CN106628710B - The insulating layer construction method of low-temperature storage tank - Google Patents
The insulating layer construction method of low-temperature storage tank Download PDFInfo
- Publication number
- CN106628710B CN106628710B CN201611252863.3A CN201611252863A CN106628710B CN 106628710 B CN106628710 B CN 106628710B CN 201611252863 A CN201611252863 A CN 201611252863A CN 106628710 B CN106628710 B CN 106628710B
- Authority
- CN
- China
- Prior art keywords
- insulating layer
- storage tank
- low
- temperature storage
- fiberglass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The insulating layer construction method of the low-temperature storage tank of the present invention, including prepare polyester insulating layer, prepare fiberglass protective layer;Cutting forms dashpot, fills elastic joint filling agent in dashpot on the fiberglass protective layer.The present invention forms buffering area using elastic joint filling agent on fiberglass protective layer; to absorb the modified difference generated due to elasticity modulus, the Poisson when difference of linear expansion coefficient between polyester insulating layer and fiberglass protective layer; efficiently solve low temperature cold insulation field because using fiberglass as mechanical protection layer, and be likely to occur glass fiber reinforced plastic surface deformation, destruction the phenomenon that.
Description
Technical field
The present invention relates to the insulating layer construction methods of the insulating layer of low-temperature storage tank more particularly to a kind of low-temperature storage tank.
Background technology
Existing part Cryo Equipment, prepares one layer of fiberglass protective layer usually outside polyester insulating layer, and fiberglass is protected
Sheath is prepared by hand-made or spraying method.Protective layer, which plays, to be prevented vapor from entering thermal insulation material, prevents from hitting
The effect hit.But due to being applied to Cryo Equipment field, thermal insulation material is prepared in thermal insulation material outer surface by cold events
Fiberglass leads to thermal insulation material shrinkage and expansion deformation due to expanding with heat and contract with cold, to cause deformation to fiberglass protective layer, destroy.
Invention content
The purpose of the present invention is exactly to solve the above-mentioned problems, to provide a kind of insulating layer construction method of low-temperature storage tank.
In order to achieve the above object, the present invention is achieved through the following technical solutions:A kind of insulating layer of low-temperature storage tank is applied
Work method, includes the following steps:
One, one strata ester insulating layer is prepared by the technique of spraying on the surface of low-temperature storage tank;
Two, using cutting machine and sander, cutting polishing is carried out to the polyester insulating layer of spraying, makes polyester insulation layer surface
It is smooth;
Three, it by hand-made or spraying method, prepares one layer of fiberglass in smooth polyester insulation layer surface and protects
Sheath;
Four, it after waiting for that fiberglass is fully cured, is slightly polished glass fiber reinforced plastic surface using sander, abrades uneven surface
The fiberglass in main plot domain, and the region of existing defects is repaired;
Five, in fiberglass protective layer, dashpot cutting track is marked using marking pen;
Six, fiberglass protective layer is cut along cutting track using trimmer, removes the glass within the scope of cutting track
Glass steel forms dashpot;
Seven, in one layer of thin adhesive tape of each stickup at the 1cm of dashpot both sides;
Eight, using elastic joint filling agent fill tool, elastic joint filling agent is filled between two thin adhesive tapes, makes to fill out in dashpot
Full elastic joint filling agent, forms buffering area, is used in combination the tools such as scraper plate to apply surface and is scraped;
Nine, tearing-off adhesive tape after the completion of scraping is applied, the insulating layer construction of low-temperature storage tank is completed.
The thickness of the polyester insulating layer is 100-400mm.
The thickness of the fiberglass protective layer is 2-3mm.
The width of the buffering area is 5-8mm.
The quantity of dashpot is set according to the size of low-temperature storage tank, it is a plurality of along being axially and radially respectively set for low-temperature storage tank
Dashpot, the spacing between adjacent buffer slot are 80cm-100cm.
The elastic joint filling agent is: MS 930TM。
The present invention forms buffering area using elastic joint filling agent on fiberglass protective layer, to absorb polyester insulating layer and glass
The modified difference generated due to elasticity modulus, the Poisson when difference of linear expansion coefficient between steel protective layer, efficiently solves low
Warm cold insulation field because using fiberglass as mechanical protection layer, and be likely to occur glass fiber reinforced plastic surface deformation, destruction the phenomenon that.
