CN106515129A - Multifunctional upper fabric - Google Patents
Multifunctional upper fabric Download PDFInfo
- Publication number
- CN106515129A CN106515129A CN201610140175.1A CN201610140175A CN106515129A CN 106515129 A CN106515129 A CN 106515129A CN 201610140175 A CN201610140175 A CN 201610140175A CN 106515129 A CN106515129 A CN 106515129A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- corrosion
- fiber
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a multifunctional upper fabric. The multifunctional upper fabric comprises a base fabric layer, a waterproof layer, a corrosion-resistant layer and a wear-resistant layer, wherein the waterproof layer is adhered to the upper surface of the base fabric layer through an adhesive, the corrosion-resistant layer is arranged on the upper surface of the waterproof layer, the wear-resistant layer is arranged on the upper surface of the corrosion-resistant layer, the base fabric layer is made of warps and wefts through weaving, the warps and the wefts are made from silver nanofibers through spinning, the waterproof layer is made from a PTFE film, and the corrosion-resistant layer is made from glass fiber cloth. According to the multifunctional upper fabric, the base fabric layer is made of the warps and the wefts through weaving, the warps and the wefts are made from the silver nanofibers through spinning, and the silver nanofibers can play high roles in inhibiting and killing tens of kinds of pathogenic microorganisms such as Escherichia coli, Neisseria gonorrhoeae and Chlamydia trachomatis, so that the antibacterial effect is relatively good; meanwhile, due to the waterproof layer, the corrosion-resistant layer and the wear-resistant layer, the waterproof performance, corrosion resistance and wear resistance of the upper fabric are improved; the wear-resistant layer soaked with a Chinese herbal medicine decoction further has a faint-scent flavor.
Description
Technical field
The present invention relates to a kind of cloth, specifically a kind of multi-functional upper of a shoe cloth.
Background technology
China is footwear big producing country, and the cloth for shoes material demand for matching therewith is also very big, but existing footwear
Excessively single with cloth general utility functions, some are exactly only have heat insulation effect, and cause waterproof or poor, now
Research of the society to cloth function also tends to development in pluralism, and current cloth holds when acid & alkali liquid is run into very much
Easily be corroded, so as to cause the damage of shoes, larger economic loss is brought to user.While existing cloth
Material there is no water-proof function, after meeting water, shoes are moist, and whole shoes weight penalty, wearer can feel pole
It is uncomfortable, and shoes are easier breed bacteria in wet condition, affect the health of wearer.People are every in addition
It can all be worn shoes and learn, works, lives in various occasions, will touch various antibacterials between not feeling,
Long-term accumulated is enriched with, and can produce harm to the health of human body.Above-mentioned various reasons lead to not meet existing footwear
Requirements at the higher level to upper of a shoe cloth, therefore await further being improved.
The content of the invention
It is an object of the invention to provide the multi-functional upper of a shoe cloth of a kind of corrosion resistant antibiotic, wear-resisting waterproof, to solve
The problem proposed in certainly above-mentioned background technology.
For achieving the above object, the present invention provides following technical scheme:
A kind of multi-functional upper of a shoe cloth, including bottom cloth layer, also including waterproof layer, anti-corrosion layer and wearing layer, institute
State bottom cloth layer upper surface and waterproof layer is stained with by adhesive, waterproof layer upper surface is provided with anti-corrosion layer, it is described
Anti-corrosion layer upper surface is provided with wearing layer, and the bottom cloth layer is worked out by warp thread and weft yarn, the warp thread and
Weft yarn is formed by weaving using nano silver fibre, and the waterproof layer is PTFE thin film, and the anti-corrosion layer adopts glass
Glass fiber cloth is 0.1-0.2mm into the thickness of, the waterproof layer, and the thickness of the anti-corrosion layer 3 is
0.4-0.6mm, the thickness of the wearing layer is 0.5-0.7mm;The wearing layer includes according to the raw material of weight portion:
Polyester fiber 60-80 parts, cotton fiber 60-80 parts, polypropylene fiber 50-60 parts, Radix Glycyrrhizae 4-6 parts, Radix Bupleuri
4-6 parts, Lignum cinnamomi camphorae 4-6 parts, Flos Lonicerae 4-6 parts, raw tarragon 4-6 part, Herba Ephedrae (processed) 3-5 parts, Rhizoma Atractylodis Macrocephalae 3-5 parts,
Gypsum Fibrosum 3-5 parts, Fructus Gleditsia 3-5 parts, Folium Bambusae 2-4 parts, Aloe 2-4 parts, Radix Paeoniae Alba 2-4 parts, Flos Magnoliae 2-4
Part, Myrrha 2-4 parts, Fructus Corni 1-2 parts, Herba Menthae 1-2 parts, Herba speranskiae tuberculatae 1-2 parts.
