CN106497532A - A kind of preparation method of organo-mineral complexing Gelling Water shutoff Agent - Google Patents
A kind of preparation method of organo-mineral complexing Gelling Water shutoff Agent Download PDFInfo
- Publication number
- CN106497532A CN106497532A CN201610801863.8A CN201610801863A CN106497532A CN 106497532 A CN106497532 A CN 106497532A CN 201610801863 A CN201610801863 A CN 201610801863A CN 106497532 A CN106497532 A CN 106497532A
- Authority
- CN
- China
- Prior art keywords
- waterglass
- inorganic composite
- organic
- reaction vessel
- technical grade
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation method of organo-mineral complexing Gelling Water shutoff Agent, waterglass is soluble in water in reaction vessel under room temperature, polysaccharide is added under stirring in reaction vessel, then in reaction vessel, add pH adjusting agent to adjust and stabilizer, stir the organo-mineral complexing gel precursors that obtain, organo-mineral complexing gel precursors are stood more than 2 hours, organo-mineral complexing gel is obtained, the gel is as a result of polysaccharide as silicic acid gel additive, raw material has the feature of environmental protection, low cost, easy to operate, water used is low to prescription, can nearby using water source in application.
Description
Technical field
The present invention relates to the preparation and application technical field of Organic-inorganic composite gel, and in particular to a kind of organic and inorganic
The preparation method of pluralgel water shutoff agent.
Background technology
Late period of oil field well water problem generally existing, not only have impact on oil recovery efficiency and oil quality, and
And huge economic losses are caused, need to carry out profile control and water plugging, especially with the oil field of waterflooding extraction commingling production mode, water blockoff
Operation was particularly important in the later stage of recovering the oil.More effectively method is that chemical plugging agent is injected oil well and note to administer well water
The water exit interval of well, reduces the water phase permeability of Thief zone water exit interval, has effectively blocked Thief zone, can force injection water
Less permeable layer in entrance, improves its sweep efficiency, improves reservoir recovery.With water-blocking operation more and more frequent, blocking agent
Consumption constantly increases.At present oil field with relatively broad be polymer organic water plugging profile control agent, because its price is higher, increased
Water-blocking operation cost, and there is no the feature of environmental protection.By contrast, silicic acid gel blocking agent have cheap, closure efficiency high with
And the advantages of good temperature resistance, salt resistance, the near wellbore zone profile control agent as the non-selective water shutoff agent and well of oil well is extensive
It is applied in oil development.But it is short to there is also gel time, the shortcomings of the hard brittleness of colloid is easily broken greatly, this all affects water blockoff
Efficiency.
Content of the invention
In order to overcome the shortcoming of above-mentioned prior art, it is an object of the invention to provide a kind of Organic-inorganic composite gel
The preparation method of water shutoff agent, the water shutoff agent improve its toughness and gel-forming property, strengthen the effect of water blockoff.
In order to achieve the above object, the technical solution used in the present invention is:
A kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent, comprises the following steps:
The first step, is dissolved in waterglass in its 5-20 times of quality water under room temperature in reaction vessel, and the waterglass includes industry
Level and its above purity modulus are not more than 2 waterglass, and the water is that salinity is not more than 4 × 104/mg·L-1River, well
Water, oil produced water and its mixed liquor;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:The polysaccharide of 10-500, stirs, institute
Polysaccharide is stated for the guar gum of technical grade and its above purity, Fructus Gleditsia glue, gumshiraz, xanthan gum, carboxymethyl starch, carboxymethyl cellulose
Element, sodium alginate and combinations thereof;
3rd step, adds mass concentration in reaction vessel for the mixing of the stabilizer of the pH adjusting agent and 0.1-0.5% of 1-10%
Liquid, stir the Organic-inorganic composite gel precursors that obtain, and the pH adjusting agent is the acetic acid of technical grade and its above purity
Acid anhydride, propionic andydride, maleic anhydride, benzoyl oxide and combinations thereof, the stabilizer are technical grade and its above purity dodecyl
Sodium sulfonate, sodium lauryl sulphate, dodecylbenzene sodium sulfonate, sodium heavy alkyl benzene sulfonate or petroleum sulfonate;
Organic-inorganic composite gel precursors are stood more than 2 hours, that is, obtain Organic-inorganic composite gel by the 4th step.
Beneficial effects of the present invention are:As a result of polysaccharide as silicic acid gel additive, raw material has ring to the gel
Guarantor property, low cost are easy to operate, and water used is low to prescription, can nearby using water source in application.
