CN106521612A - Novel environmental-friendly electrolysis hanger stripping powder - Google Patents
Novel environmental-friendly electrolysis hanger stripping powder Download PDFInfo
- Publication number
- CN106521612A CN106521612A CN201610854305.8A CN201610854305A CN106521612A CN 106521612 A CN106521612 A CN 106521612A CN 201610854305 A CN201610854305 A CN 201610854305A CN 106521612 A CN106521612 A CN 106521612A
- Authority
- CN
- China
- Prior art keywords
- hanger
- powder
- sodium
- alum
- protective agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of hanger electrolysis, in particular to novel environmental-friendly electrolysis hanger stripping powder. The novel environmental-friendly electrolysis hanger stripping powder comprises, by weight, 15-20 g/l of sodium sulfate, 30-40 g/l of sodium nitrate, 15-20 g/l of sodium borate, 20-30 g/l of a stainless steel protective agent, 2-3 g/l of an accelerant A and 2-3 g/l of alums, and can remove a copper-nickel-chromium coating on a stainless steel hook of an electroplating hanger at a time without damaging the hook. The stainless steel hanger is electroplated again after deplating, the binding force of a hook coating is good, and slag falling and burrs are not prone to occurring; and the powder does not contain a complexing agent which is hard to treat by sewage.
Description
Technical field
The present invention relates to hanger electrolysis field, is in particular that a kind of novel environment friendly electrolytic hanger peels off powder.
Background technology
In plating production process, need to use repeatedly stainless steel hanger, traditional method is to use nitric acid strip, can produce big
Amount tobacco, current electrolytic hanger peel off powder, though nitric acid is instead of, because containing a large amount of complexing agents, sewage is difficult to process.
The content of the invention
The invention mainly solves the technical problem of providing a kind of novel environment friendly electrolytic hanger peels off powder, disposably can strip
The copper-nickel-chrome plating of Electropolating hangers stainless steel gib head, does not hinder gib head;Re-plating after stainless steel hanger strip, gib head binding force of cladding material
It is good, it is difficult quarrel grain raising;Without the intractable complexing agent of sewage.
For solving above-mentioned technical problem, the present invention relates to hanger electrolysis field, is in particular a kind of novel environment friendly electricity
Solution hanger peels off powder, including sodium sulphate, sodium nitrate, Boratex, stainless protective agent, accelerator and alum, can disposably strip electricity
The copper-nickel-chrome plating of plating hanger stainless steel gib head, does not hinder gib head;Re-plating after stainless steel hanger strip, gib head binding force of cladding material
It is good, it is difficult quarrel grain raising;Without the intractable complexing agent of sewage.
In described formula, each composition is respectively by weight proportion:15-20 g/l of sodium sulphate, 30-40 g/l of sodium nitrate,
15-20 g/l of Boratex, 20-30 g/l of stainless protective agent, accelerant A 2-3 g/l, 2-3 g/l of alum.
Used as the further optimization of the technical program, a kind of novel environment friendly electrolytic hanger of the invention peels off the formula described in powder
In each composition be specially by weight proportion:15 g/l of sodium sulphate, 30 g/l of sodium nitrate, 15 g/l of Boratex, stainless protective agent
20 g/l, 2 g/l of accelerant A, 2 g/l of alum.
Used as the further optimization of the technical program, a kind of novel environment friendly electrolytic hanger of the invention peels off the formula described in powder
In each composition be specially by weight proportion:20 g/l of sodium sulphate, 40 g/l of sodium nitrate, 20 g/l of Boratex, stainless protective agent
30 g/l, 3 g/l of accelerant A, 3 g/l of alum.
Used as the further optimization of the technical program, a kind of novel environment friendly electrolytic hanger of the invention peels off the formula described in powder
In each composition be specially by weight proportion:17.5 g/l of sodium sulphate, 35 g/l of sodium nitrate, 17.5 g/l of Boratex, stainless guarantor
25 g/l of agent of shield, 2.5 g/l of accelerant A, 2.5 g/l of alum.
