CN106567247A - Preparation method of regenerated cellulose fabric capable of preventing protein pollution - Google Patents
Preparation method of regenerated cellulose fabric capable of preventing protein pollution Download PDFInfo
- Publication number
- CN106567247A CN106567247A CN201610932282.8A CN201610932282A CN106567247A CN 106567247 A CN106567247 A CN 106567247A CN 201610932282 A CN201610932282 A CN 201610932282A CN 106567247 A CN106567247 A CN 106567247A
- Authority
- CN
- China
- Prior art keywords
- regenerated cellulose
- protein
- fabric
- cellulose fabric
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a preparation method of a regenerated cellulose fabric capable of preventing the protein pollution. The preparation method comprises the following steps: (1) washing and grinding fresh ginger slices and carrots, adding grinded gingers and carrots into sodium chloride and deionized water, heating the solution until the solution is boiling, filtering the solution to obtain a plant extract, adding subtilisin, nano titanium dioxide, and polyethylene glycol into the plant extract, and fully stirring the mixture to obtain a finishing agent capable of preventing the protein pollution; (2) adding a regenerated cellulose fabric into an ethanol solution, washing the fabric under vibration, taking out the fabric, washing the fabric by water, drying the fabric, and finally activating the fabric to obtain a preprocessed regenerated cellulose fabric; and (3) dipping the activated regenerated cellulose fabric into an ethyl gallate solution, taking out the fabric, then dipping the fabric into the finishing agent capable of preventing the protein pollution, carrying out two dipping and padding, taking out the fabric, pre-drying the fabric, washing the fabric by an ethanol water solution, and drying the fabric to obtain the regenerated cellulose fabric capable of preventing the protein pollution.
Description
Technical field
The invention belongs to textile material technical field, and in particular to a kind of regenerated cellulose fabric of anti-protein-contamination
Preparation method.
Background technology
With the continuous development of modern technology, to functional requirement of textile also more and more higher.It is well known that
The excellent adsorption of textile, after contacting with the material such as spot, milk stain, oil stain, will be difficult to clean, therefore anti-protein-contamination
Textile is also operated and is formed.
A kind of potent anti-soil fibrous material disclosed in Chinese patent CN 104419998A, by castor oil ethylene oxide condensation
Thing and butyl titanate anti-protein-contamination agent are added in the raw material of polytetrafluoroethylene (PTFE) and nylon, and Jing melt spinnings prepare tool
There is the fibrous material of potent anti-soil effect.A kind of anti-protein-contamination leather disclosed in Chinese patent CN202047291U, by skin
Leather includes nano coating, conventional oil process layer, PVC surface layers, PVC foam layer and base fabric, and by nano material the anti-of leather is improved
Protein contamination ability.A kind of nano antifouling uvioresistant coated fabric disclosed in Chinese patent CN 1710179A, clothes and add
Work technique, by nano-titanium oxide, nano zine oxide, nano silicon oxide nanometer finishing agent is made, and is carried out arrangement to fabric and is refused
Water refuses the antifouling textile product or clothes of oil.
From above-mentioned prior art, the anti-protein-contamination arrangement currently for textile is for oil stain and dirt mostly
Stain, actually rare for the soil-release finish of protein milk stain class, milk stain falls within spot relatively conventional in daily life, milk stain
Belong to protein, its soil-release finish is different from oil stain and water stain, study a kind of fabric with anti-protein-contamination and also have one
Fixed market prospects.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of preparation side of the regenerated cellulose fabric of anti-protein-contamination
Method, the present invention combines subtilopeptidase A, nano titanium oxide and polyethylene glycol from the effective ingredients in plant of ginger splices and radish
Used as anti-protein-contamination finishing agent, the regenerated cellulose fabric to activating carries out anti-protein-contamination arrangement, obtains green ring
The anti-protein-contamination regenerated cellulose fabric of guarantor.