As further scheme of the invention:The wearing layer includes according to the raw material of weight portion:Polyester fiber
70 parts, 70 parts of cotton fiber, 55 parts of polypropylene fiber, 5 parts of Radix Glycyrrhizae, 5 parts of Radix Bupleuri, 5 parts of Lignum cinnamomi camphorae, gold
5 parts of Flos Lonicerae, 5 parts of raw tarragon, 4 parts of Herba Ephedrae (processed), 4 parts of the Rhizoma Atractylodis Macrocephalae, 4 parts of Gypsum Fibrosum, 4 parts of Fructus Gleditsia, Folium Bambusae
3 parts, 3 parts of Aloe, 3 parts of the Radix Paeoniae Alba, 3 parts of Flos Magnoliae, 3 parts of Myrrha, 1.5 parts of Fructus Corni, 1.5 parts of Herba Menthae,
1.5 parts of Herba speranskiae tuberculatae.
As further scheme of the invention:The adhesive adopts PUR.
The preparation method of the wearing layer, comprises the following steps that:
1) each raw material is weighed according to weight portion;
2) by polyester fiber, cotton fiber and polypropylene fiber using clean water 2-3 time post-drying, then will drying
Polypropylene fiber afterwards carries out roller dye 40-60min to which in being put into treatment fluid, standby after the completion of roller dye;
3) by Radix Glycyrrhizae, Radix Bupleuri, Lignum cinnamomi camphorae, Flos Lonicerae, raw tarragon, Herba Ephedrae (processed), the Rhizoma Atractylodis Macrocephalae, Gypsum Fibrosum, soap
Angle, Folium Bambusae, Aloe, the Radix Paeoniae Alba, Flos Magnoliae, Myrrha, Fructus Corni, Herba Menthae and Herba speranskiae tuberculatae decoct 3-5h with water slow fire,
It is filtrated to get Chinese herbal medicine fluid;
4) Chinese herbal medicine fluid is injected in 35-45 DEG C of water, polyester fiber that addition was processed, cotton fiber and third
Synthetic fibre fiber, adds the softening agent of 4-6 parts, carries out supersound process, supersound process 4-8h simultaneously in immersion line;
5) will weave into interweaving after the drying of polyester fiber containing herbal mediciment, cotton fiber and polypropylene fiber again wear-resisting
Layer.
As further scheme of the invention:The treatment fluid includes according to the raw material of weight portion:Modified starch
15-20 parts, ethylene glycol 10-15 parts, acrylate 10-15 parts, fatty alcohol-polyoxyethylene ether 0.02-0.03 parts,
Distilled water 50-70 parts.
Compared with prior art, the invention has the beneficial effects as follows:
In the present invention, bottom cloth layer is worked out by warp thread and weft yarn, and the warp thread and weft yarn are spun using nano silver fibre
Knit and form, nano silver fibre can be to the tens of kinds of pathogenic microorganism such as escherichia coli, gonococcuss, chlamydia trachomatiss
There are strong suppression and killing action, antibacterial effect is preferable;Simultaneously as possessing waterproof layer, corrosion-resistant
Layer and wearing layer, improve water resistance, corrosion resistance and the wearability of upper of a shoe cloth, are soaked with Chinese herbal medicine fluid
The wearing layer crossed also with delicate fragrance taste, this abnormal smells from the patient can be kept for a long time, thus long-time storage cloth or
Person's shoes are infested mouldy without worrying.
