CN106625951A - Imitated-weathering treatment process of elm panel - Google Patents
Imitated-weathering treatment process of elm panel Download PDFInfo
- Publication number
- CN106625951A CN106625951A CN201610866581.6A CN201610866581A CN106625951A CN 106625951 A CN106625951 A CN 106625951A CN 201610866581 A CN201610866581 A CN 201610866581A CN 106625951 A CN106625951 A CN 106625951A
- Authority
- CN
- China
- Prior art keywords
- paint
- sheet material
- elm
- time
- weathering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an imitated-weathering treatment process of an elm panel. The invention has the technical scheme main point that the imitated-weathering treatment process of the elm panel comprises the following steps of (1) wiredrawing the elm panel; (2) polishing the bare elm panel treated through the step (1); (3) coloring the elm panel treated through the step (2); and (4) painting the elm panel treated through the step (3). The invention provides a process method for improving an anti-slip performance of the elm panel.
Description
Technical field
The present invention relates to a kind of sheet material handling process, the imitative weathering handling process of more particularly to a kind of elm sheet material.
Background technology
Elm, main product temperate zone, deciduous tree, the height of tree is big, and throughout northern various places, the especially Huanghe valley is seen everywhere.Elm
Wood is tough and tensile, and texture is sensible clear, hardness and moderate strength, and planing surface is smooth, and chord plane decorative pattern is beautiful, can be used to make desk,
Plate.
The desktop of desk and floor need preferable non-skid property.
The content of the invention
It is an object of the invention to provide a kind of imitative weathering handling process of elm sheet material, it is preferable that it has can elm sheet material
Non-skid property.
The present invention above-mentioned purpose technical scheme is that：Science and engineering at a kind of imitative weathering of elm sheet material
Skill, comprises the following steps：
1) elm sheet material is carried out into wire drawing process；
2) by through step 1) process elm sheet material carry out white stubble polishing；
3) by through step 2) process elm sheet material carry out coloring treatment；
4) by through step 3) process elm sheet material carry out paint process.
By adopting above-mentioned technical proposal, after wire drawing, surface can produce texture, ditch slot texture to elm sheet material,
Compare before wire drawing process that its surface is more coarse, dynamic friction factor is bigger, non-skid property more preferably, using this elm sheet material system
The desktop made or floor, non-skid property is also more superior.After wire drawing, there is burr in surface to elm sheet material, affect to make
Comfortableness.To be polished smooth through the elm plate surface of wire drawing by white tea polishing, increase the comfortableness for using.If
Elm sheet material long-time is exposed to used in air, is vulnerable to ambient influnence, when it bears the wetness impregnation in midsummer, then experiences the spring
The difference of air-dried, the contraction that internal organizational structure can be uneven of day, particularly radial contraction and tangential contraction, so as to occur receiving
Compression deformation and buckling deformation.The moth erosion of rainy season, mould and insects simultaneously may also be elm plate surface and mottling, small holes caused by worms occurs, and
Gradually inwardly spread, cause sheet material prematurely rotten breaking-up.First it is in plate so to process the surface of elm sheet material
Carry out coloring treatment using colouring agent on material, enable colouring agent penetrate into timber fibrous inside it is in combination, more preferable reserve
The mechanism of material.Then again spray painting process is carried out to elm sheet material, increases the thickness of its sealer, extend its service life.
The present invention is further arranged to：The white stubble polishing of elm sheet material is that 120 mesh sand paper sandings are first used on sander,
Then manually with 240 mesh sand paper sanding is carried out.
By adopting above-mentioned technical proposal, the mesh number of sand paper is more little more coarse, and the upper and lower surface of sheet material is entered using sander
The preliminary polishing of row is processed, and then manually further polishing is carried out to the upper and lower surface of sheet material using 240 mesh sand paper simultaneously right
The side of sheet material carries out polishing process.
The present invention is further arranged to：Under field conditions (factors) indoor temperature is relatively wet at 15～28 DEG C for sheet material after coloring
Degree less than 70%, winter at least places 12 hours, and summer at least places 4 hours.
