CN106564256B - A kind of printed film combines the manufacturing process of highlighted membrana granulosa one contraposition chromatography - Google Patents

A kind of printed film combines the manufacturing process of highlighted membrana granulosa one contraposition chromatography Download PDF

Info

Publication number
CN106564256B
CN106564256B CN201510657415.0A CN201510657415A CN106564256B CN 106564256 B CN106564256 B CN 106564256B CN 201510657415 A CN201510657415 A CN 201510657415A CN 106564256 B CN106564256 B CN 106564256B
Authority
CN
China
Prior art keywords
glue
manufacturing process
highlighted
chromatography
contraposition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510657415.0A
Other languages
Chinese (zh)
Other versions
CN106564256A (en
Inventor
赖志锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan Dingsheng Plastic Film Co Ltd
Original Assignee
Dongguan Dingsheng Plastic Film Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongguan Dingsheng Plastic Film Co Ltd filed Critical Dongguan Dingsheng Plastic Film Co Ltd
Priority to CN201510657415.0A priority Critical patent/CN106564256B/en
Publication of CN106564256A publication Critical patent/CN106564256A/en
Application granted granted Critical
Publication of CN106564256B publication Critical patent/CN106564256B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to the manufacturing process that thermal transfer printing field more particularly to a kind of printed film combine highlighted membrana granulosa one contraposition chromatography.It is the following steps are included: basement membrane is selected, ink toning, ink printing, cooling is wound and hot pressing processing.Wherein, ink printing uses intaglio printing mode, and ink is imprinted on basement membrane simultaneously baking and curing using one group of mode of the same colour first, until completing the printing and baking and curing of whole colour cells；Then last group is coated on after hot-melt glue or solvent type glue being melted again in textured high solid version, and glue set is imprinted on alignment mode by corresponding pattern, one group of basement membrane integrally formed and that there is default flower pattern is made, it is 0.02~0.6 millimeter that glue, which can print thickness range, and drying temperature is 60 DEG C~100 DEG C；Using manufacturing process provided by the invention, high production efficiency, production cost is low, flower pattern and glue registration, and the product level processed is clearly demarcated.

Description

A kind of printed film combines the manufacturing process of highlighted membrana granulosa one contraposition chromatography
Technical field
The present invention relates to thermal transfer printing fields more particularly to a kind of printed film to combine the integrally contraposition chromatography of highlighted membrana granulosa Manufacturing process.
Background technique
All it is to turn mode using heat twice to process on the market at present, first highlighted membrana granulosa heat is turned in textile fabric or leather On face, wait 3~4 hours it is cold it is true substrate could be removed, then printed film is transferred on highlighted membrana granulosa, it is cold really after divide again From.Cause processing efficiency slow in this way, processing cost is double, and high solid glue is not only easily deformed and reduces product after heating twice Modelling effect, and the flower pattern processed twice can only do print of muddling things up, and not align flower pattern beauty.
Summary of the invention
For overcome the deficiencies in the prior art, purpose is intended to provide a kind of highlighted membrana granulosa one of printed film combination to the present invention The manufacturing process of chromatography is aligned, which does not have sewage discharge and environmental protection, high production efficiency, production cost It is low, flower pattern and glue registration, and the product level processed is clearly demarcated.
In order to solve the above technical problems, basic technical scheme proposed by the present invention are as follows:
A kind of printed film combines the manufacturing process of highlighted membrana granulosa one contraposition chromatography, wherein the manufacturing process is using recessed Version printing adds roll coating model, comprising the following steps:
S1, basement membrane are selected；Basement membrane uses PET or BOPP film, and the thickness range of PET or BOPP film is 0.012~ 0.10 millimeter, width range are 600~3500 millimeters；
S2, ink toning；Ink is using organic pigment or reactive dye or acid dyes；
S3, ink printing；Using intaglio printing mode, ink is imprinted on basement membrane and is dried using one group of mode of the same colour first Solidization, until completing the printing and baking and curing of whole colour cells；Then again after hot-melt glue or the fusing of solvent type glue It is coated on last group to consolidate in version with textured height, and glue set is imprinted on alignment mode by corresponding pattern position, be made one Group is integrally formed and has the pattern of default flower pattern, and it is 0.02~0.6 millimeter that glue, which can print thickness range, and drying temperature is 60 DEG C ~100 DEG C；
S4, cooling winding；Basement membrane passes sequentially through the cooling and solidifying of chill roll, packaged air conditioner, winds basement membrane after the completion of solidification；It is cold But at 10 DEG C~20 DEG C, the temperature of packaged air conditioner is controlled at 15 DEG C~25 DEG C for the temperature control of roller；
S5, hot pressing processing；Transfer membrane is pressed on textile fabric, corium or leather by make-up machine, make-up machine setting temperature Degree is 120~180 DEG C, and pressure is 2~5kg.
