CN106543772A - The special compounding dispersed blue dye of dacron ultrafine fiber - Google Patents
The special compounding dispersed blue dye of dacron ultrafine fiber Download PDFInfo
- Publication number
- CN106543772A CN106543772A CN201610902274.9A CN201610902274A CN106543772A CN 106543772 A CN106543772 A CN 106543772A CN 201610902274 A CN201610902274 A CN 201610902274A CN 106543772 A CN106543772 A CN 106543772A
- Authority
- CN
- China
- Prior art keywords
- blue dye
- dispersed blue
- parts
- carrier
- alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of special compounding dispersed blue dye of superfine fibre, it is made up of dispersed blue dye main body, water-solubility carrier, alcohol-soluble carrier and auxiliary agent, according to the mass fraction, 1～5 part of 50 parts of dispersed blue dye main body, 10～20 parts of water-solubility carrier, 10～20 parts of alcohol-soluble carrier and auxiliary agent.Special compounding dispersed blue dye provided by the present invention has that high intensity, high color fastness, heat-resist, chromatophilia be good, equalization is good and uncomplicated laundering.
Description
Technical field
The invention belongs to technical field of fine, and in particular to a kind of dacron ultrafine fiber is special to compound disperse blue dye
Material.
Background technology
Dacron ultrafine fiber be it is a kind of with high-quality, high-performance, high technology content, high added value new product.It
Monofilament linear density is more much lower than conventional polyester fiber, and this just imparts its excellent taking different from conventional polyester fiber
Can, such as moisture absorption, ventilative, soft, plentiful, high resilience, bulkiness and elegant sense etc..Dacron ultrafine fiber is due to line density
It is more much lower than conventional fibre, therefore have the dyeing property different from conventional fibre, this is mainly manifested in dyeing rate, upper dye amount, dyestuff
Enhancing, color depth, level-dyeing property, migration property, bright-colored degree and dyefastness etc. and conventional fibre have significantly difference.
The surface area that line density low strap comes increases, to the dye adsorption increase for conciliating suction degree when causing dyeing first, degree of absorption
Increase result in the decline of the increase, wet fastness and fastness to light of dyeing rate, next to that causing the depth of dyed fabric
Reduce.Improve the dyeability of dacron ultrafine fiber and fabric, become enterprise's topic very interested.In fact, superfine fibre is
The one kind for the fibre in differentiation for quickly growing in recent years, is referred to as the synthetic fibers of a new generation, is a kind of high-quality, high-tech
Textile raw material, is the Typical Representative of the shin-gosen that chemical fibre develops to high-tech, high summylation direction.Superfine fibre, also known as
Super fine denier.(denier is the Denier unit of fiber, and a long silk of 9000 meters of grammes per square metre is denier, and the Denier unit of silkworm silk is 1.1 denier).Because
It is than traditional fiber finer, so more more fluffy than general fiber, soft sense of touch, and the easy wrinkle of natural fiber, people can be overcome
Make the air-locked shortcoming of fiber.Additionally, it also have it is warming, not mouldy, stay without worm, many such as light weight, waterproof can not be substituted
Good characteristic.The kind of superfine fibre has super fine denier viscose, super fine denier Polyamide Yarns, superfine denier polyester silk, Super-fine polyacrylic
Etc..Superfine fibre is due to diameter very little, therefore its bending stiffness very little, fabric hand particularly soft；The ratio table of superfine fibre
Area is very big, therefore the spreadability of Superfine Fibre Fabric, bulkiness and warmth retention property are significantly improved, the big fiber of specific surface area and ash
The number of times of dirt or greasy dirt contact is more, and greasy dirt is more from the chance of gap penetration between fiber surface, therefore with extremely strong
Cleaning function；Superfine fibre is made into super high density fabric, interfibrous space between drop diameter and water vapour diameter of droplets it
Between, therefore ultra-fine fabrics have good waterproof and breathable effect；Superfine fibre has many fine holes between microfibre,
Form capillary tube construction, if being processed into the towel-like cloth that can be spontaneously wet out by water, with high-hydroscopicity, washed Hair grooming this
Plant towel to sop up moisture content quickly, make hair quick-drying.
Superfine fibre filament number and individual filament cross section diameter are less than any natural fiber, and fiber is thinner, identical special number
In the section of yarn, number of fiber is more, and fiber total surface area is big.Although strength of filament is little, and the overall strength of yarn is higher；It is ultra-fine
The monofilament resistance of stiffness and bending of fiber is relatively low, adds the structure of multifilament so that Superfine Fibre Fabric have excellent drapability,
It is soft；Very close fabric can be formed using superfine fibre, so that its feature is improved, waterproof, Radix Saposhnikoviae, thoroughly
Wet, thermal insulation is improved, and with silk sample outward appearance, gloss is soft.
