CN106630888A - Pouring slurry for light board - Google Patents
Pouring slurry for light board Download PDFInfo
- Publication number
- CN106630888A CN106630888A CN201611009049.9A CN201611009049A CN106630888A CN 106630888 A CN106630888 A CN 106630888A CN 201611009049 A CN201611009049 A CN 201611009049A CN 106630888 A CN106630888 A CN 106630888A
- Authority
- CN
- China
- Prior art keywords
- parts
- slurry
- light plate
- light
- water reducer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to pouring slurry for a light board. The pouring slurry is prepared from the following raw materials in parts by weight: 60-120 parts of cement, 70-120 parts of light materials, 2-6 parts of emulsion powder, 5-25 parts of coal ash, 30-50 parts of gypsum powder, 10-25 parts of triangular pyramid cage type glass fiber reinforced plastic particles, 0.05-3.5 parts of sodium carboxymethylcellulose, 0.8-3.0 parts of lignocelluloses, 0.6-2.0 parts of carbon fiber, 0.1-0.5 part of cellulose ether, 2.7-7.8 parts of beta-cyclodextrin, 0.01-10 parts of an early strength agent, 0.1-5 parts of a water reducer and 0.05-4 parts of an air entraining agent. The pouring slurry has the characteristics of light weight, high strength, heat resistance and shock resistance.
Description
Technical field
The present invention relates to a kind of light plate perfusion slurry.
Background technology
At present, steel skeleton light-duty plate is applied to coal transporting trestle, public building enclosure roofing, flooring, the metope such as civilian.Reinforcing bar
Frame light plate is by light weight steel frame, cold drawn steel wire, the modified cement perlite composite core materials of BAS, the composite impervious wear-resistant coatings of BAS
Composition.Steel skeleton light-duty plate (referred to as " day substrate ") collects the functions such as lightweight, load-bearing, energy-conservation, fire prevention, sound insulation, venting of dust explosion, antidetonation in one
Body, had both maintained conventional steel bar concrete component degree of safety height, the advantage of long service life, and modern architecture is met again to light
Matter, the requirement of energy-saving and environmental protection.Light plate performance requirement lightweight and high-strength, but current light plate the two performances be difficult and
Turn round and look at, especially have no idea to ensure in intensity, therefore it is outstanding to invent a kind of high-strength, light weight function admirable light plate perfusion slurry
For important.
The content of the invention
The technical problem to be solved is to provide a kind of light plate perfusion slurry.
To solve the above problems, the technical solution used in the present invention is：
A kind of light plate perfusion slurry, its key technology point is to be composed of the following raw materials by weight：
Cement 60-120 parts；
Light material 70-120 parts；
Latex powder 2-6 part；
Flyash 15-25 parts；
Gypsum Fibrosum powder 30-50 parts；
Triangular pyramid cage glass steel grit 10-25 parts；
Sodium carboxymethyl cellulose 0.05-3.5 parts；
Lignocellulose 0.8-3.0 parts；
Carbon fiber 0.6-2.0 parts；
Cellulose ether 0.1-0.5 parts；
Beta-schardinger dextrin -2.7-7.8 parts；
Early strength agent 0.01-10 parts；
Water reducer 0.1-5 parts；
Air entraining agent 0.05-4 parts.
As further improvement of the invention, described light plate perfusion slurry, it is composed of the following raw materials by weight：
90 parts of cement；
95 parts of light material；
4 parts of latex powder；
20 parts of flyash；
40 parts of Gypsum Fibrosum powder；
18 parts of triangular pyramid cage glass steel grit；
2 parts of sodium carboxymethyl cellulose；
1.2 parts of lignocellulose；
1.3 parts of carbon fiber；
0.3 part of cellulose ether；
5.1 parts of beta-schardinger dextrin-；
3.0 parts of early strength agent；
1.1 parts of water reducer；
0.6 part of air entraining agent.
As further improvement of the invention, a length of 2-5mm of rib of the triangular pyramid cage glass steel grit.
Used as further improvement of the invention, the light material is one or more in perlite and glass bead.
Used as further improvement of the invention, the early strength agent is lithium carbonate, calcium formate, sodium nitrate, calcium chloride and silicic acid
One or more in sodium.
Used as further improvement of the invention, the water reducer is naphthalene water reducer, sulfamate water reducer, aliphatic
One kind in water reducer, polycarboxylate dehydragent.
Air entraining agent is the sodium salt compound of dodecylbenzene sodium sulfonate or rosin tree lipid.
