CN106541681A - The gluing method for adhering film of eyeglass - Google Patents
The gluing method for adhering film of eyeglass Download PDFInfo
- Publication number
- CN106541681A CN106541681A CN201611038809.9A CN201611038809A CN106541681A CN 106541681 A CN106541681 A CN 106541681A CN 201611038809 A CN201611038809 A CN 201611038809A CN 106541681 A CN106541681 A CN 106541681A
- Authority
- CN
- China
- Prior art keywords
- tac
- eyeglass
- glue
- pad pastings
- backform
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of gluing method for adhering film of eyeglass, its drip irrigation device is to include following steps：1), from flat-shaped TAC pad pastings, TAC pad pastings thickness is between 0.08 0.5mm；2), the nerve of a covering plate on TAC pad pastings, on web plate, mesh specification is between 100 1000 mesh；3), glue is poured on web plate, the glue viscosity is between 1000 10000cps；4), scraper promotion glue at the uniform velocity will be used after web plate and TAC attachment films, glue is uniformly coated on TAC pad pastings by mesh；5) glue is carried out into semi-solid preparation drying, between 40 80 DEG C, drying time is not more than 10 minutes drying temperature；6) TAC pad pastings being dried into curved, the another side of glue being coated with the backform top TAC pad pastings of heating, the top of backform is arcwall face, and is adapted with the arcwall face of eyeglass, between 100 120 DEG C, baking bent through process control at 4 10 minutes for the heating-up temperature of backform；7), TAC pad pastings are fitted with eyeglass.The method is conducive to the uniform coating of glue, effectively improves yield rate.
Description
Technical field
The present invention relates to glasses processing and manufacturing technical field, more specifically, it relates to a kind of painting bond paper facing side of eyeglass
Method.
Background technology
Have the final lens product of the number of degrees in manufacturing process, be on the basis of Optical blanks distinguish attrition process convex lens face and
Concave mirror surface, makes two minute surfaces reach predetermined curved surface angle, so that eyeglass reaches predetermined diopter；And have the polariscope of the number of degrees
Piece in manufacturing process, be on the basis of final lens product on convex lens face or concave mirror surface fit polarisation substrate so that eyeglass
Possess polarizing function, and need polarisation substrate completely to fit with eyeglass, so as to not interfere with original diopter.
It can thus be appreciated that the pad pasting of eyeglass is fitted on the convex surface or concave surface of eyeglass, regardless of whether glue is coated on eyeglass
Or on pad pasting, glue can be slid along cambered surface downwards, so as to cause glue coating uneven, and then cause eyeglass pad pasting effect
Difference, in addition because glue layer it is uneven make final lens product perspective when produce refraction, cause to scrap.
The content of the invention
In view of the shortcomings of the prior art, it is an object of the invention to provide a kind of gluing method for adhering film of eyeglass, is somebody's turn to do
Method is conducive to the uniform coating of glue, effectively improves yield rate.
For achieving the above object, the invention provides following technical scheme：A kind of gluing method for adhering film of eyeglass, includes
Following steps：
1), from flat-shaped TAC pad pastings, the thickness of the TAC pad pastings is between 0.08-0.5mm；
2), the nerve of a covering plate on TAC pad pastings, the mesh specification on web plate is between 100-1000 mesh；
3), glue is poured on web plate, the viscosity of the glue is between 1000-10000cps；
4), scraper promotion glue at the uniform velocity will be used after web plate and TAC attachment films, glue is uniformly applied by mesh
Overlay on TAC pad pastings；
5) glue being coated on TAC pad pastings is carried out into semi-solid preparation drying, drying temperature between 40-80 DEG C, during drying
Between be not more than 10 minutes；
6) TAC pad pastings being dried into curved, the another side of glue being coated with the backform top TAC pad pastings of heating, the top of backform is
Arcwall face, and the arcwall face of backform is adapted with the arcwall face of eyeglass, the heating-up temperature of backform are dried between 100-120 DEG C
Process control is bent through in 4-10 minutes；
7) curved TAC pad pastings will be dried, to fit with eyeglass.
