CN106566637A - Aluminum alloy waterborne emulsion release agent - Google Patents
Aluminum alloy waterborne emulsion release agent Download PDFInfo
- Publication number
- CN106566637A CN106566637A CN201610944852.5A CN201610944852A CN106566637A CN 106566637 A CN106566637 A CN 106566637A CN 201610944852 A CN201610944852 A CN 201610944852A CN 106566637 A CN106566637 A CN 106566637A
- Authority
- CN
- China
- Prior art keywords
- parts
- aluminum alloy
- defoamer
- rotating speed
- aluminium alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses an aluminum alloy waterborne emulsion release agent. The aluminum alloy waterborne emulsion release agent is composed of the following raw materials including, by mass, 60-100 parts of oxidization modification polyethylene wax, 1-15 parts of paraffin, 1-10 parts of stearic acid, 3-15 parts of lauryl sodium sulfate, 1-8 parts of castor oil polyoxyethylene ether, 1-5 parts of fatty acid polyoxyethylene ester, 0.1-5 parts of a rust protection corrosion inhibitor, 0.1-3 parts of an antibacterial agent, 0.1-1 part of a defoamer and 500-600 parts of deionized water. The aluminum alloy waterborne emulsion release agent has the beneficial effects of being good in stability, easily forming a film, and being free of mold gluing, less in mold residue, smooth in surface, good in release effect, resistant to high temperature, safe in use, free of pollution and the like.
Description
Technical field
The present invention relates to technical field of coatings, and in particular to a kind of aluminium alloy water-base emulsion releasing agent.
Background technology
Aluminium alloy is a kind of aluminum alloy materials, and its density is little, intensity is big, plasticity is good, is widely used in war industry, the people
With numerous areas such as industry, building industry.Aluminum alloy materials, for smooth membrane, need after heating fusing, high pressure injection film
Spraying releasing agent in mold cavity.Mainly there are oil-based release agent, water based mold release agent and split releasing agent at present.Oil-based release agent is looked for be made
Over-emitting black exhaust, pollution of ecological environment with during, and easily pollute aluminum alloy surface.Powder releasing agent in use, effectively
Uneven components, aluminum alloy surface unsightly, high cost, using less.And water based mold release agent has good cooling results, does not produce
Pile up, surface quality of continuous castings it is good, contribute to reduce internal porosity rate and using it is safe and pollution-free the advantages of.Thus it is water base de-
Mould agent is more suitable for the demoulding demand of aluminium alloy.
The content of the invention
It is an object of the present invention to be directed to prior art, there is provided a kind of aluminium alloy water-base emulsion releasing agent.
For achieving the above object, the present invention takes technical scheme below:A kind of aluminium alloy water-base emulsion releasing agent, it is by matter
The following raw material composition of amount part:60~100 parts of oxidation modification Tissuemat E, 1~15 part of paraffin, 1~10 part of stearic acid, dodecane
3~15 parts of base sodium sulphate, 1~8 part of castor oil polyoxyethylene ether, 1~5 part of polyoxyethylene carboxylate, rust inhibitor 0.1~
5 parts, 0.1~1 part of defoamer, 500~600 parts of deionized water.
Wherein, described rust inhibitor is triethanolamine oleate, diethanol amine, MEA, hexamethylenetetramine
One or more.
Wherein, described defoamer is polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether, dimethyl silicone polymer
In one or more.
Further, a kind of preparation method of described aluminium alloy water-base emulsion releasing agent is comprised the following steps:By quality
The rotating speed that part weighs oxidation modification Tissuemat E and paraffin is placed in stirring container with rotating speed as 400R/min is added in heating
Emulsifying agent, after waiting material to be completely melt, adds stearic acid, lauryl sodium sulfate, castor oil polyoxyethylene ether, fatty acid polyglycol
Oxygen vinyl acetate, rust inhibitor, defoamer and temperature are 90~99 DEG C, and pH value is 7.5~8.5 deionized water, is with rotating speed
The rotating speed constant temperature of 600R/min stirs temperature is cooled to after 40~60min to be 60 DEG C and takes out from stirring container and obtain final product the present invention's
Aluminum alloy mould release agent.
