CN106630838B - 一种建筑装饰工程用防水涂料 - Google Patents
一种建筑装饰工程用防水涂料 Download PDFInfo
- Publication number
- CN106630838B CN106630838B CN201611199384.XA CN201611199384A CN106630838B CN 106630838 B CN106630838 B CN 106630838B CN 201611199384 A CN201611199384 A CN 201611199384A CN 106630838 B CN106630838 B CN 106630838B
- Authority
- CN
- China
- Prior art keywords
- agent
- water
- building decoration
- decoration engineering
- repellent paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明属于建筑装饰工程技术领域，特别涉及一种建筑装饰工程用防水涂料，是由固体组分和液体组分按质量比5‑9:7组成的，所述固体组分包括以下质量百分比的物质：锂渣粉10％‑30％、陶瓷砖抛光粉5％‑10％、氧化镁膨胀剂1％‑2％、N‑全氟新酰基氨酸盐0.05％‑1％、硅铝酸钠0.1％‑1％、增强剂0.01％‑0.1％、增粘保水剂0.1％‑0.5％、分散剂0.1％‑0.5％、消泡剂0.01％‑0.05％、余量为水泥。本发明具有良好的弹性和防水性能，本适用于卫生间、厨房、阳台等房屋装饰时时的二次防水工程。
Description
技术领域
本发明属于建筑装饰工程技术领域，特别涉及一种建筑装饰工程用防水涂料。
背景技术
我国政府对建筑防水非常重视，防水材料在建材产品中占有很重要的位置。目前市场上的防水涂料主要以聚氨酯防水涂料为主。但是聚氨酯防水涂料中含有疑似致癌物质和大量有机溶剂，这些物质对人体健康和环境非常不利。随着社会的发展和人们生活水平的不断提高，人们的环保、健康意识明显增强，对居住环境的安全性要求越来越高，相关的法律法规也日益严格，因此发展绿色环保无污染的防水涂料迫在眉睫。
国家法律规定房屋在交房之前卫生间、厨房、阳台等用水的地方要做上防水，但是有的开发商只是敷衍了事，防水不过关，因此多数人在装修的环节中还要为卫生间、厨房、阳台等用水的地方做一道防水。
发明内容
本发明提供一种建筑装饰工程用防水涂料，该涂料与水泥基基材相容性好，防水效果好，且绿色环保无污染。
为达到上述目的，本发明采用以下技术方案：
一种建筑装饰工程用防水涂料由固体组分和液体组分按质量比5-9:7组成。
所述固体组分包括以下质量百分比的物质：
锂渣粉10％-30％
陶瓷砖抛光粉5％-10％
氧化镁膨胀剂1％-2％
N-全氟辛酰基氨酸盐0.05％-1％
硅铝酸钠0.1％-1％
增强剂0.01％-0.1％
增粘保水剂0.1％-0.5％
分散剂0.1％-0.5％
消泡剂0.01％-0.05％
余量为水泥。
所述水泥为P·O42.5水泥；所述锂渣粉是由硫酸法生产碳酸锂时产生的废渣烘干、粉磨得到，细度为400目-600目；所述陶瓷砖抛光粉是由陶瓷抛光砖在刮平定厚、研磨抛光以及磨边倒角等一系列深加时所产生的废料烘干、粉磨得到，细度为400目-600目。
