CN106543740A - A kind of automobile excellent nitrile rubber composite damping material of sound absorbing capabilities and preparation method thereof - Google Patents
A kind of automobile excellent nitrile rubber composite damping material of sound absorbing capabilities and preparation method thereof Download PDFInfo
- Publication number
- CN106543740A CN106543740A CN201610882450.7A CN201610882450A CN106543740A CN 106543740 A CN106543740 A CN 106543740A CN 201610882450 A CN201610882450 A CN 201610882450A CN 106543740 A CN106543740 A CN 106543740A
- Authority
- CN
- China
- Prior art keywords
- parts
- nitrile rubber
- damping material
- nbr
- mah
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of excellent nitrile rubber composite damping material of automobile sound absorbing capabilities, is made up of the raw material of following weight portion:47 65 parts of nitrile rubber, 26 36 parts of chlorinated scoline, 130 160 parts of tetrahydrofuran, 40 58 parts of maleic anhydride, 16 parts of benzoyl peroxide, appropriate amount of ethanol, 25 parts of hydroxide sodium hypophosphite, appropriate dimethylbenzene, 26 38 parts of cork fibrous, 12 parts of stearic acid, 48 parts of white carbon black, 12 parts of sulfur, 47 parts of hollow aluminosilicate ball, 26 parts of spherical white Vermiculitum, 37 parts of Pulvis Talci.The present invention is grafted nitrile rubber using maleic anhydride, then compound with cork fibrous grafting, on the one hand strengthen the internal friction resistance of rubber molecular chain activity, the damping capacity of reinforcing material, on the other hand the sqouynd absorption lowering noise performance of damping material is improved using the characteristic of cork fibrous, prepare a kind of nitrile rubber damping material of damping noise reduction excellent performance.
Description
Technical field
The invention belongs to auto parts preparation field, and in particular to a kind of automobile is multiple with the excellent nitrile rubber of sound absorbing capabilities
Close damping material and preparation method thereof.
Background technology
Damping material is that a kind of material of damping noise reduction developed in recent years can be converted into heat vibration and acoustic energy
The new function material that can be dissipated, extensively applies in various plant equipment, front panel especially in the automobile seat room, car
There is application at the 8-12 position such as door, car roof, car bottom plate, boot, therefore researches and develops the new of excellent combination property
Efficient Damping material has become the focus of domestic and international concern.
What Tian Min, Lu Xun et al. were delivered《The preparation and performance study of blending type wide temperature zone high damping elastomeric material》One is literary
In, using having intensive pending methyl group, the chlorinated scoline of low pole to be blended with highly polar nitrile rubber in molecular structure, make
Binary CIIR/NBR blend is obtained, due to sterically hindered effect big in low pole rubber structure and the pressure after vulcanization crosslinking
Winding, it will increase the internal friction resistance of polar rubber strand activity, cause molecular chain movement to be obstructed, prepare wide temperature range
Damping material.
In nature, cork is a kind of very excellent material of damping performance, and it is the crust product of cork tree, is had
The performances such as good elasticity, sealing, heat-insulated, sound insulation, insulation, wear-resisting, corrosion resistance, protection against the tide, fire prevention, damping, can be used as ground
Plate, bottle stopper and woodwind instrument sealing gasket, packaging and energy absorbing material, heat-barrier material, damping damping material etc., are a kind of many work(
Can natural material.
Therefore, the present invention is grafted nitrile rubber using maleic anhydride, compounds with cork fibrous grafting then, on the one hand strengthens
On the other hand the internal friction resistance of rubber molecular chain activity, the damping capacity of reinforcing material is improved using the characteristic of cork fibrous
The sqouynd absorption lowering noise performance of damping material, prepares a kind of nitrile rubber damping material of damping noise reduction excellent performance.
The content of the invention
The invention aims to solve the problems, such as that existing damping material damping, sound absorbing capabilities are not enough, there is provided a kind of vapour
Excellent nitrile rubber composite damping material of automobile-used sound absorbing capabilities and preparation method thereof.
A kind of automobile excellent nitrile rubber composite damping material of sound absorbing capabilities, is made up of the raw material of following weight portion:
Nitrile rubber 47-65 parts, chlorinated scoline 26-36 parts, tetrahydrofuran 130-160 parts, maleic anhydride 40-58 parts, peroxidating
Benzoyl 1-6 parts, appropriate amount of ethanol, hydroxide sodium hypophosphite 2-5 parts, appropriate dimethylbenzene, cork fibrous 26-38 parts, stearic acid 1-2
Part, white carbon black 4-8 parts, sulfur 1-2 parts, hollow aluminosilicate ball 4-7 parts, spherical white Vermiculitum 2-6 parts, Pulvis Talci 3-7 parts.
