CN106520286A - Preparation method for quick-drying antirust oil - Google Patents
Preparation method for quick-drying antirust oil Download PDFInfo
- Publication number
- CN106520286A CN106520286A CN201610892962.1A CN201610892962A CN106520286A CN 106520286 A CN106520286 A CN 106520286A CN 201610892962 A CN201610892962 A CN 201610892962A CN 106520286 A CN106520286 A CN 106520286A
- Authority
- CN
- China
- Prior art keywords
- oil
- antirust oil
- parts
- subsequently
- lemon grass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method for quick-drying antirust oil and belongs to the technical field of chemical engineering. The preparation method comprises the following steps: heating and stirring dried and ground lemon-grass stem and leaf particles with deionized water; extracting lemon-grass essential oil; taking alkyl alcohol, ketene dimer and the like for a water-bath reaction; adjusting the pH with alkaline liquor; after filtration and concentration, mixing the mixture with the lemon-grass essential oil and performing ultrasonic dispersion and aging; and then adding auxiliary materials such as Vaseline for an oil bath to obtain the quick-drying antirust oil. The antirust oil prepared by the method is stable in product property, the drying time is obviously shortened, and the antirust oil is excellent in damp and hot resistance and salt mist resistance and extremely good in lubricating property, maintains the original color of a metal and prevents the metal from being rusted, and is fragrance in smell. Through detection, the drying time of the obtained antirust oil is 3-4h which is shortened by 3-5 times compared with a conventional antirust oil drying time; the service life of the metal coated with the antirust oil is prolonged by 5-8 years, and the antirust oil has a relatively wide application prospect.
Description
Technical field
The invention discloses a kind of preparation method of quick-dry type antirust oil, belongs to technical field of chemistry and chemical engineering.
Background technology
Metal during storage, transport and use, due to by environment, steam, oxygen, acid, alkali, salt and carbonization in air
The impact of the materials such as thing, under conditions of certain temperature, humidity and time duration, it may occur that physics, chemical change and occur
Corrosion.The corrosion of metal, can cause the loss of metal and the decline and forfeiture of metal parts function.According to incompletely statistics every year by
The 2%～4% of total value of production in national economy is accounted in the direct economic loss caused by metal erosion.China is maximum in the world
Textile production and exported country, the sustained, stable growth of textile exports is to ensureing China's foreign exchange reserve, balance of international payments/ balance of payment, people
People's coin stable exchange rates, solve social employment most important.Corrosion is that the components of machine such as bearing, standards for gears part, hydraulic part are damaged
Wound causes the one of the main reasons of deterioration, and automobile, motorcycle and various vehicles, plant equipment etc. are mainly by metal zero
Part is constituted.And the metal surface of metallic element is easy to corrosion, its performance is not only affected, shortens its service life,
Serious meeting causes security incident, causes personal injury while equipment is directly scrapped.The main cause of metallic element corrosion
Have：（1）Metal surface there occurs oxidation reaction with the oxygen in air so that metal surface generates metal oxide；（2）It is general
The microbiologic(al) corrosion that the microorganism contained in logical antirust oil is produced with metal surface, the anaerobism for mainly having sulfate reducing bacteria to cause
Corrosion, toughness bacterial membrane generate microbial corrosion and other forms of corrosions；（3）By corrosive mediums such as extraneous chlorions
Impact, destroy original metal surface.For avoiding the components of machine such as bearing, standards for gears part, hydraulic part in transport, storage
And during use, there is corrosion, relatively common means of defence is the antirust oil on its surface applies or soaks, by metal
Surface forms oil film to completely cut off air, reduces corrosion.However, current tradition antirust oil long, the rustless property that there is drying time
Short with the time, the defect of comprehensive rustless property difference makes the service behaviour and service life of equipment undesirable.