As dacron ultrafine fiber has the advantages that the above, therefore increasingly by the very intimate of market, then, its dyeing is
Topic is but a difficult problem, as the big therefore dye adsorption and fast dye speed of its specific surface area is high, causes to be difficult to even dyeing.By
Irregular in its cross section, surface is not smooth enough, light is reflected and is scattered by force, caused color rendering propertiess poor, obtain color shallow.Due to its surface
Rough, section is irregular, and loose colour is difficult to clean, and causes dry labor, wet labor to decline.As its amorphous region ratio is high, easy heat is moved
Move, cause its heat-resisting, fastness to light to decline.Thus the requirement to dyestuff is high！Therefore a kind of special dyestuff is needed to expire
The particular/special requirement of sufficient superfine fibre.
The content of the invention
Goal of the invention：For weak point of the prior art, the invention provides a kind of dacron ultrafine fiber is special multiple
With dispersed blue dye.
Technical scheme：The special compounding dispersed blue dye of dacron ultrafine fiber provided by the present invention, by dispersed blue dye master
Body, water-solubility carrier, alcohol-soluble carrier and auxiliary agent composition, according to the mass fraction, 50 parts of dispersed blue dye main body, water-solubility carrier
1～5 part of 10～20 parts, 10～20 parts of alcohol-soluble carrier and auxiliary agent；The structural formula of described dispersed blue dye main body is
Further, described auxiliary agent is defoamer, dispersant and surfactant.
Further, the mass ratio of described auxiliary agent each component is：0.2～1 part of defoamer, 0.5～2.5 part of dispersant
With 0.3～1.5 part of surfactant.
Further, compound of the dispersant for Leax85A and MF, ratio is 3：7.
Further, surfactant is T-77.
Further, water-solubility carrier is sodium alginate；Described described alcohol-soluble carrier is ethyl cellulose.
Beneficial effect：The dyestuff of the present invention have that high intensity, high color fastness, heat-resist, chromatophilia be good, equalization is good and
Uncomplicated laundering.
Specific embodiment：
Embodiment 1
50 parts of dispersed blue dye main body, 10 parts of water-solubility carrier, 10 parts of alcohol-soluble carrier, 0.2～1 part of defoamer, dispersion
0.3～1.5 part of 0.5～2.5 part of agent and surfactant.Above-mentioned raw materials are mixed in proportion, are ground, is then spray-dried, wrapped
Dress, obtains product.Intensity 100% after testing, coloured light：Uniformly, sublimation reliability：210℃*30″.
Embodiment 2
50 parts of dispersed blue dye main body, 20 parts of water-solubility carrier, 20 parts of alcohol-soluble carrier, 1 part of defoamer, dispersant 2.5
1.5 parts of part and surfactant.Above-mentioned raw materials are mixed in proportion, are ground, is then spray-dried, packed, obtain product.Jing is examined
Survey intensity 100%, coloured light：Uniformly, sublimation reliability：210℃*30″.
Embodiment 3
50 parts of dispersed blue dye main body, 10 parts of water-solubility carrier, 10 parts of alcohol-soluble carrier, 1 part of defoamer, dispersant 2.5
1.5 parts of part and surfactant.Above-mentioned raw materials are mixed in proportion, are ground, is then spray-dried, packed, obtain product.Jing is examined
Survey intensity 100%, coloured light：Uniformly, sublimation reliability：210℃*30″.
Embodiment 4
50 parts of dispersed blue dye main body, 20 parts of water-solubility carrier, 20 parts of alcohol-soluble carrier, 0.2 part of defoamer, dispersant
0.5 part and 0.3 part of surfactant.Above-mentioned raw materials are mixed in proportion, are ground, is then spray-dried, packed, obtain product.
Intensity 100% after testing, coloured light：Uniformly, sublimation reliability：210℃*30″.
Embodiment 5
50 parts of dispersed blue dye main body, 10 parts of water-solubility carrier, 20 parts of alcohol-soluble carrier, 1 part of defoamer, dispersant 0.5
1.5 parts of part and surfactant.Above-mentioned raw materials are mixed in proportion, are ground, is then spray-dried, packed, obtain product.Jing is examined
Survey intensity 100%, coloured light：Uniformly, sublimation reliability：210℃*30″.
Claims (6)
1. the special compounding dispersed blue dye of a kind of dacron ultrafine fiber, it is characterised in that carried by dispersed blue dye main body, water solublity
Body, alcohol-soluble carrier and auxiliary agent composition, according to the mass fraction, 50 parts of dispersed blue dye main body, 10～20 parts of water-solubility carrier, alcohol
1～5 part of 10～20 parts of solubleness carrier and auxiliary agent；The structural formula of described dispersed blue dye main body is
2. compounding dispersed blue dye according to claim 1, it is characterised in that described auxiliary agent be defoamer, dispersant and
Surfactant.
3. compounding dispersed blue dye according to claim 2, it is characterised in that the mass ratio of described auxiliary agent each component
For：0.3～1.5 part of 0.2～1 part of defoamer, 0.5～2.5 part of dispersant and surfactant.
4. compounding dispersed blue dye according to claim 1, it is characterised in that described dispersant is Leax85A's and MF
Compound, ratio are 3：7.
5. compounding dispersed blue dye according to claim 1, it is characterised in that described surfactant is T-77.
6. compounding dispersed blue dye according to claim 1, it is characterised in that described water-solubility carrier is sodium alginate；
Described described alcohol-soluble carrier is ethyl cellulose.