To solve above-mentioned technical problem, the technical scheme is that:
A kind of preparation method of the regenerated cellulose fabric of anti-protein-contamination, comprises the following steps:
(1) after fresh ginger splices and radish clean up, smash to pieces, in adding sodium chloride and deionized water, heating is boiled, mistake
Filter obtains plant extraction liquid, adds subtilopeptidase A, nano titanium oxide and polyethylene glycol, is sufficiently stirred for obtaining anti-egg
White matter pollutes finishing agent;
(2) regenerated cellulose fabric is placed in ethanol solution, oscillation cleaning, is taken out, washing drying, after activated process
Obtain the regenerated cellulose fabric for pre-processing;
(3) regenerated cellulose fabric of the activation for preparing step (2) first impregnated in progallin A solution, take
Go out, then impregnated in the anti-protein-contamination finishing agent of step (1) preparation, two leachings two are rolled, and are taken out, and preliminary drying uses ethanol water
Cleaning, drying, obtains the regenerated cellulose fabric of anti-protein-contamination.
Used as the preferred of above-mentioned technical proposal, in the step (1), the mass ratio of ginger splices, radish and sodium chloride is 1:1-2:
0.5-0.8。
Used as the preferred of above-mentioned technical proposal, in the step (1), the time that heating is boiled is 2-3h.
Used as the preferred of above-mentioned technical proposal, in the step (1), the mass fraction of active ingredient is in plant extraction liquid
5-12%.
As the preferred of above-mentioned technical proposal, in the step (1), plant extraction liquid, subtilopeptidase A, nanometer two
The liquor ratio of chatting of titanium oxide and polyethylene glycol is 50ml:0.3-0.5g:0.2-0.3g:2-5g.
Used as the preferred of above-mentioned technical proposal, in the step (2), the time of oscillation cleaning is 24h.
Used as the preferred of above-mentioned technical proposal, in the step (2), activation process is corona treatment and alkali process.
Used as the preferred of above-mentioned technical proposal, in the step (3), the mass fraction of progallin A solution is 1-
2%.
Used as the preferred of above-mentioned technical proposal, in the step (3), the bath raio of dipping is 1:50-80.
Used as the preferred of above-mentioned technical proposal, in the step (3), the temperature rolled of two leaching two are 80-100 DEG C, and the time is
60-90min, pick-up is 85-90%.
Compared with prior art, the invention has the advantages that:
(1) anti-protein-contamination regenerated cellulose fabric prepared by the present invention adopts regenerated cellulose fabric as substrate,
Regenerated cellulose fabric green is capable of circulation, transparent glossy, and mechanical strength and elongation are good, by regenerated cellulose fabric
After carrying out oxygenation pretreatment and plasma-activated arrangement, substantial amounts of hydroxyl and micropore knot are contained in the surface of regenerated cellulose fabric
Structure, Jing gallic acids suppress under the protection of antioxidant, can be with the effective ingredients in plant of ginger splices and radish, bacillus subtilis protein
Chemical bond and hydrogen bond are formed between enzyme, nano titanium oxide and polyethylene glycol, the work(of regenerated cellulose anti-protein-contamination is given
Can property.
(2) ginger splices is contained on anti-protein-contamination regenerated cellulose fabric surface prepared by the present invention and the plant of radish is effective
The effective ingredients in plant of composition, subtilopeptidase A, nano titanium oxide and polyethylene glycol, ginger splices and radish and hay bacillus
Protease, sodium chloride effect can decompose to protein materials such as milk stain, blood, and nano titanium oxide is understood in cellulose
Surface form the absorption that film suppresses the spot such as protein, polyethylene glycol has unique effectively anti-protein adsorption capacity,
Additionally, this several raw material is all nontoxic without protein contamination, environmental protection is good with the compatibility of skin, by this several coating substance
The performance of fabric anti-protein-contamination is given with the surface of anti-protein-contamination regenerated cellulose fabric.
(3) anti-protein-contamination regenerated cellulose fabric preparation technology prepared by the present invention is easy, low cost, efficiency high,
Fabric has good anti-protein-contamination performance, and environmental protection can be used for industrial production, good in economic efficiency, can be used for
The fields such as weaving, medical treatment, packaging for foodstuff.
