CN106618345A - Epoxy resin liner waterless toilet - Google Patents
Epoxy resin liner waterless toilet Download PDFInfo
- Publication number
- CN106618345A CN106618345A CN201611050498.8A CN201611050498A CN106618345A CN 106618345 A CN106618345 A CN 106618345A CN 201611050498 A CN201611050498 A CN 201611050498A CN 106618345 A CN106618345 A CN 106618345A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- epoxy
- plate
- parts
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an epoxy resin liner waterless toilet including a body with a pit. A turnover plate is arranged on the bottom of the pit and is connected with a pedal through a connecting rod mechanism, the pedal being arranged on the body. A storage bag is arranged under the turnover plate. The toilet is characterized in that the body is formed by an acrylic panel and an inner liner plate. The inner liner plate comprises a glass fiber layer and an epoxy resin particle plate from top to bottom successively. The epoxy resin particle plate is a regenerated epoxy resin composite glass fiber plate. According to the invention, 191 resin residuals and epoxy resin waste materials are used to produce the inner liner plate of a toilet, which solves the difficulty of utilizing epoxy resin and 191 resin and is energy-saving and environment-friendly. After epoxy resin particles are added into the inner liner plate, the heat resistance of the toilet is improved, the adaptability to environment is enhanced, and the toilet is more suitable for usage in open air environments such as building sites.
Description
Technical field
The present invention relates to a kind of epoxy resin liner waterless closestool.
Background technology
Existing squat type closet typically rinses solid feces using clear water, but for some use environments without water source,
Existing squatting pot is helpless.And with the increase of the density of population, the deterioration of natural environment, many local water resources are increasingly
Scarcity, and toilet, used as the articles for daily use of people's daily life system, its wash water is also that very big waste is brought to water resource,
Therefore it is badly in need of providing a kind of toilet without the need for water.
Chinese patent literature CN204889845U discloses a kind of anhydrous squatting pot, including a sheet containing latrine pit
Body, it is characterised in that the bottom surface of the latrine pit is provided with a turnover panel, and the turnover panel is by linkage and the pedal on body
It is connected, below the turnover panel storage bag is provided with.The characteristics of with simple structure, health reliability.
But inventor is in practice, it has been found that the material of the toilet is 191 resins and acrylic, in high temperature environments cannot
Normally use, because material is excessively soft, panel turnover mechanism cannot be used normally, and this waterless closestool is used for construction site, therefore
The defect leverages promoting the use of for the toilet.
The content of the invention
To solve the deficiency that above-mentioned prior art is present, the invention provides a kind of epoxy resin liner waterless closestool, adopts
With acrylic composite epoxy resin interior lining panel, the heat resistance and durability of toilet are improved.
The present invention adopt concrete technical scheme be：
A kind of epoxy resin liner waterless closestool, including a body containing latrine pit, the bottom surface of latrine pit is provided with one and turns over
Plate, the turnover panel is connected by linkage with the pedal on body, and below the turnover panel storage bag is provided with, and its feature exists
Be made up of acrylic panel and interior lining panel in the body, the interior lining panel under the acrylic panel, the interior lining panel from
Top to bottm includes successively glass layer and epoxy particles plate.
The epoxy particles plate is regenerative epoxy resin composite glass fiber plate, by epoxy resin leaf regeneration system
Into specifically, the epoxy particles plate includes regenerative epoxy resin particle, macromolecule resin, staple glass fibre, filling
Agent, modifying agent.
In the epoxy particles plate, regenerative epoxy resin particle, macromolecule resin, staple glass fibre, filler, change
Good dose of mass fraction is respectively 30～60 parts, 20～50 parts, 10～40 parts, 5～20 parts, 1～10 part.
Further, the regenerative epoxy resin particle is by the epoxy resin blade cuts of wind-power electricity generation, is ground into particle diameter
Particle for 1～5mm is obtained；
Macromolecule resin in the epoxy particles plate is unsaturated polyester resin, further, described unsaturated poly-
Ester resin is preferably adjacent benzene-type unsaturated polyester resin, more preferably 196 resins and 191 resins, and mass ratio is 1:0.5～3.
191 resin can be the particle that 191 resin leftover pieces are ground into 1～10mm of particle diameter using 191 resins of regeneration
Obtain.
The staple glass fibre refers to the glass fibre of 0.1～10mm of fibre length, preferably 0.2～5mm.
The filler be silica flour, aluminium hydrate powder, silicon dioxide powder, marble powder, Paris white in one kind or
Two or more mixing.