所述增强剂由三乙醇胺、乙二胺四亚甲基膦酸和蔗糖化钙组成。
优选的，所述增强剂由三乙醇胺、乙二胺四亚甲基膦酸和蔗糖化钙按质量比1-2:1-2:1组成。
所述增粘保水剂由聚丙烯酸钠、温轮胶和瓜尔胶羟丙基三甲基氯化铵按质量比1-3:1-3:1组成。
优选的，所述聚丙烯酸钠的分子量在800万-1000万之间。
所述的分散剂由乙二醇和椰油酰胺烷醇硫酸钠组成。
所述的椰油酰胺烷醇硫酸钠分子式为RCONCH2CH2OSO3Na(R为C10-15)。
所述的消泡剂为磷酸三丁酯或聚氧丙烯聚氧乙烯丙二醇醚中的一种或两种。
所述液体组分包括以下质量百分比的物质：
阳离子型丙烯酸酯共聚物乳液50％-65％
三聚氰胺高效减水剂1％-2％
余量为蒸馏水。
所述阳离子型丙烯酸酯共聚物乳液是指由丙烯酸酯、阳离子单体等进行聚合而成的微乳液。
锂渣中的SiO2绝大多数是以无定形的SiO2的形式存在，能够强烈吸附水泥熟料水化后产生的Ca(OH)2生成以水化硅酸钙为主体的水化产物，使水泥的硬化加速进行，同时其内比表面积大，可与有机反应物紧密结合；氧化镁膨胀剂可缓慢产生微膨胀使结构更为致密；N-全氟辛酰基氨酸盐(分子式C7F15CONHCH2COOM)具有良好的防水性能，可增加本发明防水涂料的防水效果；增粘保水剂能增加本发明防水涂料的粘结性能，并能保持水分使其中的硅酸盐体系水化反应更好的进行；增强剂能够增加无机胶凝材料的强度；分散剂不仅可以防止粉体固结，有效改善分散性，其中的椰油酰胺烷醇硫酸钠还能引入微小的密闭气泡，增加涂料的弹性和抗渗性能。
本发明中的阳离子型丙烯酸酯共聚物乳液对水泥基材料的渗透性更好，有更好的亲和力，可与硅酸盐材料水化生成的Ca(OH)2发生化学反应，生成离子键结合的大分子网络交织结构，且随龄期越长，水化程度越高，网络交织结构就越多，体系强度和耐水性越好。三聚氰胺高效减水剂有效提高各种物料的分散性，使更多的水泥和陶瓷砖抛光粉参与水化，形成硅酸盐骨架结构。消泡剂可消除因搅拌引起的大气泡，减少大气泡造成的缺陷，有效提高涂层的性能。本发明中的有机物质能够在表层反应形成憎水膜，无机物质能够渗入混凝土孔隙中反应生成不溶晶体堵塞混凝土孔隙。
本发明适用于卫生间、厨房、阳台等房屋装饰时时的二次防水工程，以及防渗和防潮的工程如地下室、地下车库等。
本发明的有益效果：
(1)本发明防水涂料既有水泥基材料抗压强度高、耐久性好的优点，又具有良好的弹性和防水性能，涂覆后可形成高强、坚韧、耐久的防水涂膜。
(2)本发明大量利用锂渣、抛光砖废渣，显著减轻排废企业的环保压力和排废负担，同时降低生产企业资源短缺的压力，既可以降低生产成本，又能改善生态环境，实现了变废为宝。
具体实施方式
以下结合实施例子具体说明本发明。
实施例1
一种建筑装饰工程用防水涂料由固体组分和液体组分按质量比5:7组成。
所述固体组分包括以下质量百分比的物质：锂渣粉10％、陶瓷砖抛光粉5％、氧化镁膨胀剂1％、N-全氟辛酰基氨酸盐0.05％、硅铝酸钠0.1％、增强剂0.01％、增粘保水剂0.1％、分散剂0.1％、消泡剂0.01％、余量为水泥。
所述水泥为P·O42.5水泥；所述锂渣粉细度为400目；所述陶瓷砖抛光粉细度为400目。
所述增强剂由三乙醇胺、乙二胺四亚甲基膦酸和蔗糖化钙按质量比1:2:1组成。
