CN106118308A - A kind of solubilising modified anti-corrosive coating - Google Patents
A kind of solubilising modified anti-corrosive coating Download PDFInfo
- Publication number
- CN106118308A CN106118308A CN201610564157.6A CN201610564157A CN106118308A CN 106118308 A CN106118308 A CN 106118308A CN 201610564157 A CN201610564157 A CN 201610564157A CN 106118308 A CN106118308 A CN 106118308A
- Authority
- CN
- China
- Prior art keywords
- zinc
- solubilising
- amine salt
- silicate solution
- rich
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses modified zinc-rich anti-corrosive paint of a kind of solubilising and preparation method thereof, the method is: first by a certain amount of potassium silicate solution and sodium silicate solution Hybrid Heating, add Ludox mix homogeneously, certain Di(dioctylpyrophosphato) ethylene titanate amine salt chelate measured and alkylphenol polyethylene oxide ether is added the most again in container, high-speed stirred is uniform, finally be sequentially added into silicone acrylic emulsion and the zinc powder of 700 mesh, continuously stirred uniformly after i.e. obtain product.
Description
Technical field
The present invention relates to a kind of modified anti-corrosive coating and preparation method thereof, particularly to a kind of increasing adding surfactant
Molten modified anti-corrosive coating, belongs to coating manufacture field.
Background technology
Along with the progress of science and technology, coating is applied more and more extensive in life, particularly functional paint, as anti-corrosion of metal is coated with
Material.Common metal anticorrosive paint is at steel surface, simply prevents steel corrosion in the way of isolation air, and zinc-rich anticorrosion
Coating not only can completely cut off air, and can form galvanic element protection, and the normal potential of the zinc in zinc-rich anti-corrosive paint is low compared with iron and steel,
When corrosive medium penetrates into, iron and steel forms galvanic element with zinc powder, and zinc powder loses electronics as the negative pole of galvanic element, and iron and steel is as positive pole
Obtain electronics and obtain protection.Zinc-rich paint is divided into organic zinc-rich paint and inorganic zinc coating, and organic zinc-rich paint commonly uses ring
Epoxy resins, chlorinated rubber, vinylite and polyurethane resin are film forming binder, but the organic binder of organic zinc rich paint
Electric conductivity is poor.Inorganic zinc coating is divided into again solvent-borne type and aqueous two class, and wherein aqueous inorganic zinc-enriched coating is by aqueous
The compositions such as inorganic silicate (receive, potassium, lithium) resin, zinc powder, auxiliary agent.
Aqueous inorganic zinc-enriched coating due to its organic solvent-free, have free from extraneous odour, do not fire the most quick-fried, free from environmental pollution etc. excellent
Point, but owing to solvent is few, zinc powder wettability is bad, and zinc powder easily settles, and affects product quality.
Surfactant refers to significantly reduce their molecule of material of surface tension of liquid or liquid-liquid interface tension force all
Hydrophilic group and nonpolar hydrophobic group two parts by polarity form, and one end of surfactant molecule is dredging of non-pole oleophylic
Water base, otherwise referred to as lipophilic group;The other end of molecule is the hydrophilic group of polar hydrophilic, otherwise referred to as lipophobic group or visually
It is referred to as hydrophilic head.Two class formations and the diametrically opposite molecular fragment of performance or group office are in the two ends of same a part and with chemistry
Key is connected, and defines a kind of asymmetric, structure of polarity, thus imparts that such particular molecule is the most hydrophilic, but also oleophylic, again
It not the overall hydrophilic or characteristic of oleophylic, it is thus possible to play the characteristic such as moistening, solubilising.
The present invention, by dope preparing process, adds a kind of alkylphenol polyethylene oxide ether surface active agent, improves
Metal zinc wettability, thus prepare the zinc-rich anti-corrosive paint that a kind of solubilising is modified.
Summary of the invention
The present invention is that the zinc-rich anticorrosion preparing a kind of modification is coated with by adding specific surfactant raising lyotropy
Material, for realizing this purpose, this coating includes the raw material of following mass percent:
Potassium silicate 5%-10%;
Sodium silicate 5%-10%;
Ludox 20%-40%;
Di(dioctylpyrophosphato) ethylene titanate amine salt chelate 3%-7%;
Alkylphenol polyethylene oxide ether 2%-3%
Silicone acrylic emulsion 20%-30%;
Zinc powder 20%-30%.
