乌头胺盐酸钠76份，搅拌均匀；
(3)将温度降至室温，加入丁苯乳胶89份，搅拌均匀，倾倒在模具中成型，自然晾干或者烘干制成。
实施例7
一种木粉工艺品，包括如下重量份数的原料：木粉450份，环氧树脂60份，桃胶40份，聚丙烯纤维60份，凹凸棒土30份，天然乳胶100份，3-(4,4,5,5-四甲基-1,3,2-二氧硼戊环-2-基)苯甲酸乙酯2份。
上述的工艺品的制备方法，按照如下步骤进行：
(1)按照重量份数，取桃胶40份，加热至70℃，加入木粉450份，凹凸棒土30份，搅拌均匀；
(2)将温度升至85℃，加入环氧树脂60份，聚丙烯纤维60份，搅拌均匀；
(3)将温度降至室温，加入天然乳胶100份，3-(4,4,5,5-四甲基-1,3,2-二氧硼戊环-2-基)苯甲酸乙酯2份，搅拌均匀，倾倒在模具中成型，自然晾干或者烘干制成。
实施例8
一种木粉工艺品，包括如下重量份数的原料：木粉300份，丙烯酸树脂30份，黄蓍胶30份，石棉段50份，凹凸棒土20份，聚丁二烯乳胶50份，对异丙氧基苯甲酸甲酯2份。
上述的工艺品的制备方法，按照如下步骤进行：
(1)按照重量份数，取黄蓍胶30份，加热至60℃，加入木粉300份，凹凸棒土20份，搅拌均匀；
(2)将温度升至80℃，加入丙烯酸树脂30份，石棉段50份，搅拌均匀；
(3)将温度降至室温，加入聚丁二烯乳胶50份，对异丙氧基苯甲酸甲酯2份，搅拌均匀，倾倒在模具中成型，自然晾干或者烘干制成。
对比例1
一种木粉工艺品，包括如下重量份数的原料：木粉600份，茄替胶50份，甲基丙烯酸甲酯一丁二烯一苯乙烯共聚物100份，凹凸棒土50份，羧基丁腈胶乳胶200份。
上述的工艺品的制备方法，按照如下步骤进行：
(1)按照重量份数，取茄替胶50份，加热至80℃，加入木粉600份，凹凸棒土50份，搅拌均匀；
(2)将温度升至90℃，加入甲基丙烯酸甲酯一丁二烯一苯乙烯共聚物100份，搅拌均匀；
(3)将温度降至室温，加入羧基丁腈胶乳胶200份，搅拌均匀，倾倒在模具中成型，自然晾干或者烘干制成。
对比例2
一种木粉工艺品，包括如下重量份数的原料：木粉455份，苯乙烯-异戊二烯-苯乙烯嵌段共聚物66份，卡拉雅胶33份，4-叔丁基苯硼酸77份，丁苯乳胶145份。
上述的工艺品的制备方法，按照如下步骤进行：
(1)按照重量份数，取卡拉雅胶33份，加热至65℃，加入木粉455份，搅拌均匀；
(2)将温度升至85℃，加入苯乙烯-异戊二烯-苯乙烯嵌段共聚物66份，4-叔丁基苯硼酸77份，搅拌均匀；
(3)将温度降至室温，加入丁苯乳胶145份，搅拌均匀，倾倒在模具中成型，自然晾干或者烘干制成。
性能测试:采用万能材料试验机，按GB/T228-2002标准规定的速度让试验机对标准拉力试样进行拉伸，测抗拉强度，采用抗压测试机测抗压强度，结果见表1：
表1
以上配方配比以及工艺的实施例只是阐述了本发明的基本原理和特性，本发明不受上述工艺和配比的实施限制，在不脱离本发明的精神和范围下，本发明还可以做出各种修改和变换。因此这些变化和改变都属于本发明范围内。
Claims (7)
1.一种木粉工艺品，其特征在于，包括如下重量份数的原料：木粉300-600份，树脂30-100份，树胶30-50份，增韧剂50-100份，凹凸棒土20-50份，乳胶50-200份。
2.根据权利要求1所述的木粉工艺品，其特征在于，所述树胶为桃胶，黄蓍胶，茄替胶，卡拉雅胶，罗望子胶中的一种或一种以上。
3.根据权利要求1所述的木粉工艺品，其特征在于，所述树脂为环氧树脂，丙烯酸树脂，苯乙烯-丁二烯-苯乙烯嵌段共聚物，苯乙烯-异戊二烯-苯乙烯嵌段共聚物，苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物中的一种或一种以上。
4.根据权利要求1所述的木粉工艺品，其特征在于，所述增韧剂为聚丙烯纤维，石棉段，甲基丙烯酸甲酯一丁二烯一苯乙烯共聚物，4-叔丁基苯硼酸，苯甲酰中乌头胺盐酸盐中的一种或一种以上。
5.根据权利要求1所述的木粉工艺品，其特征在于，所述乳胶为天然乳胶，聚丁二烯乳胶，丁苯乳胶，羧基丁腈胶乳胶中的一种或一种以上。
6.根据权利要求1所述的木粉工艺品，其特征在于，所述工艺品中还含有1-3份亚硫酸金钠。
7.权利要求1所述的木粉工艺品的制备方法，其特征在于，按照如下步骤进行：
(1)按照重量份数，取树胶30-50份，加热至60-80℃，加入木粉300-600份，凹凸棒土20-50份，搅拌均匀；
(2)将温度升至80-90℃，加入树脂30-100份，增韧剂50-100份，搅拌均匀；
(3)将温度降至室温，加入乳胶50-200份，搅拌均匀，倾倒在模具中成型，自然晾干或者烘干制成。