Description of the drawings
Fig. 1 is the structural representation of the present invention.
Specific embodiment
The technical scheme of this patent is described in more detail with reference to specific embodiment.
Embodiment 1
Fig. 1 is referred to, a kind of multi-functional upper of a shoe cloth, including bottom cloth layer 1, also including waterproof layer 2, corrosion resistant
Erosion layer 3 and wearing layer 4,1 upper surface of the bottom cloth layer is stained with waterproof layer 2 by PUR, in waterproof layer 2
Upper surface is provided with anti-corrosion layer 3, and 3 upper surface of the anti-corrosion layer is provided with wearing layer 4, the bottom cloth layer
1 is worked out by warp thread and weft yarn, and the warp thread and weft yarn are formed by weaving using nano silver fibre, the waterproof
Layer 2 is PTFE thin film, and the anti-corrosion layer 3 made using glass fabric, the thickness of the waterproof layer 2
For 0.1mm, the thickness of the anti-corrosion layer 3 is 0.4mm, and the thickness of the wearing layer 4 is 0.5mm;
The wearing layer 4 includes according to the raw material of weight portion:60 parts of polyester fiber, 60 parts of cotton fiber, polypropylene fiber
50 parts, 4 parts of Radix Glycyrrhizae, 4 parts of Radix Bupleuri, 4 parts of Lignum cinnamomi camphorae, 4 parts of Flos Lonicerae, 4 parts of raw tarragon, Herba Ephedrae (processed) 3
Part, 3 parts of the Rhizoma Atractylodis Macrocephalae, 3 parts of Gypsum Fibrosum, 3 parts of Fructus Gleditsia, 2 parts of Folium Bambusae, 2 parts of Aloe, 2 parts of the Radix Paeoniae Alba, Flos Magnoliae
2 parts, 2 parts of Myrrha, 1 part of Fructus Corni, 1 part of Herba Menthae, 1 part of Herba speranskiae tuberculatae.
The preparation method of the wearing layer 4, comprises the following steps that:
1) each raw material is weighed according to weight portion;
2) polyester fiber, cotton fiber and polypropylene fiber are adopted into 2 times post-dryings of clean water, then after drying
Polypropylene fiber be put into treatment fluid in which is carried out roller dye 40min, roller dye after the completion of it is standby;The treatment fluid is pressed
Include according to the raw material of weight portion:15 parts of modified starch, 10 parts of ethylene glycol, 10 parts of acrylate, fatty alcohol
0.02 part of polyoxyethylene ether, 50 parts of distilled water;
3) by Radix Glycyrrhizae, Radix Bupleuri, Lignum cinnamomi camphorae, Flos Lonicerae, raw tarragon, Herba Ephedrae (processed), the Rhizoma Atractylodis Macrocephalae, Gypsum Fibrosum, soap
Angle, Folium Bambusae, Aloe, the Radix Paeoniae Alba, Flos Magnoliae, Myrrha, Fructus Corni, Herba Menthae and Herba speranskiae tuberculatae decoct 3h with water slow fire,
It is filtrated to get Chinese herbal medicine fluid;
4) Chinese herbal medicine fluid is injected in 35 DEG C of water, polyester fiber, cotton fiber and polypropylene that addition was processed
Fiber, adds 4 parts of softening agent, carries out supersound process, supersound process 4h simultaneously in immersion line;
5) will weave into interweaving after the drying of polyester fiber containing herbal mediciment, cotton fiber and polypropylene fiber again wear-resisting
Layer 4.