By adopting above-mentioned technical proposal, when temperature is higher, colouring agent is dried comparatively fast, and levelability is bad, in turn results in painting
Brush is uneven.When temperature is relatively low, the viscosity of colouring agent is higher, it is difficult to brush uniform, it is impossible to ensure preferable brushing quality.When
By temperature control during brushing colouring agent at 15～28 DEG C, relative humidity is controlled below 70%, the coloring effect of elm sheet material
Fruit preferably, is at least placed 12 hours in the winter time after the coloring of elm sheet material, and summer at least places 4 hours can fully be dried.
The present invention is further arranged to：At 10 DEG C -35 DEG C, relative humidity control exists temperature control during paint process
Less than 70%.
By adopting above-mentioned technical proposal, when paint is sprayed in the higher environment of temperature, the curing rate of paint compared with
Hurry up, on its surface the speed of dry film is formed, dry film can stop the volatilization of solvent and diluent in internal paint, these volatilizations
The accumulated gases of generation to it is a certain amount of when, can make dry film formed fold or produce bubble, affect paint spraying effect, cause
The paint out-of-flatness of spraying.In the relatively low environment of temperature during spray paint, the viscosity with temperature of paint is reduced and increased, and is brushed
Degradation, must be added to the diluent of additional quantity to obtain preferable brushing performance sometimes, but be difficult to reach the oil of regulation
Paint brushes to obtain flatness, affects the quality of painting layer.
The present invention is further arranged to：Temperature control during paint process is at 25 DEG C.
By adopting above-mentioned technical proposal, under 25 DEG C of this temperature conditionss, the spraying effect of paint is best.
The present invention is further arranged to：Paint during paint process uses spray gun spraying, the pressure of the spraying of spray gun
Control is in 0.35-0.6Mpa.
By adopting above-mentioned technical proposal, when Stress control is between 0.35-0.6Mpa, spray gun will can paint to paint
The form of mist uniformly sprays, and then can uniformly spray above sheet material, and spraying effect is preferable.
The present invention is further arranged to：The nozzle of spray gun is maintained at 200-250 ㎜ with the distance of plate face.
By adopting above-mentioned technical proposal, during hypotelorism, the painting layer that spray gun sprays easily is piled up at one, spraying
It is not uniform enough, easy sagging；Painting layer can become crude when too far, brightless, and lacquer painting has orange peel, out-of-flatness；When serious also
Minute bubbles occur, can cause the adhesive force of film reduces, paint atomizing loss increases.
The present invention is further arranged to：Elm sheet material sprays altogether five times paint, arbitrarily paint spraying time interval twice
Winter and summer, summer is divided to be not less than 8 hours, winter is not less than 12 hours.
By adopting above-mentioned technical proposal, the tentatively air-dried quick degree of skin of paint and the close phase of the height of environment temperature
Close, summer is not less than 8 hours, and winter is not less than 12 hours, first the skin of paint of previous time can be air-dried tentatively, can be sprayed thereon
Apply second time paint.
The present invention is further arranged to：With 240 mesh sand papering one time after spraying first pass paint, second time paint is sprayed
Afterwards first with 240 mesh sand papering first passes, then with 320 mesh sand papering second time, spray after the 3rd time paint first with 240 mesh sand
Paper is polished first pass, then with 320 mesh sand papering second time, is sprayed after the 4th time paint first with 240 mesh sand papering first passes,
Again with 320 mesh sand papering second time.
By adopting above-mentioned technical proposal, needs when second time paint is sprayed on first pass paints the skin of paint to be formed
The skin of paint to be formed is painted to first pass to polish so as to which surface becomes coarse, increase its bonding with second time skin of paint
Ability.Also first to be polished when spraying the 3rd time skin of paint on second time skin of paint simultaneously, by that analogy, the 3rd, the
Four times paint also will be polished, because the 5th time paint is the surface layer of elm sheet material, without the need for entering again after spraying is finished
Row polishing.
The present invention is further arranged to：Spraying first pass paint is 120～140 grams/m, second time paint for 100～
110 grams/m, the 3rd time paint is 100～110 grams/m, and the 4th time is 100～110 grams/m, the 5th time 120
～140 grams/m.