Further, it is coated on last group after the hot-melt glue fusing to consolidate in version with textured height, including following Step:
S11, hot-melt glue go out machine heating by agent and are fused into after liquid and are transported to hopper, and hopper temperature is controlled 170 DEG C~230 DEG C；
S12, the surface that hot-melt glue is coated on to high solid version will be adhered to the high solid non-printed region of version by scraper Surplus glue is struck off, and then the glue for being formed in high solid version printing area and is imprinted on corresponding pattern position with alignment mode set, One group of pattern integrally formed and that there is default flower pattern is made.
Preferably, the hot-melt glue uses polyamide or polyurethane hot melt.
Preferably, molten polyamide index range is 80~200cm3/ 10min (160 DEG C/2.16kg), range of viscosities is 50~120pa*s (160 DEG C/2.16kg).
Preferably, the melt index of the polyurethane hot melt is 10~100g/10min (160 DEG C/2.16kg), viscosity Range is (MFR---10~100g/10min).
Further, it is coated on last group after the solvent type glue fusing to consolidate in version with textured height, including following Step:
By solvent hopper is placed on after glue fusing dispersion, the solvent is butanone and cyclohexanone for S21, solvent type glue Mixture；
S22, the surface that solvent type glue application is consolidated to version in height will be adhered to the high solid non-printed region of version by scraper Surplus glue is struck off, and then the glue for being formed in high solid version printing area and is imprinted on corresponding pattern position with alignment mode set, One group of pattern integrally formed and that there is default flower pattern is made.
Further, by weight percentage, the solvent type glue includes following components: polyurethane PU glue 15%~40%, Butanone 30%~50%, cyclohexanone 15%~25%, cured powder 1%~3%.
Further, by weight percentage, the organic pigment includes following components: organic pigment 10%~20%, butanone 10%~30%, cyclohexanone 20%~30%, inking resin 20%~40%, defoaming agent 0.2%~0.5%, levelling agent 0.2% ~0.5%, antistatic agent 0.2%~0.5%.
Further, by weight percentage, reactive dye include following components: reactive dye 10%~20%, butanone 10% ~30%, cyclohexanone 20%~30%, inking resin 20%~40%, defoaming agent 0.2%~0.5%, levelling agent 0.2%~ 0.5%, antistatic agent 0.2%~0.5%.
Further, by weight percentage, reactive dye include following components: acid dyes 10%~20%, butanone 10% ~30%, cyclohexanone 20%~30%, inking resin 20%~40%, defoaming agent 0.2%~0.5%, levelling agent 0.2%~ 0.5%, antistatic agent 0.2%~0.5%.
The beneficial effects of the present invention are: ink is imprinted on baking and curing on basement membrane using one group of mode of the same colour by the present invention, and Glue is imprinted on corresponding pattern position with alignment mode set, one group of pattern integrally formed and that there is default flower pattern is made, is not necessarily to Midway waits cooling treatment, therefore high production efficiency, at low cost.The present invention also uses alignment mode can be accurately by glue set It is imprinted on corresponding pattern, glue can print 0.02~0.6 millimeter of thickness range, and thickness is higher, and feel is stronger, the height of glue printing Height has concurrently, therefore manufactured product three-dimensional sense and stereovision are strong, and flower pattern is abundant.
Detailed description of the invention
Fig. 1 is the manufacturing process process that a kind of printed film provided in this embodiment combines highlighted membrana granulosa one contraposition chromatography Figure.
Specific embodiment
Below with reference to attached drawing 1, the present invention is described further, but should not limit protection model of the invention with this It encloses.For convenience of explanation and understand technical solution of the present invention, illustrates that the used noun of locality is shown with attached drawing below Orientation subject to.