所述增粘保水剂由聚丙烯酸钠、温轮胶和瓜尔胶羟丙基三甲基氯化铵按1:3:1的质量比组成，所述聚丙烯酸钠的分子量在800万-1000万之间。
所述的分散剂由乙二醇和椰油酰胺烷醇硫酸钠按质量比1:1组成。
所述的消泡剂为磷酸三丁酯。
所述液体组分包括以下质量百分比的物质：
阳离子型丙烯酸酯共聚物乳液50％、三聚氰胺高效减水剂1％、余量为蒸馏水。
实施例2
一种建筑装饰工程用防水涂料由固体组分和液体组分按质量比9:7组成。
所述固体组分包括以下质量百分比的物质：锂渣粉30％、陶瓷砖抛光粉10％、氧化镁膨胀剂2％、N-全氟辛酰基氨酸盐1％、硅铝酸钠1％、增强剂.1％、增粘保水剂0.5％、分散剂0.5％、消泡剂0.05％、余量为水泥。
所述水泥为P·O42.5水泥；所述锂渣粉细度为600目；所述陶瓷砖抛光粉细度为600目。
所述增强剂由三乙醇胺、乙二胺四亚甲基膦酸和蔗糖化钙按质量比2:1:1组成。
所述增粘保水剂由聚丙烯酸钠、温轮胶和瓜尔胶羟丙基三甲基氯化铵按3:1:1的质量比组成，所述聚丙烯酸钠的分子量在800万-1000万之间。
所述的分散剂由乙二醇和椰油酰胺烷醇硫酸钠按质量比1:2组成。
所述的消泡剂为聚氧丙烯聚氧乙烯丙二醇醚。
所述液体组分包括以下质量百分比的物质：阳离子型丙烯酸酯共聚物乳液65％、三聚氰胺高效减水剂2％、余量为蒸馏水。
实施例3
一种建筑装饰工程用防水涂料由固体组分和液体组分按质量比7:7组成。
所述固体组分包括以下质量百分比的物质：锂渣粉20％、陶瓷砖抛光粉8％、氧化镁膨胀剂1.4％、N-全氟辛酰基氨酸盐0.5％、硅铝酸钠0.5％、增强剂0.05％、增粘保水剂0.2％、分散剂0.3％、消泡剂0.03％、余量为水泥。
所述水泥为P·O42.5水泥；所述锂渣粉细度为500目；所述陶瓷砖抛光粉细度为500目。
所述增强剂由三乙醇胺、乙二胺四亚甲基膦酸和蔗糖化钙按质量比2:2:1组成。
所述增粘保水剂由聚丙烯酸钠、温轮胶和瓜尔胶羟丙基三甲基氯化铵按3:2:1的质量比组成，所述聚丙烯酸钠的分子量在800万-1000万之间。
所述的分散剂由乙二醇和椰油酰胺烷醇硫酸钠按质量比1:3组成。
所述的消泡剂由磷酸三丁酯或聚氧丙烯聚氧乙烯丙二醇醚中按质量比1:1组成。
所述液体组分包括以下质量百分比的物质：阳离子型丙烯酸酯共聚物乳液60％、三聚氰胺高效减水剂1.3％、余量为蒸馏水。
实施例4
一种建筑装饰工程用防水涂料由固体组分和液体组分按质量比8:7组成。
所述固体组分包括以下质量百分比的物质：锂渣粉18％、陶瓷砖抛光粉9％、氧化镁膨胀剂1.3％、N-全氟辛酰基氨酸盐0.6％、硅铝酸钠0.8％、增强剂0.08％、增粘保水剂0.3％、分散剂0.2％、消泡剂0.04％、余量为水泥。
所述液体组分包括以下质量百分比的物质：阳离子型丙烯酸酯共聚物乳液55％、三聚氰胺高效减水剂1.8％、余量为蒸馏水。
实施例5
一种建筑装饰工程用防水涂料由固体组分和液体组分按质量比6:7组成。
所述固体组分包括以下质量百分比的物质：锂渣粉10％-30％、陶瓷砖抛光粉5％-10％、氧化镁膨胀剂1％-2％、N-全氟辛酰基氨酸盐0.05％-1％、硅铝酸钠0.4％、三乙醇胺0.01％、乙二胺四亚甲基膦酸0.01％、蔗糖化钙0.01％、聚丙烯酸钠0.1％、温轮胶0.1％、瓜尔胶羟丙基三甲基氯化铵0.1％、乙二醇0.1％、椰油酰胺烷醇硫酸钠0.2％、磷酸三丁酯0.03％、聚氧丙烯聚氧乙烯丙二醇醚0.01％、余量为水泥。