By adopting above-mentioned technical proposal, when paint spraying it is relatively thin when, affect plumpness, spraying it is too thick when affect oil
The absorption affinity of paint.The THICKNESS CONTROL of paint is more suitable in the range of 110-120 gram/m, simultaneously as first pass
Paint has certain infiltration closest to plate surface, thus the thickness of spraying it is relative will it is thick a bit, select 120-140 gram/
In the range of square metre.5th time paint is surface layer, needs certain intensity, and thickness is relatively larger, is selected in 120-140
In the range of gram/m.
In sum, the invention has the advantages that：After wire drawing, surface can produce line to elm sheet material
Reason, ditch slot texture, compare before wire drawing process that its surface is more coarse, and dynamic friction factor is bigger, and non-skid property more preferably, uses this
Desktop or the floor of the manufacture of elm sheet material are planted, non-skid property is also more superior.After wire drawing, surface exists elm sheet material
Burr, affects the comfortableness for using.To be polished smooth through the elm plate surface of wire drawing by white tea polishing, what increase was used
Comfortableness.If elm sheet material long-time is exposed to used in air, it is vulnerable to ambient influnence, when it bears the moist leaching in midsummer
Stain, then experience the difference of air-drying for springtime, the contraction that internal organizational structure can be uneven, particularly radial contraction and tangential contraction
It is different, so as to there is contraction distortion and buckling deformation.The moth erosion of rainy season, mould and insects simultaneously may also be the appearance of elm plate surface
Mottling, small holes caused by worms, and gradually inwardly spread, cause sheet material prematurely rotten breaking-up.So at will be to the surface of elm sheet material
Reason, be first to carry out coloring treatment using colouring agent on sheet material, enable colouring agent penetrate into timber fibrous inside it is in combination,
Preferably retain the mechanism of timber.Then again spray painting process is carried out to elm sheet material, increases the thickness of its sealer, extended
Its service life.
Specific embodiment
The present invention is described in further detail below.
Embodiment：Elm sheet material is put into wire drawing machine, first wire drawing is carried out to one face, afterwards turned over to its another side
Carry out wire drawing.It is manually bad to local wire-drawing effect on its side and upper and lower surface again after the completion of using wire drawing machine wire drawing
Place carries out wire drawing.
Start white stubble polishing after elm sheet material wire drawing, first with 120 mesh sand paper sandings, Ran Houren on sander during polishing
Work carries out sanding with 240 mesh sand paper, firmly appropriate, uniform according to along the grain direction sanding during sanding, is not allow for sanding
Enclose, coarse sand trace prints, leakage sand, scuffing phenomenon, it is ensured that corner is neat, and nothing collapses stubble.The positive veneer seam of elm sheet material, black line, it is rotten,
The defects such as gap will supplement plate or wood wool, the uncommon back side is carefully stitched (width be less than 0.5mm) and can be mended with soil is mended.
Elm sheet material is starting to do coloring treatment after the polishing of white stubble, and the deeper portion of sheet material intrinsic colour is directed to before coloring
Position carries out bleaching using hydrogen peroxide, it is ensured that its integral color is close.At veneer crack, often locate gap and be less than 0.1mm, table
Edge-gluing veneer necessary color in face is close.Along the grain to colour in direction during coloring, according to the difference of timber intrinsic colour, select different
The colouring agent of color, it is ensured that sheet material color after finished pigmented is uniform, the depth is close.
It is especially noted that impact of the season humidity to colouring, carries out aeration-drying, prevent sheet material from returning after colouring white.Coloring
Sheet material afterwards under natural environmental condition indoor temperature at 15～28 DEG C, relative humidity is below 70%, and it is little that winter at least places 12
When, summer at least places 4 hours.
When temperature is higher, colouring agent is dried comparatively fast, and levelability is bad, in turn results in brushing uneven.When temperature is relatively low,
The viscosity of colouring agent is higher, it is difficult to brush uniform, it is impossible to ensure preferable brushing quality.Temperature control when by brushing colouring agent
At 15～28 DEG C, relative humidity is controlled less than 70% system, the coloring effect of elm sheet material preferably, elm sheet material colour after
Winter at least places 12 hours, and summer at least places 4 hours can fully be dried.