The present embodiment provides a kind of printed films to combine the manufacturing process for highlighting membrana granulosa and integrally aligning chromatography, the present embodiment Manufacturing process adds roll coating model using intaglio printing, comprising the following steps:
S1, basement membrane are selected；Basement membrane uses PET or BOPP film, and the thickness range of PET or BOPP film is 0.012~ 0.10 millimeter, width range are 600~3500 millimeters；
S2, ink toning；Ink is using organic pigment or reactive dye or acid dyes；
S3, ink printing；Using intaglio printing mode, ink is imprinted on basement membrane and is dried using one group of mode of the same colour first Solidization, until completing the printing and baking and curing of whole colour cells；Then again after hot-melt glue or the fusing of solvent type glue It is coated on last group to consolidate in version with textured height, and glue set is imprinted on alignment mode by corresponding pattern position, be made one Group is integrally formed and has the pattern of default flower pattern, and it is 0.02~0.6 millimeter that glue, which can print thickness range, and drying temperature is 60 DEG C ~100 DEG C；
S4, cooling winding；Basement membrane passes sequentially through the cooling and solidifying of chill roll, packaged air conditioner, winds basement membrane after the completion of solidification；It is cold But at 10 DEG C~20 DEG C, the temperature of packaged air conditioner is controlled at 15 DEG C~25 DEG C for the temperature control of roller；
S5, hot pressing processing；Transfer membrane is pressed on textile fabric, corium or leather by make-up machine, make-up machine setting temperature Degree is 120~180 DEG C, and pressure is 2~5kg.
For step S3, more specifically, for example need to print four kinds of colors on basement membrane, production scene there are four groups of colourings Board.First color first is printed on flower pattern on basement membrane by first group of board, solidifies by 60 DEG C~100 DEG C oven heats Afterwards, the second color is printed on basement membrane by second group of board, after solidifying using 60 DEG C~100 DEG C oven heats, with such It pushes away and prints third color and the 4th color again, until the design and color of needs.For step S3, since the present embodiment is of the same colour using one group Ink is imprinted on basement membrane simultaneously baking and curing by mode, and glue is imprinted on corresponding position with alignment mode set, and one group of one is made The pattern of default flower pattern is shaped and had, waits cooling treatment, therefore high production efficiency without midway, it is at low cost.The present embodiment Also accurately glue set can be imprinted on corresponding pattern using alignment mode, glue can print 0.02~0.6 millimeter of thickness range, Thickness is higher, and feel is stronger, and the height height of glue printing has concurrently, therefore manufactured product three-dimensional sense and stereovision are strong, and flower pattern is rich It is rich.
For step S4, basement membrane is solidified using chill roll and packaged air conditioner, compares existing curing mode, in step S4 The temperature of chill roll is controlled at 10 DEG C~20 DEG C, wherein the temperature of chill roll is 15 DEG C more moderate, because of the temperature of chill roll When relatively low, basement membrane supercooling roller is easy to appear droplet, and product is contaminated；When the temperature is excessively high, chill roll is cold to basement membrane for chill roll Ineffective, influence product curing rate.
Packaged air conditioner can further solidify transfer membrane in step S4, and temperature is controlled at 15 DEG C~25 DEG C, wherein packaged air conditioner Temperature is more moderate when being 20 DEG C, because basement membrane crosses packaged air conditioner and is easy to appear droplet when packaged air conditioner temperature is relatively low, product is got dirty Dye.When the temperature is excessively high, packaged air conditioner is bad to basement membrane cooling effect for packaged air conditioner, influences product curing rate.
For step S5, after basement membrane is pressed in textile fabric or leather, refrigerated separation is also needed, product later can reach solid The effect of sense and stereovision.
The glue of the present embodiment can use hot-melt glue or solvent type glue.
Embodiment one:
When using hot-melt glue, it is coated on last group after hot-melt glue fusing in textured high solid version, wraps Include following steps:
S11, hot-melt glue go out machine heating by agent and are fused into after liquid and are transported to hopper, and hopper temperature is controlled 170 DEG C~230 DEG C；
S12, the surface that hot-melt glue is coated on to high solid version will be adhered to the high solid non-printed region of version by scraper Surplus glue is struck off, and then being formed in the high glue of version printing area admittedly and being imprinted on corresponding pattern with alignment mode set, makes At one group of basement membrane integrally formed and that there is default flower pattern.