Specific embodiment
With reference to embodiment, the invention will be further described.
Embodiment 1
A kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent, comprises the following steps:
The first step, is dissolved in waterglass in its 5 times of quality water under room temperature in reaction vessel, and the waterglass is technical grade purity
Modulus is 2 waterglass, and it is 4 × 10 that the water is salinity4/mg·L-1Oil produced water;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:200 polysaccharide, stirs, described
Guar gum of the polysaccharide for technical grade purity;
3rd step, in reaction vessel add mass concentration be 1% pH adjusting agent and 0.1% stabilizer mixed liquor, stirring
Organic-inorganic composite gel precursors are uniformly obtained, and acetic anhydride of the pH adjusting agent for technical grade, the stabilizer are industry
Level dodecyl sodium sulfate;
Organic-inorganic composite gel precursors are stood 8 hours, that is, obtain Organic-inorganic composite gel by the 4th step.
As a result of polysaccharide as silicic acid gel additive, raw material has the feature of environmental protection, low cost, operation letter to the gel
Just, water used is low to prescription, can nearby using water source in application.
Embodiment 2
A kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent, comprises the following steps:
The first step, is dissolved in waterglass in its 8 times of quality water under room temperature in reaction vessel, and the waterglass is technical grade purity
Modulus is 1.5 waterglass, and it is 1 × 10 that the water is salinity4/mg·L-1Oil produced water;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:50 polysaccharide, stirs, described poly-
Fructus Gleditsia glue of the sugar for technical grade purity;
3rd step, in reaction vessel add mass concentration be 2% pH adjusting agent and 0.2% stabilizer mixed liquor, stirring
Organic-inorganic composite gel precursors are uniformly obtained, and the pH adjusting agent is technical grade maleic anhydride, and the stabilizer is industrial
Level sodium lauryl sulphate;
Organic-inorganic composite gel precursors are stood 7 hours, that is, obtain Organic-inorganic composite gel by the 4th step.
As a result of polysaccharide as silicic acid gel additive, raw material has the feature of environmental protection, low cost, operation letter to the gel
Just, water used is low to prescription, can nearby using water source in application.
Embodiment 3
A kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent, comprises the following steps:
The first step, is dissolved in waterglass in its 10 times of quality water under room temperature in reaction vessel, and the waterglass is that technical grade is pure
Degree modulus is 1.2 waterglass, and it is 5 × 10 that the water is salinity3/mg·L-1Well water;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:100 polysaccharide, stirs, described
Xanthan gum of the polysaccharide for technical grade purity;
3rd step, in reaction vessel add mass concentration be 5% pH adjusting agent and 0.5% stabilizer mixed liquor, stirring
Organic-inorganic composite gel precursors are uniformly obtained, and the pH adjusting agent is that chemical purified petroleum benzin formic anhydride, the stabilizer are analysis
Pure dodecylbenzene sodium sulfonate;
Organic-inorganic composite gel precursors are stood 5 hours, that is, obtain Organic-inorganic composite gel by the 4th step.
As a result of polysaccharide as silicic acid gel additive, raw material has the feature of environmental protection, low cost, operation letter to the gel
Just, water used is low to prescription, can nearby using water source in application.
Embodiment 4
A kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent, comprises the following steps:
The first step, is dissolved in waterglass in its 15 times of quality water under room temperature in reaction vessel, and the waterglass is that technical grade is pure
Degree modulus is 1.5 waterglass, and it is 2 × 10 that the water is salinity2/mg·L-1River;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:150 polysaccharide, stirs, described
Carboxymethyl starch of the polysaccharide for technical grade purity;
3rd step, in reaction vessel add mass concentration be 6% pH adjusting agent and 0.5% stabilizer mixed liquor, stirring
Organic-inorganic composite gel precursors are uniformly obtained, and the pH adjusting agent is technical grade propionic andydride, and the stabilizer is technical grade
Sodium heavy alkyl benzene sulfonate;
Organic-inorganic composite gel precursors are stood 6 hours, that is, obtain Organic-inorganic composite gel by the 4th step.
As a result of polysaccharide as silicic acid gel additive, raw material has the feature of environmental protection, low cost, operation letter to the gel
Just, water used is low to prescription, can nearby using water source in application.