Time needed for colouring agent is dried when listing different temperatures here and painting brushing effects during different temperatures
As can be seen from the table, temperature at 10 DEG C and its it is following when, the viscosity of colouring agent is larger, smoothens effect bad.Temperature is big
Although colouring agent significantly shortens the time required to being dried when 30 DEG C, high temperature equally also contributes to the levelability of toner, causes
The brushing of colouring agent is uneven.So by temperature control in the range of 15～28 DEG C when, the effect of brushing colouring agent is best.
Start to do paint process after elm sheet material coloring treatment, 25 ° or so of operation area optimum temperature, temperature when paint is processed
Should control at 10 °～35 °, relative humidity is below 70%.Paint uses the spray pressure of spray gun spraying, spray gun to control 0.35
～0.6Mpa, Spray gun nozzle should be maintained at 200～250mm with the distance of plate face.The relative face that is sprayed-on of nozzle is close to vertically during spraying
At the uniform velocity move spraying, abreast upper and lower or left and right, it is ensured that the flatness of coating.Spraying method-as be first to sheet material across grain side
Spray to moving in parallel to come and go, then along grain direction moved in parallel round spraying again.The speed of spray gun movement is uniform, moves
The speed of dynamic speed, be according to the thickness of the coating for being sprayed or whether sagging is defined.
When paint is sprayed in the higher environment of temperature, the curing rate of paint is very fast, and on its surface dry film is formed
Speed, dry film can stop the volatilization of solvent and diluent in internal paint, and the accumulated gases that these volatilizations are produced are to necessarily
During amount, dry film can be made to form fold or produce bubble, affect the spraying effect of paint, cause the paint out-of-flatness for spraying.
In the relatively low environment of temperature during spray paint, the viscosity with temperature of paint is reduced and increased, brushing degradation, must be added sometimes
Enter the diluent of additional quantity to obtain preferable brushing performance, but be difficult to brush to obtain flatness with the paint for reaching regulation, affect
The quality of painting layer.
The uniform effect that paint is brushed when painting to form dry film required time and different temperatures when listing different temperatures here
Really
As can be seen from the table, temperature is at 5 DEG C, and the viscosity of paint is too high, it is difficult to brushes uniformly, in turn results in painting layer
Flatness is poor.When temperature reaches more than 10 DEG C, the viscosity of paint is suitable, can spray uniform, the flatness of painting layer
Preferably.Temperature it is higher formed dry film time it is shorter, the solvent and diluent in paint it is more readily volatilized, when temperature reaches 40
DEG C when, form the time of dry film at 7 minutes or so, temperature at this moment has begun to affect paint to brush to obtain flatness, so applying
During brush paint, temperature should be limited to 10 °～35 °.Simultaneously the temperature when spray paint at 25 DEG C, wave by solvent and diluent
That what is sent out is relatively slow, and this temperature also is adapted for the work of technical staff, so temperature is at 25 DEG C, the spraying effect of paint is best.
Twice paint spraying time interval divides winter and summer, summer to be not less than 8 hours, and winter is not less than 12 hours.One
Sheet material after secondary spraying without trickling, sagging, tangerine peel, tacky, no concave-convex, without splitting paint, corner, rib is straight, it is full, round and smooth, without swollen
Side, lacquer painting without bubbling, pin hole, grit, white point, white stupefied, cut, without wooden hole depression etc., thickness is uniform, and color-cause, thickness should
With quantity for spray control.Forbid paint film too thick, in case affecting the adhesive force of paint.
Strict control quantity for spray, first pass paint is 120～140 grams/m, second time paint for 100～110 grams/it is flat
Square rice, the 3rd time paint be 100～110 grams/m, the 4th time be 100～110 grams/m, the 5th time 120～140 grams/
Square metre.