The present invention is further arranged to：In step 1, the thickness of TAC pad pastings selects 0.3mm.
The present invention is further arranged to：In step 2, the mesh specification on web plate selects 200 mesh.
The present invention is further arranged to：In step 3, the viscosity of glue selects 6000-8000cps.
The present invention is further arranged to：Step 4 is to keeping TAC pad pastings during step 5 under horizontality.
The present invention is further arranged to：In step 5, the semi-solid preparation drying temperature of glue between 60-80 DEG C, drying time
For 5 minutes.
The present invention is further arranged to：In step 6, the heating-up temperature of backform is 110 DEG C, and baking bent through process control at 5 minutes.
The present invention is further arranged to：In step 6 when the arcwall face of backform is adapted with the arc-shaped concave of eyeglass, step
TAC pad pastings are fitted with the arc-shaped concave of eyeglass in 7；And in step 6 when backform arcwall face and eyeglass arc convex phase
During adaptation, need baking curved TAC pad pastings are done anti-folding first in step 7, then TAC pad pastings are fitted with the arc convex of eyeglass.
The present invention is further arranged to：TAC pad pastings before coating glue, the coated side of TAC pad pastings is adopted acetone or
Ethanol is cleaned；Eyeglass was cleaned using acetone or ethanol to the binding face of eyeglass before being fitted with TAC pad pastings.
The present invention is further arranged to：Step 3 started to step 7 finishing control in 30 minutes.
In sum, the invention has the advantages that：Raising glue is conducive to be coated in TAC patches by web plate gluing
Uniformity coefficient on film, so as to effectively improve yield rate during eyeglass pad pasting.
Specific embodiment
With reference to embodiment, the present invention is described in more detail.
A kind of gluing method for adhering film of eyeglass, includes following steps：
1), from flat-shaped TAC pad pastings, the thickness of the TAC pad pastings is between 0.08-0.5mm, and TAC pad pastings
The preferred 0.3mm of thickness.
2), the nerve of a covering plate on TAC pad pastings, the mesh specification on web plate is between 100-1000 mesh；Mesh on web plate
Specification preferably 200 mesh.
3), glue is poured on web plate, the viscosity of the glue is between 1000-10000cps；The viscosity of glue is preferred
6000-8000cps。
4), scraper promotion glue at the uniform velocity will be used after web plate and TAC attachment films, glue is uniformly applied by mesh
Overlay on TAC pad pastings；
5) glue being coated on TAC pad pastings is carried out into semi-solid preparation drying, drying temperature between 40-80 DEG C, during drying
Between be not more than 10 minutes；Preferably between 60-80 DEG C, drying time is preferably 5 minutes the semi-solid preparation drying temperature of glue；
6) TAC pad pastings being dried into curved, the another side of glue being coated with the backform top TAC pad pastings of heating, the top of backform is
Arcwall face, and the arcwall face of backform is adapted with the arcwall face of eyeglass, the heating-up temperature of backform are dried between 100-120 DEG C
Process control is bent through in 4-10 minutes；The heating-up temperature of backform is preferably 110 DEG C, and baking bends through journey and is preferably controlled in 5 minutes.
7) curved TAC pad pastings will be dried, to fit with eyeglass.
Numerical range in such scheme is defined by following purpose：
In step 1, the thickness size of TAC pad pastings affects later stage TAC pad pasting and dries curved processing, and TAC pad pastings are thinner, heating
Backform is easier to be burnt TAC pad pastings, therefore the curved processing of phase baking after an action of the bowels of TAC pad pasting Yue Hou Vietnamese side；But TAC pad pastings are equal with eyeglass
Belong to light transmission medium, and refraction can be produced after different light transmission medium laminatings, therefore TAC pad pastings are thicker, the refractive effect of printing opacity
It is bigger, need choose facilitate molding and do not interfere with have an X-rayed this basic function size range, that is, 0.08-0.5mm it
Between.In addition the preferred 0.3mm of the thickness of TAC pad pastings, it, obtained by Jing practical experiences, is 0.3mm in the thickness of TAC pad pastings to be
When, not only ratio of briquetting is high, while affecting also relatively controllable to the perspective of eyeglass.