The modifying agent is one or more the mixing in toughener, antiager, fire retardant, bulking agent.It is described
Toughener can be dioctyl phthalate, dibutyl phthalate (DBP), polyvinyl acetate or chlorinated paraffin etc..
The epoxy particles plate can pass through to pour or Jing hot press hot pressing is made.
The preferred unsaturated polyester resin composite glass fiber plate of the glass layer, i.e. unsaturated polyester (UP) glass steel.
Further, in the unsaturated polyester resin composite glass fiber plate, unsaturated polyester resin is preferably adjacent benzene-type
Unsaturated polyester resin, more preferably 196 resins and/or 191 resins.
Further, the unsaturated polyester resin composite glass fiber plate includes unsaturated polyester resin, the short fibre of glass
Dimension, filler, modifying agent, wherein, unsaturated polyester resin, staple glass fibre, filler, the mass fraction of modifying agent are respectively
30～80 parts, 10～40 parts, 5～20 parts, 1～10 part.The modifying agent is toughener, antiager, fire retardant, bulking agent, draws
Send out one or more the mixing in agent, accelerator, curing agent.The toughener can for dioctyl phthalate,
Dibutyl phthalate (DBP), polyvinyl acetate or chlorinated paraffin etc..
The unsaturated polyester resin composite glass fiber plate can pass through to pour or Jing hot press hot pressing is made.
The body can also include bottom, and under interior lining panel, the bottom can be froth bed to the bottom.
When the bottom is froth bed, play a part of sound-absorbing damping.The froth bed can for polyurethane foam and/or
Unsaturated polyester (UP) foam.
The present invention also provides a kind of interior lining panel for waterless closestool, and the interior lining panel includes successively from top to bottom glass fibers
Dimension layer and epoxy particles plate.Bottom is also provided with the interior lining panel, the bottom can be froth bed.
The regenerative epoxy resin bathroom interior lining panel that the present invention is provided, is strengthened using glass layer, and recycles epoxy
Resin particle, equally using glass fiber reinforcement, improves the intensity of interior lining panel, and froth bed sound-absorbing damping, and traditional
Interior lining panel is compared with more preferable erasure effect.
The present invention recycles 191 resin leftover pieces and epoxy resin waste material makes toilet interior lining panel, solves asphalt mixtures modified by epoxy resin
A utilization difficult problem for fat and 191 resins, energy-conserving and environment-protective.Add after epoxy particles in interior lining panel, be effectively improved the horse
The heat resistance of bucket, environment fitness is high, under being more applicable for the open-air atmospheres such as construction site.
Description of the drawings
The sectional structure chart of Fig. 1 interior lining panels.
The sectional structure chart of the another embodiment of Fig. 2 interior lining panels.
Reference：1 is glass layer, and 2 is epoxy particles plate, and 3 is froth bed.
Specific embodiment
Below technical scheme is described further with specific embodiment, but protection scope of the present invention is not
It is limited to this.
Embodiment 1
The present invention provides a kind of epoxy resin liner waterless closestool, including a body containing latrine pit, the bottom surface of latrine pit
A turnover panel is provided with, the turnover panel is connected by linkage with the pedal on body, and storage is provided with below the turnover panel
Bag, it is characterised in that the body is made up of acrylic panel and interior lining panel, the interior lining panel is located under acrylic panel, institute
Interior lining panel sectional structure chart is stated as shown in figure 1, including glass layer 1 and epoxy particles plate 2 successively from top to bottom.
Wherein epoxy particles plate is regenerative epoxy resin composite glass fiber plate, by epoxy resin leaf regeneration system
Into, specifically, the epoxy particles plate by regenerative epoxy resin particle, macromolecule resin, staple glass fibre, filler,
Modifying agent is constituted.
In the present embodiment, in epoxy particles plate, regenerative epoxy resin particle, macromolecule resin, staple glass fibre,
Filler, the mass fraction of modifying agent are respectively 60 parts, 50 parts, 20 parts, 10 parts, 5 parts.
The regenerative epoxy resin particle is by the epoxy resin blade cuts of wind-power electricity generation, is ground into bar, is then cut
Cut, be ground into the particle that particle diameter is 1～5mm；
The macromolecule resin is mass ratio 1:2 196 resins and 191 resins.
The staple glass fibre refers to the glass fibre of 0.5～3mm of fibre length.
The filler is Paris white.
The modifying agent is toughener.
The epoxy particles plate be by each raw material mix after, directly pour and make.
The preferred unsaturated polyester resin composite glass fiber plate of the glass layer, i.e. unsaturated polyester (UP) glass steel.