Specific embodiment
Describe the present invention, the illustrative examples of the here present invention and explanation in detail below in conjunction with specific embodiment
It is for explaining the present invention but not as a limitation of the invention.
Embodiment 1:
(1) after the fresh ginger splices of 1g and the radish of 1g clean up, smash to pieces, add the sodium chloride of 0.5g and going for 50ml
In ionized water, 2h is boiled in heating, is filtrated to get the plant extraction liquid that mass fraction is 5%, adds 0.3g bacillus subtilis proteins
Enzyme, 0.2g nano titanium oxides and 2g polyethylene glycol, are sufficiently stirred for obtaining anti-protein-contamination finishing agent.
(2) regenerated cellulose fabric is placed in ethanol solution, oscillation cleaning 24h, is taken out, washing drying first impregnated in
Alkali process 5min in the sodium hydroxide solution of 5g/l, take out, after washing drying, then the corona treatment under 150W power
5min, obtains the regenerated cellulose fabric for pre-processing.
(3) regenerated cellulose fabric of the activation for preparing step (2), with bath raio 1:50, first impregnated in mass fraction is
5min in 1% progallin A solution, takes out, then impregnated in the anti-protein-contamination finishing agent of step (1) preparation, two
Leaching two is rolled, and temperature is 80 DEG C, and the time is 60min, and pick-up is 85%, is taken out, and 110 DEG C of preliminary drying 15min are clear with ethanol water
Wash, dry at 60 DEG C, obtain the regenerated cellulose fabric of anti-protein-contamination.
Embodiment 2:
(1) after the fresh ginger splices of 1g and the radish of 2g clean up, smash to pieces, add the sodium chloride of 0.8g and going for 50ml
In ionized water, 3h is boiled in heating, is filtrated to get the plant extraction liquid that mass fraction is 12%, adds 0.5g bacillus subtilis proteins
Enzyme, 0.3g nano titanium oxides and 5g polyethylene glycol, are sufficiently stirred for obtaining anti-protein-contamination finishing agent.
(2) regenerated cellulose fabric is placed in ethanol solution, oscillation cleaning 24h, is taken out, washing drying first impregnated in
Alkali process 20min in the sodium hydroxide solution of 15g/l, take out, after washing drying, then the corona treatment under 200W power
10min, obtains the regenerated cellulose fabric for pre-processing.
(3) regenerated cellulose fabric of the activation for preparing step (2), with bath raio 1:80, first impregnated in mass fraction is
10min in 2% progallin A solution, takes out, then impregnated in the anti-protein-contamination finishing agent of step (1) preparation,
Two leachings two are rolled, and temperature is 100 DEG C, and the time is 90min, and pick-up is 90%, are taken out, and 110 DEG C of preliminary drying 20min are water-soluble with ethanol
Liquid is cleaned, and is dried at 80 DEG C, obtains the regenerated cellulose fabric of anti-protein-contamination.
Embodiment 3:
(1) after the fresh ginger splices of 1g and the radish of 1.5g clean up, smash to pieces, add the sodium chloride and 50ml of 0.6g
In deionized water, 2.5h is boiled in heating, is filtrated to get the plant extraction liquid that mass fraction is 8%, adds 0.4g hay bacilluses
Protease, 0.25g nano titanium oxides and 3g polyethylene glycol, are sufficiently stirred for obtaining anti-protein-contamination finishing agent.
(2) regenerated cellulose fabric is placed in ethanol solution, oscillation cleaning 24h, is taken out, washing drying first impregnated in
Alkali process 15min in the sodium hydroxide solution of 10g/l, take out, after washing drying, then the corona treatment under 180W power
7min, obtains the regenerated cellulose fabric for pre-processing.