In step 2, when the mesh of web plate is less than 100 mesh, glue is poured into, it is impossible to controlled
When glue water coats uniformity coefficient, and the mesh of web plate more than 1000 mesh, the stickiness that glue is carried makes it difficult to be pushed through by scraper
Mesh, therefore inefficiency.It is preferred that the mesh specification on web plate is 200 mesh, it is 6000-8000cps so as to be conducive to viscosity
Glue be pushed on TAC pad pastings by scraper.
In step 3, when the viscosity of glue is less than 1000cps, glue is diluter, and easily the mesh from web plate is directly flowed down
Go, it is impossible to control glue coating uniformity coefficient, when the viscosity of glue is more than 10000cps, glue stickiness makes it difficult to by force very much be scraped
Knife pushes through mesh, therefore inefficiency.Glue of the preferred viscosities for 6000-8000cps, so as to be conducive to using mesh specification
Web plate for 200 mesh is pushed on TAC pad pastings by scraper.
In step 4, scraper promotes glue remain a constant speed, so as to the glue for being conducive to being coated on TAC pad pastings is protected
Hold uniform, and step 4 so can be avoided because of TAC to needing to keep TAC pad pastings under horizontality during step 5
The inclination of pad pasting and the glue slide downward that makes to be coated on TAC pad pastings, affect glue coating uniformity coefficient.
In step 5, drying temperature needs glue to reach semi-solid preparation when being less than 40 DEG C needs the time longer, and efficiency is low, and warm
Again easily by drying adhesive, manipulation inconvenience when degree is higher than 80 DEG C, therefore its preferred drying temperature is arranged between 60-80 DEG C,
Drying time is 5 minutes, plays the optimization manipulation of glue semi-solid preparation.
In step 6, as TAC pad pastings need to carry out web plate gluing in a flat state, and eyeglass is arcwall face, therefore
Need to be dried curved, curved operations are dried in many heating using backform in prior art, it is noted that backform can not one in which
TAC pad pastings top to anticipated shape is needed to separate repeatedly top TAC pad pastings by secondary property, at the same backform it is tentative when can not rollback, after rollback
Easily make TAC pad pastings form gauffer, so as to scrap, therefore during normal operation, be that heating backform heads on TAC pad pastings and moves a certain distance
After suspend, then backform is continued to move to, then is suspended, until TAC pad pasting deformation is to anticipated shape.And the temperature of backform is less than 100
DEG C when, not enough, TAC pad pastings are easily pulled for the temperature of backform, or even damaged, and percent defective is high；When the temperature of backform is higher than 120 DEG C,
Relatively thin AC pad pastings are easily burnt by backform, cause percent defective high.Therefore the heating-up temperature of backform is set to into 110 DEG C preferably,
Baking bent through process control at 5 minutes, was conducive to improving the yield rate of AC pad pastings.
In step 7 it should be noted that, when in step 6, the arcwall face of backform is adapted with the arc-shaped concave of eyeglass, TAC patch
The arcwall face of film deformation is adapted with the arc-shaped concave of eyeglass, thus in step 7 be by TAC pad pastings be coated with the one side of glue with
The arc-shaped concave of eyeglass is fitted；And in step 6 when the arcwall face of backform is adapted with the arc convex of eyeglass, TAC pad pastings
The arcwall face of deformation is adapted with the arc convex of eyeglass, therefore needs baking curved TAC pad pastings are done anti-folding first in step 7,
The glue one side being exactly originally coated on the outside of arc TAC pad pastings, manually breaks the mode of folding, by soft TAC pad pastings
Turn, so that the one side for being coated with glue becomes the inner side of arc TAC pad pastings, then arc TAC pad pastings are coated with into glue
The medial surface of water is fitted with the arc convex of eyeglass.
Control is additionally needed, starts to step 7 to terminate from step 3, all times need control in 30 minutes, keep away
Exempt from glue to expose overlong time in atmosphere and reduce its stickiness, affect bonding effect.
