CN106495515A - 抗裂纤维膨胀剂 - Google Patents
抗裂纤维膨胀剂 Download PDFInfo
- Publication number
- CN106495515A CN106495515A CN201610949237.3A CN201610949237A CN106495515A CN 106495515 A CN106495515 A CN 106495515A CN 201610949237 A CN201610949237 A CN 201610949237A CN 106495515 A CN106495515 A CN 106495515A
- Authority
- CN
- China
- Prior art keywords
- swelling agent
- fiber
- crack
- agent
- crack fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及混泥土添加剂领域,尤其涉及一种抗裂纤维膨胀剂;技术方案为:抗裂纤维膨胀剂,以质量百分比计,其组成为:膨胀剂 95‑99%,纤维 0.1‑0.2%,分散剂 0.5‑5%;本发明提供一种抗裂纤维剂,可以有效防止开裂,大大增加混泥土的使用寿命。
Description
技术领域
本发明涉及混泥土添加剂领域,尤其涉及一种抗裂纤维膨胀剂。
背景技术
目前,现有技术在全程抗裂方的存在不足,未能从不同层面,以不同方式,在不同的时段对混泥土表现出抵御收缩混泥土进行施工,这难以达到预期技术效果,不仅增加了成本,而且人工投料带来的投料危险和投料精准度等问题已凸显出来。
纤维膨胀剂是国内新一代多功能抗裂型聚合物纤维膨胀剂。它是以可再分散高分子聚合物,三元膨胀组份及高强度的砼伴纤维,经科学复配而成。由于聚合物纤维膨胀剂中的单丝纤维以单位体积内较大的数量均匀分布于混凝土内部,故微裂缝在发展的过程中必然遭遇到纤维的阻挡,消耗了大部分能量,CaO-MgO-Al2O3-SO3四种组份形成三个不同的膨胀源,它们同时水化的速度不同,在混凝土形成的过程中,建立起早期、中期、后期不同的微膨胀力,抵卸混凝土在形成过程中不同时期的收缩力,所以裂缝难以进一步发展,从而阻断裂缝的发展,达到抗裂的作用。尤其是纤维的加入就同在混凝土中掺入巨大数量的微细筋,在混凝土中形成二次加筋效应,使膨胀组份在限制条件下更充分的发挥,形成的叠加效应使混凝土更加密实,稳定;很大程度减弱了开裂的进程,提高了混凝土的断裂韧性,而这些单靠加强钢筋是不能实现的。
发明内容
本发明的目的在于提供一种抗裂纤维剂,可以有效防止开裂,大大增加混泥土的使用寿命。
为解决上述技术问题,本发明的技术方案为:
抗裂纤维膨胀剂,以质量百分比计,其组成为:膨胀剂 95-99%,纤维 0.1-0.2%,分散剂0.5-5%;
所述膨胀剂的比表面积为200m2/kg。
所述膨胀剂为粉煤灰、石膏粉、铝矿渣中的至少一种。
所述纤维为改性聚丙烯纤维。
所述分散剂为六偏磷酸钠、焦磷酸钠中的一种。
本发明同现有技术相比具有的有益效果为:通过改性聚丙烯纤维的处理,增大了纤维的比表面积,提高了混泥土的防开裂性能,使得混泥土具有良好的膨胀性能,延长混泥土的使用寿命。
具体实施方式
本发明公开了抗裂纤维膨胀剂,本领域技术人员可以借鉴本文内容,适当改进工艺参数实现。特别需要指出的是,所有类似的替换和改动对本领域技术人员来说是显而易见的,它们都被视为包括在本发明。本发明所述产品已经通过较佳实施例进行了描述,相关人员明显能在不脱离本发明内容、精神和范围内对本文所述的组合物和应用进行改动或适当变更与组合,来实现和应用本发明技术。
以下结合具体实施例对本发明作进一步说明。
实施例1
抗裂纤维膨胀剂,以质量百分比计,粉煤灰 45%,石膏粉 53%,改性聚丙烯纤维 0.1%,六偏磷酸钠 1.9%。
实施例2
抗裂纤维膨胀剂剂,以质量百分比计,粉煤灰 98%,改性聚丙烯纤维 0.2%,六偏磷酸钠1.8%。
实施例3
抗裂纤维膨胀剂剂,以质量百分比计,粉石膏粉 99%,改性聚丙烯纤维 0.2%,六偏磷酸钠 0.8%。
实施例4
抗裂纤维膨胀剂剂,以质量百分比计,粉煤灰 94.8%,改性聚丙烯纤维 0.2%,六偏磷酸钠 5%。
实施例5
抗裂纤维膨胀剂剂,以质量百分比计,铝矿渣 98%,改性聚丙烯纤维 0.2%,六偏磷酸钠1.8%。
实施例6
抗裂纤维膨胀剂剂,以质量百分比计,粉煤灰 98%,改性聚丙烯纤维 0.2%,六偏磷酸钠1.8%。
实施例7
抗裂纤维膨胀剂剂,以质量百分比计,粉煤灰 99%,改性聚丙烯纤维 0.5%,六偏磷酸钠0.5%。
实施例8
抗裂纤维膨胀剂剂,以质量百分比计,粉煤灰 45%,铝矿渣 53%,改性聚丙烯纤维0.2%,六偏磷酸钠 1.8%。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (4)
1. 抗裂纤维膨胀剂,其特征在于,以质量百分比计,其组成为:膨胀剂 95-99%,纤维0.1-0.2%,分散剂 0.5-5%;
所述膨胀剂的比表面积为200m2/kg。
2.根据权利要求1所述的抗裂纤维膨胀剂,其特征在于,所述膨胀剂为粉煤灰、石膏粉、铝矿渣中的至少一种。
3.根据权利要求1所述的抗裂纤维膨胀剂,其特征在于,所述纤维为改性聚丙烯纤维。
4.根据权利要求1所述的抗裂纤维膨胀剂,其特征在于,所述分散剂为六偏磷酸钠、焦磷酸钠中的一种。