CN106519772A - Inner wall putty used in architectural decoration engineering - Google Patents
Inner wall putty used in architectural decoration engineering Download PDFInfo
- Publication number
- CN106519772A CN106519772A CN201611198074.6A CN201611198074A CN106519772A CN 106519772 A CN106519772 A CN 106519772A CN 201611198074 A CN201611198074 A CN 201611198074A CN 106519772 A CN106519772 A CN 106519772A
- Authority
- CN
- China
- Prior art keywords
- powder
- decoration engineering
- wall putty
- building decoration
- fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the technical field of architectural decoration engineering, in particular to an inner wall putty used in architectural decoration engineering. The inner wall putty used in architectural decoration engineering is prepared from, by weight, 25%-30% of white cement, 10%-15% of mountain flour, 5%-8% of lithium slag, 1%-2% of nanometer titania, 0.5%-2% of chopped fiber, 1.5%-2.2% of dispersable emulsion powder, 1%-5% of tackifying water-retaining agent, 1%-3% of suspending agent, 2%-5% of anion powder, 0.05%-0.25% of mould-proof bactericide, 0.2%-0.8% of wetting agent, 0.02%-0.1% of antifoaming agent, and the balance quartz sand powder. The inner wall putty powder used in architectural decoration engineering is green and environmentally friendly, and has the functions of bacteria and mould prevention, moisture absorption and release, air freshness and the like; meanwhile, the inner wall putty used in architectural decoration engineering has a good overcoating effect, and can be directly used as a coating material.
Description
Technical field
The invention belongs to building decoration engineering technology field, and in particular to a kind of building decoration engineering inner wall putty.
Technical background
Putty is the important supplementary material used in fitment process, and wherein wall surface putty consumption is big, and kind is also more, more than nearly ten
The commodity wall surface putty occurred over year, strong influence building decoration engineering.Past putty is defined as construction and decoration always
The supplementary material of paint spraying in engineering, its Main Function are the spaces for filling and leading up basic unit, in recent years, with building decoration engineering
The new demand to putty for occurring, and a large amount of uses of putty, its function progressively extend, and effect is also refined, and
Occur in that some have the feature putty of specific use accordingly.Traditional interior decoration inner wall putty is because synthesizing in a large number
Glue is adhesive, mostly containing harmful substances such as formaldehyde, the nervous system of people can be caused to be damaged, can be caused to be poisoned when serious and be caused
Cancer, particularly endangers bigger to infant.
The content of the invention
The present invention is directed to the problems referred to above, there is provided a kind of building decoration engineering inner wall putty, and the putty does not contain benzene, dimethylbenzene
Etc. harmful substance, and there is air-cleaning function, environmental protection.To reach above-mentioned purpose, the present invention is adopted the following technical scheme that, one
Building decoration engineering inner wall putty is planted, by the material composition of following percentage by weight:
White cement:25%-30%
Aragonite powder:10%-15%
Lithium ground-slag:5%-8%
Nano titanium oxide:1%-2%
Chopped strand:0.5%-2%
Polymer dispersion powder:1.5%-3%
Sticking enhancing water-loss reducer:1%-5%
Suspending agent:1%-3%
Negative ion powder:2%-5%
Antimildew disinfectant:0.05%-0.25%
Wetting agent:0.2%-0.8%
Defoamer:0.02%-0.1%
Quartz sand powder:Surplus
The whiteness of the white cement is not less than 87, and strength grade is 42.5 grades.
The aragonite powder fineness is not less than 500 mesh, and whiteness is not less than 90.
The chopped strand is brown fine for be chopped silicon carbide fibre, polyacrylonitrile fibre, glass fibre, polypropylene fibre, coconut palm
One or more in dimension, sisal fiber, ramee, basalt fibre.
Preferably, the chopped strand presses 1-5 by polyacrylonitrile fibre, basalt fibre and coconut fibre:1-5:1
Weight is than composition.
Preferably, the chopped strand diameter 5um-10um, draw ratio 8-12:1.
The sticking enhancing water-loss reducer is propylene glycol alginate, guar hydroxypropyltrimonium ammonium chloride, sodium alginate, welan gum
In one or more.
Preferably, the sticking enhancing water-loss reducer by welan gum and guar hydroxypropyltrimonium ammonium chloride according to 1-6:1 weight
Amount is than composition.
The negative ion powder is the one kind or in legibility stone flour, osmanthus jewel powder, pyrochlore powder, stone needle powder and six ring stone flours
More than kind.
Preferably, the negative ion powder by legibility stone flour, osmanthus jewel powder and pyrochlore powder according to 1-3:1-5:1 weight ratio
Composition.