And TAC pad pastings before coating glue needed the coated side of TAC pad pastings is wiped using acetone or ethanol
Wash, its effect is, for removing the impurity in the coated side of TAC pad pastings, spot even oils and fatss, to be conducive to improving glue coating
In the stickiness of TAC pad pastings, it is to avoid because of the yield rate of impurity effect eyeglass pad pasting.
Eyeglass is before fitting with TAC pad pastings simultaneously, it is also desirable to which the binding face of eyeglass is carried out using acetone or ethanol
Clean, its effect is equally for removing the impurity on the binding face of eyeglass, spot even oils and fatss, when being conducive to improving pad pasting
With the firmness of eyeglass bonding, it is to avoid because of the yield rate of impurity effect eyeglass pad pasting.
The above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned enforcement
Example, all technical schemes belonged under thinking of the present invention belong to protection scope of the present invention.It should be pointed out that for the art
Those of ordinary skill for, some improvements and modifications without departing from the principles of the present invention, these improvements and modifications
Should be regarded as protection scope of the present invention.
Claims (10)
1. a kind of gluing method for adhering film of eyeglass, is characterized in that：Include following steps：
1), from flat-shaped TAC pad pastings, the thickness of the TAC pad pastings is between 0.08-0.5mm；
2), the nerve of a covering plate on TAC pad pastings, the mesh specification on web plate is between 100-1000 mesh；
3), glue is poured on web plate, the viscosity of the glue is between 1000-10000cps；
4), scraper promotion glue at the uniform velocity will be used after web plate and TAC attachment films, glue is uniformly coated in by mesh
On TAC pad pastings；
5) glue being coated on TAC pad pastings is carried out into semi-solid preparation drying, between 40-80 DEG C, drying time is or not drying temperature
More than 10 minutes；
6) TAC pad pastings being dried into curved, the another side of glue being coated with the backform top TAC pad pastings of heating, the top of backform is arc
Face, and the arcwall face of backform is adapted with the arcwall face of eyeglass, between 100-120 DEG C, baking bends through for the heating-up temperature of backform
Process control is in 4-10 minutes；
7) curved TAC pad pastings will be dried, to fit with eyeglass.
2. the gluing method for adhering film of eyeglass according to claim 1, is characterized in that：In step 1, the thickness gauge of TAC pad pastings
Very little selection 0.3mm.
3. the gluing method for adhering film of eyeglass according to claim 1, is characterized in that：Mesh specification in step 2, on web plate
From 200 mesh.
4. the gluing method for adhering film of eyeglass according to claim 1, is characterized in that：In step 3, the viscosity of glue is selected
6000-8000cps。
5. the gluing method for adhering film of eyeglass according to claim 1, is characterized in that：Step 4 is kept to during step 5
TAC pad pastings are under horizontality.
6. the gluing method for adhering film of eyeglass according to claim 1, is characterized in that：In step 5, the semi-solid preparation drying of glue
Between 60-80 DEG C, drying time is 5 minutes to temperature.
7. the gluing method for adhering film of eyeglass according to claim 1, is characterized in that：In step 6, the heating-up temperature of backform is
110 DEG C, baking bent through process control at 5 minutes.
8. the gluing method for adhering film of the eyeglass according to any one in claim 1-7, is characterized in that：Work as top in step 6
When the arcwall face of mould is adapted with the arc-shaped concave of eyeglass, TAC pad pastings are fitted with the arc-shaped concave of eyeglass in step 7；And
In step 6 when the arcwall face of backform is adapted with the arc convex of eyeglass, need first to do baking curved TAC pad pastings in step 7
Anti- folding, then TAC pad pastings are fitted with the arc convex of eyeglass.
9. the gluing method for adhering film of the eyeglass according to any one in claim 1-7, is characterized in that：TAC pad pastings are being applied
Before covering glue, the coated side of TAC pad pastings is cleaned using acetone or ethanol；Eyeglass before fitting with TAC pad pastings,
The binding face of eyeglass is cleaned using acetone or ethanol.
10. the gluing method for adhering film of the eyeglass according to any one in claim 1-7, is characterized in that：Step 3 start to
Step 7 finishing control is in 30 minutes.