Comprise the following steps that:
(1)Maleic anhydride is grafted nitrile rubber(MAH-g-NBR)Preparation:
Nitrile rubber is dissolved completely in tetrahydrofuran, maleic anhydride is added dropwise over benzoyl peroxide with Dropping funnel
Mixed solution, is passed through nitrogen protection, is warming up to 60-72 DEG C, and isothermal reaction 6-9 hours go out graft product with ethanol precipitation afterwards,
With washing with alcohol for several times, the graft product after washing is placed in 38-45 DEG C of vacuum drying oven and is dried, that is, obtain MAH-g-NBR,
It is standby;
(2)MAH-g-NBR is grafted cork fibrous:
Dimethylbenzene, hydroxide sodium hypophosphite and step are added in the boiling flask equipped with condensing tube(1)The MAH-g- for obtaining
NBR, afterwards by the abundant cork fibrous immersion mixed solution being dried, control temperature reacts 2-4 hours at 125-140 DEG C,
After the completion of reaction, solvent is removed with Soxhlet extractor, dried to constant weight in 95-105 DEG C, obtain final product MAH-g-NBR grafting corks fine
Dimension;
(3)Mixing:
1., hollow aluminosilicate ball, spherical white Vermiculitum and Pulvis Talci are added in deionized water, is filtered after being uniformly mixed, will
Filter cake is dried to constant weight under the conditions of 95-105 DEG C, and grinding is sieved, and obtains mixed fillers, standby;
2., under the conditions of 20-30 DEG C, by step(2)The MAH-g-NBR for obtaining is grafted cork fibrous, chlorinated scoline mixing
Uniformly plasticate on a mill 3-8 minutes;
3. stearic acid, white carbon black and above-mentioned mixed fillers mixing 20-40 minutes, are subsequently adding, add sulfur mixing uniform afterwards,
It is prepared into elastomeric compound;
(4)Sulfuration:
By step(3)7-9 hours are stood after the thin pass-out piece of resulting elastomeric compound, on vulcanizing press at 160-190 DEG C
Hot press moulding vulcanizes 20-40 minutes, and a kind of automobile excellent nitrile rubber composite damping material of sound absorbing capabilities is obtained.
Wherein, described cork fibrous are formed with the white softwood pulp plate mechanical dissociation of useless industrial source and dispersion, its length
Distribution 2mm-3.5mm, width distribution are 34.2 μm -73.1 μm, and length-width ratio is 72.6.
Compared with prior art, the present invention has advantages below:
(1)The present invention carries out graft modification first by maleic anhydride monomer to nitrile rubber, changes the polarity of nitrile rubber, increases
The internal friction resistance of additive polarity nitrile rubber strand activity, causes molecular chain movement to be obstructed, and molecule interchain frictional heat increases,
Damping capacity is more excellent.
(2)There are many gauffers on cork cell wall, can greatly alleviate compression, therefore elastic return is special
Good, the special cellularity of cork fibrous can weaken flat ripple and propagate in addition, enable in particular to the propagation of noise-reducing sound wave, thus soft
The sound absorption properties of wood utilizes this characteristic of cork fibrous very well in the present invention, be grafted nitrile rubber using maleic anhydride(MAH-g-
NBR)Cork fibrous are carried out with graft modification, the compatibility of the cork fibrous in rubber matrix is improved, subtracting for damping material is improved
Shake, sqouynd absorption lowering noise performance, can be effectively improved the comfort level of environment inside car, be conducive to the physical and mental health of people.
(3)Spherical white Vermiculitum, hollow aluminosilicate ball and layer structure are added in the raw material of composite damping material of the present invention
Pulvis Talci, this different materials density and hardness is relatively low, is respectively provided with the characteristic of bulk porous, and this makes the damping material of present invention preparation
Material possesses good sound absorption characteristics, and can effectively improve the crocking resistance of material.
Specific embodiment
A kind of automobile excellent nitrile rubber composite damping material of sound absorbing capabilities, is made up of the raw material of following weight portion:
Nitrile rubber 60, chlorinated scoline 32, tetrahydrofuran 152, maleic anhydride 55, benzoyl peroxide 4, appropriate amount of ethanol, hydrogen-oxygen
Change sodium hypophosphite 3, appropriate dimethylbenzene, cork fibrous 36, stearic acid 2, white carbon black 4, sulfur 2, hollow aluminosilicate ball 6, spherical white trematodiasiss
Stone 4, Pulvis Talci 5.
Comprise the following steps that:
(1)Maleic anhydride is grafted nitrile rubber(MAH-g-NBR)Preparation:
Nitrile rubber is dissolved completely in tetrahydrofuran, maleic anhydride is added dropwise over benzoyl peroxide with Dropping funnel
Mixed solution, is passed through nitrogen protection, is warming up to 70 DEG C, and isothermal reaction 8 hours goes out graft product with ethanol precipitation afterwards, uses second
Alcohol is washed for several times, the graft product after washing is placed in 40 DEG C of vacuum drying ovens and is dried, that is, obtain MAH-g-NBR, standby;
(2)MAH-g-NBR is grafted cork fibrous:
Dimethylbenzene, hydroxide sodium hypophosphite and step are added in the boiling flask equipped with condensing tube(1)The MAH-g- for obtaining
NBR, afterwards by the abundant cork fibrous immersion mixed solution being dried, control temperature is reacted 3 hours at 130 DEG C, has reacted
Cheng Hou, removes solvent with Soxhlet extractor, dries to constant weight in 100 DEG C, obtains final product MAH-g-NBR grafting cork fibrous;
(3)Mixing:
1., hollow aluminosilicate ball, spherical white Vermiculitum and Pulvis Talci are added in deionized water, is filtered after being uniformly mixed, will
Filter cake is dried to constant weight under the conditions of 100 DEG C, and grinding is sieved, and obtains mixed fillers, standby;
2., under the conditions of 28 DEG C, by step(2)The MAH-g-NBR for obtaining is grafted cork fibrous, chlorinated scoline mix homogeneously
Plasticate on a mill 7 minutes;
3. stearic acid, white carbon black and above-mentioned mixed fillers, are subsequently adding to knead 36 minutes, add sulfur mixing uniform afterwards, system
It is standby to obtain elastomeric compound;
(4)Sulfuration:
By step(3)After the thin pass-out piece of resulting elastomeric compound stand 8 hours, on vulcanizing press at 170 DEG C high temperature mould
Pressure sulfuration 30 minutes, is obtained a kind of automobile excellent nitrile rubber composite damping material of sound absorbing capabilities.