The content of the invention
Present invention mainly solves technical problem：For current tradition antirust oil long, the rustless property that there is drying time
Short with the time, the defect of comprehensive rustless property difference, the lemon grass (Cymbopogon citratus) cauline leaf particle after drying is milled by the present invention are added with deionized water
Thermal agitation, refines lemon grass (Cymbopogon citratus) essential oil, then after taking the water-baths such as alkylol, ketene dimer, adjusts its pH, filtration, concentration with alkali lye
Mix with lemon grass (Cymbopogon citratus) essential oil afterwards and ultrasonic disperse, ageing, after adding the auxiliary material oil baths such as vaseline, obtain final product a kind of quick-dry type antirust oil,
Gained antirust oil antirust oil properties of product of the invention are stable, and drying time substantially shortens, with excellent heat resistance and salt fog resistance
Performance, lubricity are splendid, and modest viscosity, coated area are wide, it is not necessary to which other solvents dilute, mechanical component to labyrinth,
Part is easy to use, good fluidity, and after transparency height and solvent volatilization, formation layer of transparent, compactness are good, and adhesive force is strong, prevent
The good flexible film of rust property, keeps metal primary colors to prevent corrosion of metal, and fragrant, with wide application prospect.
In order to solve above-mentioned technical problem, the technical solution adopted in the present invention is：
（1）Fresh Lemon grass blade leaf is chosen, is cleaned with clear water and 6～8h of freeze-drying, subsequently milled and cross 60 mesh sieves, collect
Lemon grass (Cymbopogon citratus) cauline leaf particle, then in mass ratio 1:8, lemon grass (Cymbopogon citratus) cauline leaf particle is mixed with deionized water stirring, subsequently heat up heating
After 1～2h of boiling, stop heating 6～8h of stratification, separate and collect upper oil phase, be prepared into volatilization lemon grass (Cymbopogon citratus) essential oil,
It is standby；
（2）Count by weight, weigh 45～50 parts of alkylols, 10～15 parts of ketene dimers and 5～8 parts of mass fractions respectively
65% sulfuric acid is placed in conical flask, after subsequently logical nitrogen excludes air, conical flask is placed in 85～90 DEG C in a nitrogen atmosphere
60～75min of lower heating water bath, subsequently stands and is cooled to room temperature, adjust pH to 7.0, mistake with 10% sodium carbonate liquor of mass fraction
Filtrate is filtered and collects, rotation is evaporated to the 1/5 of original volume at 75～80 DEG C after stratification, is prepared into modified concentrate；
（3）In mass ratio 1:3, by step（1）The volatilization lemon grass (Cymbopogon citratus) essential oil of preparation is mixed with the modified concentrate stirring of above-mentioned preparation
Close, under 200～300W, ultrasonic disperse processes 10～15min, and subsequently still aging 6～8h, is prepared into modified volatile spirits；
（4）Count by weight, weigh modified volatile spirits, 15～20 parts of vaseline and 5 of 60～65 parts of above-mentioned preparations respectively
～10 parts of dodecenylsuccinic acids are placed in beaker, 10～15min of oil bath heating at 120～125 DEG C, subsequently stop heating simultaneously
Standing is cooled to 70～75 DEG C, stands and is cooled to room temperature, you can be prepared into a kind of quick-dry type antirust after 25～30min of insulated and stirred
Oil.
The present invention application process be：First metal works are immersed in deionized water, the ultrasound washing under 200～300W
10～13min, is immersed in 1～3min in quick-dry type antirust oil obtained in the present invention, and shakes by hand after drying so as to which immersion is equal
It is even, dry under normal temperature in then proceeding to centrifuge, after testing, the drying time for coating the metal works after antirust oil is
3～4h, more traditional antirust oil drying time shorten 3～5 times, coat the metal service life after antirust oil and extend 5～8 years.
