CN106633744A - PC light diffusion material - Google Patents
PC light diffusion material Download PDFInfo
- Publication number
- CN106633744A CN106633744A CN201510709678.1A CN201510709678A CN106633744A CN 106633744 A CN106633744 A CN 106633744A CN 201510709678 A CN201510709678 A CN 201510709678A CN 106633744 A CN106633744 A CN 106633744A
- Authority
- CN
- China
- Prior art keywords
- mass fraction
- auxiliary agent
- nylon
- powder
- ebs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PC light diffusion material. The PC light diffusion material comprises polycarbonate resin, diffusion powder, fluorescent brightener, polydecamethylene sebacamide, EBS, ABS, rubber powder, bromine, E920 and PETS; the PC light diffusion material has good combination of rigidity and flexibility, excellent heat resistance and anti-impact property, good injection molding performance, weather-proof, and UV-resistance; the material can effectively achieve environment-friendly, and is good in heat conductivity and short molding time.
Description
Technical field
The present invention relates to a kind of PC photodiffusion materials.
Background technology
Light diffusion PC plastics are with transparent PC (Merlon）Plastics are base material, add a kind of printing opacity and opaque photodiffusion material particle being necessarily polymerized through special process than row light diffusing agent and other auxiliary agents.Because light diffusing agent is spherical in shape, in being dispersed in PC resin, island structure is formed, because PC resin is different with the refraction index of light diffusing agent, light, through multiple reflections, reaches light diffusion effect in the similar mirror-reflection in light diffusing agent surface.The addition of light diffusing agent, particle size and distribution, refraction index determine the optical property of material.Evaluating the index of photodiffusion material optical property includes full light light transmittance, mist degree, decentralization；Wherein decentralization refers to the angle that relative light transmission is 50%, how to accomplish diffusion material high transmission rate, haze, and this is a difficult point.
The content of the invention
In order to solve the problems referred to above of the prior art, the invention provides a kind of PC photodiffusion materials.
A kind of PC photodiffusion materials that the present invention is provided, including polycarbonate resin, spread powder, fluorescent whitening agent, nylon 1010, EBS, ABS, high glue powder, bromine, E920 and PETS, component is arranged in 1000mL polycarbonate resins by following mass fraction：
Spread powder
88.0~90.1%
Fluorescent whitening agent
4.1~5.0%
Auxiliary agent
5.5~6.5%
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
0.25~0.33%
EBS
0.55~0.64%
ABS
5.80~6.40%
High glue powder
6.55~7.33%
Bromine
12.30~13.70%
E920
7.11~9.37%
PETS
2.2~3.9%。
One of preferably, component is set by following mass fraction in 1000mL polycarbonate resins：
Spread powder
89.0~90.0%
Fluorescent whitening agent
4.3~4.9%
Auxiliary agent
5.5~6.4%
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
0.26~0.33%
EBS
0.57~0.63%
ABS
5.90~6.35%
High glue powder
6.58~7.15%
Bromine
12.80~13.50%
E920
7.89~8.98%
PETS
2.3~3.7%。
One of preferably, component is set by following mass fraction in 1000mL polycarbonate resins：
Spread powder
89.2~89.8%
Fluorescent whitening agent
4.5~4.9%
Auxiliary agent
5.8~6.2%
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
0.28~0.32%
EBS
0.59~0.63%
ABS
6.10~6.35%
High glue powder
6.78~7.05%
Bromine
12.80~13.10%
E920
8.33~8.98%
PETS
2.3~3.1%。
Or, the PC photodiffusion materials press mass fraction including following components in 1000mL polycarbonate resins：
Spread powder
89.6%
Fluorescent whitening agent
4.6%
Auxiliary agent
5.8%
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
0.29%
EBS
0.61%
ABS
6.15%
High glue powder
6.83%
Bromine
12.88%
E920
8.51%
PETS
2.6%。
One of preferably, the PC photodiffusion materials press mass fraction including following components in 1000mL polycarbonate resins：
Spread powder
21g
Fluorescent whitening agent
1.1g
Auxiliary agent
1.4g
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
4.2mg
EBS
8.5mg
ABS
86.0mg
High glue powder
960.0mg
Bromine
180.0mg
E920
120.0mg
PETS
35.4mg。
One of preferably, one of nylon 1010 model 7026u or 1250Z100.
Beneficial effect of the present invention：The PC photodiffusion materials that this formula is prepared have excellent optical property, and good rigidity is combined with toughness, and heat-resisting, resistance to impact is good, injection molding processability is excellent, weatherability, uvioresistant, effectively realize environmental protection, with good heat conductivity and shorter molding time.
Specific embodiment
Embodiment 1：
A kind of PC photodiffusion materials, including polycarbonate resin, spread powder, fluorescent whitening agent, nylon 1010, EBS, ABS, high glue powder, bromine, E920 and PETS, component is arranged in 1000mL polycarbonate resins by following mass fraction：
Spread powder
88.0~90.1%
Fluorescent whitening agent
4.1~5.0%
Auxiliary agent
5.5~6.5%
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
0.25~0.33%
EBS
0.55~0.64%
ABS
5.80~6.40%
High glue powder
6.55~7.33%
Bromine
12.30~13.70%
E920
7.11~9.37%
PETS
2.2~3.9%。
One of nylon 1010 model 7026u or 1250Z100..
