CN106520112A - Luminous signboard and preparing method thereof - Google Patents
Luminous signboard and preparing method thereof Download PDFInfo
- Publication number
- CN106520112A CN106520112A CN201611100939.0A CN201611100939A CN106520112A CN 106520112 A CN106520112 A CN 106520112A CN 201611100939 A CN201611100939 A CN 201611100939A CN 106520112 A CN106520112 A CN 106520112A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- agent
- zinc
- luminous signboard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a luminous signboard and a preparing method thereof. The luminous signboard consists of the following formula components in parts by mass: 20-30 parts of polymethyl methacrylate based on molecular weight, 1-3 parts of morin, 6-8 parts of a ring phenolic compound, 2-4 parts of zirconium oxide, 1-3 parts of a light diffusing agent, 6-10 parts of black powder, 6-10 parts of violet powder, 1-3 parts of an antistatic agent, 3-5 parts of zinc silicate, 4-8 parts of zinc cadmium sulfide, 6-8 parts of fluorescein, 5-7 parts of blue powder, 1-3 parts of an ultraviolet agent and 5-7 parts of aluminum oxide. The problem that a black LOGO cannot be seen at night is effectively solved. The luminous signboard has the characteristics of high production efficiency, low cost, great quality and the like.
Description
Technical field
The present invention relates to field of new, in particular to a kind of luminous signboard and preparation method thereof.
Background technology
Polymethyl methacrylate, is referred to as acrylics with the polymer obtained by acrylicacidandesters Type of Collective,
Corresponding plastics are referred to as polyacrylic plastics, wherein most widely used with polymethyl methacrylate.Poly-methyl methacrylate
Ester abbreviation code name is PMMA, is commonly called as lucite, be synthesize transparent material so far in quality it is most excellent, price is relatively fitted again
Suitable kind.Application aspect：PMMA is dissolved in organic solvent, such as phenol, methyl phenyl ethers anisole etc., can form good thin by spin coating
Film, with good dielectric properties, can be also known as Jie of OTFT (OTFT) as organic field-effect tube (OFET)
Matter layer.
PMMA is the material of asepsis environment-protecting, can be used to producing tableware, cleaners and polishes etc., with good chemical stability and
Weatherability.
The content of the invention
The invention provides a kind of luminous signboard and preparation method thereof, effectively solving black LOGO evenings of the present invention cannot
The problem seen, with low cost, the characteristic such as superior in quality high with production efficiency.
For achieving the above object, the present invention provides following technical scheme：
A kind of luminous signboard and preparation method thereof, is made up of following mass fraction formula components：Molecular weight 20-30 parts,
Morin 1-3 parts, cyclic phenol compound 6-8 part, zirconium oxide 2-4 parts, astigmatism agent 1-3 parts, black powder 6-10 parts, purple powder 6-10
Part, antistatic additive 1-3 parts, zinc silicate 3-5 parts, zinc-cadmium sulfide 4-8 parts, fluorescein 6-8 part, blue powder 5-7 parts, UV agent 1-3 parts,
Aluminum oxide 5-7 parts.
Further：It is made up of following mass fraction formula components：20 parts of molecular weight, 1 part of morin, cyclic phenol compound 6
Part, 2 parts of zirconium oxide, 1 part of astigmatism agent, 6 parts of black powder, 6 parts of purple powder, 1 part of antistatic additive, 3 parts of zinc silicate, 4 parts of zinc-cadmium sulfide,
6 parts of fluorescein, blue 5 parts of powder, 1 part of UV agent, 5 parts of aluminum oxide.
Further：It is made up of following mass fraction formula components：25 parts of molecular weight, 2 parts of morin, cyclic phenol compound 7
Part, 3 parts of zirconium oxide, 2 parts of astigmatism agent, 8 parts of black powder, 8 parts of purple powder, 2 parts of antistatic additive, 4 parts of zinc silicate, 6 parts of zinc-cadmium sulfide,
7 parts of fluorescein, blue 6 parts of powder, 2 parts of UV agent, 6 parts of aluminum oxide.
Further：It is made up of following mass fraction formula components：30 parts of molecular weight, 3 parts of morin, cyclic phenol compound 8
Part, 4 parts of zirconium oxide, 3 parts of astigmatism agent, 10 parts of black powder, 10 parts of purple powder, 3 parts of antistatic additive, 5 parts of zinc silicate, zinc-cadmium sulfide 8
Part, 8 parts of fluorescein, blue 7 parts of powder, 3 parts of UV agent, 7 parts of aluminum oxide.
Further：Preparation method of the present invention has following steps：
Step one, toner input mixer is mixed, mixed on low speed 30 seconds first then turns 90 seconds at a high speed；
Step 2, will be well mixed with molecular weight obtained by step one；
Step 3, step 2 is mixed with leftover materials；
Step 4, the expression that step 3 is made needs.
The invention has the beneficial effects as follows：
1st, the problem that cannot see in the effectively solving black LOGO evenings of the present invention；
2nd, it is high with production efficiency, with low cost, the characteristic such as superior in quality.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than the embodiment of whole.Based in the present invention
Embodiment, the every other embodiment obtained under the premise of creative work is not made by those of ordinary skill in the art, all
Belong to the scope of protection of the invention.