Wherein, hot-melt glue use polyamide or polyurethane hot melt, molten polyamide index range be 80~ 200cm3/ 10min (160 DEG C/2.16kg), range of viscosities are 50~120pa*s (160 DEG C/2.16kg).Polyurethane hot melt Melt index is 10~100g/10min (160 DEG C/2.16kg), and range of viscosities is (MFR---10~100g/10min).
Embodiment two:
When using solvent type glue, it is coated on last group after the fusing of solvent type glue in textured high solid version, wraps Include following steps:
S21, solvent type glue are placed in hopper after glue fusing is dispersed by solvent；
S22, the surface that solvent type glue application is consolidated to version in height will be adhered to the high solid non-printed region of version by scraper Surplus glue is struck off, and then being formed in the high glue of version printing area admittedly and being imprinted on corresponding pattern with alignment mode set, makes At one group of basement membrane integrally formed and that there is default flower pattern.
By weight percentage, solvent type glue includes following components: polyurethane PU glue 15%~40%, and butanone 30%~ 50%, cyclohexanone 15%~25%, cured powder 1%~3%.
For embodiment two, the present embodiment provides a kind of solvent type glue, by weight percentage comprising following components: Polyurethane PU glue 24%, butanone 50%, cyclohexanone 25%, cured powder 1%.
For embodiment two, the present embodiment provides a kind of solvent type glue, by weight percentage comprising following components: Polyurethane PU glue 40%, butanone 42%, cyclohexanone 15%, cured powder 3%.
For embodiment two, the present embodiment provides a kind of solvent type glue, by weight percentage comprising following components: Polyurethane PU glue 30%, butanone 48.5%, cyclohexanone 20%, cured powder 1.5%.
Using the solvent type glue of above-mentioned formula, the mobility and curing rate of glue are good, and can be improved board production Stability.
For the step S2 of ink toning, the present embodiment provides a kind of ink toners, by weight percentage, organic pigment Including following components: organic pigment 10%~20%, butanone 10%~30%, cyclohexanone 20%~30%, inking resin 20% ~40%, defoaming agent 0.2%~0.5%, levelling agent 0.2%~0.5%, antistatic agent 0.2%~0.5%.
For the step S2 of ink toning, the present embodiment provides a kind of ink toners, by weight percentage, reactive dye Including following components: reactive dye 10%~20%, butanone 10%~30%, cyclohexanone 20%~30%, inking resin 20% ~40%, defoaming agent 0.2%~0.5%, levelling agent 0.2%~0.5%, antistatic agent 0.2%~0.5%.
For the step S2 of ink toning, the present embodiment provides a kind of ink toners, by weight percentage, acid dyes Including following components: acid dyes 10%~20%, butanone 10%~30%, cyclohexanone 20%~30%, inking resin 20% ~40%, defoaming agent 0.2%~0.5%, levelling agent 0.2%~0.5%, antistatic agent 0.2%~0.5%.
To sum up, the manufacturing process of the integrated contraposition chromatography of highlighted membrana granulosa is combined using a kind of printed film provided by the invention, Its high production efficiency, production cost is low, flower pattern and glue registration, and the product level processed is clearly demarcated.
According to the disclosure and teachings of the above specification, those skilled in the art in the invention can also be to above-mentioned embodiment party Formula is changed and is modified.Therefore, the invention is not limited to the specific embodiments disclosed and described above, to of the invention Some modifications and changes should also be as falling into the scope of the claims of the present invention.In addition, although being used in this specification Some specific terms, these terms are merely for convenience of description, does not limit the present invention in any way.

Claims (9)

1. the manufacturing process that a kind of printed film combines highlighted membrana granulosa one contraposition chromatography, it is characterised in that: the manufacturing process Using intaglio printing plus roll coating model, comprising the following steps:
S1, basement membrane are selected；Basement membrane uses PET or BOPP film, and the thickness range of PET or BOPP film is 0.012~0.10 milli Rice, width range are 600~3500 millimeters；
S2, ink toning；Ink is using organic pigment or reactive dye or acid dyes；
S3, ink printing；Using intaglio printing mode, ink is imprinted on basement membrane using one group of mode of the same colour first and is dried solid Change, until completing the printing and baking and curing of whole colour cells, the design and color needed；Then again hot-melt glue or It is coated on last group after the fusing of solvent type glue to consolidate in version with textured height, and glue set is imprinted on accordingly with alignment mode One group of pattern that is integrally formed and having default flower pattern is made in pattern position, and it is 0.02~0.6 milli that glue, which can print thickness range, Rice, drying temperature are 60 DEG C~100 DEG C；
S4, cooling winding；Basement membrane passes sequentially through the cooling and solidifying of chill roll, packaged air conditioner, winds basement membrane after the completion of solidification；Chill roll Temperature control at 10 DEG C~20 DEG C, the temperature of packaged air conditioner is controlled at 15 DEG C~25 DEG C；
S5, hot pressing processing；Transfer membrane is pressed on textile fabric, corium or leather by make-up machine, make-up machine set temperature is 120~180 DEG C, pressure is 2~5kg.