The invention has the beneficial effects as follows：
（1）There is very strong adhesion property between the antirust oil and metal of gained of the invention, drying time substantially shortens, Neng Gouwen
Surely adsorb substantial amounts of oil molecule, stable Rust Preventing Oil Film is formed in metal surface；
（2）After metallic element is applied or soaks the antirust oil of upper gained, can be formed than common antirust oil oil film more on its surface
Stable oil film protective layer, can preferably prevent the harmful substances such as water in environment, oxygen, acid, alkali, salt to metallic element
Corrosion, is adapted to large-scale production and application so as to improve its antirust ability.
Specific embodiment
Fresh Lemon grass blade leaf is chosen first, is cleaned with clear water and 6～8h of freeze-drying, subsequently mill and cross 60 mesh sieves,
Collect to obtain lemon grass (Cymbopogon citratus) cauline leaf particle, then in mass ratio 1:8, lemon grass (Cymbopogon citratus) cauline leaf particle is mixed with deionized water stirring, is subsequently risen
After warm 1～2h of ebuillition of heated, stop heating 6～8h of stratification, separate and collect upper oil phase, be prepared into volatilization lemon grass (Cymbopogon citratus)
Essential oil, it is standby；Count by weight, weigh 45～50 parts of alkylols, 10～15 parts of ketene dimers and 5～8 parts of quality point respectively
Several 65% sulfuric acid are placed in conical flask, after subsequently logical nitrogen excludes air, conical flask are placed in 85～90 in a nitrogen atmosphere
60～75min of heating water bath at DEG C, subsequently stands and is cooled to room temperature, adjusts pH to 7.0 with 10% sodium carbonate liquor of mass fraction,
Filtrate is filtered and collects, rotation is evaporated to the 1/5 of original volume at 75～80 DEG C after stratification, is prepared into modified concentrate；
In mass ratio 1:3, the volatilization lemon grass (Cymbopogon citratus) essential oil for preparing is mixed with the modified concentrate stirring of above-mentioned preparation, in 200～300W
Lower ultrasonic disperse processes 10～15min, and subsequently still aging 6～8h, is prepared into modified volatile spirits；Count by weight, point
The modified volatile spirits of 60～65 parts of above-mentioned preparations of another name amount, 15～20 parts of vaseline and 5～10 parts of dodecenylsuccinic acids are put
In beaker, 10～15min of oil bath heating at 120～125 DEG C subsequently stops heating and standing being cooled to 70～75 DEG C, protects
Stand after temperature 25～30min of stirring and be cooled to room temperature, you can be prepared into a kind of quick-dry type antirust oil.
Example 1
Fresh Lemon grass blade leaf is chosen first, is cleaned with clear water and freeze-drying 6h, subsequently mill and cross 60 mesh sieves, collect to obtain lemon
Lemon grass blade leaf particle, then in mass ratio 1:8, lemon grass (Cymbopogon citratus) cauline leaf particle is mixed with deionized water stirring, subsequently heat up heating boiling
After rising 1h, stop heating stratification 6h, separate and collect upper oil phase, be prepared into volatilization lemon grass (Cymbopogon citratus) essential oil, it is standby；By weight
Amount number meter, weighs 45 parts of alkylols, 10 parts of ketene dimers and 5 parts of 65% sulfuric acid of mass fraction respectively and is placed in conical flask, with
After leading to nitrogen exclusion air afterwards, conical flask is placed in into heating water bath 60min at 85 DEG C in a nitrogen atmosphere, subsequently stands cooling
To room temperature, pH is adjusted to 7.0 with 10% sodium carbonate liquor of mass fraction, filter and collect filtrate, in 75 DEG C of backspins after stratification
Turn to be evaporated to the 1/5 of original volume, be prepared into modified concentrate；In mass ratio 1:3, by prepare volatilization lemon grass (Cymbopogon citratus) essential oil with it is above-mentioned
The modified concentrate stirring mixing for preparing, under 200W, ultrasonic disperse processes 10min, and subsequently still aging 6h, is prepared into modified
Volatile spirits；Count by weight, respectively the modified volatile spirits of 60 parts of above-mentioned preparations of weighing, 15 parts of vaseline and 5 part 12
Alkenyl succinic acid is placed in beaker, oil bath heating 10min at 120 DEG C, subsequently is stopped heating and standing being cooled to 70 DEG C, is incubated
Stand after stirring 25min and be cooled to room temperature, you can be prepared into a kind of quick-dry type antirust oil.