Embodiment 5
A kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent, comprises the following steps:
The first step, is dissolved in waterglass in its 20 times of quality water under room temperature in reaction vessel, and the waterglass is that technical grade is pure
Degree modulus is 1.2 waterglass, and it is 3 × 10 that the water is salinity2/mg·L-1River;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:30 polysaccharide, stirs, described poly-
Carboxymethyl cellulose of the sugar for technical grade purity;
3rd step, in reaction vessel add mass concentration be 10% pH adjusting agent and 0.5% stabilizer mixed liquor, stirring
Organic-inorganic composite gel precursors are uniformly obtained, and the pH adjusting agent is technical grade acetic anhydride, and the stabilizer is technical grade
Petroleum sulfonate;
Organic-inorganic composite gel precursors are stood 4 hours, that is, obtain Organic-inorganic composite gel by the 4th step.
As a result of polysaccharide as silicic acid gel additive, raw material has the feature of environmental protection, low cost, operation letter to the gel
Just, water used is low to prescription, can nearby using water source in application.
Embodiment 6
A kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent, comprises the following steps:
The first step, is dissolved in waterglass in its 10 times of quality water under room temperature in reaction vessel, and the waterglass is that technical grade is pure
Degree modulus is 2 waterglass, and it is 2 × 10 that the water is salinity4/mg·L-1River and oil produced water mixed liquor;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:80 polysaccharide, stirs, described poly-
Sodium alginate of the sugar for technical grade purity;
3rd step, in reaction vessel add mass concentration be 6% pH adjusting agent and 0.4% stabilizer mixed liquor, stirring
Organic-inorganic composite gel precursors are uniformly obtained, and it is 4 that the pH adjusting agent is mass ratio:1 technical grade acetic anhydride and Malaysia
Anhydride, the stabilizer are technical grade sodium lauryl sulphate;
Organic-inorganic composite gel precursors are stood more than 2 hours, that is, obtain Organic-inorganic composite gel by the 4th step.
As a result of polysaccharide as silicic acid gel additive, raw material has the feature of environmental protection, low cost, operation letter to the gel
Just, water used is low to prescription, can nearby using water source in application.
Claims (7)
1. a kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent, it is characterised in that:Comprise the following steps:
The first step, is dissolved in waterglass in its 5-20 times of quality water under room temperature in reaction vessel, and the waterglass includes industry
Level and its above purity modulus are not more than 2 waterglass, and the water is that salinity is not more than 4 × 104/mg·L-1River, well
Water, oil produced water and its mixed liquor;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:The polysaccharide of 10-500, stirs, institute
Polysaccharide is stated for the guar gum of technical grade and its above purity, Fructus Gleditsia glue, gumshiraz, xanthan gum, carboxymethyl starch, carboxymethyl cellulose
Element, sodium alginate and combinations thereof;
3rd step, adds mass concentration in reaction vessel for the mixing of the stabilizer of the pH adjusting agent and 0.1-0.5% of 1-10%
Liquid, stir the Organic-inorganic composite gel precursors that obtain, and the pH adjusting agent is the acetic acid of technical grade and its above purity
Acid anhydride, propionic andydride, maleic anhydride, benzoyl oxide and combinations thereof, the stabilizer are technical grade and its above purity dodecyl
Sodium sulfonate, sodium lauryl sulphate, dodecylbenzene sodium sulfonate, sodium heavy alkyl benzene sulfonate or petroleum sulfonate;
Organic-inorganic composite gel precursors are stood more than 2 hours, that is, obtain Organic-inorganic composite gel by the 4th step.
2. a kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent according to claim 1, it is characterised in that bag
Include following steps:
The first step, is dissolved in waterglass in its 5 times of quality water under room temperature in reaction vessel, and the waterglass is technical grade purity
Modulus is 2 waterglass, and it is 4 × 10 that the water is salinity4/mg·L-1Oil produced water;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:200 polysaccharide, stirs, described
Guar gum of the polysaccharide for technical grade purity;
3rd step, in reaction vessel add mass concentration be 1% pH adjusting agent and 0.1% stabilizer mixed liquor, stirring
Organic-inorganic composite gel precursors are uniformly obtained, and acetic anhydride of the pH adjusting agent for technical grade, the stabilizer are industry
Level dodecyl sodium sulfate;
Organic-inorganic composite gel precursors are stood 8 hours, that is, obtain Organic-inorganic composite gel by the 4th step.