It is using the beneficial effect produced by above-mentioned technical proposal：
Formula of the present invention, triangular pyramid cage glass steel grit possesses preferable rigid structure, inserts embedding mutually in the slurry,
Skeletal support effect is played, and triangular pyramid cage construction possesses in itself preferable stability and intensity.Compound with carbon in formula
Fiber and wood fibre, effectively enhance the overall degree of cross linking, improve the anti-cracking performance of mortar, resist performance and shock resistance
Energy.Beta-schardinger dextrin-, can form hybridization network in entirety, for spatially forming cement and perlitic skeleton, increase
Amalgamation between each several part, makes cement and the perlitic performance organically be merged, and takes into account load-bearing and heat insulating ability.Lightweight
Material is effectively reduced overall quality, the characteristics of integrally possess light weight, high-strength, heat-resisting and antidetonation.
Description of the drawings
In order to be illustrated more clearly that the specific embodiment of the invention or technical scheme of the prior art, below will be to concrete
The accompanying drawing to be used needed for embodiment or description of the prior art is briefly described, it should be apparent that, in describing below
Accompanying drawing is some embodiments of the present invention, for those of ordinary skill in the art, before creative work is not paid
Put, can be with according to these other accompanying drawings of accompanying drawings acquisition.
Fig. 1 is the structural representation of triangular pyramid cage glass steel grit.
Specific embodiment
To make the object, technical solutions and advantages of the present invention clearer, invention is carried out with reference to specific embodiment
Clear, complete description.
The shape of the triangular pyramid cage glass steel grit described in following examples is as shown in figure 1, a length of 2-5mm of its rib.
Embodiment 1
Light plate perfusion slurry, is composed of the following raw materials by weight：
Cement 90Kg；
Perlite 40Kg；
Vitreous microgranule 55Kg；
Latex powder 4Kg；
Flyash 20Kg；
Gypsum Fibrosum powder 40Kg；
Triangular pyramid cage glass steel grit 18Kg；
Sodium carboxymethyl cellulose 2Kg；
Lignocellulose 1.2Kg；
Carbon fiber 1.3Kg；
Cellulose ether 0.3Kg；
Beta-schardinger dextrin -5.1Kg；
Calcium formate 3.0Kg；
Naphthalene water reducer 1.1Kg；
Dodecylbenzene sodium sulfonate 0.6Kg.
The preparation method of slurry is as follows：
(1) it is first that latex powder, Gypsum Fibrosum powder, triangular pyramid cage glass steel grit, sodium carboxymethyl cellulose, lignocellulose, carbon is fine
Dimension, cellulose ether, beta-schardinger dextrin-, calcium formate, naphthalene water reducer and dodecylbenzene sodium sulfonate, mix well mixing, obtain compound；
(2) by perlite, vitreous microgranule and cement are added in blender, fully mix, be subsequently adding what step (1) was obtained
Compound, adds the water of 500Kg, and rotating speed is 80 revs/min, is stirred 10 minutes, is tuned into pulpiness and obtains final product.
Embodiment 2
Light plate perfusion slurry, is composed of the following raw materials by weight：
Cement 60Kg；
Perlite 50Kg；
Vitreous microgranule 70Kg；
Latex powder 2Kg；
Flyash 25Kg；
Gypsum Fibrosum powder 30Kg；
Triangular pyramid cage glass steel grit 25Kg；
Sodium carboxymethyl cellulose 3.5Kg；
Lignocellulose 0.8Kg；
Carbon fiber 2.0Kg；
Cellulose ether 0.1Kg；
Beta-schardinger dextrin -7.8Kg；
Calcium formate 0.05Kg；
Naphthalene water reducer 3.0Kg；
Dodecylbenzene sodium sulfonate 0.05Kg.
The preparation method of slurry is as follows：
(1) it is first that latex powder, Gypsum Fibrosum powder, triangular pyramid cage glass steel grit, sodium carboxymethyl cellulose, lignocellulose, carbon is fine
Dimension, cellulose ether, beta-schardinger dextrin-, calcium formate, naphthalene water reducer and dodecylbenzene sodium sulfonate, mix well mixing, obtain compound；
(2) by perlite, vitreous microgranule and cement are added in blender, fully mix, be subsequently adding what step (1) was obtained
Compound, adds the water of 500Kg, and rotating speed is 80 revs/min, is stirred 10 minutes, is tuned into pulpiness and obtains final product.
