CN106554698A - A kind of formulation for coating material suitable for refrigerator top layer - Google Patents
A kind of formulation for coating material suitable for refrigerator top layer Download PDFInfo
- Publication number
- CN106554698A CN106554698A CN201510627016.XA CN201510627016A CN106554698A CN 106554698 A CN106554698 A CN 106554698A CN 201510627016 A CN201510627016 A CN 201510627016A CN 106554698 A CN106554698 A CN 106554698A
- Authority
- CN
- China
- Prior art keywords
- agent
- formulation
- coating material
- top layer
- material suitable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of formulation for coating material suitable for refrigerator top layer, the formulation for coating material includes epoxy resin 31-40%, curing agent 15-19%, auxiliary agent 6%, levelling agent 3%, barium sulfate 10-15%, optical brightener 1%, titanium dioxide 5-6%, color masterbatch 1-2%, growth agent 2%, antioxidant 5-7%, fire-resistant gas agent 7-12% and carborundum 1% by weight percentage, and the peeked amount sum of each component is equal to 100%.The present invention has the advantages that covering performance is good and low cost.
Description
Technical field
The present invention relates to art of powder coatings, and in particular to a kind of formulation for coating material suitable for refrigerator top layer.
Background technology
Powdery paints is a kind of new without 100% solid powdery coating of solvent.With solvent-free, pollution-free, recyclable, environmentally friendly, save energy and resource, reduce labor intensity high with coating machinery intensity the features such as.In prior art; its powdery paints is made up of polyester resin, the different Fo Er copper diisocyanate of enclosed type, styrax and dibutyltin dilaurate; its shortcoming is that physics characteristic is poor, coverage effect is poor, is also easy to produce rill, it is impossible to meet electrical equipment spraying and top layer protection.I.e. existing powdery paints covering performance is poor, it is impossible to meet productive life needs.
The content of the invention
The technical problem to be solved in the present invention is to overcome above-mentioned deficiency, there is provided a kind of good formulation for coating material of covering performance.
In order to solve above-mentioned technical problem, it is carried out by the following technical programs：
A kind of formulation for coating material suitable for refrigerator top layer, it is characterised in that：The formulation for coating material includes epoxy resin 31-40%, curing agent 15-19%, auxiliary agent 6%, levelling agent 3%, barium sulfate 10-15%, optical brightener 1%, titanium dioxide 5-6%, color masterbatch 1-2%, growth agent 2%, antioxidant 5-7%, fire-resistant gas agent 7-12% and carborundum 1% by weight percentage, and the peeked amount sum of each component is equal to 100%.
As a further improvement on the present invention, the formulation for coating material includes epoxy resin 35.5%, curing agent 17%, auxiliary agent 6%, levelling agent 3%, barium sulfate 12.5%, optical brightener 1%, titanium dioxide 5.5%, color masterbatch 1.5%, growth agent 2%, antioxidant 5.5%, fire-resistant gas agent 9.5% and carborundum 1% by weight percentage, and the peeked amount sum of each component is equal to 100%.
As a further improvement on the present invention, the levelling agent is Siloxane-Oxyalkylene Copolymers copolymer.The antioxidant is N,N' di sec butyl p phenylene diamine.
As a further improvement on the present invention, the optical brightener is methyl methacrylate and butyl acrylate copolymer.
The present invention compared with prior art, with advantages below.
The powdery paints of above-mentioned formula, cost is taken to reduce relative to existing formulation for coating material, overall film layer is stable after product spray mo(u)lding, possesses good prospect of the application.The toasted film coated surface that excellent performance is obtained after the coating spraying of the present invention, the film possess rub, impact, adherence, toughness, corrosion resistance and chemical resistance etc..
The coating of the present invention is once sprayed and can reach 50-300 μm, and flow leveling is good, will not drip the phenomenon generation such as vertical or stagnant as having when coatings volatile organic compoundses thickness is applied.Because containing growth agent in formula, can be sprayed using electrostatic principle, coating equipment can reach full-automation, without waste of manpower resource, reduces cost and quality is more easy to control, it is to avoid cause to waste.
Specific embodiment
With reference to embodiment the present invention will be further explained explanation.
Embodiment one：
A kind of formulation for coating material suitable for refrigerator top layer, formulation for coating material includes epoxy resin 31%, curing agent 15%, auxiliary agent 6%, levelling agent 3%, barium sulfate 15%, optical brightener 1%, titanium dioxide 6%, color masterbatch 2%, growth agent 2%, antioxidant 6%, fire-resistant gas agent 12% and carborundum 1% by weight percentage, and the peeked amount sum of each component is equal to 100%.
Embodiment two：
A kind of formulation for coating material suitable for refrigerator top layer, formulation for coating material includes epoxy resin 35.5%, curing agent 17%, auxiliary agent 6%, levelling agent 3%, barium sulfate 12.5%, optical brightener 1%, titanium dioxide 5.5%, color masterbatch 1.5%, growth agent 2%, antioxidant 5.5%, fire-resistant gas agent 9.5% and carborundum 1% by weight percentage, and the peeked amount sum of each component is equal to 100%.
Embodiment three：
A kind of formulation for coating material suitable for refrigerator top layer, formulation for coating material includes epoxy resin 40%, curing agent 19%, auxiliary agent 6%, levelling agent 3%, barium sulfate 10%, optical brightener 1%, titanium dioxide 5%, color masterbatch 1%, growth agent 2%, antioxidant 5%, fire-resistant gas agent 7% and carborundum 1% by weight percentage, and the peeked amount sum of each component is equal to 100%.
When prepared by the composite coating formula of the present invention, each component dispensing is ready to by formula, is put into mixer, 30min is sufficiently mixed with 600 revs/min of speed, be then placed in drying machine drying and form sheet, then powdery paints is obtained final product by flour mill milling.
The above is the example of the present invention and explanation; but do not mean that obtainable advantage of the invention is so limited, may be to wherein one or more of the advantage realized in the simple transformation of structure, and/or some embodiments in the protection domain of the application in every practice process of the present invention.
Claims (5)
1. a kind of formulation for coating material suitable for refrigerator top layer, it is characterised in that：The formulation for coating material includes epoxy resin 31-40%, curing agent 15-19%, auxiliary agent 6%, levelling agent 3%, barium sulfate 10-15%, optical brightener 1%, titanium dioxide 5-6%, color masterbatch 1-2%, growth agent 2%, antioxidant 5-7%, fire-resistant gas agent 7-12% and carborundum 1% by weight percentage, and the peeked amount sum of each component is equal to 100%.
2. the formulation for coating material suitable for refrigerator top layer according to claim 1, it is characterised in that：The formulation for coating material includes epoxy resin 35.5%, curing agent 17%, auxiliary agent 6%, levelling agent 3%, barium sulfate 12.5%, optical brightener 1%, titanium dioxide 5.5%, color masterbatch 1.5%, growth agent 2%, antioxidant 5.5%, fire-resistant gas agent 9.5% and carborundum 1% by weight percentage, and the peeked amount sum of each component is equal to 100%.
3. the formulation for coating material suitable for refrigerator top layer according to claim 1, it is characterised in that：The levelling agent is Siloxane-Oxyalkylene Copolymers copolymer.
4. the formulation for coating material suitable for refrigerator top layer according to claim 1, it is characterised in that：The antioxidant is N,N' di sec butyl p phenylene diamine.
5. the formulation for coating material suitable for refrigerator top layer according to claim 1, it is characterised in that：The optical brightener is methyl methacrylate and butyl acrylate copolymer.