According to the thickness and spray-coating surface of required coating whether level, appropriate viscosity is selected, added by the size proportioning of viscosity
Solvent or diluent, stirs after proportioning, wait paint bubble disappeared just use, can otherwise affect coating quality；Curing agent is by the ratio for specifying
Example add paint in, to add curing agent paint should be finished as early as possible ,-as be less than 4 hours.Paint palpus side to PE to add, side
Reconcile, while using, the paint for mixing up is less than 10 minutes, and otherwise paint will be gelled, it is impossible to cover with paint, lacquer, colour wash, etc., and causes to waste.
First pass is painted and second time paint spray time is separated by, and sealing effect should be not less than 24 hours；Open effect is not low
In 12 hours.With 240 mesh sand paper sand one time after spraying first pass paint, spraying paint for second time after first with 240 mesh sand paper sand the
One time, then with the soft sand paper sand of 320 mesh second time, then spray the 3rd time paint.Spray after the 3rd time paint first with 240 mesh sand paper
Sand first pass, then with the soft sand paper sand of 320 mesh second time, then spray the 4th time paint.Spray and first use 240 mesh after the 4th time paint
Sand paper sand first pass, then with the soft sand paper sand of 320 mesh second time, then spray the 5th time paint.
This specific embodiment is only explanation of the invention, and it is not limitation of the present invention, people in the art
Member can make as needed the modification without creative contribution after this specification is read to the present embodiment, but as long as at this
All protected by Patent Law in the right of invention.
Claims (10)
1. a kind of elm sheet material imitates weathering handling process, it is characterised in that：Comprise the following steps：1) elm sheet material is carried out into wire drawing
Process；
2) by through step 1) process elm sheet material carry out white stubble polishing；
3) by through step 2) process elm sheet material carry out coloring treatment；
4) by through step 3) process elm sheet material carry out paint process.
2. a kind of elm sheet material according to claim 1 imitates weathering handling process, it is characterised in that：The white stubble of elm sheet material
Polishing is that 120 mesh sand paper sandings are first used on sander, then manually with 240 mesh sand paper carries out sanding.
3. a kind of elm sheet material according to claim 1 imitates weathering handling process, it is characterised in that：Elm plate after coloring
Material under field conditions (factors) indoor temperature at 15～28 DEG C, relative humidity below 70%, at least place 12 hours, and summer is extremely by winter
Place 4 hours less.
4. a kind of elm sheet material according to claim 1 imitates weathering handling process, it is characterised in that：During paint process
Temperature control at 10 DEG C -35 DEG C, relative humidity is controlled below 70%.
5. a kind of elm sheet material according to claim 4 imitates weathering handling process, it is characterised in that：During paint process
Temperature control at 25 DEG C.
6. a kind of elm sheet material according to claim 1 imitates weathering handling process, it is characterised in that：During paint process
Paint use spray gun spraying, the Stress control of the spraying of spray gun is in 0.35-0.6Mpa.
7. a kind of elm sheet material according to claim 6 imitates weathering handling process, it is characterised in that：The nozzle of spray gun and elm
The distance of wood plank is maintained at 200-250 ㎜.
8. a kind of elm sheet material according to claim 7 imitates weathering handling process, it is characterised in that：Elm sheet material sprays altogether
Five times paint are applied, arbitrarily twice paint spraying time interval divides winter and summer, summer to be not less than 8 hours, and winter is not less than 12
Hour.
9. a kind of elm sheet material according to claim 8 imitates weathering handling process, it is characterised in that：Spraying first pass paint
Afterwards with 240 mesh sand papering one time, spray after second time paint first with 240 mesh sand papering first passes, then beaten with 320 mesh sand paper
Mill second time, sprays and first use after the 3rd time paint 240 mesh sand papering first passes, then with 320 mesh sand papering second time, sprays
First with 240 mesh sand papering first passes after 4th time paint, then with 320 mesh sand papering second time.
10. a kind of elm sheet material according to claim 9 imitates weathering handling process, it is characterised in that：Spraying first pass oil
Paint as 120～140 grams/m, second time paint is 100～110 grams/m, and the 3rd time paint is 100～110 grams/square
Rice, the 4th time be 100～110 grams/m, the 5th time 120～140 grams/m.