CN1065444A - 用石英闪长玢岩生产岩棉的方法 - Google Patents
用石英闪长玢岩生产岩棉的方法 Download PDFInfo
- Publication number
- CN1065444A CN1065444A CN 91101900 CN91101900A CN1065444A CN 1065444 A CN1065444 A CN 1065444A CN 91101900 CN91101900 CN 91101900 CN 91101900 A CN91101900 A CN 91101900A CN 1065444 A CN1065444 A CN 1065444A
- Authority
- CN
- China
- Prior art keywords
- rock wool
- rock
- porphyrite
- raw material
- diorite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种采用石英闪长玢岩生产岩棉的方法,由于采
用石英闪长玢岩为生产岩棉的主要原料,采用转炉渣
为熔剂,经冲天炉熔炼,冲天炉流口处的熔体温度为
1350~1420℃,经高速离心机成纤,生产岩棉产品,
提高了岩棉产量和质量,降低焦炭的消耗,本发明原
料配方容易获得酸度系数1.61。
Description
一种采用石英闪长玢岩生产岩棉的方法,是一种人造矿物纤维。主要用作工业、建筑物的保温、隔离或防火材料。
目前国内外生产岩棉,均以玄武岩或辉绿岩为主要原料,这类原料的SiO2含量在45~52%之间。原料熔点低、粘度小,再配以碱性熔剂,如石灰石,白云方石等经过熔融、离心(或喷吹)等工序成纤,制成岩棉,其工艺流程是将玄武岩等原料,石灰石和焦碳分别破碎,筛分后贮入料仓,并按要求比例称量配料后加入冲天炉,熔炼成熔融状态,再经高速离心机(或高压空气喷吹)离心成纤维状棉,使之在沉降室集中铺平、即成岩棉原棉,原棉可以通过已有的工艺制成各种岩棉制品。如:岩棉板、岩棉毡、岩棉管套、吸收板等,但上述工艺方法所用的玄武岩与石灰石,应用冲天炉熔制岩棉时一般只能用玄武岩,辉缘岩等含SiO2较低的矿石,如用石灰石等作熔剂,其岩棉的生产量低,焦炭的用量高,另外有很多地地区缺少玄武岩或辉缘岩须要从外地运入,这样一来成本就高了,有的地区就用另外一种用料方法来生产岩棉,如中国专利公开了一种用钠长石阳起石片岩生产岩棉的方法CN87101885A。
本发明提供了一种采用石英闪光玢岩为主要原料融制岩棉的一种新方法生产岩棉,可以提高产量和质量也降低焦炭的消耗量。
本发明的技术方案是按下述内容实现的,主要采用一种酸性岩浆岩-石英闪长玢岩以转炉渣为熔剂(特殊选择的碱性熔剂,其重量百分比为:
石英闪光玢岩 46%
转炉渣 54%
将石英闪光玢岩,转炉渣和焦炭分别破碎筛分后贮入料仓并按要求比例称量配料后加入冲天炉,熔炼成熔融状态,经高速离心机离心成纤维状棉,使之在沉降室集中铺平,即成岩棉原棉,原棉可以通过已知工艺制成各种岩棉。
经冲天炉熔炼,冲天炉流口处的熔体温度为1350℃~1420℃经高速离心机成纤。石英闪光玢岩,其矿物组成为角闪石28.45%,斜长石60%、石英11%、磁铁矿0.55%,其化学成份为:二氧化硅67%、三氧化二铝14.35%、氧化钙3.32%。
氧化镁2.11%、氧化铁4.01%、氧化钾3.55%、氧化钠3.8%、氧化钛0.45%、
总计:98.29%
岩石的酸度系数为15.0
所选用的转炉渣为碱性熔剂、该熔剂的特点是碱性氧化物含量高、含有适量氧化铁并且没有灼减。该转炉渣的化学成份。
二氧化硅15.14%、三氧化二铝2.88%、氧化钙46.89% 氧化亚铁11.28%其它5.32%总计100.00%。
采用上述工艺方法,其特点在于凡二氧化硅含量大于65%的酸性岩类,均可以做为主要原料来生产岩棉。
本发明与现有技术相比,由于采用石英闪长玢岩为主要原料,扩大了岩棉的原料来源,突破了常规的以玄武岩或辉缘岩,及主要原料来生产岩棉拓宽了冲天炉岩棉原料的品钟,这在过去是难以做到的,再配以特殊选择的碱性熔剂代替传统的石灰石或白云石,可使岩棉产量比用玄武岩,石灰石提高,降低了焦炭用量,过去的工艺中采用的玄武岩、辉缘岩中,二氧化硅含量仅45~52%,岩石酸度系数仅4.0左右,可见用的石灰石,白云石作熔剂必将使熔剂加入量大增,使岩棉的产量下降,焦耗上升,又使岩棉的质量得到改善,产品酸度系数大于1.5,在生产过程中可以节能5%左右,能提高岩棉产量10%以上。对于凡二氧化硅含量大于65%的酸性岩类,均可用本发明的方法熔炼出合格的岩棉。冲天炉的冶炼强度达1927公斤/米2时,每吨棉的焦炭消耗降低4.5%。
附图是本工艺方法的工序流程图。
下面将具体叙述本发明的实施例。
使用本发明的原料和配方。
石英闪长玢岩46%、转炉渣54%(重量百分比)
冲天炉流口处熔体温度1350~1420℃、经高速离心机减纤。
岩棉的化学成份:
二氧化硅37.66%、三氧化二铝14.30%、氧化钙27.27%、氧化镁4.95%、三氧化二铁0.11%、氧化亚铁10.74%。产品酸度系数Mk=1.61。
Claims (3)
1、一种采用石英闪长玢岩生产棉的方法,其特征是采用英闪长玢岩为主要原料,以转炉渣为熔剂,经冲天炉熔炼生产岩棉的方法。
2、根据权利要求1所述生产岩棉的方法,其特征在于其配方按重量百分比,石英闪光玢岩 46%
转炉渣54%
冲天炉流口处的熔体温度为1350~1420℃经高速离心机成纤。
3、根据权利要求1所述的生产岩棉的方法,其特征在于凡二氧化硅含量大于65%的酸性岩类,均可以做为主要原料生产岩棉。