2. a kind of printed film according to claim 1 combines the manufacturing process of highlighted membrana granulosa one contraposition chromatography, special Sign is: last group is coated on after the hot-melt glue fusing in textured high solid version, comprising the following steps:
S11, hot-melt glue go out machine heating by agent and are fused into after liquid and are transported to hopper, the control of hopper temperature 170 DEG C~ 230℃；
S12, the surface that hot-melt glue is coated on to high solid version will be adhered to the extra of the high solid non-printed region of version by scraper Glue strikes off, and then being formed in the high glue of version printing area admittedly and being imprinted on corresponding pattern with alignment mode set, is made one Group is integrally formed and has the basement membrane of default flower pattern.
3. a kind of printed film according to claim 2 combines the manufacturing process of highlighted membrana granulosa one contraposition chromatography, special Sign is: the hot-melt glue uses polyamide or polyurethane hot melt.
4. a kind of manufacturing process of the highlighted membrana granulosa one contraposition chromatography of printed film combination according to claim 3, It is characterized by: melt index range of polyamide under the conditions of 160 DEG C/2.16kg is 80~200cm3/ 10min, viscosity model It encloses for 50~120pa*s.
5. a kind of printed film according to claim 1 combines the manufacturing process of highlighted membrana granulosa one contraposition chromatography, special Sign is: last group is coated on after the solvent type glue fusing in textured high solid version, comprising the following steps:
By solvent being placed on hopper after glue fusing dispersion, the solvent is the mixed of butanone and cyclohexanone for S21, solvent type glue Close object；
S22, the surface that solvent type glue application is consolidated to version in height will be adhered to the extra of the high solid non-printed region of version by scraper Glue strikes off, and then being formed in the high glue of version printing area admittedly and being imprinted on corresponding pattern with alignment mode set, is made one Group is integrally formed and has the pattern of default flower pattern.
6. a kind of printed film according to claim 5 combines the manufacturing process of highlighted membrana granulosa one contraposition chromatography, special Sign is: by weight percentage, the solvent type glue includes following components: polyurethane PU glue 15%~40%, butanone 30% ~50%, cyclohexanone 15%~25%, cured powder 1%~3%.
7. a kind of printed film according to claim 1 combines the manufacturing process of highlighted membrana granulosa one contraposition chromatography, special Sign is: by weight percentage, the organic pigment includes following components: organic pigment 10%~20%, and butanone 10%~ 30%, cyclohexanone 20%~30%, inking resin 20%~40%, defoaming agent 0.2%~0.5%, levelling agent 0.2%~ 0.5%, antistatic agent 0.2%~0.5%.
8. a kind of printed film according to claim 1 combines the manufacturing process of highlighted membrana granulosa one contraposition chromatography, special Sign is: by weight percentage, reactive dye include following components: reactive dye 10%~20%, butanone 10%~30%, ring Hexanone 20%~30%, inking resin 20%~40%, defoaming agent 0.2%~0.5%, levelling agent 0.2%~0.5% are prevented quiet Electric agent 0.2%~0.5%.
9. a kind of printed film according to claim 1 combines the manufacturing process of highlighted membrana granulosa one contraposition chromatography, special Sign is: by weight percentage, reactive dye include following components: acid dyes 10%~20%, butanone 10%~30%, ring Hexanone 20%~30%, inking resin 20%~40%, defoaming agent 0.2%~0.5%, levelling agent 0.2%~0.5% are prevented quiet Electric agent 0.2%~0.5%.
CN201510657415.0A 2015-10-13 2015-10-13 A kind of printed film combines the manufacturing process of highlighted membrana granulosa one contraposition chromatography Active CN106564256B (en)