The present invention application process be：First metal works are immersed in deionized water, the ultrasound washing under 200W
10min, is immersed in 1min in the quick-dry type antirust oil obtained by the present invention, and shakes by hand after drying so as to which immersion is uniform, then
Dry under normal temperature in proceeding to centrifuge, after testing, the drying time for coating the metal works after antirust oil is 3h, is relatively passed
System antirust oil drying time shortens 3 times, coats the metal service life after antirust oil and extends 5 years.
Example 2
Fresh Lemon grass blade leaf is chosen first, is cleaned with clear water and freeze-drying 8h, subsequently mill and cross 60 mesh sieves, collect to obtain lemon
Lemon grass blade leaf particle, then in mass ratio 1:8, lemon grass (Cymbopogon citratus) cauline leaf particle is mixed with deionized water stirring, subsequently heat up heating boiling
After rising 2h, stop heating stratification 8h, separate and collect upper oil phase, be prepared into volatilization lemon grass (Cymbopogon citratus) essential oil, it is standby；By weight
Amount number meter, weighs 50 parts of alkylols, 15 parts of ketene dimers and 8 parts of 65% sulfuric acid of mass fraction respectively and is placed in conical flask, with
After leading to nitrogen exclusion air afterwards, conical flask is placed in into heating water bath 75min at 90 DEG C in a nitrogen atmosphere, subsequently stands cooling
To room temperature, pH is adjusted to 7.0 with 10% sodium carbonate liquor of mass fraction, filter and collect filtrate, in 80 DEG C of backspins after stratification
Turn to be evaporated to the 1/5 of original volume, be prepared into modified concentrate；In mass ratio 1:3, by prepare volatilization lemon grass (Cymbopogon citratus) essential oil with it is above-mentioned
The modified concentrate stirring mixing for preparing, under 300W, ultrasonic disperse processes 15min, and subsequently still aging 8h, is prepared into modified
Volatile spirits；Count by weight, respectively the modified volatile spirits of 65 parts of above-mentioned preparations of weighing, 20 parts of vaseline and 10 part 12
Alkenyl succinic acid is placed in beaker, oil bath heating 15min at 125 DEG C, subsequently is stopped heating and standing being cooled to 75 DEG C, is incubated
Stand after stirring 30min and be cooled to room temperature, you can be prepared into a kind of quick-dry type antirust oil.
The present invention application process be：First metal works are immersed in deionized water, the ultrasound washing under 300W
13min, is immersed in 3min in the quick-dry type antirust oil obtained by the present invention, and shakes by hand after drying so as to which immersion is uniform, then
Dry under normal temperature in proceeding to centrifuge, after testing, the drying time for coating the metal works after antirust oil is 4h, is relatively passed
System antirust oil drying time shortens 5 times, coats the metal service life after antirust oil and extends 8 years.