A kind of novel environment friendly electrolytic hanger of the present invention peels off having the beneficial effect that for powder:
A kind of novel environment friendly electrolytic hanger of the present invention peels off powder, can disposably strip the cupro-nickel chromium plating of Electropolating hangers stainless steel gib head
Layer, does not hinder gib head;Re-plating after stainless steel hanger strip, gib head binding force of cladding material are good, are difficult quarrel grain raising;It is difficult without sewage
The complexing agent of process.
Specific embodiment
Specific embodiment one:
The present invention relates to hanger electrolysis field, is in particular that a kind of novel environment friendly electrolytic hanger peels off powder, including sodium sulphate,
Sodium nitrate, Boratex, stainless protective agent, accelerator and alum, can disposably strip the cupro-nickel chromium of Electropolating hangers stainless steel gib head
Coating, does not hinder gib head;Re-plating after stainless steel hanger strip, gib head binding force of cladding material are good, are difficult quarrel grain raising;Without sewage
Intractable complexing agent.
In described formula, each composition is respectively by weight proportion:15-20 g/l of sodium sulphate, 30-40 g/l of sodium nitrate,
15-20 g/l of Boratex, 20-30 g/l of stainless protective agent, accelerant A 2-3 g/l, 2-3 g/l of alum.
Specific embodiment two:
Present embodiment is described further to embodiment one, and in described formula, each composition is specially by weight proportion:Sulphur
15 g/l of sour sodium, 30 g/l of sodium nitrate, 15 g/l of Boratex, 20 g/l of stainless protective agent, 2 g/l of accelerant A, alum 2
G/l.
Specific embodiment three:
Present embodiment is described further to embodiment one, and in described formula, each composition is specially by weight proportion:Sulphur
20 g/l of sour sodium, 40 g/l of sodium nitrate, 20 g/l of Boratex, 30 g/l of stainless protective agent, 3 g/l of accelerant A, alum 3
G/l.
Specific embodiment four:
Present embodiment is described further to embodiment one, and in described formula, each composition is specially by weight proportion:Sulphur
17.5 g/l of sour sodium, 35 g/l of sodium nitrate, 17.5 g/l of Boratex, 25 g/l of stainless protective agent, 2.5 grams of accelerant A/
Liter, 2.5 g/l of alum.
Preparing process:After above-mentioned six kinds of raw material are well mixed, bag distribution packaging.
Proportioning is carried out by each composition Different Weight percentage so that the performance height of the product for obtaining differs.
Certainly, described above not limitation of the present invention, the present invention are also not limited to the example above, the art
Change, remodeling, addition or replacement that those of ordinary skill is made in the essential scope of the present invention, fall within the guarantor of the present invention
Shield scope.
Claims (4)
1. a kind of novel environment friendly electrolytic hanger peels off powder, it is characterised in that:Described formula includes sodium sulphate, sodium nitrate, boric acid
Sodium, stainless protective agent, accelerator and alum, in described formula, each composition is respectively by weight proportion:15-20 gram of sodium sulphate/
It is liter, 30-40 g/l of sodium nitrate, 15-20 g/l of Boratex, 20-30 g/l of stainless protective agent, accelerant A 2-3 g/l, bright
2-3 g/l of alum.
2. a kind of novel environment friendly electrolytic hanger according to claim 1 peels off powder, it is characterised in that each in described formula
Composition is specially by weight proportion:15 g/l of sodium sulphate, 30 g/l of sodium nitrate, 15 g/l of Boratex, stainless protective agent 20
G/l, 2 g/l of accelerant A, 2 g/l of alum.
3. a kind of novel environment friendly electrolytic hanger according to claim 1 peels off powder, it is characterised in that each in described formula
Composition is specially by weight proportion:20 g/l of sodium sulphate, 40 g/l of sodium nitrate, 20 g/l of Boratex, stainless protective agent 30
G/l, 3 g/l of accelerant A, 3 g/l of alum.
4. a kind of novel environment friendly electrolytic hanger according to claim 1 peels off powder, it is characterised in that each in described formula
Composition is specially by weight proportion:17.5 g/l of sodium sulphate, 35 g/l of sodium nitrate, 17.5 g/l of Boratex, stainless protective agent
25 g/l, 2.5 g/l of accelerant A, 2.5 g/l of alum.