The preparation method of the zinc-rich anti-corrosive paint that a kind of solubilising is modified comprises the steps:
(1) pouring a certain amount of potassium silicate solution and sodium silicate solution in container Hybrid Heating, temperature controls at 50-70 DEG C;
(2), under ceaselessly stirring, it is slowly added dropwise the Ludox of metering so that it is be sufficiently mixed;
Certain Di(dioctylpyrophosphato) ethylene titanate amine salt chelate measured and alkane is added the most again in container
Base phenol poly(ethylene oxide) ether, high-speed stirred is uniform;
(4) stop heating, when temperature is down to room temperature, add silicone acrylic emulsion;
(5) the last zinc powder adding a certain amount of 700 mesh, continuously stirred uniformly after the modified zinc-rich anticorrosion of a kind of solubilising
Coating.
The present invention has following advantages and a characteristic:
(1) the zinc-rich anti-corrosive paint prepared is the best;
(2) preparation technology is simply, easily operate.
Detailed description of the invention
Embodiment one:
50g potassium silicate solution and 50g sodium silicate solution are poured into respectively in a container and mix, and be mixed thing heating, heating
Temperature controls, at about 50 DEG C, ceaselessly to stir with blender.In whipping process, then it is slowly added dropwise 300g Ludox, dropping
After, then toward container adds Di(dioctylpyrophosphato) ethylene titanate amine salt chelate and the alkane of 20g of 30g
Base phenol poly(ethylene oxide) ether, and mixing speed will be improved, stop heating after 5 minutes, when temperature is down to room temperature, add 250g
Silicone acrylic emulsion, finally adds the 700 mesh zinc powders of 300g, continuously stirred uniformly after the modified zinc-rich anticorrosion of a kind of solubilising is coated with
Material.
Embodiment two:
70g potassium silicate solution and 70g sodium silicate solution are poured into respectively in a container and mix, and be mixed thing heating, heating
Temperature controls, at about 60 DEG C, ceaselessly to stir with blender.In whipping process, then it is slowly added dropwise 300g Ludox, dropping
After, then toward container adds Di(dioctylpyrophosphato) ethylene titanate amine salt chelate and the alkane of 25g of 35g
Base phenol poly(ethylene oxide) ether, and mixing speed will be improved, stop heating after 5 minutes, when temperature is down to room temperature, add
300g silicone acrylic emulsion, finally adds the 700 mesh zinc powders of 200g, continuously stirred uniformly after the modified zinc-rich of a kind of solubilising is prevented
Rotten coating.
Embodiment three:
100g potassium silicate solution and 100g sodium silicate solution are poured into respectively in a container and mix, and be mixed thing heating, add
Hot temperature controls, at about 70 DEG C, ceaselessly to stir with blender.In whipping process, then it is slowly added dropwise 200g Ludox, drips
After adding, then toward container adds the Di(dioctylpyrophosphato) ethylene titanate amine salt chelate of 70g and 30g
Alkylphenol polyethylene oxide ether, and mixing speed will be improved, stop heating after 5 minutes, when temperature is down to room temperature, add
200g silicone acrylic emulsion, finally adds the 700 mesh zinc powders of 300g, continuously stirred uniformly after the modified zinc-rich of a kind of solubilising is prevented
Rotten coating.
Claims (2)
1. the zinc-rich anti-corrosive paint that a solubilising is modified, it is characterised in that the preparation method of this coating comprises the following steps:
(1) pouring a certain amount of potassium silicate solution and sodium silicate solution in container Hybrid Heating, temperature controls at 50-70 DEG C;
(2), under ceaselessly stirring, it is slowly added dropwise the Ludox of metering so that it is be sufficiently mixed;
Certain Di(dioctylpyrophosphato) ethylene titanate amine salt chelate measured and alkane is added the most again in container
Base phenol poly(ethylene oxide) ether, high-speed stirred is uniform;
(4) stop heating, when temperature is down to room temperature, add silicone acrylic emulsion;
(5) the last zinc powder adding a certain amount of 700 mesh, continuously stirred uniformly after the modified zinc-rich anticorrosion of a kind of solubilising
Coating.
The zinc-rich anti-corrosive paint that a kind of solubilising the most according to claim 1 is modified, it is characterised in that this coating composition content
Mass percent be: potassium silicate 5%-10%, sodium silicate 5%-10%, Ludox 20%-40%, double (two octyloxy pyrophosphoric acid ester groups)
Ethylene titanate esters amine salt chelate Di(dioctylpyrophosphato) ethylene titanate amine salt chelate, alkyl phenol polycyclic oxygen second
Alkane ether 2%-3%, silicone acrylic emulsion 20%-30%, zinc powder 20%-30%.