Preferably, the negative ion powder fineness is more than 600 mesh
It is furthermore preferred that the legibility stone flour is cerium legibility stone flour.
The polymer dispersion powder is the of a relatively high ethylene-vinyl acetate copolymer of ethylene contents.
The antimildew disinfectant is barium metaborate, tetrachloroquinone, alum, one or more in penta sodium pentachlorophenate.
Preferably, the antimildew disinfectant is alum.
The wetting agent is AEO sulfosuccinate disodium salt, propane diols, the one kind in Arlacel-80
Or more than one.
Preferably, the wetting agent is AEO sulfosuccinate disodium salt.
The defoamer is polyoxyethylene polyoxypropylene glycerin ether, triisopropanolamine polyoxyethylene polyoxypropylene ether, polyoxy
One or more in propylene polyoxyethylene propylene glycol.
Preferably, the defoamer is by polyoxyethylene polyoxypropylene glycerin ether, triisopropanolamine polyoxyethylene polyoxypropylene
Ether and polyoxyethylene polyoxypropylene propylene glycol press 1-2:1-3:1 weight is than composition.
The suspending agent is aluminium-magnesium silicate, one or two in lithium magnesium silicate.
Preferably, the suspending agent is lithium magnesium silicate.
The quartz sand powder fineness is more than 400 mesh.
In the present invention nano titanium oxide have brighten, disperse, the function of antibacterial;The lithium slag is to prepare carbon by sulfuric acid process
What the residue drying that sour lithium is discharged was obtained, in powder, particle is less, loose structure, with larger inner ratio surface area, has pole
Strong adsorptivity, can adsorb the noxious material in air, adjust indoor humidity, make with fresh air.Sticking enhancing water-loss reducer is stirred with water
There is after mixing the pseudoplastic fluid bulk properties of high viscosity and non-newtonian fluid, with good thixotropy and smoothness, be difficult sagging,
Sagging, additionally aiding improves the settleability of putty, increases the adhesion strength of putty, makes water not volatile or is absorbed by basic unit, protects
The moisture needed for silicate mineral aquation has been demonstrate,proved, water retention has been played, while adjusting the viscosity of putty, putty has been made in pointing
Crack will not be not likely to produce because sagging and pointing is not full during gap between plate;Suspending agent can give putty appropriate thixotropy,
Improve the viscosity of putty, solve the sedimentation lamination problem in putty storing process, forever can synergistic thickening, moreover it is possible to adsorb bacterium;
Negative ion powder being capable of pure and fresh, purify air;Alum not only has intensity excitation to white cement and breeze, also sterilized well
Effect, has good inhibiting effect to typhoid bacillus, pneumobacillus, corynebacterium diphtheriae etc.;Wetting agent can be by reducing its surface
Tension force or interfacial tension, allow the water to be deployed on solid material surface, or penetrate its surface, and solid material is soaked;Quartz
Sand fine powder can improve the wear-resisting intensity of putty.
Beneficial effects of the present invention:
(1) building decoration engineering inner wall putty of the present invention with the addition of chopped strand, and good toughness, crack resistance are good;
(2) building decoration engineering inner wall putty of the present invention has the functions such as antibacterial and mouldproof, humidity absorption and release, fresh air,
Facing use can directly be done.
(3) building decoration engineering of the present invention is fine and smooth, closely knit with inner wall putty, has good workability.
Specific embodiment
Son illustrates the present invention with reference to embodiments.
Embodiment 1
A kind of building decoration engineering inner wall putty, by the material composition of following percentage by weight:White cement 25%, aragonite
Powder 10%, lithium ground-slag 5%, nano titanium oxide 1%, chopped strand 0.5%, polymer dispersion powder 1.5%, sticking enhancing water-loss reducer
1%th, suspending agent 1%, negative ion powder 2%, antimildew disinfectant 0.05%, wetting agent 0.2%, defoamer 0.02%, balance of stone
Sand powder.
The whiteness of the white cement is 87, and strength grade is 42.5 grades.
The aragonite powder fineness is 500 mesh, and whiteness is 90.
The chopped strand is the silicon carbide fibre that is chopped, a diameter of 5um, draw ratio 12:1.
The sticking enhancing water-loss reducer is propylene glycol alginate.
The negative ion powder is by stone needle powder and six ring stone flours according to 1:1 weight is not less than 600 mesh than composition, fineness.
The polymer dispersion powder is ethylene-vinyl acetate copolymer.
The antimildew disinfectant presses 1 by barium metaborate and tetrachloroquinone:2 weight is than composition.
The wetting agent is by propane diols and Arlacel-80 according to 2:1 weight is than composition.