(3) regenerated cellulose fabric of the activation for preparing step (2), with bath raio 1:60, first impregnated in mass fraction is
7min in 1.5% progallin A solution, takes out, then impregnated in the anti-protein-contamination finishing agent of step (1) preparation,
Two leachings two are rolled, and temperature is 90 DEG C, and the time is 70min, and pick-up is 88%, are taken out, and 110 DEG C of preliminary drying 18min use ethanol water
Cleaning, dries at 70 DEG C, obtains the regenerated cellulose fabric of anti-protein-contamination.
Embodiment 4:
(1) after the fresh ginger splices of 1g and the radish of 1.6g clean up, smash to pieces, add the sodium chloride and 50ml of 0.7g
In deionized water, 2.4h is boiled in heating, is filtrated to get the plant extraction liquid that mass fraction is 8%, adds 0.3g hay bacilluses
Protease, 0.2g nano titanium oxides and 4g polyethylene glycol, are sufficiently stirred for obtaining anti-protein-contamination finishing agent.
(2) regenerated cellulose fabric is placed in ethanol solution, oscillation cleaning 24h, is taken out, washing drying first impregnated in
Alkali process 15min in the sodium hydroxide solution of 12g/l, take out, after washing drying, then the corona treatment under 200W power
5min, obtains the regenerated cellulose fabric for pre-processing.
(3) regenerated cellulose fabric of the activation for preparing step (2), with bath raio 1:70, first impregnated in mass fraction is
5min in 2% progallin A solution, takes out, then impregnated in the anti-protein-contamination finishing agent of step (1) preparation, two
Leaching two is rolled, and temperature is 95 DEG C, and the time is 70min, and pick-up is 85%, is taken out, and 110 DEG C of preliminary drying 20min are clear with ethanol water
Wash, dry at 60 DEG C, obtain the regenerated cellulose fabric of anti-protein-contamination.
Embodiment 5:
(1) after the fresh ginger splices of 1g and the radish of 2g clean up, smash to pieces, add the sodium chloride of 0.5g and going for 50ml
In ionized water, 3h is boiled in heating, is filtrated to get the plant extraction liquid that mass fraction is 10%, adds 0.5g bacillus subtilis proteins
Enzyme, 0.2g nano titanium oxides and 5g polyethylene glycol, are sufficiently stirred for obtaining anti-protein-contamination finishing agent.
(2) regenerated cellulose fabric is placed in ethanol solution, oscillation cleaning 24h, is taken out, washing drying first impregnated in
Alkali process 20min in the sodium hydroxide solution of 5g/l, take out, after washing drying, then the corona treatment under 150W power
10min, obtains the regenerated cellulose fabric for pre-processing.
(3) regenerated cellulose fabric of the activation for preparing step (2), with bath raio 1:80, first impregnated in mass fraction is
5min in 2% progallin A solution, takes out, then impregnated in the anti-protein-contamination finishing agent of step (1) preparation, two
Leaching two is rolled, and temperature is 100 DEG C, and the time is 60min, and pick-up is 90%, is taken out, and 110 DEG C of preliminary drying 15min use ethanol water
Cleaning, dries at 80 DEG C, obtains the regenerated cellulose fabric of anti-protein-contamination.
Embodiment 6:
(1) after the fresh ginger splices of 1g and the radish of 2g clean up, smash to pieces, add the sodium chloride of 0.7g and going for 50ml
In ionized water, 3h is boiled in heating, is filtrated to get the plant extraction liquid that mass fraction is 10%, adds 0.5g bacillus subtilis proteins
Enzyme, 0.2g nano titanium oxides and 5g polyethylene glycol, are sufficiently stirred for obtaining anti-protein-contamination finishing agent.
(2) regenerated cellulose fabric is placed in ethanol solution, oscillation cleaning 24h, is taken out, washing drying first impregnated in
Alkali process 10min in the sodium hydroxide solution of 12g/l, take out, after washing drying, then the corona treatment under 200W power
10min, obtains the regenerated cellulose fabric for pre-processing.