Embodiment 2
Fig. 1 is referred to, a kind of multi-functional upper of a shoe cloth, including bottom cloth layer 1, also including waterproof layer 2, corrosion resistant
Erosion layer 3 and wearing layer 4,1 upper surface of the bottom cloth layer is stained with waterproof layer 2 by PUR, in waterproof layer 2
Upper surface is provided with anti-corrosion layer 3, and 3 upper surface of the anti-corrosion layer is provided with wearing layer 4, the bottom cloth layer
1 is worked out by warp thread and weft yarn, and the warp thread and weft yarn are formed by weaving using nano silver fibre, the waterproof
Layer 2 is PTFE thin film, and the anti-corrosion layer 3 made using glass fabric, the thickness of the waterproof layer 2
For 0.15mm, the thickness of the anti-corrosion layer 3 is 0.5mm, and the thickness of the wearing layer 4 is 0.6mm;
The wearing layer 4 includes according to the raw material of weight portion:70 parts of polyester fiber, 70 parts of cotton fiber, polypropylene fiber
55 parts, 5 parts of Radix Glycyrrhizae, 5 parts of Radix Bupleuri, 5 parts of Lignum cinnamomi camphorae, 5 parts of Flos Lonicerae, 5 parts of raw tarragon, Herba Ephedrae (processed) 4
Part, 4 parts of the Rhizoma Atractylodis Macrocephalae, 4 parts of Gypsum Fibrosum, 4 parts of Fructus Gleditsia, 3 parts of Folium Bambusae, 3 parts of Aloe, 3 parts of the Radix Paeoniae Alba, Flos Magnoliae
3 parts, 3 parts of Myrrha, 1.5 parts of Fructus Corni, 1.5 parts of Herba Menthae, 1.5 parts of Herba speranskiae tuberculatae.
The preparation method of the wearing layer 4, comprises the following steps that:
1) each raw material is weighed according to weight portion;
2) polyester fiber, cotton fiber and polypropylene fiber are adopted into 3 times post-dryings of clean water, then after drying
Polypropylene fiber be put into treatment fluid in which is carried out roller dye 50min, roller dye after the completion of it is standby;The treatment fluid is pressed
Include according to the raw material of weight portion:18 parts of modified starch, 12 parts of ethylene glycol, 12 parts of acrylate, fatty alcohol
0.025 part of polyoxyethylene ether, 60 parts of distilled water;
3) by Radix Glycyrrhizae, Radix Bupleuri, Lignum cinnamomi camphorae, Flos Lonicerae, raw tarragon, Herba Ephedrae (processed), the Rhizoma Atractylodis Macrocephalae, Gypsum Fibrosum, soap
Angle, Folium Bambusae, Aloe, the Radix Paeoniae Alba, Flos Magnoliae, Myrrha, Fructus Corni, Herba Menthae and Herba speranskiae tuberculatae decoct 4h with water slow fire,
It is filtrated to get Chinese herbal medicine fluid;
4) Chinese herbal medicine fluid is injected in 40 DEG C of water, polyester fiber, cotton fiber and polypropylene that addition was processed
Fiber, adds 5 parts of softening agent, carries out supersound process, supersound process 6h simultaneously in immersion line;
5) will weave into interweaving after the drying of polyester fiber containing herbal mediciment, cotton fiber and polypropylene fiber again wear-resisting
Layer 4.
Embodiment 3
Fig. 1 is referred to, a kind of multi-functional upper of a shoe cloth, including bottom cloth layer 1, also including waterproof layer 2, corrosion resistant
Erosion layer 3 and wearing layer 4,1 upper surface of the bottom cloth layer is stained with waterproof layer 2 by PUR, in waterproof layer 2
Upper surface is provided with anti-corrosion layer 3, and 3 upper surface of the anti-corrosion layer is provided with wearing layer 4, the bottom cloth layer
1 is worked out by warp thread and weft yarn, and the warp thread and weft yarn are formed by weaving using nano silver fibre, the waterproof
Layer 2 is PTFE thin film, and the anti-corrosion layer 3 made using glass fabric, the thickness of the waterproof layer 2
For 0.2mm, the thickness of the anti-corrosion layer 3 is 0.6mm, and the thickness of the wearing layer 4 is 0.7mm;
The wearing layer 4 includes according to the raw material of weight portion:80 parts of polyester fiber, 80 parts of cotton fiber, polypropylene fiber
60 parts, 6 parts of Radix Glycyrrhizae, 6 parts of Radix Bupleuri, 6 parts of Lignum cinnamomi camphorae, 6 parts of Flos Lonicerae, 6 parts of raw tarragon, Herba Ephedrae (processed) 5
Part, 5 parts of the Rhizoma Atractylodis Macrocephalae, 5 parts of Gypsum Fibrosum, 5 parts of Fructus Gleditsia, 4 parts of Folium Bambusae, 4 parts of Aloe, 4 parts of the Radix Paeoniae Alba, Flos Magnoliae
4 parts, 4 parts of Myrrha, 2 parts of Fructus Corni, 2 parts of Herba Menthae, 2 parts of Herba speranskiae tuberculatae.