Example 3
Fresh Lemon grass blade leaf is chosen first, is cleaned with clear water and freeze-drying 7h, subsequently mill and cross 60 mesh sieves, collect to obtain lemon
Lemon grass blade leaf particle, then in mass ratio 1:8, lemon grass (Cymbopogon citratus) cauline leaf particle is mixed with deionized water stirring, subsequently heat up heating boiling
After rising 1.5h, stop heating stratification 7h, separate and collect upper oil phase, be prepared into volatilization lemon grass (Cymbopogon citratus) essential oil, it is standby；Press
Parts by weight meter, weighs 47 parts of alkylols, 13 parts of ketene dimers and 7 parts of 65% sulfuric acid of mass fraction respectively and is placed in conical flask,
After subsequently logical nitrogen excludes air, conical flask is placed in into heating water bath 68min at 87 DEG C in a nitrogen atmosphere, is subsequently stood cold
But to room temperature, pH is adjusted to 7.0 with 10% sodium carbonate liquor of mass fraction, filter and collect filtrate, after stratification at 77 DEG C
Rotary evaporation is prepared into modified concentrate to the 1/5 of original volume；In mass ratio 1:3, by prepare volatilization lemon grass (Cymbopogon citratus) essential oil with it is upper
The modified concentrate stirring mixing of preparation is stated, ultrasonic disperse processes 13min under 250W, and subsequently still aging 7h, is prepared into and changes
Property volatile spirits；Count by weight, respectively the modified volatile spirits of 63 parts of above-mentioned preparations of weighing, 17 parts of vaseline and 7 part ten
Dialkylene succinic acid is placed in beaker, oil bath heating 13min at 123 DEG C, subsequently is stopped heating and standing being cooled to 73 DEG C, is protected
Stand after temperature stirring 27min and be cooled to room temperature, you can be prepared into a kind of quick-dry type antirust oil.
The present invention application process be：First metal works are immersed in deionized water, the ultrasound washing under 250W
12min, is immersed in 2min in the quick-dry type antirust oil obtained by the present invention, and shakes by hand after drying so as to which immersion is uniform, then
Dry under normal temperature in proceeding to centrifuge, after testing, the drying time for coating the metal works after antirust oil is 3.5h, compared with
Traditional antirust oil drying time shortens 4 times, coats the metal service life after antirust oil and extends 7 years.
Claims (1)
1. a kind of preparation method of quick-dry type antirust oil, it is characterised in that concrete preparation process is：
（1）Fresh Lemon grass blade leaf is chosen, is cleaned with clear water and 6～8h of freeze-drying, subsequently milled and cross 60 mesh sieves, collect
Lemon grass (Cymbopogon citratus) cauline leaf particle, then in mass ratio 1:8, lemon grass (Cymbopogon citratus) cauline leaf particle is mixed with deionized water stirring, subsequently heat up heating
After 1～2h of boiling, stop heating 6～8h of stratification, separate and collect upper oil phase, be prepared into volatilization lemon grass (Cymbopogon citratus) essential oil,
It is standby；
（2）Count by weight, weigh 45～50 parts of alkylols, 10～15 parts of ketene dimers and 5～8 parts of mass fractions respectively
65% sulfuric acid is placed in conical flask, after subsequently logical nitrogen excludes air, conical flask is placed in 85～90 DEG C in a nitrogen atmosphere
60～75min of lower heating water bath, subsequently stands and is cooled to room temperature, adjust pH to 7.0, mistake with 10% sodium carbonate liquor of mass fraction
Filtrate is filtered and collects, rotation is evaporated to the 1/5 of original volume at 75～80 DEG C after stratification, is prepared into modified concentrate；
（3）In mass ratio 1:3, by step（1）The volatilization lemon grass (Cymbopogon citratus) essential oil of preparation is mixed with the modified concentrate stirring of above-mentioned preparation
Close, under 200～300W, ultrasonic disperse processes 10～15min, and subsequently still aging 6～8h, is prepared into modified volatile spirits；
（4）Count by weight, weigh modified volatile spirits, 15～20 parts of vaseline and 5 of 60～65 parts of above-mentioned preparations respectively
～10 parts of dodecenylsuccinic acids are placed in beaker, 10～15min of oil bath heating at 120～125 DEG C, subsequently stop heating simultaneously
Standing is cooled to 70～75 DEG C, stands and is cooled to room temperature, you can be prepared into a kind of quick-dry type antirust after 25～30min of insulated and stirred
Oil.