(3) regenerated cellulose fabric of the activation for preparing step (2), with bath raio 1:60, first impregnated in mass fraction is
8min in 1% progallin A solution, takes out, then impregnated in the anti-protein-contamination finishing agent of step (1) preparation, two
Leaching two is rolled, and temperature is 100 DEG C, and the time is 80min, and pick-up is 90%, is taken out, and 110 DEG C of preliminary drying 15min use ethanol water
Cleaning, dries at 80 DEG C, obtains the regenerated cellulose fabric of anti-protein-contamination.
After testing, embodiment 1-6 prepare anti-protein-contamination regenerated cellulose fabric mechanical performance and anti-protein,
The result of the performance of spot is as follows:
As seen from the above table, the mechanical strength of the regenerated cellulose fabric of anti-protein-contamination prepared by the present invention is good, thoroughly
Gas is good, has more good rejection to sludge and protein.
The principle and its effect of above-described embodiment only illustrative present invention, it is of the invention not for limiting.It is any ripe
Know the personage of this technology all can carry out modifications and changes under the spirit and the scope without prejudice to the present invention to above-described embodiment.Cause
This, such as those of ordinary skill in the art is complete with institute under technological thought without departing from disclosed spirit
Into all equivalent modifications or change, should by the present invention claim be covered.
Claims (10)
1. a kind of preparation method of the regenerated cellulose fabric of anti-protein-contamination, it is characterised in that comprise the following steps:
(1) after fresh ginger splices and radish clean up, smash to pieces, in adding sodium chloride and deionized water, heating is boiled, and is filtered
To plant extraction liquid, subtilopeptidase A, nano titanium oxide and polyethylene glycol are added, be sufficiently stirred for obtaining anti-protein
Pollution finishing agent;
(2) regenerated cellulose fabric is placed in ethanol solution, oscillation cleaning, is taken out, washing drying is obtained after activated process
The regenerated cellulose fabric of pretreatment;
(3) regenerated cellulose fabric of the activation for preparing step (2) first impregnated in progallin A solution, take out, then
In impregnated in the anti-protein-contamination finishing agent of step (1) preparation, two leachings two are rolled, and are taken out, and preliminary drying is cleaned with ethanol water,
Drying, obtains the regenerated cellulose fabric of anti-protein-contamination.
2. a kind of preparation method of the regenerated cellulose fabric of anti-protein-contamination according to claim 1, its feature exists
In:In the step (1), the mass ratio of ginger splices, radish and sodium chloride is 1:1-2:0.5-0.8.
3. a kind of preparation method of the regenerated cellulose fabric of anti-protein-contamination according to claim 1, its feature exists
In:In the step (1), the time that heating is boiled is 2-3h.
4. a kind of preparation method of the regenerated cellulose fabric of anti-protein-contamination according to claim 1, its feature exists
In:In the step (1), the mass fraction of active ingredient is 5-12% in plant extraction liquid.
5. a kind of preparation method of the regenerated cellulose fabric of anti-protein-contamination according to claim 1, its feature exists
In:In the step (1), the liquor ratio of chatting of plant extraction liquid, subtilopeptidase A, nano titanium oxide and polyethylene glycol is
50ml:0.3-0.5g:0.2-0.3g:2-5g.
6. a kind of preparation method of the regenerated cellulose fabric of anti-protein-contamination according to claim 1, its feature exists
In:In the step (2), the time of oscillation cleaning is 24h.
7. a kind of preparation method of the regenerated cellulose fabric of anti-protein-contamination according to claim 1, its feature exists
In:In the step (2), activation process is corona treatment and alkali process.
8. a kind of preparation method of the regenerated cellulose fabric of anti-protein-contamination according to claim 1, its feature exists
In:In the step (3), the mass fraction of progallin A solution is 1-2%.
9. a kind of preparation method of the regenerated cellulose fabric of anti-protein-contamination according to claim 1, its feature exists
In:In the step (3), the bath raio of dipping is 1:50-80.
10. a kind of preparation method of the regenerated cellulose fabric of anti-protein-contamination according to claim 1, its feature exists
In:In the step (3), the temperature that two leachings two are rolled is 80-100 DEG C, and the time is 60-90min, and pick-up is 85-90%.