In the present invention, oxidation modification Tissuemat E fusing point is high, and with higher viscosity and moulding property, it contains and is easy to emulsification
- OH bases ,-COOH bases ,-O- base isopolarity groups, thus oxidation modification Tissuemat E is a kind of excellent filmogen.
In the present invention, paraffin melting point is low, has good compatibility with high molecular polymer, and it can change in the present invention
The mobility of kind material, present invention auxiliary addition paraffin contributes to forming uniform film.
The present invention is compound with stearic acid, lauryl sodium sulfate, castor oil polyoxyethylene ether, polyoxyethylene carboxylate
Emulsifying agent, can make oxidation modification Tissuemat E and paraffin form oil-in-water type that is uniform, stable, being difficult to be layered, emulsion is fine and smooth micro-
Emulsion.
The invention has the beneficial effects as follows:A kind of aluminium alloy water-base emulsion releasing agent of the present invention has good stability, Yi Cheng
Film, not sticking to mould, mould residue is few, surface is smooth, stripping result good, high temperature resistant, using safe and pollution-free and other effects.
Specific embodiment
With reference to specific embodiment, to further instruction of the present invention.
Embodiment 1
A kind of aluminium alloy water-base emulsion releasing agent is made up of the following raw material of mass parts:100 parts of oxidation modification Tissuemat E,
1 part of paraffin, 10 parts of stearic acid, 3 parts of lauryl sodium sulfate, 8 parts of castor oil polyoxyethylene ether, 1 part of polyoxyethylene carboxylate,
5 parts of rust inhibitor, 1 part of defoamer, 600 parts of deionized water;Wherein, rust inhibitor be triethanolamine oleate, diethanol amine,
MEA, hexamethylenetetramine;Defoamer is polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether, poly dimethyl silicon
Oxygen alkane.
Its preparation method is comprised the following steps:Oxidation modification Tissuemat E is weighed by mass parts and paraffin is placed in stirring container
In rotating speed with rotating speed as 400R/min add emulsifying agent in heating, after waiting material to be completely melt, add stearic acid, 12
Sodium alkyl sulfate, castor oil polyoxyethylene ether, polyoxyethylene carboxylate, rust inhibitor, defoamer and temperature are 99 DEG C, PH
It is worth the deionized water for 7.5, temperature is cooled to for 60 DEG C from stirring after the rotating speed constant temperature stirring 60min with rotating speed as 600R/min
The aluminum alloy mould release agent for obtaining final product the present invention is taken out in container.
Embodiment 2
A kind of aluminium alloy water-base emulsion releasing agent is made up of the following raw material of mass parts:60 parts of oxidation modification Tissuemat E,
15 parts of paraffin, 1 part of stearic acid, 15 parts of lauryl sodium sulfate, 1 part of castor oil polyoxyethylene ether, polyoxyethylene carboxylate 5
Part, 0.1 part of rust inhibitor, 0.1 part of defoamer, 500 parts of deionized water;Wherein, rust inhibitor be triethanolamine oleate and
Diethanol amine;Defoamer is polyoxyethylene polyoxy propyl alcohol amidogen ether and polypropylene glycerol aether.
Its preparation method is comprised the following steps:Oxidation modification Tissuemat E is weighed by mass parts and paraffin is placed in stirring container
In rotating speed with rotating speed as 400R/min add emulsifying agent in heating, after waiting material to be completely melt, add stearic acid, 12
Sodium alkyl sulfate, castor oil polyoxyethylene ether, polyoxyethylene carboxylate, rust inhibitor, defoamer and temperature are 99 DEG C, PH
It is worth the deionized water for 8.5, temperature is cooled to for 60 DEG C from stirring after the rotating speed constant temperature stirring 40min with rotating speed as 600R/min
The aluminum alloy mould release agent for obtaining final product the present invention is taken out in container.
