CN106584964A - Carbon fiber for computer shells - Google Patents
Carbon fiber for computer shells Download PDFInfo
- Publication number
- CN106584964A CN106584964A CN201611177424.0A CN201611177424A CN106584964A CN 106584964 A CN106584964 A CN 106584964A CN 201611177424 A CN201611177424 A CN 201611177424A CN 106584964 A CN106584964 A CN 106584964A
- Authority
- CN
- China
- Prior art keywords
- carbon fiber
- fibre material
- computer
- carbon fibre
- carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides carbon fiber for computer shells, which comprises a carbon fiber material body, waterproof layers are respectively arranged on the upper surface and lower surface of the carbon fiber material body, an insulating layer is arranged on the upper surface of the waterproof layer of the upper surface of the carbon fiber material body, a surface layer is arranged on the upper surface of the insulating layer, a bottom layer is arranged on the lower surface of the waterproof layer of the lower surface of the carbon fiber material body, and the carbon fiber material body is composed of a carbon fiber warp-knitted fabric and matrix resin. The computer shell material adopting the technical solution solves defects existing in the process of producing a computer body, such as low speed, high energy consumption and easy deformation and abrasion, has high shock resistance and oxidation resistance, prolongs the service lives of computers, and perfectly meets the requirement of computer production.
Description
Technical field
The invention belongs to technical field of polymer materials, specially a kind of carbon fiber for computer casing.
Background technology
Computer is that information produces developing inevitable outcome, and it is powerful to be widely used in every field, to promoting
The further development of society plays an important role, thus with powerful vitality, attracts widespread attention and welcome.
It is that the metal materials such as steel, ferrum, aluminium alloy are fabricated by adopt traditional computer body more, and adopts metal material system
Have that speed is slow, energy consumption is big during making computer body, yielding abrasion the shortcomings of, and the condition of molding of these materials answers
Miscellaneous, molding difficulty is big, because of the characteristic of metal material itself after molding so that the computer body shock resistance for having manufactured and non-oxidizability
It is not good.
The content of the invention
The problem to be solved in the present invention is to provide a kind of carbon fiber for computer casing, and it has high rigidity, HI high impact
Toughness solves the problems, such as that computer collides with and is easily damaged.
To solve above-mentioned technical problem, the technical solution used in the present invention is:A kind of carbon fiber for computer casing, bag
Include:Carbon fibre material body, the upper and lower surface of carbon fibre material body is respectively equipped with waterproof layer, carbon fibre material body upper surface
The upper surface of waterproof layer be provided with insulating barrier;The upper surface of insulating barrier is provided with top layer;The waterproof of carbon fibre material body lower surface
The lower surface of layer is provided with bottom.
Further limit, the carbon fiber warp-knitted cloth of the carbon fibre material body is three carbon fibers for axially weaving;It is described
The matrix resin of carbon fibre material body is epoxy resin, such design, reduce silk and silk produced by common braiding it
Between shearing abrasion;Carbon fiber inside is replaced to use steel wire to strengthen intensity with warp-knit mode, can be with lightening material weight.
Further limit, the waterproof layer that the upper and lower surface of the carbon fibre material body is respectively equipped with is by vinyon structure
Into.
Further limit, the insulating barrier is made up of Merlon, such design, it is fine by the carbon for covering Merlon
Dimension material enhances the toughness of carbon fibre material while insulating properties is improved.
Further limit, the bottom and top layer are made up of polyester material, such design, it is fine to carbon by polyester material
Surface carries out covering protection when further improving carbon fibre material performance and molding to insulating barrier.
Further limit, the carbon fibre material body is made up of carbon fiber warp-knitted cloth and matrix resin.
The invention has the beneficial effects as follows, the mistake for making computer body is solved using the computer body material of the technical program
Have that speed is slow, energy consumption is big in journey, yielding abrasion the shortcomings of, with stronger shock resistance and non-oxidizability, improve computer
Service life meet well computer production needs.
Specific embodiment
In order that those skilled in the art may be better understood the present invention, with reference to embodiment to the technology of the present invention
Scheme is further illustrated.
Embodiment 1
A kind of carbon fiber for computer casing, including:Carbon fibre material body, the upper and lower surface of carbon fibre material body
Waterproof layer is respectively equipped with, the upper surface of the waterproof layer of carbon fibre material body upper surface is provided with insulating barrier;The upper surface of insulating barrier
It is provided with top layer;The lower surface of the waterproof layer of carbon fibre material body lower surface is provided with bottom, and carbon fibre material body is by carbon fiber
Warp knitting cloth and matrix resin are constituted.
First with the cloth of soft material the dust and spot on computer body surface are dabbed off during making, then in clean electricity
Brain fuselage surface coats layer of plastic film, then, whole computer outer mold is preheated, then computer external mold after preheat
Uniform coating releasing agent, then lays the carbon fibre material structure of said structure on computer body, by what is laid on tool inner chamber
Computer body is placed in sealed environment and is warming up to 140 DEG C, then injects air inside toward confined space until air pressure is 10KG/ in bag
m3So that carbon fibre material is attached on computer body, heating is stopped after 2min and is taken out after cooling.
