CN106554721A - A kind of antirust paint - Google Patents
A kind of antirust paint Download PDFInfo
- Publication number
- CN106554721A CN106554721A CN201510622894.2A CN201510622894A CN106554721A CN 106554721 A CN106554721 A CN 106554721A CN 201510622894 A CN201510622894 A CN 201510622894A CN 106554721 A CN106554721 A CN 106554721A
- Authority
- CN
- China
- Prior art keywords
- parts
- antirust paint
- dispersant
- emulsion
- oxidation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of antirust paint, belongs to paint technology field.A kind of antirust paint, is made using the raw material of following weight portion:Emulsion 50-60 part, the red ferrum 20-50 parts of oxidation, zinc phosphate 2-4 parts, aluminium powder 0.2-0.4 parts, sodium propionate 0.5-0.8 parts, Pulvis Talci 2-6 parts, dispersant 0.4-0.8 parts, film former 0.4-0.8 parts, sodium nitrite composite corrosion inhibitor 3-4.5 parts, water 30-60 parts, levelling agent 0.3-0.5 parts, surface activity 0.4-0.6 part, inositol hexaphosphate 3-4.5 parts.The antirust paint of the present invention, with stronger adhesive force, favorable rust preventing effect, while having anti-corrosion waterproof ability, nontoxic pollution-free, environment protection health is safe from harm to human body.
Description
Technical field
The present invention relates to a kind of antirust paint, belongs to paint technology field.
Background technology
As coatings industry and application develop to low stainization, water paint increasingly rises.Caused by metal erosion, loss is extremely serious, and the anticorrosive coating of metal material causes concern both at home and abroad.Solvent-borne type antirusting paint, in contained formaldehyde, benzene, dimethylbenzene be all poisonous carcinogen, there is several aspects such as atmosphere pollution, toxicity and fire hazard.
The content of the invention
It is an object of the invention to solve the deficiency of prior art, there is provided a kind of nontoxic free of contamination antirust paint.
A kind of antirust paint of the present invention is achieved through the following technical solutions:
A kind of antirust paint, is made using the raw material of following weight portion:
Emulsion 50-60 part, the red ferrum 20-50 parts of oxidation, zinc phosphate 2-4 parts, aluminium powder 0.2-0.4 parts, sodium propionate 0.5-0.8 parts, Pulvis Talci 2-6 parts, dispersant 0.4-0.8 parts, film former 0.4-0.8 parts, sodium nitrite composite corrosion inhibitor 3-4.5 parts, water 30-60 parts, levelling agent 0.3-0.5 parts, surface activity 0.4-0.6 part, inositol hexaphosphate 3-4.5 parts.
Preferably, emulsion 52-58 part, the red ferrum 25-45 parts of oxidation, zinc phosphate 2.5-3.5 parts, aluminium powder 0.2-0.3 parts, sodium propionate 0.6-0.7 parts, Pulvis Talci 3-5 parts, dispersant 0.5-0.7 parts, film former 0.5-0.7 parts, sodium nitrite composite corrosion inhibitor 3.5-4 parts, water 35-55 parts, levelling agent 0.3-0.4 parts, surface activity 0.4-0.5 part, inositol hexaphosphate 3.5-4 parts.
Further:40 parts of emulsion, 30 parts of the red ferrum of oxidation, 3 parts of zinc phosphate, 0.3 part of aluminium powder, 0.65 part of sodium propionate, 4 parts of Pulvis Talci, 0.6 part of dispersant, 0.6 part of film former, 3.8 parts of sodium nitrite composite corrosion inhibitor, 45 parts of water, 0.4 part of levelling agent, 0.5 part of surface activity, 3.8 parts of inositol hexaphosphate.
The antirust paint of the present invention, with stronger adhesive force, favorable rust preventing effect, while having anti-corrosion waterproof ability, nontoxic pollution-free, environment protection health is safe from harm to human body.
Specific embodiment
Form by the following examples, the above of the present invention is described in further detail again, but this scope for being interpreted as above-mentioned theme of the invention should not be only limitted to Examples below, all technologies realized based on the above of the present invention belong to the scope of the present invention.
Embodiment 1:A kind of antirust paint, is made using the raw material of following weight portion:
40 parts of emulsion, 30 parts of the red ferrum of oxidation, 3 parts of zinc phosphate, 0.3 part of aluminium powder, 0.65 part of sodium propionate, 4 parts of Pulvis Talci, 0.6 part of dispersant, 0.6 part of film former, 3.8 parts of sodium nitrite composite corrosion inhibitor, 45 parts of water, 0.4 part of levelling agent, 0.5 part of surface activity, 3.8 parts of inositol hexaphosphate.Embodiment 2:A kind of antirust paint, is made using the raw material of following weight portion:
50 parts of emulsion, 20 parts of the red ferrum of oxidation, 2 parts of zinc phosphate, 0.2 part of aluminium powder, 0.5 part of sodium propionate, 2 parts of Pulvis Talci, 0.4 part of dispersant, 0.4 part of film former, 3 parts of sodium nitrite composite corrosion inhibitor, 30 parts of water, 0.3 part of levelling agent, 0.4 part of surface activity, 3 parts of inositol hexaphosphate.
Embodiment 3:A kind of antirust paint, is made using the raw material of following weight portion:
60 parts of emulsion, 50 parts of the red ferrum of oxidation, 4 parts of zinc phosphate, 0.4 part of aluminium powder, 0.8 part of sodium propionate, 6 parts of Pulvis Talci, 0.8 part of dispersant, 0.8 part of film former, 4.5 parts of sodium nitrite composite corrosion inhibitor, 60 parts of water, 0.5 part of levelling agent, 0.6 part of surface activity, 4.5 parts of inositol hexaphosphate.
Claims (3)
1. a kind of antirust paint, it is characterised in that:Made using the raw material of following weight portion:
Emulsion 50-60 part, the red ferrum 20-50 parts of oxidation, zinc phosphate 2-4 parts, aluminium powder 0.2-0.4 parts, sodium propionate 0.5-0.8 parts, Pulvis Talci 2-6 parts, dispersant 0.4-0.8 parts, film former 0.4-0.8 parts, sodium nitrite composite corrosion inhibitor 3-4.5 parts, water 30-60 parts, levelling agent 0.3-0.5 parts, surface activity 0.4-0.6 part, inositol hexaphosphate 3-4.5 parts.
2. a kind of antirust paint according to claim 1, it is characterised in that:Emulsion 52-58 part, the red ferrum 25-45 parts of oxidation, zinc phosphate 2.5-3.5 parts, aluminium powder 0.2-0.3 parts, sodium propionate 0.6-0.7 parts, Pulvis Talci 3-5 parts, dispersant 0.5-0.7 parts, film former 0.5-0.7 parts, sodium nitrite composite corrosion inhibitor 3.5-4 parts, water 35-55 parts, levelling agent 0.3-0.4 parts, surface activity 0.4-0.5 part, inositol hexaphosphate 3.5-4 parts.
3. a kind of antirust paint according to claim 1 or claim 2, it is characterised in that:40 parts of emulsion, 30 parts of the red ferrum of oxidation, 3 parts of zinc phosphate, 0.3 part of aluminium powder, 0.65 part of sodium propionate, 4 parts of Pulvis Talci, 0.6 part of dispersant, 0.6 part of film former, 3.8 parts of sodium nitrite composite corrosion inhibitor, 45 parts of water, 0.4 part of levelling agent, 0.5 part of surface activity, 3.8 parts of inositol hexaphosphate.