Embodiment one：
A kind of luminous signboard is made up of following mass fraction formula components：Molecular weight 20-30 parts, morin 1-3 parts, ring
Shape phenolic compounds 6-8 parts, zirconium oxide 2-4 parts, astigmatism agent 1-3 parts, black powder 6-10 parts, purple powder 6-10 parts, antistatic additive 1-3
Part, zinc silicate 3-5 parts, zinc-cadmium sulfide 4-8 parts, fluorescein 6-8 part, blue powder 5-7 parts, UV agent 1-3 parts, aluminum oxide 5-7 parts.
Embodiment two：
A kind of luminous signboard is made up of following mass fraction formula components：20 parts of molecular weight, 1 part of morin, ring-type phenol
6 parts of compound, 2 parts of zirconium oxide, 1 part of astigmatism agent, 6 parts of black powder, 6 parts of purple powder, 1 part of antistatic additive, 3 parts of zinc silicate, sulfuration
4 parts of zinc cadmium, 6 parts of fluorescein, blue 5 parts of powder, 1 part of UV agent, 5 parts of aluminum oxide.
Embodiment three：
A kind of luminous signboard is made up of following mass fraction formula components：25 parts of molecular weight, 2 parts of morin, ring-type phenol
7 parts of compound, 3 parts of zirconium oxide, 2 parts of astigmatism agent, 8 parts of black powder, 8 parts of purple powder, 2 parts of antistatic additive, 4 parts of zinc silicate, sulfuration
6 parts of zinc cadmium, 7 parts of fluorescein, blue 6 parts of powder, 2 parts of UV agent, 6 parts of aluminum oxide.
Example IV：
A kind of luminous signboard is made up of following mass fraction formula components：30 parts of molecular weight, 3 parts of morin, ring-type phenol
8 parts of compound, 4 parts of zirconium oxide, 3 parts of astigmatism agent, 10 parts of black powder, 10 parts of purple powder, 3 parts of antistatic additive, 5 parts of zinc silicate, sulphur
Change 8 parts of zinc cadmium, 8 parts of fluorescein, blue 7 parts of powder, 3 parts of UV agent, 7 parts of aluminum oxide.
Embodiment five：
A kind of preparation method preparation method of luminous signboard comprises the steps：
Step one, toner input mixer is mixed, mixed on low speed 30 seconds first then turns 90 seconds at a high speed；
Step 2, will be well mixed with molecular weight obtained by step one；
Step 3, step 2 is mixed with leftover materials；
Step 4, the expression that step 3 is made needs.
Moreover, it will be appreciated that although this specification is been described by according to embodiment, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that those skilled in the art should for clarity
Using specification as an entirety, the technical scheme in each embodiment can also Jing it is appropriately combined, form those skilled in the art
Understandable other embodiment.
Claims (5)
1. a kind of luminous signboard, it is characterised in that：It is made up of following mass fraction formula components：
Molecular weight 20-30 parts, morin 1-3 parts, cyclic phenol compound 6-8 part, zirconium oxide 2-4 parts, astigmatism agent 1-3 parts, black
Powder 6-10 parts, purple powder 6-10 parts, antistatic additive 1-3 parts, zinc silicate 3-5 parts, zinc-cadmium sulfide 4-8 parts, fluorescein 6-8 part, indigo plant
Toner 5-7 parts, UV agent 1-3 parts, aluminum oxide 5-7 parts.
2. a kind of luminous signboard according to claim 1, it is characterised in that：By following mass fraction formula components group
Into：
20 parts of molecular weight, 1 part of morin, 6 parts of cyclic phenol compound, 2 parts of zirconium oxide, 1 part of astigmatism agent, 6 parts of black powder, purple powder
6 parts, 1 part of antistatic additive, 3 parts of zinc silicate, 4 parts of zinc-cadmium sulfide, 6 parts of fluorescein, blue 5 parts of powder, 1 part of UV agent, 5 parts of aluminum oxide.
3. a kind of luminous signboard according to claim 1, it is characterised in that：By following mass fraction formula components group
Into：
25 parts of molecular weight, 2 parts of morin, 7 parts of cyclic phenol compound, 3 parts of zirconium oxide, 2 parts of astigmatism agent, 8 parts of black powder, purple powder
8 parts, 2 parts of antistatic additive, 4 parts of zinc silicate, 6 parts of zinc-cadmium sulfide, 7 parts of fluorescein, blue 6 parts of powder, 2 parts of UV agent, 6 parts of aluminum oxide.
4. a kind of luminous signboard according to claim 1, it is characterised in that：By following mass fraction formula components group
Into：
30 parts of molecular weight, 3 parts of morin, 8 parts of cyclic phenol compound, 4 parts of zirconium oxide, 3 parts of astigmatism agent, 10 parts of black powder, purple
10 parts of powder, 3 parts of antistatic additive, 5 parts of zinc silicate, 8 parts of zinc-cadmium sulfide, 8 parts of fluorescein, blue 7 parts of powder, 3 parts of UV agent, aluminum oxide 7
Part.
5. a kind of a kind of preparation method of luminous signboard according to claim 1, it is characterised in that：Including following step
Suddenly：
Step one, toner input mixer is mixed, mixed on low speed 30 seconds first then turns 90 seconds at a high speed；
Step 2, will be well mixed with molecular weight obtained by step one；
Step 3, step 2 is mixed with leftover materials；
Step 4, the expression that step 3 is made needs.