Embodiment 3
Light plate perfusion slurry, is composed of the following raw materials by weight：
Cement 120Kg；
Perlite 30Kg；
Vitreous microgranule 40Kg；
Latex powder 2Kg；
Flyash 20Kg；
Gypsum Fibrosum powder 40Kg；
Triangular pyramid cage glass steel grit 18Kg；
Sodium carboxymethyl cellulose 2Kg；
Lignocellulose 1.2Kg；
Carbon fiber 1.3Kg；
Cellulose ether 0.5Kg；
Beta-schardinger dextrin -2.7Kg；
Calcium formate 4.2Kg；
Naphthalene water reducer 5.0Kg；
Dodecylbenzene sodium sulfonate 3.5Kg.
The preparation method of slurry is as follows：
(1) it is first that latex powder, Gypsum Fibrosum powder, triangular pyramid cage glass steel grit, sodium carboxymethyl cellulose, lignocellulose, carbon is fine
Dimension, cellulose ether, beta-schardinger dextrin-, calcium formate, naphthalene water reducer and dodecylbenzene sodium sulfonate, mix well mixing, obtain compound；
(2) by perlite, vitreous microgranule and cement are added in blender, fully mix, be subsequently adding what step (1) was obtained
Compound, adds the water of 500Kg, and rotating speed is 80 revs/min, is stirred 10 minutes, is tuned into pulpiness and obtains final product.
Comparative example 1
Light plate perfusion slurry, is composed of the following raw materials by weight：
Cement 90Kg；
Perlite 40Kg；
Vitreous microgranule 55Kg；
Latex powder 4Kg；
Flyash 20Kg；
Gypsum Fibrosum powder 40Kg；
The solid formula glass steel grit 18Kg of triangular pyramid；
Sodium carboxymethyl cellulose 2Kg；
Lignocellulose 1.2Kg；
Carbon fiber 1.3Kg；
Cellulose ether 0.3Kg；
Beta-schardinger dextrin -5.1Kg；
Calcium formate 3.0Kg；
Naphthalene water reducer 1.1Kg；
Dodecylbenzene sodium sulfonate 0.6Kg.
The preparation method of slurry is as follows：
(1) it is first that latex powder, Gypsum Fibrosum powder, triangular pyramid cage glass steel grit, sodium carboxymethyl cellulose, lignocellulose, carbon is fine
Dimension, cellulose ether, beta-schardinger dextrin-, calcium formate, naphthalene water reducer and dodecylbenzene sodium sulfonate, mix well mixing, obtain compound；
(2) by perlite, vitreous microgranule and cement are added in blender, fully mix, be subsequently adding what step (1) was obtained
Compound, adds the water of 500Kg, and rotating speed is 80 revs/min, is stirred 10 minutes, is tuned into pulpiness and obtains final product.
Comparative example 2
Light plate perfusion slurry, is composed of the following raw materials by weight：
Cement 90Kg；
Perlite 40Kg；
Vitreous microgranule 55Kg；
Latex powder 4Kg；
Flyash 20Kg；
Gypsum Fibrosum powder 40Kg；
Sodium carboxymethyl cellulose 2Kg；
Lignocellulose 1.2Kg；
Carbon fiber 1.3Kg；
Cellulose ether 0.3Kg；
Beta-schardinger dextrin -5.1Kg；
Calcium formate 3.0Kg；
Naphthalene water reducer 1.1Kg；
Dodecylbenzene sodium sulfonate 0.6Kg.
The preparation method of slurry is as follows：
(1) it is first that latex powder, Gypsum Fibrosum powder, triangular pyramid cage glass steel grit, sodium carboxymethyl cellulose, lignocellulose, carbon is fine
Dimension, cellulose ether, beta-schardinger dextrin-, calcium formate, naphthalene water reducer and dodecylbenzene sodium sulfonate, mix well mixing, obtain compound；
(2) by perlite, vitreous microgranule and cement are added in blender, fully mix, be subsequently adding what step (1) was obtained
Compound, adds the water of 500Kg, and rotating speed is 80 revs/min, is stirred 10 minutes, is tuned into pulpiness and obtains final product.
Comparative example 3
Light plate perfusion slurry, is composed of the following raw materials by weight：
Cement 90Kg；
Perlite 40Kg；
Vitreous microgranule 55Kg；
Latex powder 4Kg；
Flyash 20Kg；
Gypsum Fibrosum powder 40Kg；
Triangular pyramid cage glass steel grit 18Kg；
Sodium carboxymethyl cellulose 2Kg；
Lignocellulose 1.2Kg；
Carbon fiber 1.3Kg；
Cellulose ether 0.3Kg；
Calcium formate 3.0Kg；
Naphthalene water reducer 1.1Kg；
Dodecylbenzene sodium sulfonate 0.6Kg.
