CN106566598B - Universal non-ferrous metal and stainless-steel cold-rolling oil compound additive and preparation method thereof - Google Patents
Universal non-ferrous metal and stainless-steel cold-rolling oil compound additive and preparation method thereof Download PDFInfo
- Publication number
- CN106566598B CN106566598B CN201610986121.7A CN201610986121A CN106566598B CN 106566598 B CN106566598 B CN 106566598B CN 201610986121 A CN201610986121 A CN 201610986121A CN 106566598 B CN106566598 B CN 106566598B
- Authority
- CN
- China
- Prior art keywords
- additive
- butyl
- stainless
- compound additive
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of universal non-ferrous metal and stainless-steel cold-rolling oil compound additive and preparation method thereof, belong to field of lubricant.The present invention selects lauryl alcohol, butyl stearate, pentaerythritol oleate and lauric acid as oiliness improver, 2,6-di-tert-butyl p-cresol is as antioxidant, and benzotriazole and thiadiazoles derivative are as metal deactivator, dialkyl dithiophosphate is as antiwear additive, and hydrogenated base oil is as solvent.The present invention use with alcohol -ester type oiliness improver it is compound based on, be aided with a small amount of acid type oiliness improver;A small amount of dialkyl dithiophosphate, with reinforcement oil film, improves stocking surface quality as antiwear additive;A small amount of antioxidant and metal deactivator improve the service life of ROLLING OIL, and number can be recycled in increase, and prevents rolled piece from being corroded.The present invention is easy to use, and at low cost, dosage is few, has film strength high, antiwear and antifriction effect is good, and inoxidizability is strong, the excellent feature of Annealing Property.
Description
Technical field
The present invention relates to lubricants and metal plate and belt foil cold rolling field, the lubrication belonged in process of metal working specifically to relate to
And a kind of universal cold-rolled lubricating oil compound additive and preparation method thereof.
Background technique
During non-ferrous metal stocking (such as aluminium sheet, band, foil, copper foil) and stainless-steel cold-rolling, to guarantee the operation of rolling
Go on smoothly, and obtain the regular stocking of excellent surface quality, plate shape, it is necessary to use Lubrication Technology.
ROLLING OIL is made of base oil and additive, and the base oil of Modern New is mainly the mineral by hydrofinishing
Oil, ingredient are mainly the different alkane of carbon chain lengths and cycloalkanes hydrocarbon mixture;Additive can improve the specificity of oil product
Matter improves the greasy property of mineral oil.Generally require to add in ROLLING OIL a certain amount of oiliness improver, antiwear additive, antioxidant etc. with
Achieve the effect that improve lubrication.The additive of single type can not play comprehensive effect, in actual production often using multiple
Additive is closed, film strength is improved to reach, reduces abrasion loss, improves ROLLING OIL service life and other effects.
In technical field of lubricant, additive types are various, and various formula types mix in industrialized production, to using
Person causes inconvenience.Therefore it needs to study a kind of universal compound additive, for the processing of different metal, it is suitable to select
Compound additive dosage improves the convenience used and can reach excellent resultant effect.
Summary of the invention
The object of the present invention is to provide a kind of universal non-ferrous metals and stainless-steel cold-rolling oil compound additive, the present invention to make
With conveniently, at low cost, dosage is few, can reach use by the dosage of change compound additive for different metal stocking and wants
It asks.According to experimental results, the present invention has film strength high, and antiwear and antifriction effect is good, and inoxidizability is strong, and Annealing Property is excellent
Good feature.
The technical scheme is that: select lauryl alcohol, butyl stearate, pentaerythritol oleate and
Lauric acid is as oiliness improver, and 2,6-di-tert-butyl p-cresol is as antioxidant, benzotriazole and thiadiazoles derivative as gold
Belong to passivator, dialkyl dithiophosphate is as antiwear additive, and hydrogenated base oil is as solvent naphtha.
The specific ingredient of compound additive by mass percentage, in oiliness improver, lauryl alcohol: 28~42%;
Butyl stearate and pentaerythritol oleate mixed ester: 28~42%:
Lauric acid: 2~5%;
Antioxidant is 2,6-di-tert-butyl p-cresol: 0.5~1%;
In metal deactivator, benzotriazole: 0.3~0.9%;
Thiadiazoles derivative: 0.3~0.9%;
Antiwear additive is dialkyl dithiophosphate: 0.5~2%;
Solvent naphtha is hydrogenated base oil: surplus.
In specific ingredient, mixed ester that oiliness improver lauryl alcohol and butyl stearate and pentaerythritol oleate are constituted is answered
It is 2:3~3:2 with mass ratio range, the two gross mass is overall 70% of compound additive;Butyl stearate in mixed ester
With the compounding mass ratio range of pentaerythritol oleate are as follows: 2:3~3:2, metal deactivator benzotriazole and thiadiazoles spread out
The compounding mass ratio range of biology is 1:3~3:1.