The preparation method of the wearing layer 4, comprises the following steps that:
1) each raw material is weighed according to weight portion;
2) polyester fiber, cotton fiber and polypropylene fiber are adopted into 2 times post-dryings of clean water, then after drying
Polypropylene fiber be put into treatment fluid in which is carried out roller dye 60min, roller dye after the completion of it is standby;The treatment fluid is pressed
Include according to the raw material of weight portion:20 parts of modified starch, 15 parts of ethylene glycol, 15 parts of acrylate, fatty alcohol
0.03 part of polyoxyethylene ether, 70 parts of distilled water;
3) by Radix Glycyrrhizae, Radix Bupleuri, Lignum cinnamomi camphorae, Flos Lonicerae, raw tarragon, Herba Ephedrae (processed), the Rhizoma Atractylodis Macrocephalae, Gypsum Fibrosum, soap
Angle, Folium Bambusae, Aloe, the Radix Paeoniae Alba, Flos Magnoliae, Myrrha, Fructus Corni, Herba Menthae and Herba speranskiae tuberculatae decoct 5h with water slow fire,
It is filtrated to get Chinese herbal medicine fluid;
4) Chinese herbal medicine fluid is injected in 45 DEG C of water, polyester fiber, cotton fiber and polypropylene that addition was processed
Fiber, adds 6 parts of softening agent, carries out supersound process, supersound process 8h simultaneously in immersion line;
5) will weave into interweaving after the drying of polyester fiber containing herbal mediciment, cotton fiber and polypropylene fiber again wear-resisting
Layer 4.
In the present invention, bottom cloth layer 1 is worked out by warp thread and weft yarn, and the warp thread and weft yarn adopt nano silver fibre
It is formed by weaving, nano silver fibre can be to tens of kinds of micro- lifes of causing a disease such as escherichia coli, gonococcuss, chlamydia trachomatiss
Thing has strong suppression and killing action, and antibacterial effect is preferable;Simultaneously as possessing waterproof layer 2, resistance to
Corrosion layer 3 and wearing layer 4, improve water resistance, corrosion resistance and the wearability of upper of a shoe cloth, use medium-height grass
The wearing layer 4 that medicinal liquid the soaked also taste with delicate fragrance, can keep this abnormal smells from the patient for a long time, so long-time
Storage cloth or shoes are infested mouldy without worrying.
Above the better embodiment of this patent is explained in detail, but this patent is not limited to above-mentioned enforcement
Mode, in the ken that one skilled in the relevant art possesses, can be with without departing from this patent ancestor
On the premise of purport, various changes can be made.