The defoamer is polyoxyethylene polyoxypropylene propylene glycol.
The suspending agent is aluminium-magnesium silicate.
The quartzy powder fineness is 400 mesh.
Embodiment 2
A kind of building decoration engineering inner wall putty, by the material composition of following percentage by weight:White cement 30%, aragonite
It is powder 15%, lithium ground-slag 8%, nano titanium oxide 2%, chopped strand 2%, polymer dispersion powder 3%, sticking enhancing water-loss reducer 5%, outstanding
Floating agent 3%, negative ion powder 5%, antimildew disinfectant 0.25%, wetting agent 0.8%, defoamer 0.1%, balance of quartz sand powder.
The whiteness of the white cement is 89, and strength grade is 42.5 grades.
The aragonite powder fineness is 600 mesh, and whiteness is 91.
The chopped strand presses 1 by polyacrylonitrile fibre, glass fibre, polypropylene fibre, sisal fiber and ramee:
1:1:1:1 weight is than composition.
The sticking enhancing water-loss reducer is by sodium alginate and welan gum according to 2:1 mass ratio composition.
Preferably, the sticking enhancing water-loss reducer by welan gum and guar hydroxypropyltrimonium ammonium chloride according to 1-6:1 weight
Amount is than composition.
The negative ion powder presses 1 by osmanthus jewel powder and pyrochlore powder:Than composition, fineness is 700 mesh to 2 weight.
The polymer dispersion powder is ethylene-vinyl acetate copolymer.
During the antimildew disinfectant is penta sodium pentachlorophenate.
The wetting agent is by AEO sulfosuccinate disodium salt and propane diols according to 1:3 weight ratio
Composition.
The defoamer is triisopropanolamine polyoxyethylene polyoxypropylene ether.
The suspending agent presses 5 by aluminium-magnesium silicate and lithium magnesium silicate:1 mass ratio composition.
The quartzy powder fineness fineness is 450 mesh.
Embodiment 3
A kind of building decoration engineering inner wall putty, by the material composition of following percentage by weight:White cement 29%, aragonite
Powder 12%, lithium ground-slag 7%, nano titanium oxide 1.5%, chopped strand 1%, polymer dispersion powder 2%, sticking enhancing water-loss reducer 4%,
Suspending agent 2%, negative ion powder 4%, antimildew disinfectant 0.1%, wetting agent 0.7%, defoamer 0.06%, balance of quartz sand
Powder.
The whiteness of the white cement is 90, and strength grade is 42.5 grades.
The aragonite powder fineness is 550 mesh, and whiteness is 91.
The chopped strand presses 2 by polyacrylonitrile fibre, basalt fibre and coconut fibre:3:1 weight ratio composition,
Fibre diameter 5um-7um, draw ratio 8-10:1.
The sticking enhancing water-loss reducer is by welan gum and guar hydroxypropyltrimonium ammonium chloride according to 3:1 weight is than composition.
The negative ion powder is by cerium legibility stone flour, osmanthus jewel powder and pyrochlore powder according to 3:2:1 weight is than composition, fineness
For 680 mesh.
The polymer dispersion powder is ethylene-vinyl acetate copolymer.
The antimildew disinfectant is alum.
The wetting agent is AEO sulfosuccinate disodium salt.
The defoamer is by polyoxyethylene polyoxypropylene glycerin ether, triisopropanolamine polyoxyethylene polyoxypropylene ether and polyoxy
Propylene polyoxyethylene propylene glycol presses 1:2:1 weight is than composition.
The suspending agent is lithium magnesium silicate.
The quartzy powder fineness is 430 mesh.
Embodiment 4
A kind of building decoration engineering inner wall putty, by the material composition of following percentage by weight:White cement 29%, aragonite
Powder 12%, lithium ground-slag 6%, nano titanium oxide 1.3%, chopped strand 1.4%, polymer dispersion powder 2%, sticking enhancing water-loss reducer
3%th, suspending agent 2%, negative ion powder 3%, antimildew disinfectant 0.15%, wetting agent 0.6%, defoamer 0.08%, balance of stone
Sand powder.
The whiteness of the white cement is 88, and strength grade is 42.5 grades.
The aragonite powder fineness is 500 mesh, and whiteness is 91.
The chopped strand presses 1 by polyacrylonitrile fibre, basalt fibre and coconut fibre:5:1 weight ratio composition,
Fibre diameter 8um-10um, draw ratio 12:1.
The sticking enhancing water-loss reducer is by welan gum and guar hydroxypropyltrimonium ammonium chloride according to 1:1 weight is than composition.