The preparation step of above-mentioned universal non-ferrous metal and stainless-steel cold-rolling oil compound additive are as follows:
The butyl stearate of above-mentioned formula ratio and pentaerythritol oleate are first added to reaction vessel according to corresponding ratio
In, then sequentially add lauryl alcohol, lauric acid, 2,6-di-tert-butyl p-cresol, benzotriazole, thiadiazoles derivative, dioxane
Base phosphorodithioate, is eventually adding hydrogenated base oil.Reaction vessel is placed on thermostatic electromagnetic blender and is heated while stirring
To 60~70 DEG C, mixing speed is 100~180r/min, and constant temperature mixing time is 10~20 minutes until the mixing of each additive is equal
It is even, it then cools to room temperature to get a kind of universal non-ferrous metal and stainless-steel cold-rolling oil compound additive is arrived.
The advantage of the invention is that the comprehensive consideration film strength of ROLLING OIL, antiwear and friction reduction property, inoxidizability and moving back
Fiery detergency.By optimizing oiliness improver in the absorption array of metal surface, being optimal effect, monoesters to the compound of oiliness improver
The butyl stearate of type has excellent annealing cleanness and extreme pressure property is slightly worse, and the pentaerythritol oleate of polyalcohol ester type
It can show preferably to lubricate and extreme pressure property, the functionality of the two are complementary to one another;By add a small amount of annealing cleanness compared with
Good antiwear additive improves the antiwear and antifriction effect of ROLLING OIL, while the control of its content is having no significant effect annealing cleanness
In range;The service life that oil product is improved by addition antioxidant, reduces costs;Inhibit gold by addition metal deactivator
Belong to the catalytic action of ion pair ROLLING OIL oxidation, and prevent corrosion of metal, improves the surface quality of rolled piece.
The present invention carries out assessment of performance using following experimental method in the lab:
◆ lubricant extreme pressure property measuring method (four ball method) (GB/T 12583)
◆ lubrication oil antiwear damages performance measurement method (four ball method) (SH/T 0189)
◆ the measurement (rotary bomb oxidation test) (SH/T 0193) of lubricating oil oxidation stability
◆ EXXON standard anneal box method
◆ oil product copper corrosion experimental method (GB/T 5096)
Specific embodiment
Embodiment 1
The formula of embodiment 1 is shown in Table 1 (based on gross mass 100g):
Table 1
Serial number | Ingredient names | Quality (g) |
1 | Lauryl alcohol | 28.0 |
2 | Butyl stearate | 16.8 |
3 | Pentaerythritol oleate | 25.2 |
4 | Lauric acid | 2.0 |
5 | 2,6-di-tert-butyl p-cresol | 0.5 |
6 | Benzotriazole | 0.3 |
7 | Thiadiazoles derivative | 0.9 |
8 | Dialkyl dithiophosphate | 0.5 |
9 | Hydrogenated base oil | 25.8 |
By each component quality formula of upper table, universal non-ferrous metal and stainless-steel cold-rolling oil compound additive are prepared.It will
Lauryl alcohol (28.0g), butyl stearate (16.8g), pentaerythritol oleate (25.2g), lauric acid (2.0g), the tertiary fourth of 2,6- bis-
Base paracresol (0.5g), benzotriazole (0.3g), thiadiazoles derivative (0.9g), dialkyl dithiophosphate (0.5g) and
Hydrogenated base oil (25.8g) after specifying sequence that container is added in by specification, is placed on thermostatic electromagnetic blender top heating side and stirs
It mixes to 60~70 DEG C, constant temperature mixing time is 10~20 minutes, and mixing speed is 100~180r/min, until each additive is mixed
It closes uniformly, obtains uniform oil body, then cool to room temperature.
Embodiment 2
The formula of embodiment 2 is shown in Table 2 (based on gross mass 100g):
Table 2
Serial number | Ingredient names | Quality (g) |
1 | Lauryl alcohol | 35.0 |
2 | Butyl stearate | 17.5 |
3 | Pentaerythritol oleate | 17.5 |
4 | Lauric acid | 3.0 |
5 | 2,6-di-tert-butyl p-cresol | 0.7 |
6 | Benzotriazole | 0.5 |
7 | Thiadiazoles derivative | 0.5 |
8 | Dialkyl dithiophosphate | 1.0 |
9 | Hydrogenated base oil | 24.3 |
By each component quality formula of upper table, universal non-ferrous metal and stainless-steel cold-rolling oil compound additive are prepared.It will
Lauryl alcohol (35.0g), butyl stearate (17.5g), pentaerythritol oleate (17.5g), lauric acid (3.0g), the tertiary fourth of 2,6- bis-
Base paracresol (0.7g), benzotriazole (0.5g), thiadiazoles derivative (0.5g), dialkyl dithiophosphate (1.0g) and
Hydrogenated base oil (24.3g) after specifying sequence that container is added in by specification, is placed on thermostatic electromagnetic blender top heating side and stirs
It mixes to 60~70 DEG C, constant temperature mixing time is 10~20 minutes, and mixing speed is 100~180r/min, until each additive is mixed
It closes uniformly, obtains uniform oil body, then cool to room temperature.