3. a kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent according to claim 1, it is characterised in that bag
Include following steps:
The first step, is dissolved in waterglass in its 8 times of quality water under room temperature in reaction vessel, and the waterglass is technical grade purity
Modulus is 1.5 waterglass, and it is 1 × 10 that the water is salinity4/mg·L-1Oil produced water;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:50 polysaccharide, stirs, described poly-
Fructus Gleditsia glue of the sugar for technical grade purity;
3rd step, in reaction vessel add mass concentration be 2% pH adjusting agent and 0.2% stabilizer mixed liquor, stirring
Organic-inorganic composite gel precursors are uniformly obtained, and the pH adjusting agent is technical grade maleic anhydride, and the stabilizer is industrial
Level sodium lauryl sulphate;
Organic-inorganic composite gel precursors are stood 7 hours, that is, obtain Organic-inorganic composite gel by the 4th step.
4. a kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent according to claim 1, it is characterised in that bag
Include following steps:
The first step, is dissolved in waterglass in its 10 times of quality water under room temperature in reaction vessel, and the waterglass is that technical grade is pure
Degree modulus is 1.2 waterglass, and it is 5 × 10 that the water is salinity3/mg·L-1Well water;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:100 polysaccharide, stirs, described
Xanthan gum of the polysaccharide for technical grade purity;
3rd step, in reaction vessel add mass concentration be 5% pH adjusting agent and 0.5% stabilizer mixed liquor, stirring
Organic-inorganic composite gel precursors are uniformly obtained, and the pH adjusting agent is that chemical purified petroleum benzin formic anhydride, the stabilizer are analysis
Pure dodecylbenzene sodium sulfonate;
Organic-inorganic composite gel precursors are stood 5 hours, that is, obtain Organic-inorganic composite gel by the 4th step.
5. a kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent according to claim 1, it is characterised in that bag
Include following steps:
The first step, is dissolved in waterglass in its 15 times of quality water under room temperature in reaction vessel, and the waterglass is that technical grade is pure
Degree modulus is 1.5 waterglass, and it is 2 × 10 that the water is salinity2/mg·L-1River;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:150 polysaccharide, stirs, described
Carboxymethyl starch of the polysaccharide for technical grade purity;
3rd step, in reaction vessel add mass concentration be 6% pH adjusting agent and 0.5% stabilizer mixed liquor, stirring
Organic-inorganic composite gel precursors are uniformly obtained, and the pH adjusting agent is technical grade propionic andydride, and the stabilizer is technical grade
Sodium heavy alkyl benzene sulfonate;
Organic-inorganic composite gel precursors are stood 6 hours, that is, obtain Organic-inorganic composite gel by the 4th step.
6. a kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent according to claim 1, it is characterised in that bag
Include following steps:
The first step, is dissolved in waterglass in its 20 times of quality water under room temperature in reaction vessel, and the waterglass is that technical grade is pure
Degree modulus is 1.2 waterglass, and it is 3 × 10 that the water is salinity2/mg·L-1River;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:30 polysaccharide, stirs, described poly-
Carboxymethyl cellulose of the sugar for technical grade purity;
3rd step, in reaction vessel add mass concentration be 10% pH adjusting agent and 0.5% stabilizer mixed liquor, stirring
Organic-inorganic composite gel precursors are uniformly obtained, and the pH adjusting agent is technical grade acetic anhydride, and the stabilizer is technical grade
Petroleum sulfonate;
Organic-inorganic composite gel precursors are stood 4 hours, that is, obtain Organic-inorganic composite gel by the 4th step.
7. a kind of preparation method of Organic-inorganic composite Gelling Water shutoff Agent according to claim 1, it is characterised in that bag
Include following steps:
The first step, is dissolved in waterglass in its 10 times of quality water under room temperature in reaction vessel, and the waterglass is that technical grade is pure
Degree modulus is 2 waterglass, and it is 2 × 10 that the water is salinity4/mg·L-1River and oil produced water mixed liquor;
Second step, it is 1 to add the ratio with waterglass quality under stirring in reaction vessel:80 polysaccharide, stirs, described poly-
Sodium alginate of the sugar for technical grade purity;
3rd step, in reaction vessel add mass concentration be 6% pH adjusting agent and 0.4% stabilizer mixed liquor, stirring
Organic-inorganic composite gel precursors are uniformly obtained, and it is 4 that the pH adjusting agent is mass ratio:1 technical grade acetic anhydride and Malaysia
Anhydride, the stabilizer are technical grade sodium lauryl sulphate;
Organic-inorganic composite gel precursors are stood more than 2 hours, that is, obtain Organic-inorganic composite gel by the 4th step.