The negative ion powder is by legibility stone flour, osmanthus jewel powder and pyrochlore powder according to 3:1:Than constituting, fineness is 1 weight
800 mesh.
The polymer dispersion powder is ethylene-vinyl acetate copolymer.
The antimildew disinfectant is barium metaborate.
The wetting agent is Arlacel-80.
The defoamer is by polyoxyethylene polyoxypropylene glycerin ether, triisopropanolamine polyoxyethylene polyoxypropylene ether and polyoxy
Propylene polyoxyethylene propylene glycol presses 1:3:1 weight is than composition.
The suspending agent is lithium magnesium silicate.
The quartzy powder fineness is 400 mesh.
Embodiment 5
A kind of building decoration engineering inner wall putty, by the material composition of following percentage by weight:White cement 30%, aragonite
Powder 10%, lithium ground-slag 7%, nano titanium oxide 1.5%, chopped strand 1.2%, polymer dispersion powder 1.9%, sticking enhancing water-loss reducer
4%th, suspending agent 2%, negative ion powder 2.5%, antimildew disinfectant 0.16%, wetting agent 0.25%, defoamer 0.08%, balance of
Quartz sand powder.
Embodiment 6
A kind of building decoration engineering inner wall putty, by the material composition of following percentage by weight:White cement 27%, aragonite
Powder 13%, lithium ground-slag 7%, nano titanium oxide 1.8%, chopped strand 0.8%, polymer dispersion powder 2.5%, sticking enhancing water-loss reducer
4%th, suspending agent 2%, negative ion powder 4%, antimildew disinfectant 0.2%, wetting agent 0.6%, defoamer 0.08%, balance of quartz
Emery dust.
The whiteness of the white cement is 87, and strength grade is 42.5 grades.
The aragonite powder fineness is 550 mesh, and whiteness is 90.
The chopped strand presses 5 by polyacrylonitrile fibre, basalt fibre and coconut fibre:1:1 weight ratio composition,
Diameter 5um-8um, draw ratio 8-10:1.
The sticking enhancing water-loss reducer is by welan gum and guar hydroxypropyltrimonium ammonium chloride according to 6:1 weight is than composition.
The negative ion powder is the one kind or in legibility stone flour, osmanthus jewel powder, pyrochlore powder, stone needle powder and six ring stone flours
More than kind.
Preferably, the negative ion powder by cerium legibility stone flour, osmanthus jewel powder and pyrochlore powder according to 1:5:1 weight compares group
Into fineness is 650 mesh
The polymer dispersion powder is ethylene-vinyl acetate copolymer.
The antimildew disinfectant is alum.
The wetting agent is AEO sulfosuccinate disodium salt.
The defoamer is by polyoxyethylene polyoxypropylene glycerin ether, triisopropanolamine polyoxyethylene polyoxypropylene ether and polyoxy
Propylene polyoxyethylene propylene glycol presses 2:1:1 weight is than composition.
The suspending agent is aluminium-magnesium silicate.
The quartzy powder fineness is 500 mesh.
Embodiment 7
A kind of building decoration engineering inner wall putty, by the material composition of following percentage by weight:White cement 27%, aragonite
Powder 12%, lithium ground-slag 6%, nano titanium oxide 1.2%, silicon carbide fibre 0.5%, coconut fibre 0.5%, sisal fiber
0.5%th, basalt fibre 0.5%, polymer dispersion powder 2%, propylene glycol alginate 1%, guar hydroxypropyltrimonium chlorination
Ammonium 1%, sodium alginate 1%, welan gum 1%, aluminium-magnesium silicate 1%, lithium magnesium silicate 1.5%, legibility stone flour 1%, osmanthus jewel powder
1%th, pyrochlore powder 2%, alum 0.05%, barium metaborate 0.05%, propane diols 0.4%, Arlacel-80 0.2%, polyoxypropylene
Polyoxyethylene glycerol ether 0.03%, triisopropanolamine polyoxyethylene polyoxypropylene ether 0.03%, polyoxyethylene polyoxypropylene the third two
Alcohol ether 0.03%, balance of quartz sand powder.
Comparative example 1
A kind of building decoration engineering inner wall putty, by the material composition of following percentage by weight:White cement 29%, aragonite
Powder 12%, nano titanium oxide 1.5%, polymer dispersion powder 2%, sticking enhancing water-loss reducer 4%, suspending agent 2%, negative ion powder 4%,
Wetting agent 0.7%, defoamer 0.06%, balance of quartz sand powder.
The whiteness of the white cement is 90, and strength grade is 42.5 grades.
The aragonite powder fineness is 550 mesh, and whiteness is 91.