The preparation method of slurry is as follows：
(1) it is first that latex powder, Gypsum Fibrosum powder, triangular pyramid cage glass steel grit, sodium carboxymethyl cellulose, lignocellulose, carbon is fine
Dimension, cellulose ether, beta-schardinger dextrin-, calcium formate, naphthalene water reducer and dodecylbenzene sodium sulfonate, mix well mixing, obtain compound；
(2) by perlite, vitreous microgranule and cement are added in blender, fully mix, be subsequently adding what step (1) was obtained
Compound, adds the water of 500Kg, and rotating speed is 80 revs/min, is stirred 10 minutes, is tuned into pulpiness and obtains final product.
Effect example
The slurry prepared with the embodiment of the present invention 1, comparative example 1, comparative example 2 and comparative example 3 is poured in light steel skeleton, obtains light
Steel skeleton light-duty plate, product specification is QB6015 6000mm*1500mm*120mm, and specific performance is as follows：
| Embodiment 1 | Comparative example 1 | Comparative example 2 | Comparative example 3 | |
| Comprcssive strength | 8.9 Mpa | 3.0 Mpa | 2.4 Mpa | 3.7 Mpa |
| Deadweight KN/m2 | 0.60 | 0.82 | 0.47 | 0.60 |
Finally it should be noted that：Above example only to illustrate technical scheme, rather than a limitation；Although reference
Previous embodiment has been described in detail to the present invention, it will be understood by those within the art that：It still can be right
Technical scheme described in previous embodiment is modified, or carries out equivalent to which part technical characteristic；And these
Modification is replaced, and does not make the spirit and scope of the essence disengaging embodiment of the present invention technical scheme of appropriate technical solution.
Claims (7)
1. a kind of light plate is used and irrigates slurry, it is characterised in that be composed of the following raw materials by weight：
Cement 60-120 parts；
Light material 70-120 parts；
Latex powder 2-6 part；
Flyash 15-25 parts；
Gypsum Fibrosum powder 30-50 parts；
Triangular pyramid cage glass steel grit 10-25 parts；
Sodium carboxymethyl cellulose 0.05-3.5 parts；
Lignocellulose 0.8-3.0 parts；
Carbon fiber 0.6-2.0 parts；
Cellulose ether 0.1-0.5 parts；
Beta-schardinger dextrin -2.7-7.8 parts；
Early strength agent 0.01-10 parts；
Water reducer 0.1-5 parts；
Air entraining agent 0.05-4 parts.
2. a kind of light plate according to claim 1 is used and irrigates slurry, it is characterised in that described light plate perfusion slurry
Material, is composed of the following raw materials by weight：
90 parts of cement；
95 parts of light material；
4 parts of latex powder；
20 parts of flyash；
40 parts of Gypsum Fibrosum powder；
18 parts of triangular pyramid cage glass steel grit；
2 parts of sodium carboxymethyl cellulose；
1.2 parts of lignocellulose；
1.3 parts of carbon fiber；
0.3 part of cellulose ether；
5.1 parts of beta-schardinger dextrin-；
3.0 parts of early strength agent；
1.1 parts of water reducer；
0.6 part of air entraining agent.
3. a kind of light plate perfusion mortar according to claim 1 and 2, it is characterised in that the triangular pyramid cage glass
The a length of 2-5mm of rib of glass steel grit.
4. a kind of light plate according to claim 1 and 2 is used and irrigates slurry, it is characterised in that the light material is Margarita
One or more in rock and glass bead.
5. a kind of light plate according to claim 1 and 2 is used and irrigates slurry, it is characterised in that the early strength agent is carbonic acid
One or more in lithium, calcium formate, sodium nitrate, calcium chloride and sodium silicate.
6. a kind of light plate according to claim 1 and 2 is used and irrigates slurry, it is characterised in that the water reducer is naphthalene system
One kind in water reducer, sulfamate water reducer, aliphatic water reducing agent, polycarboxylate dehydragent.
7. a kind of light plate according to claim 1 and 2 is used and irrigates slurry, it is characterised in that the air entraining agent is 12
The sodium salt compound of sodium alkyl benzene sulfonate or rosin tree lipid.