所述液体组分包括以下质量百分比的物质：阳离子型丙烯酸酯共聚物乳液55％、三聚氰胺高效减水剂1.5％、余量为蒸馏水。
对比例1
一种建筑装饰工程用防水涂料由固体组分和液体组分按质量比7:7组成。
所述固体组分包括以下质量百分比的物质：锂渣粉20％、陶瓷砖抛光粉8％、硅铝酸钠0.6％、增强剂0.05％、增粘保水剂0.2％、分散剂0.3％、消泡剂0.03％、余量为水泥。
所述水泥为P·O42.5水泥；所述锂渣粉细度为500目；所述陶瓷砖抛光粉细度为500目。
所述增强剂由三乙醇胺、乙二胺四亚甲基膦酸和蔗糖化钙按质量比2:2:1组成。
所述增粘保水剂由聚丙烯酸钠、温轮胶和瓜尔胶羟丙基三甲基氯化铵按3:2:1的质量比组成，所述聚丙烯酸钠的分子量在800万-1000万之间。
所述的分散剂由乙二醇和椰油酰胺烷醇硫酸钠按质量比1:3组成。
所述的消泡剂由磷酸三丁酯或聚氧丙烯聚氧乙烯丙二醇醚中按质量比1:1组成。
所述液体组分包括以下质量百分比的物质：阳离子型丙烯酸酯共聚物乳液60％、三聚氰胺高效减水剂1.3％、余量为蒸馏水。
对比例2
一种建筑装饰工程用防水涂料由固体组分和液体组分按质量比7:7组成。
所述固体组分包括以下质量百分比的物质：锂渣粉20％、陶瓷砖抛光粉8％、氧化镁膨胀剂1.4％、N-全氟辛酰基氨酸盐0.5％、硅铝酸钠0.6％、分散剂0.3％、消泡剂0.03％、余量为水泥。
所述水泥为P·O42.5水泥；所述锂渣粉细度为500目；所述陶瓷砖抛光粉细度为500目。
所述增强剂由三乙醇胺、乙二胺四亚甲基膦酸和蔗糖化钙按质量比2:2:1组成。
所述的分散剂由乙二醇和椰油酰胺烷醇硫酸钠按质量比1:3组成。
所述的消泡剂由磷酸三丁酯或聚氧丙烯聚氧乙烯丙二醇醚中按质量比1:1组成。
所述液体组分包括以下质量百分比的物质：阳离子型丙烯酸酯共聚物乳液60％、三聚氰胺高效减水剂1.3％、余量为蒸馏水。
性能测试
参照标准GB/T23445-2009，将实施例1-5与对比例1-2对聚合物防水涂料进行性能测试，其结果见下表1。
表1聚合物防水涂料性能
Claims (4)
1.一种建筑装饰工程用防水涂料，其特征在于，是由固体组分和液体组分按质量比5-9:7组成；所述固体组分包括以下质量百分比的物质：锂渣粉10％-30％、陶瓷砖抛光粉5％-10％、氧化镁膨胀剂1％-2％、N-全氟辛酰基氨酸盐0.05％-1％、硅铝酸钠0.1％-1％、增强剂0.01％-0.1％、增粘保水剂0.1％-0.5％、分散剂0.1％-0.5％、消泡剂0.01％-0.05％、余量为水泥；所述液体组分包括以下质量百分比的物质：阳离子型丙烯酸酯共聚物乳液50％-65％、三聚氰胺高效减水剂1％-2％、余量为蒸馏水；所述增粘保水剂由聚丙烯酸钠、温轮胶和瓜尔胶羟丙基三甲基氯化铵按质量比1-3:1-3:1组成；所述增强剂由三乙醇胺、乙二胺四亚甲基膦酸和蔗糖化钙按质量比1-2:1-2:1组成。
2.根据权利要求1所述的建筑装饰工程用防水涂料，其特征在于，所述聚丙烯酸钠的分子量在800万-1000万之间。
3.根据权利要求1所述的建筑装饰工程用防水涂料，其特征在于，所述的分散剂由乙二醇和椰油酰胺烷醇硫酸钠组成。
4.根据权利要求1所述的建筑装饰工程用防水涂料，其特征在于，所述的消泡剂为磷酸三丁酯或聚氧丙烯聚氧乙烯丙二醇醚中的一种或两种。