Wherein, described cork fibrous are formed with the white softwood pulp plate mechanical dissociation of useless industrial source and dispersion, its length
Distribution 2mm-3.5mm, width distribution are 34.2 μm -73.1 μm, and length-width ratio is 72.6.
Performance test:
Prepare according to embodiment and its material is tested, it is as a result as follows:
Density:1.193g/cm3, damping performance(23 DEG C, 200HZ):0.16, fracture elongation:597%, tensile strength:
135Mpa, resistance to ag(e)ing:4 grades, light fastness aging:4 grades, roll processability:Well.
Claims (3)
1. a kind of automobile excellent nitrile rubber composite damping material of sound absorbing capabilities, it is characterised in that by following weight portion
Raw material is constituted:Nitrile rubber 47-65 parts, chlorinated scoline 26-36 parts, tetrahydrofuran 130-160 parts, maleic anhydride 40-58
Part, benzoyl peroxide 1-6 parts, appropriate amount of ethanol, hydroxide sodium hypophosphite 2-5 parts, appropriate dimethylbenzene, cork fibrous 26-38 parts,
Stearic acid 1-2 parts, white carbon black 4-8 parts, sulfur 1-2 parts, hollow aluminosilicate ball 4-7 parts, spherical white Vermiculitum 2-6 parts, Pulvis Talci 3-7
Part.
2. preparation of a kind of automobile according to claims 1 with the excellent nitrile rubber composite damping material of sound absorbing capabilities
Method, it is characterised in that comprise the following steps that:
(1)Maleic anhydride is grafted nitrile rubber(MAH-g-NBR)Preparation:
Nitrile rubber is dissolved completely in tetrahydrofuran, maleic anhydride is added dropwise over benzoyl peroxide with Dropping funnel
Mixed solution, is passed through nitrogen protection, is warming up to 60-72 DEG C, and isothermal reaction 6-9 hours go out graft product with ethanol precipitation afterwards,
With washing with alcohol for several times, the graft product after washing is placed in 38-45 DEG C of vacuum drying oven and is dried, that is, obtain MAH-g-NBR,
It is standby;
(2)MAH-g-NBR is grafted cork fibrous:
Dimethylbenzene, hydroxide sodium hypophosphite and step are added in the boiling flask equipped with condensing tube(1)The MAH-g- for obtaining
NBR, afterwards by the abundant cork fibrous immersion mixed solution being dried, control temperature reacts 2-4 hours at 125-140 DEG C,
After the completion of reaction, solvent is removed with Soxhlet extractor, dried to constant weight in 95-105 DEG C, obtain final product MAH-g-NBR grafting corks fine
Dimension;
(3)Mixing:
1., hollow aluminosilicate ball, spherical white Vermiculitum and Pulvis Talci are added in deionized water, is filtered after being uniformly mixed, will
Filter cake is dried to constant weight under the conditions of 95-105 DEG C, and grinding is sieved, and obtains mixed fillers, standby;
2., under the conditions of 20-30 DEG C, by step(2)The MAH-g-NBR for obtaining is grafted cork fibrous, chlorinated scoline mixing
Uniformly plasticate on a mill 3-8 minutes;
3. stearic acid, white carbon black and above-mentioned mixed fillers mixing 20-40 minutes, are subsequently adding, add sulfur mixing uniform afterwards,
It is prepared into elastomeric compound;
(4)Sulfuration:
By step(3)7-9 hours are stood after the thin pass-out piece of resulting elastomeric compound, on vulcanizing press at 160-190 DEG C
Hot press moulding vulcanizes 20-40 minutes, and a kind of automobile excellent nitrile rubber composite damping material of sound absorbing capabilities is obtained.
3. system of a kind of automobile according to claims 1,2 with the excellent nitrile rubber composite damping material of sound absorbing capabilities
Preparation Method, it is characterised in that described cork fibrous are formed with the white softwood pulp plate mechanical dissociation of useless industrial source and dispersion, its
Length distribution range 2mm-3.5mm, width distribution are 34.2 μm -73.1 μm, and length-width ratio is 72.6.