Embodiment 3
The formula of embodiment 3 is shown in Table 3 (based on gross mass 100g):
Table 3
Serial number | Ingredient names | Quality (g) |
1 | Lauryl alcohol | 42.0 |
2 | Butyl stearate | 16.8 |
3 | Pentaerythritol oleate | 11.2 |
4 | Lauric acid | 5.0 |
5 | 2,6-di-tert-butyl p-cresol | 1.0 |
6 | Benzotriazole | 0.9 |
7 | Thiadiazoles derivative | 0.3 |
8 | Dialkyl dithiophosphate | 2.0 |
9 | Hydrogenated base oil | 20.8 |
By each component quality formula of upper table, universal non-ferrous metal and stainless-steel cold-rolling oil compound additive are prepared.It will
Lauryl alcohol (42.0g), butyl stearate (16.8g), pentaerythritol oleate (11.2g), lauric acid (5.0g), the tertiary fourth of 2,6- bis-
Base paracresol (1.0g), benzotriazole (0.9g), thiadiazoles derivative (0.3g), dialkyl dithiophosphate (2.0g) and
Hydrogenated base oil (20.8g) after specifying sequence that container is added in by specification, is placed on thermostatic electromagnetic blender top heating side and stirs
It mixes to 60~70 DEG C, constant temperature mixing time is 10~20 minutes, and mixing speed is 100~180r/min, until each additive is mixed
It closes uniformly, obtains uniform oil body, then cool to room temperature.
Product performance index
The compound additive formula of above three embodiments is taken, aluminium sheet basis is added to the additive amount of mass fraction 3%
(aluminium rolling is used for) in oily A100, performance indicator such as table 4:
Table 4
The compound additive formula of above three embodiments is taken, is added in No. 5 white oils with the additive amount of mass fraction 5%
(for copper material and rolled stainless steel), performance indicator such as table 5:
Table 5
The embodiment of the above be only it is of the invention preferably apply example, but not intended to limit the scope of the present invention, therefore
All component ratios according to the present invention, equivalence changes made by method and principle, should all be covered by protection scope of the present invention.
Claims (2)
1. a kind of universal non-ferrous metal and stainless-steel cold-rolling oil compound additive, which is characterized in that select lauryl alcohol, stearic acid
Butyl ester, pentaerythritol oleate and lauric acid are as oiliness improver, and 2,6-di-tert-butyl p-cresol is as antioxidant, benzotriazole
With thiadiazoles derivative as metal deactivator, dialkyl dithiophosphate is as antiwear additive, and hydrogenated base oil is as solvent
Oil;
Compound additive it is specific as follows by mass percentage at being grouped as:
Oiliness improver: lauryl alcohol: 28~42%;
Butyl stearate and pentaerythritol oleate mixed ester: 28~42%;
Lauric acid: 2~5%;
Antioxidant: 2,6-di-tert-butyl p-cresol: 0.5~1%;
Metal deactivator: benzotriazole: 0.3~0.9%;
Thiadiazoles derivative: 0.3~0.9%;
Antiwear additive: dialkyl dithiophosphate: 0.5~2%;
Solvent naphtha: hydrogenated base oil: surplus;
In specific ingredient, mixed ester that oiliness improver lauryl alcohol and butyl stearate and pentaerythritol oleate are constituted compounds matter
Amount proportional region is 2:3~3:2, and the gross mass of lauryl alcohol and mixed ester is overall 70% of compound additive;It is hard in mixed ester
The compounding mass ratio range of resin acid butyl ester and pentaerythritol oleate are as follows: 2:3~3:2, metal deactivator benzotriazole and
The compounding mass ratio range of thiadiazoles derivative is 1:3~3:1.
2. the preparation method of universal non-ferrous metal as described in claim 1 and stainless-steel cold-rolling oil compound additive, special
Sign is specific preparation step are as follows:
First the butyl stearate of above-mentioned formula ratio and pentaerythritol oleate are added in reaction vessel according to corresponding ratio, so
After sequentially add lauryl alcohol, lauric acid, 2,6-di-tert-butyl p-cresol, benzotriazole, thiadiazoles derivative, dialkyl disulfides
Substituted phosphate is eventually adding hydrogenated base oil;Reaction vessel is placed on thermostatic electromagnetic blender heat while stirring to 60~
70 DEG C, mixing speed is 100~180r/min, and constant temperature mixing time is 10~20 minutes until each additive is uniformly mixed, so
After be cooled to room temperature to get to a kind of universal non-ferrous metal and stainless-steel cold-rolling oil compound additive.