CN106498271A - 一种含铬耐磨铸铁及其制备方法 - Google Patents
一种含铬耐磨铸铁及其制备方法 Download PDFInfo
- Publication number
- CN106498271A CN106498271A CN201610931476.6A CN201610931476A CN106498271A CN 106498271 A CN106498271 A CN 106498271A CN 201610931476 A CN201610931476 A CN 201610931476A CN 106498271 A CN106498271 A CN 106498271A
- Authority
- CN
- China
- Prior art keywords
- iron
- containing chromium
- inovulant
- intermediate frequency
- ferrosilicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含铬耐磨铸铁及其制备方法,所述的含铬耐磨铸铁其成分的重量百分比为C2.7~3.6%、Si1.65~2.7%、Mn0.5~1.2%、Cr0.2~0.5%、S≤0.09%,余量为Fe。所述的制备方法包括配料、预热、熔炼、炉前快速分析、终脱氧、孕育处理、浇注。该方法铸造工艺简单,通过严格控制铬的加入量,提髙机械强度、耐磨等综合性能,其机械性能可达HT250牌号,特别适合铸造汽缸、活塞环和挺杆。
Description
技术领域
本发明涉及黑色金属的生产技术领域,尤其是一种含铬耐磨铸铁及其制备方法。
背景技术
含铬耐磨铸铁是一种性能优良的减磨材料,它具有很高的硬度和延长铸件的使用寿命的特点。作为减磨铸铁时,一般含铬量均在0.5%以下,避免出现游离碳化物。
发明内容
本发明所需解决的技术问题是提供一种含铬耐磨铸铁及其制备方法。通过控制铸铁中铬的加入量,铸造出耐磨铸铁。
本发明解决其技术问题所采用的技术方案是:它的成分的重量百分比为:C2.7~3.6%、Si1.65~2.7%、Mn0.5~1.2%、Cr0.2~0.5%、S≤0.09%,余量为Fe。
一种制备含铬耐磨铸铁的方法,包括下述几个步骤:
第一步:配料:将废钢、回炉料、生铁、锰铁、硅铁按C2.7~3.6%、Si1.65~2.7%、Mn0.5~1.2%、Cr0.2~0.5%、S≤0.09%,余量为Fe重量百分比的方式进行配料;
第二步:预热:将优化计算好的废钢、回炉料、生铁投入中频感应炉内进行预热;
第三步:熔炼:将中频感应炉内的废钢、回炉料、生铁熔化后,投入其数量为炉料19~30%,成分为石灰70%+萤石30%的脱氧剂进行预脱氧,再投入烘烤处理的锰铁和硅铁得到铁液;
第四步:炉前快速分析:取铁液浇注试样进行快速分析,根据分析结果调整化学成分;
第五步:终脱氧:将铁液温度升温至1550~1660℃,投入其数量为铁液0.1~0.3%的铝进行终脱氧;
第六步:孕育处理:铁液自中频感应炉流向浇包时进行孕育处理,加入其数量为铁液量的0.3~0.5%孕育剂,孕育剂的粒度为2~6mm,孕育剂为75硅铁;
第七步:浇注:待铁液温度降至1430~1550℃时,进行浇注,得到铸件。
本发明的有益效果是:铸造工艺简单,通过严格控制铬的加入量,提髙机械强度、耐磨等综合性能,其机械性能可达HT250牌号,特别适合铸造汽缸、活塞环和挺杆。
具体实施方式
实施例1:
本例的一种制备含铬耐磨铸铁的方法,包括下述几个步骤:
第一步:配料:将废钢、回炉料、生铁、锰铁、硅铁按C2.7%、Si1.65%、Mn0.5%、Cr0.2%、S≤0.09%,余量为Fe重量百分比的方式进行配料;
第二步:预热:将优化计算好的废钢、回炉料、生铁投入中频感应炉内进行预热;
第三步:熔炼:将中频感应炉内的废钢、回炉料、生铁熔化后,投入其数量为炉料19%,成分为石灰70%+萤石30%的脱氧剂进行预脱氧,再投入烘烤处理的锰铁和硅铁得到铁液;