Wherein, it is 150g/m from surface density2, the prepreg that resin content is 38%, first prepreg is being coated with into modeling
Two-layer is laid on the computer body of material thin film, per layer includes laying I and laying II, and laying I is along computer body length ± 45 ° side
It is entwined to alternating, thickness is 0.2mm, laying II is that thickness is 0.1mm along 0 ° of direction looping of computer body length.
The carbon fiber warp-knitted cloth of carbon fibre material body is three carbon fibers for axially weaving, by the carbon fiber of different angles
Cloth is superimposed, and the matrix resin of carbon fibre material body is epoxy resin, and such design reduces the silk produced by common braiding
Shearing abrasion between silk;Carbon fiber inside is replaced to use steel wire to strengthen intensity with warp-knit mode, can be with lightening material
Weight.The waterproof layer that the upper and lower surface of carbon fibre material body is respectively equipped with is made up of vinyon.
Insulating barrier is made up of Merlon, such design, is improving exhausted by covering the carbon fibre material of Merlon
The toughness of carbon fibre material is enhanced while edge.
Bottom and top layer are made up of polyester material, such design, by polyester material carbon fibre surface is carried out covering into
Protection when one step raising carbon fibre material performance and molding to insulating barrier.
Embodiment 2
A kind of carbon fiber for computer casing, including:Carbon fibre material body, the upper and lower surface of carbon fibre material body
Waterproof layer is respectively equipped with, the upper surface of the waterproof layer of carbon fibre material body upper surface is provided with insulating barrier;The upper surface of insulating barrier
It is provided with top layer;The lower surface of the waterproof layer of carbon fibre material body lower surface is provided with bottom, and carbon fibre material body is by carbon fiber
Warp knitting cloth and matrix resin are constituted.
First with the cloth of soft material the dust and spot on computer body surface are dabbed off during making, then in clean electricity
Brain fuselage surface coats layer of plastic film, then, whole computer outer mold is preheated, then computer external mold after preheat
Uniform coating releasing agent, then lays the carbon fibre material structure of said structure on computer body, by what is laid on tool inner chamber
Computer body is placed in sealed environment and is warming up to 150 DEG C, then injects air inside toward confined space until air pressure is 12KG/ in bag
M3 so that carbon fibre material is attached on computer body, stops heating and takes out after cooling after 3min.
Wherein, it is 150g/m from surface density2, the prepreg that resin content is 40%, first prepreg is being coated with into modeling
3 layers are laid on the computer body of material thin film, per layer includes laying I and laying II, and laying I is along computer body length ± 45 ° side
It is entwined to alternating, thickness is 0.4mm, laying II is that thickness is 0.3mm along 0 ° of direction looping of computer body length.
The carbon fiber warp-knitted cloth of carbon fibre material body is three carbon fibers for axially weaving, by the carbon fiber of different angles
Cloth is superimposed, and the matrix resin of carbon fibre material body is epoxy resin, and such design reduces the silk produced by common braiding
Shearing abrasion between silk;Carbon fiber inside is replaced to use steel wire to strengthen intensity with warp-knit mode, can be with lightening material
Weight.
The waterproof layer that the upper and lower surface of carbon fibre material body is respectively equipped with is made up of vinyon.Insulating barrier is by poly- carbon
Acid esters is constituted, such design, and carbon fibre is enhanced while insulating properties is improved by covering the carbon fibre material of Merlon
The toughness of dimension material.
Bottom and top layer are made up of polyester material, such design, by polyester material carbon fibre surface is carried out covering into
Protection when one step raising carbon fibre material performance and molding to insulating barrier.
A kind of one embodiment of the carbon fiber for computer casing of the present invention has been described in detail above, but content
Only presently preferred embodiments of the present invention, it is impossible to be considered as the practical range for limiting the present invention.It is all according to the present patent application scope
The impartial change made and improvement etc., all should still belong within the patent covering scope of the present invention.
Claims (6)
1. a kind of carbon fiber for computer casing, including:Carbon fibre material body, the upper and lower table of the carbon fibre material body
Face is equipped with waterproof layer, and the upper surface of the waterproof layer of the carbon fibre material body upper surface is provided with insulating barrier;The insulating barrier
Upper surface be provided with top layer;The lower surface of the waterproof layer of the carbon fibre material body lower surface is provided with bottom.
2. a kind of carbon fiber for computer casing according to claim 1, it is characterised in that:The carbon fibre material sheet
The carbon fiber warp-knitted cloth of body is three carbon fibers for axially weaving, and the matrix resin of the carbon fibre material body is epoxy resin.
3. a kind of carbon fiber for computer casing according to claim 2, it is characterised in that:The carbon fibre material sheet
The waterproof layer that the upper and lower surface of body is respectively equipped with is made up of vinyon.
4. a kind of carbon fiber for computer casing according to claim 3, it is characterised in that:The insulating barrier is by poly- carbon
Acid esters is constituted.
5. a kind of carbon fiber for computer casing according to claim 4, it is characterised in that:The bottom and top layer by
Polyester material is constituted.
6. a kind of carbon fiber for computer casing according to claim 5, it is characterised in that:The carbon fibre material sheet
Body is made up of carbon fiber warp-knitted cloth and matrix resin.