Embodiment 2：
A kind of PC photodiffusion materials, component is arranged in 1000mL polycarbonate resins by following mass fraction：
Spread powder
89.0~90.0%
Fluorescent whitening agent
4.3~4.9%
Auxiliary agent
5.5~6.4%
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
0.26~0.33%
EBS
0.57~0.63%
ABS
5.90~6.35%
High glue powder
6.58~7.15%
Bromine
12.80~13.50%
E920
7.89~8.98%
PETS
2.3~3.7%。
One of nylon 1010 model 7026u or 1250Z100.
Embodiment 3：
A kind of PC photodiffusion materials, component is arranged in 1000mL polycarbonate resins by following mass fraction：
Spread powder
89.2~89.8%
Fluorescent whitening agent
4.5~4.9%
Auxiliary agent
5.8~6.2%
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
0.28~0.32%
EBS
0.59~0.63%
ABS
6.10~6.35%
High glue powder
6.78~7.05%
Bromine
12.80~13.10%
E920
8.33~8.98%
PETS
2.3~3.1%。
Or, the PC photodiffusion materials press mass fraction including following components in 1000mL polycarbonate resins：
Spread powder
89.6%
Fluorescent whitening agent
4.6%
Auxiliary agent
5.8%
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
0.29%
EBS
0.61%
ABS
6.15%
High glue powder
6.83%
Bromine
12.88%
E920
8.51%
PETS
2.6%。
One of nylon 1010 model 7026u or 1250Z100.
Embodiment 4：
A kind of PC photodiffusion materials, component is arranged in 1000mL polycarbonate resins by following mass fraction：
Spread powder
89.2~89.8%
Fluorescent whitening agent
4.5~4.9%
Auxiliary agent
5.8~6.2%
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
0.28~0.32%
EBS
0.59~0.63%
ABS
6.10~6.35%
High glue powder
6.78~7.05%
Bromine
12.80~13.10%
E920
8.33~8.98%
PETS
2.3~3.1%。
One of nylon 1010 model 7026u or 1250Z100.
The present invention is relative to the difference of conventional machining process：The PC photodiffusion materials that this formula is prepared have excellent optical property, and good rigidity is combined with toughness, and heat-resisting, resistance to impact is good, injection molding processability is excellent, weatherability, uvioresistant, effectively realize environmental protection, with good heat conductivity and shorter molding time.
The invention is not restricted to above-mentioned enforcement, all employing same principles and its method realize that the numerous embodiments of constructed effect are identical with this patent.
Claims (5)
1. a kind of PC photodiffusion materials, it is characterised in that including polycarbonate resin, spread powder, fluorescent whitening agent, nylon 1010, EBS, ABS, high glue powder, bromine, E920 and PETS, component is arranged in 1000mL polycarbonate resins by following mass fraction：
Spread powder
88.0~90.1%
Fluorescent whitening agent
4.1~5.0%
Auxiliary agent
5.5~6.5%
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
0.25~0.33%
EBS
0.55~0.64%
ABS
5.80~6.40%
High glue powder
6.55~7.33%
Bromine
12.30~13.70%
E920
7.11~9.37%
PETS
2.2~3.9%。
2. PC photodiffusion materials as claimed in claim 1, it is characterised in that component is set by following mass fraction in 1000mL polycarbonate resins：
Spread powder
89.0~90.0%
Fluorescent whitening agent
4.3~4.9%
Auxiliary agent
5.5~6.4%
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
0.26~0.33%
EBS
0.57~0.63%
ABS
5.90~6.35%
High glue powder
6.58~7.15%
Bromine
12.80~13.50%
E920
7.89~8.98%
PETS
2.3~3.7%。
3. PC photodiffusion materials as described in claim 1-2, it is characterised in that component is set by following mass fraction in 1000mL polycarbonate resins：
Spread powder
89.2~89.8%
Fluorescent whitening agent
4.5~4.9%
Auxiliary agent
5.8~6.2%
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
0.28~0.32%
EBS
0.59~0.63%
ABS
6.10~6.35%
High glue powder
6.78~7.05%
Bromine
12.80~13.10%
E920
8.33~8.98%
PETS
2.3~3.1%。
Or, the PC photodiffusion materials press mass fraction including following components in 1000mL polycarbonate resins：
Spread powder
89.6%
Fluorescent whitening agent
4.6%
Auxiliary agent
5.8%
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
0.29%
EBS
0.61%
ABS
6.15%
High glue powder
6.83%
Bromine
12.88%
E920
8.51%
PETS
2.6%。
4. PC photodiffusion materials as described in claim 1-3 is any, it is characterised in that the PC photodiffusion materials press mass fraction including following components in 1000mL polycarbonate resins：
Spread powder
21g
Fluorescent whitening agent
1.1g
Auxiliary agent
1.4g
Wherein, each constituent presses mass fraction including following components in auxiliary agent：
Nylon 1010
4.2mg
EBS
8.5mg
ABS
86.0mg
High glue powder
960.0mg
Bromine
180.0mg
E920
120.0mg
PETS
35.4mg。
5. PC photodiffusion materials as described in claim 1-4 is any, it is characterised in that one of nylon 1010 model 7026u or 1250Z100.