Further, in the present embodiment, glass layer is 191 resin compounded glass mats.
Further, the unsaturated polyester resin composite glass fiber plate includes 191 resins, staple glass fibre, filling
Agent, modifying agent, wherein, 191 resins, staple glass fibre, filler, the mass fraction of modifying agent be respectively 50 parts, 30 parts, 5 parts,
3 parts.The modifying agent is toughener, initiator, accelerator.The unsaturated polyester resin composite glass fiber plate is directly poured
It is obtained.
Embodiment 2
In one preferred embodiment, the body is made up of acrylic panel and interior lining panel, and the interior lining panel is cutd open
Face structure chart is described as shown in Fig. 2 include glass layer 1 and epoxy particles plate 2 and froth bed 3 successively from top to bottom
Froth bed 3 is polyurethane sound-absorbing foam, plays a part of sound-absorbing damping.
Embodiment 3
It is identical with the structure of the interior lining panel of the closestool body of embodiment 1, except that, the formula of epoxy particles plate
Difference, wherein, regenerative epoxy resin particle, macromolecule resin, staple glass fibre, filler, modifying agent mass fraction each
For 30 parts, 40 parts, 20 parts, 10 parts, 3 parts.The macromolecule resin is mass ratio 1:1 196 resins and 191 resins.Described 191
Resin can be obtained the particle that 191 resin leftover pieces are ground into 1～5mm of particle diameter using 191 resins of regeneration.
Embodiment 4
It is identical with the structure of the interior lining panel of the closestool body of embodiment 1, except that, the formula of glass layer is not
Together, wherein, glass layer is 191 resin compounded glass mats, fills a prescription as 191 resins, staple glass fibre, filler, changes
Good dose of mass fraction is respectively 70 parts, 20 parts, 10 parts, 3 parts.The modifying agent is toughener, initiator, accelerator.It is described
Unsaturated polyester resin composite glass fiber plate directly pours prepared.
Claims (10)
1. a kind of epoxy resin liner waterless closestool, an including body containing latrine pit, the bottom surface of latrine pit is provided with a turnover panel,
The turnover panel is connected by linkage with the pedal on body, and below the turnover panel storage bag is provided with, it is characterised in that
The body is made up of acrylic panel and interior lining panel, and under the acrylic panel, the interior lining panel is from upper for the interior lining panel
Arrive down and include successively glass layer and epoxy particles plate.
2. epoxy resin liner waterless closestool as claimed in claim 1, it is characterised in that the epoxy particles plate is for again
Raw epoxy resin composite glass fiber plate.
3. epoxy resin liner waterless closestool as claimed in claim 2, it is characterised in that the epoxy particles plate includes
Regenerative epoxy resin particle, macromolecule resin, staple glass fibre, filler, modifying agent；The regenerative epoxy resin particle be by
The epoxy resin blade cuts of wind-power electricity generation, it is ground into the particle that particle diameter is 1～5mm and obtains.
4. epoxy resin liner waterless closestool as claimed in claim 3, it is characterised in that in the epoxy particles plate, then
Raw epoxy particles, macromolecule resin, staple glass fibre, filler, the mass fraction of modifying agent be respectively 30～60 parts, 20
～50 parts, 10～40 parts, 5～20 parts, 1～10 part.
5. epoxy resin liner waterless closestool as claimed in claim 3, it is characterised in that the macromolecule resin is unsaturation
Polyester resin.
6. epoxy resin liner waterless closestool as claimed in claim 5, it is characterised in that the unsaturated polyester resin is 196
Resin and 191 resins, mass ratio is 1:0.5～3.
7. epoxy resin liner waterless closestool as claimed in claim 1, it is characterised in that the glass layer is unsaturation
Polyester resin composite glass fiber plate.
8. epoxy resin liner waterless closestool as claimed in claim 7, it is characterised in that the unsaturated polyester resin is combined
In glass mat, the unsaturated polyester resin is 196 resins and/or 191 resins.
9. epoxy resin liner waterless closestool as claimed in claim 7, it is characterised in that the unsaturated polyester resin is combined
Glass mat includes unsaturated polyester resin, staple glass fibre, filler, modifying agent, wherein, unsaturated polyester resin, glass
Glass chopped fiber, filler, the mass fraction of modifying agent are respectively 30～80 parts, 10～40 parts, 5～20 parts, 1～10 part.
10. epoxy resin liner waterless closestool as claimed in claim 1, it is characterised in that the body also includes bottom, institute
Bottom is stated under interior lining panel, the bottom is froth bed.