Claims (5)
1. a kind of multi-functional upper of a shoe cloth, it is characterised in that including bottom cloth layer(1), also including waterproof layer(2), anti-corrosion layer(3)And wearing layer(4), the bottom cloth layer(1)Upper surface is stained with waterproof layer by adhesive(2), in waterproof layer(2)Upper surface is provided with anti-corrosion layer(3), the anti-corrosion layer(3)Upper surface is provided with wearing layer(4), the bottom cloth layer(1)Worked out by warp thread and weft yarn, the warp thread and weft yarn are formed by weaving using nano silver fibre, the waterproof layer(2)For PTFE thin film, the anti-corrosion layer(3)Made using glass fabric, the waterproof layer(2)Thickness be 0.1-0.2mm, the anti-corrosion layer(3)Thickness be 0.4-0.6mm, the wearing layer(4)Thickness be 0.5-0.7mm;The wearing layer(4)Raw material according to weight portion includes:Polyester fiber 60-80 parts, cotton fiber 60-80 parts, polypropylene fiber 50-60 parts, Radix Glycyrrhizae 4-6 parts, Radix Bupleuri 4-6 parts, Lignum cinnamomi camphorae 4-6 parts, Flos Lonicerae 4-6 parts, raw tarragon 4-6 part, Herba Ephedrae (processed) 3-5 parts, Rhizoma Atractylodis Macrocephalae 3-5 parts, Gypsum Fibrosum 3-5 parts, Fructus Gleditsia 3-5 parts, Folium Bambusae 2-4 parts, Aloe 2-4 parts, Radix Paeoniae Alba 2-4 parts, Flos Magnoliae 2-4 parts, Myrrha 2-4 parts, Fructus Corni 1-2 parts, Herba Menthae 1-2 parts, Herba speranskiae tuberculatae 1-2 parts.
2. multi-functional upper of a shoe cloth according to claim 1, it is characterised in that the wearing layer(4)Raw material according to weight portion includes:70 parts of polyester fiber, 70 parts of cotton fiber, 55 parts of polypropylene fiber, 5 parts of Radix Glycyrrhizae, 5 parts of Radix Bupleuri, 5 parts of Lignum cinnamomi camphorae, 5 parts of Flos Lonicerae, 5 parts of raw tarragon, 4 parts of Herba Ephedrae (processed), 4 parts of the Rhizoma Atractylodis Macrocephalae, 4 parts of Gypsum Fibrosum, 4 parts of Fructus Gleditsia, 3 parts of Folium Bambusae, 3 parts of Aloe, 3 parts of the Radix Paeoniae Alba, 3 parts of Flos Magnoliae, 3 parts of Myrrha, 1.5 parts of Fructus Corni, 1.5 parts of Herba Menthae, 1.5 parts of Herba speranskiae tuberculatae.
3. multi-functional upper of a shoe cloth according to claim 1, it is characterised in that the adhesive adopts PUR.
4. a kind of multi-functional upper of a shoe cloth as described in claim 1-2 is arbitrary, it is characterised in that the wearing layer(4)Preparation method, comprise the following steps that:
1)Each raw material is weighed according to weight portion;
2)By polyester fiber, cotton fiber and polypropylene fiber using clean water 2-3 all over post-drying, then the polypropylene fiber after drying is put in treatment fluid which is carried out roller dye 40-60min, it is standby after the completion of roller dye;
3)Radix Glycyrrhizae, Radix Bupleuri, Lignum cinnamomi camphorae, Flos Lonicerae, raw tarragon, Herba Ephedrae (processed), the Rhizoma Atractylodis Macrocephalae, Gypsum Fibrosum, Fructus Gleditsia, Folium Bambusae, Aloe, the Radix Paeoniae Alba, Flos Magnoliae, Myrrha, Fructus Corni, Herba Menthae and Herba speranskiae tuberculatae are decocted into 3-5h with water slow fire, Chinese herbal medicine fluid is filtrated to get;
4)Chinese herbal medicine fluid is injected in 35-45 DEG C of water, polyester fiber, cotton fiber and polypropylene fiber that addition was processed add the softening agent of 4-6 parts, supersound process, supersound process 4-8h is carried out simultaneously in immersion line;
5)Wearing layer will be weaved into interweaving after the drying of polyester fiber containing herbal mediciment, cotton fiber and polypropylene fiber again(4).
5. multi-functional upper of a shoe cloth according to claim 4, it is characterised in that the treatment fluid includes according to the raw material of weight portion:Modified starch 15-20 parts, ethylene glycol 10-15 parts, acrylate 10-15 parts, fatty alcohol-polyoxyethylene ether 0.02-0.03 parts, distilled water 50-70 parts.