CN106543837A - A kind of preparation technology of the coating of silanes ethane ethers composite modifier - Google Patents
A kind of preparation technology of the coating of silanes ethane ethers composite modifier Download PDFInfo
- Publication number
- CN106543837A CN106543837A CN201611017688.XA CN201611017688A CN106543837A CN 106543837 A CN106543837 A CN 106543837A CN 201611017688 A CN201611017688 A CN 201611017688A CN 106543837 A CN106543837 A CN 106543837A
- Authority
- CN
- China
- Prior art keywords
- zinc
- coating
- preparation technology
- composite modifier
- silanes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation method of the coating of addition composite modifier.Aqueous inorganic zinc-enriched coating is low because of wettability, and poor adhesive force, and easily there is sedimentation.To overcome the shortcoming, this method is, in zinc-rich paint preparation process, addition amino silicone alkanes coupling agent and alkylphenol polyethylene oxide ether surface active agent, both collaborations improve the wettability of metal zinc, increase the amalgamation of zinc powder and inorganic silicate, so as to prepare a kind of modified zinc-rich anti-corrosive paint.It is its preparation process is simple, easy to operate and with low cost.
Description
Technical field
The present invention relates to a kind of anti-corrosion zinc-rich paint and preparation method, more particularly to a kind of addition amino silicone alkanes coupling agent
With the anti-corrosion zinc-rich paint of alkylphenol polyethylene oxide ether modifying agent and preparation method thereof, belong to coating synthesis field.
Background technology
Zinc-rich paint can not only completely cut off air, and can form galvanic element protection, the normal potential of the zinc in zinc-rich paint
Low compared with iron and steel, when corrosive medium penetrates into, iron and steel forms galvanic element with zinc powder, and zinc powder loses electronics, steel as the negative pole of galvanic element
Ferrum obtains electronics as positive pole and is protected.After the position having on the film of zinc-rich paint is by mechanical damage, in certain model
In the area for enclosing, anticorrosive current can also flow to iron and steel exposed portion, then the corrosion product of zinc is deposited upon there and forms one layer of guarantor
Cuticula.Zinc rich paint is divided into organic zinc rich paint and inorganic zinc-rich paint, and organic zinc-rich paint commonly uses epoxy resin, chlorination rubber
Glue, vinylite and polyurethane resin are film forming binder.But the electric conductivity of the organic binder of organic zinc rich paint is poor.Nothing
Machine zinc rich paint is divided into again two class of solvent-borne type and aqueouss, and wherein aqueous inorganic zinc rich paint is by aqueous inorganic silicate(Receive,
Potassium, lithium)Resin, zinc powder, auxiliary agent etc. are constituted.
Aqueous inorganic zinc-enriched coating due to its organic solvent-free, with free from extraneous odour, do not fire it is not quick-fried, it is free from environmental pollution etc. excellent
Point, but simultaneously because solvent is few, wettability is low, thus adhesive force is good not as corresponding solvent based coating, and zinc powder is added to painting
In material, due to zinc powder and the more difficult fusion of inorganic silicate, attached power with ground low.For this purpose, it is general in dope preparing process, add
Plus coupling agent, improve the compatibility of metal zinc and silicate, strengthen the adhesive force of coating, but this improvement often has
Limit, in preparation process, then adds appropriate surfactant, then can play better improvement result.
Surfactant molecule is all made up of the hydrophilic group and nonpolar hydrophobic group two parts of polarity, surfactant
One end of molecule is the hydrophobic group of non-pole oleophylic, otherwise referred to as lipophilic group;Hydrophilic group of the other end of molecule for polar hydrophilic,
Otherwise referred to as lipophobic group or visually be referred to as hydrophilic head.Two class formations and the diametrically opposite molecular fragment of performance or group office
It is connected in the two ends of same molecule and with chemical bond, defines a kind of structure of asymmetric, polarity, thus impart such
Particular molecule was not only hydrophilic, but also oleophylic, and was not the characteristic of overall hydrophilic or oleophylic, so as to play the characteristics such as moistening, solubilising.
The present invention is by, in the preparation process of aqueous inorganic zinc-enriched coating, adding amino silicone alkanes coupling agent and alkyl phenol
Poly(ethylene oxide) ether surface active agent, both collaborations improve the wettability of metal zinc, and increase zinc powder is melted with inorganic silicate
Conjunction property, so as to prepare a kind of modified zinc-rich anti-corrosive paint.