The sticking enhancing water-loss reducer is by welan gum and guar hydroxypropyltrimonium ammonium chloride according to 3:1 weight is than composition.
The negative ion powder is by cerium legibility stone flour, osmanthus jewel powder and pyrochlore powder according to 3:2:1 weight is than composition, fineness
For 680 mesh.
The polymer dispersion powder is ethylene-vinyl acetate copolymer.
The wetting agent is AEO sulfosuccinate disodium salt.
The defoamer is by polyoxyethylene polyoxypropylene glycerin ether, triisopropanolamine polyoxyethylene polyoxypropylene ether and polyoxy
Propylene polyoxyethylene propylene glycol presses 1:2:1 weight is than composition.
The suspending agent is lithium magnesium silicate.
The quartzy powder fineness is 430 mesh.
Comparative example 2
A kind of building decoration engineering inner wall putty, by the material composition of following percentage by weight:White cement 29%, aragonite
Powder 12%, lithium ground-slag 7%, nano titanium oxide 1.5%, chopped strand 1%, polymer dispersion powder 2%, sticking enhancing water-loss reducer 4%,
Suspending agent 2%, antimildew disinfectant 0.1%, wetting agent 0.7%, balance of quartz sand powder.
The whiteness of the white cement is 90, and strength grade is 42.5 grades.
The aragonite powder fineness is 550 mesh, and whiteness is 91.
The chopped strand presses 2 by polyacrylonitrile fibre, basalt fibre and coconut fibre:3:1 weight ratio composition,
Fibre diameter 5um-7um, draw ratio 8-10:1.
The sticking enhancing water-loss reducer is by welan gum and guar hydroxypropyltrimonium ammonium chloride according to 3:1 weight is than composition.
The polymer dispersion powder is ethylene-vinyl acetate copolymer.
The antimildew disinfectant is alum.
The wetting agent is AEO sulfosuccinate disodium salt.
The suspending agent is lithium magnesium silicate.
The quartzy powder fineness is 430 mesh.
Performance test
According to JG/T298-2010《Architecture indoor putty》The regulation of standard, to embodiment 1-7 and comparative example 1-2
Putty carries out performance test, as a result see the table below 1.
1 putty performance of table
Claims (9)
1. a kind of building decoration engineering inner wall putty, it is characterised in that by the material composition of following percentage by weight:White cement
25%-30%, aragonite powder 10%-15%, lithium ground-slag 5%-8%, nano titanium oxide 1%-2%, chopped strand 0.5%-
2%th, polymer dispersion powder 1.5%-3%, sticking enhancing water-loss reducer 1%-5%, suspending agent 1%-3%, negative ion powder 2%-5%, anti-
Mould bactericide 0.05%-0.25%, wetting agent 0.2%-0.8%, defoamer 0.02%-0.1%, balance of quartz sand powder.
2. building decoration engineering inner wall putty according to claim 1, it is characterised in that the chopped strand is chopped
Silicon carbide fibre, polyacrylonitrile fibre, glass fibre, polypropylene fibre, coconut fibre, sisal fiber, ramee, basalt
One or more in fiber.
3. building decoration engineering inner wall putty according to claim 2, it is characterised in that the chopped strand is by poly- third
Alkene nitrile fiber, basalt fibre and coconut fibre press 1-5:1-5:1 weight is than composition.
4. building decoration engineering inner wall putty according to claim 1, it is characterised in that the sticking enhancing water-loss reducer is algae
One or more in acid propylene glycol ester, guar hydroxypropyltrimonium ammonium chloride, sodium alginate, welan gum.
5. building decoration engineering inner wall putty according to claim 1, it is characterised in that the negative ion powder is legibility
One or more in stone flour, osmanthus jewel powder, pyrochlore powder, stone needle powder and six ring stone flours.
6. building decoration engineering inner wall putty according to claim 1, it is characterised in that the antimildew disinfectant is inclined
One or more in barium borate, tetrachloroquinone, alum, penta sodium pentachlorophenate.
7. building decoration engineering inner wall putty according to claim 1, it is characterised in that the wetting agent is fatty alcohol
One or more in polyoxyethylene ether sulfosuccinic acid esters disodium salt, propane diols, Arlacel-80.
8. building decoration engineering inner wall putty according to claim 1, it is characterised in that the defoamer is polyoxy third
In alkene polyoxyethylene glycerol ether, triisopropanolamine polyoxyethylene polyoxypropylene ether, polyoxyethylene polyoxypropylene propylene glycol one
Kind or more.
9. building decoration engineering inner wall putty according to claim 1, it is characterised in that the suspending agent is magnesium silicate
One or two in aluminium, lithium magnesium silicate.