Specific implementation mode
Technique purpose
Ensure fiberglass intensity requirement and appearance requirement under, solve due to thermal insulation material expand with heat and contract with cold so as to cause
The phenomenon that fiberglass deformation failure.
Process materials
Equipment:Trimmer, elastic joint filling agent fill tool, Graco polyurethane spray automatic doubler surface glouer, cutting machine, sander, bullet
Property gap filler scraper plate etc.;
Spraying process material:Unsaturated polyester resin, accelerating agent (cobalt naphthenate), curing agent (peroxide), glass fibers
Dimension, fiberglass surfacing mat, isocyanates, polyalcohol, elastic joint filling agent, adhesive tape etc..
Processing step
The polyester insulating layer of one layer of 300mm thickness is prepared by the technique of spraying on low-temperature storage tank surface;
Using cutting machine and sander, cutting polishing is carried out to the polyester insulating layer of spraying, keeps polyester insulation layer surface flat
It is whole;
By hand-made or spraying method, it is 2mm- to prepare a layer thickness in smooth polyester insulation layer surface
The fiberglass protective layer of 3mm;
It after waiting for that fiberglass is fully cured, is slightly polished glass fiber reinforced plastic surface using sander, abrades surface irregularity
The fiberglass in region, and the region of existing defects is repaired;
Polyester fiberglass steel surface on low-temperature storage tank surface marks dashpot cutting track (low-temperature storage tank using marking pen
Adjacent two buffering separation about 1m);
Using trimmer, cut along the track that marking pen marks;
It is being parallel to dashpot, and on the both sides of the distance apart from dashpot about 1cm, is respectively pasting one layer of thin adhesive tape;
Using elastic joint filling agent fill tool, elastic joint filling agent is filled between two thin adhesive tapes, the tools such as scraper plate are used in combination
Surface is applied and is scraped.Tearing-off adhesive tape after the completion of painting is scraped.
Claims (6)
1. a kind of insulating layer construction method of low-temperature storage tank, which is characterized in that include the following steps:
One, one strata ester insulating layer is prepared by the technique of spraying on the surface of low-temperature storage tank;
Two, using cutting machine and sander, cutting polishing is carried out to the polyester insulating layer of spraying, keeps polyester insulation layer surface flat
It is whole;
Three, by hand-made or spraying method, one layer of fiberglass protective layer is prepared in smooth polyester insulation layer surface;
Four, it after waiting for that fiberglass is fully cured, is slightly polished glass fiber reinforced plastic surface using sander, abrades uneven surface main plot
The fiberglass in domain, and the region of existing defects is repaired;
Five, in fiberglass protective layer, dashpot cutting track is marked using marking pen;
Six, fiberglass protective layer is cut along cutting track using trimmer, removes the fiberglass within the scope of cutting track,
Form dashpot;
Seven, in one layer of thin adhesive tape of each stickup at the 1cm of dashpot both sides;
Eight, using elastic joint filling agent fill tool, elastic joint filling agent is filled between two thin adhesive tapes, makes to fill up bullet in dashpot
Property gap filler, formed buffering area, be used in combination scraper plate by surface apply be scraped;
Nine, tearing-off adhesive tape after the completion of scraping is applied, the insulating layer construction of low-temperature storage tank is completed.
2. the insulating layer construction method of low-temperature storage tank according to claim 1, it is characterised in that:The polyester insulating layer
Thickness is 100-400mm.
3. the insulating layer construction method of low-temperature storage tank according to claim 1, it is characterised in that:The fiberglass protective layer
Thickness be 2-3mm.
4. the insulating layer construction method of low-temperature storage tank according to claim 1, it is characterised in that:The width of the buffering area
For 5-8mm.
5. the insulating layer construction method of low-temperature storage tank according to claim 1, it is characterised in that:According to the big of low-temperature storage tank
The quantity of small setting dashpot, is axially and radially respectively set a plurality of dashpot, between adjacent buffer slot along low-temperature storage tank
Spacing is 80cm-100cm.
6. the insulating layer construction method of low-temperature storage tank according to claim 1, it is characterised in that:The bullet used in dashpot
Property gap filler is MS 930TM。