The content of the invention
It is an object of the invention to provide a kind of modified zinc-rich anti-corrosive paint, is to realize this purpose, the coating include with
The raw material of lower mass percent:
Lithium metasilicate 5%-10%;
Sodium silicate 5%-10%;
Ludox 20%-40%;
Amino silicone alkanes coupling agent 3%-7%;
Alkylphenol polyethylene oxide ether 2%-3%;
Silicone acrylic emulsion 20%-30%;
Zinc powder 20%-30%.
A kind of preparation method of modified zinc-rich anti-corrosive paint comprises the steps:
(1), first with just a certain amount of Lithium metasilicate solution of a container and sodium silicate solution Hybrid Heating, temperature control is in 50-70
℃;
(2), in the case where ceaselessly stirring, the Ludox of metering is slowly added dropwise so as to be sufficiently mixed;
(3) the amino silicone alkanes coupling agent and alkylphenol polyethylene oxide ether of certain metering are added toward container again, and high-speed stirred is equal
It is even;
(4) stop heating, when temperature is down to room temperature, add silicone acrylic emulsion;
(5) finally add a certain amount of super-fine zinc dust, after persistently stirring by a kind of modified zinc-rich anti-corrosive paint.
Preferential, in preparation process, the size of super-fine zinc dust granule is more than 700 mesh.
The present invention has following advantages and characteristic:
(1) preparation process is simple, easy to operate;
(2) abundant raw material source, with low cost.
Specific embodiment
Embodiment one:
50g Lithium metasilicates solution and 50g sodium silicate solutions are mixed with a container first, be then mixed thing heating, heating temperature
Degree control is at 50 DEG C or so, and ceaselessly stirs.In whipping process, then 300g Ludox is slowly added dropwise, after completion of dropping, then
The alkylphenol polyethylene oxide ether of the amino silicone alkanes coupling agent and 20g of 30g is added toward container, and mixing speed will be improved, 5
Stop heating after minute, when temperature is down to room temperature, add 250g silicone acrylic emulsions, finally add the super-fine zinc dust of 300g, hold
A kind of modified zinc-rich anti-corrosive paint is obtained by continuing after stirring.
Embodiment two:
70g Lithium metasilicates solution and 70g sodium silicate solutions are mixed with a container first, be then mixed thing heating, heating temperature
Degree control is at 60 DEG C or so, and ceaselessly stirs.In whipping process, then 300g Ludox is slowly added dropwise, after completion of dropping, then
The alkylphenol polyethylene oxide ether of the amino silicone alkanes coupling agent and 25g of 35g is added toward container, and mixing speed will be improved, 5
Stop heating after minute, when temperature is down to room temperature, add 300g silicone acrylic emulsions, finally add the super-fine zinc dust of 200g, hold
A kind of modified zinc-rich anti-corrosive paint is obtained by continuing after stirring.
Embodiment three:
100g Lithium metasilicates solution and 100g sodium silicate solutions are mixed with a container first, be then mixed thing heating, heating
Temperature control is at 70 DEG C or so, and ceaselessly stirs.In whipping process, then 200g Ludox is slowly added dropwise, after completion of dropping,
Add the alkylphenol polyethylene oxide ether of the amino silicone alkanes coupling agent and 30g of 70g again toward container, and stirring speed will be improved
Degree, stops heating, when temperature is down to room temperature, adds 200g silicone acrylic emulsions, finally add the ultra-fine zinc of 300g after 5 minutes
Powder, after persistently stirring by a kind of modified zinc-rich anti-corrosive paint.
Claims (2)
1. the preparation technology of the coating of a kind of silanes-ethane ethers composite modifier, it is characterised in that the preparation technology include as
Lower step:
(1), first with just a certain amount of Lithium metasilicate solution of a container and sodium silicate solution Hybrid Heating, temperature control is in 50-70
℃;
(2), in the case where ceaselessly stirring, the Ludox of metering is slowly added dropwise so as to be sufficiently mixed;
(3) the amino silicone alkanes coupling agent and alkylphenol polyethylene oxide ether of certain metering are added toward container again, and high-speed stirred is equal
It is even;
(4) stop heating, when temperature is down to room temperature, add silicone acrylic emulsion;
(5) finally add a certain amount of super-fine zinc dust, after persistently stirring by a kind of modified zinc-rich anti-corrosive paint.
2. the preparation technology of the coating of a kind of silanes according to claim 1-ethane ethers composite modifier, its feature
Be, preparation process (5) middle addition zinc particle size be 700 mesh more than.