Embodiment 3
A kind of aluminium alloy water-base emulsion releasing agent is made up of the following raw material of mass parts:90 parts of oxidation modification Tissuemat E,
12 parts of paraffin, 5 parts of stearic acid, 7 parts of lauryl sodium sulfate, 3 parts of castor oil polyoxyethylene ether, 4 parts of polyoxyethylene carboxylate,
1 part of rust inhibitor, 1 part of defoamer, 550 parts of deionized water;Wherein, rust inhibitor is diethanol amine and MEA and six
Methine tetramine;Defoamer is polypropylene glycerol aether and dimethyl silicone polymer.
Its preparation side is with embodiment 1.
Embodiment 4
A kind of aluminium alloy water-base emulsion releasing agent is made up of the following raw material of mass parts:90 parts of oxidation modification Tissuemat E,
10 parts of paraffin, 8 parts of stearic acid, 5 parts of lauryl sodium sulfate, 3 parts of castor oil polyoxyethylene ether, 2 parts of polyoxyethylene carboxylate,
2 parts of rust inhibitor, 0.5 part of defoamer, 520 parts of deionized water;Wherein, rust inhibitor is MEA;Defoamer is poly-
Dimethyl siloxane.
Its preparation method is with embodiment 2.
Embodiment 5
A kind of aluminium alloy water-base emulsion releasing agent is made up of the following raw material of mass parts:70 parts of oxidation modification Tissuemat E,
11 parts of paraffin, 7 parts of stearic acid, 7 parts of lauryl sodium sulfate, 7 parts of castor oil polyoxyethylene ether, 2 parts of polyoxyethylene carboxylate,
4 parts of rust inhibitor, 0.8 part of defoamer, 580 parts of deionized water;Wherein, rust inhibitor is triethanolamine oleate;Defoamer
For polyoxyethylene polyoxy propyl alcohol amidogen ether.
Its preparation method is with embodiment 2.
Claims (4)
1. a kind of aluminium alloy water-base emulsion releasing agent, it is characterised in that it is made up of the following raw material of mass parts:Oxidation modification gathers
60~100 parts of ethylene waxes, 1~15 part of paraffin, 1~10 part of stearic acid, 3~15 parts of lauryl sodium sulfate, castor oil polyoxy second
1~8 part of alkene ether, 1~5 part of polyoxyethylene carboxylate, 0.1~5 part of rust inhibitor, 0.1~1 part of defoamer, deionized water
500~600 parts.
2. a kind of aluminium alloy water-base emulsion releasing agent according to claim 1, it is characterised in that described rust inhibitor
One or more for triethanolamine oleate, diethanol amine, MEA, hexamethylenetetramine.
3. a kind of aluminium alloy water-base emulsion releasing agent according to claim 1, it is characterised in that described defoamer is poly-
One or more in oxygen ethene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether, dimethyl silicone polymer.
4. according to a kind of preparation method of the arbitrary described aluminium alloy water-base emulsion releasing agent of claim 1-3, it is characterised in that
Comprise the following steps:Oxidation modification Tissuemat E is weighed by mass parts and paraffin is placed in stirring container with rotating speed as 400R/min
Rotating speed while heating while add emulsifying agent, after waiting material to be completely melt, add stearic acid, lauryl sodium sulfate, castor oil
APEO, polyoxyethylene carboxylate, rust inhibitor, defoamer and temperature are 90~99 DEG C, and pH value is 7.5~8.5
Deionized water, rotating speed constant temperature with rotating speed as 600R/min stirs and temperature is cooled to after 40~60min holds from stirring for 60 DEG C
The aluminum alloy mould release agent for obtaining final product the present invention is taken out in device.