第四步:炉前快速分析:取铁液浇注试样进行快速分析,根据分析结果调整化学成分;
第五步:终脱氧:将铁液温度升温至1550℃,投入其数量为铁液0.1%的铝进行终脱氧;
第六步:孕育处理:铁液自中频感应炉流向浇包时进行孕育处理,加入其数量为铁液量的0.3%孕育剂,孕育剂的粒度为2mm,孕育剂为75硅铁;
第七步:浇注:待铁液温度降至1430℃时,进行浇注,得到铸件。
实施例2:
本例的一种制备含铬耐磨铸铁的方法,包括下述几个步骤:
第一步:配料:将废钢、回炉料、生铁、锰铁、硅铁按C3.15%、Si2.175%、Mn0.85%、Cr0.35%、S≤0.09%,余量为Fe重量百分比的方式进行配料;
第二步:预热:将优化计算好的废钢、回炉料、生铁投入中频感应炉内进行预热;
第三步:熔炼:将中频感应炉内的废钢、回炉料、生铁熔化后,投入其数量为炉料24%,成分为石灰70%+萤石30%的脱氧剂进行预脱氧,再投入烘烤处理的锰铁和硅铁得到铁液;
第四步:炉前快速分析:取铁液浇注试样进行快速分析,根据分析结果调整化学成分;
第五步:终脱氧:将铁液温度升温至1605℃,投入其数量为铁液0.2%的铝进行终脱氧;
第六步:孕育处理:铁液自中频感应炉流向浇包时进行孕育处理,加入其数量为铁液量的0.4%孕育剂,孕育剂的粒度为4mm,孕育剂为75硅铁;
第七步:浇注:待铁液温度降至1495℃时,进行浇注,得到铸件。
实施例3:
本例的一种制备含铬耐磨铸铁的方法,包括下述几个步骤:
第一步:配料:将废钢、回炉料、生铁、锰铁、硅铁按C3.6%、Si2.7%、Mn1.2%、Cr0.5%、S≤0.09%,余量为Fe重量百分比的方式进行配料;
第二步:预热:将优化计算好的废钢、回炉料、生铁投入中频感应炉内进行预热;
第三步:熔炼:将中频感应炉内的废钢、回炉料、生铁熔化后,投入其数量为炉料30%,成分为石灰70%+萤石30%的脱氧剂进行预脱氧,再投入烘烤处理的锰铁和硅铁得到铁液;
第四步:炉前快速分析:取铁液浇注试样进行快速分析,根据分析结果调整化学成分;
第五步:终脱氧:将铁液温度升温至1660℃,投入其数量为铁液0.3%的铝进行终脱氧;
第六步:孕育处理:铁液自中频感应炉流向浇包时进行孕育处理,加入其数量为铁液量的0.5%孕育剂,孕育剂的粒度为6mm,孕育剂为75硅铁;
第七步:浇注:待铁液温度降至1550℃时,进行浇注,得到铸件。
以上对本发明的具体实施方式作了说明,但这些说明不能被理解为限制了本发明的范围,本发明的保护范围由随附的权利要求书限定,仼何在本发明权利要求基础上的任何修改、等同替换和改进等,均落入本发明的保护范围之內。
Claims (2)
1.一种含铬耐磨铸铁,其特征在于:它的成分的重量百分比为:C2.7~3.6%、Si1.65~2.7%、Mn0.5~1.2%、Cr0.2~0.5%、S≤0.09%,余量为Fe。
2.一种制备权利要求1所述的含铬耐磨铸铁的方法,其特征在于:包括下述几个步骤:
第一步:配料:将废钢、回炉料、生铁、锰铁、硅铁按C2.7~3.6%、Si1.65~2.7%、Mn0.5~1.2%、Cr0.2~0.5%、S≤0.09%,余量为Fe重量百分比的方式进行配料;
第二步:预热:将优化计算好的废钢、回炉料、生铁投入中频感应炉内进行预热;
第三步:熔炼:将中频感应炉内的废钢、回炉料、生铁熔化后,投入其数量为炉料19~30%,成分为石灰70%+萤石30%的脱氧剂进行预脱氧,再投入烘烤处理的锰铁和硅铁得到铁液;
第四步:炉前快速分析:取铁液浇注试样进行快速分析,根据分析结果调整化学成分;
第五步:终脱氧:将铁液温度升温至1550~1660℃,投入其数量为铁液0.1~0.3%的铝进行终脱氧;
第六步:孕育处理:铁液自中频感应炉流向浇包时进行孕育处理,加入其数量为铁液量的0.3~0.5%孕育剂,孕育剂的粒度为2~6mm,孕育剂为75硅铁;
第七步:浇注:待铁液温度降至1430~1550℃时,进行浇注,得到铸件。