CN106479437A - A kind of antistatic high brightness aqueouss composite and preparation method thereof - Google Patents

A kind of antistatic high brightness aqueouss composite and preparation method thereof Download PDF

Info

Publication number
CN106479437A
CN106479437A CN201610748311.5A CN201610748311A CN106479437A CN 106479437 A CN106479437 A CN 106479437A CN 201610748311 A CN201610748311 A CN 201610748311A CN 106479437 A CN106479437 A CN 106479437A
Authority
CN
China
Prior art keywords
parts
aqueouss
composite
silicone oil
high brightness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610748311.5A
Other languages
Chinese (zh)
Inventor
吴家猛
吴刚
陈铖
丁维
李伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI SKY EYE INTELLIGENT TECHNOLOGY Co Ltd
Original Assignee
ANHUI SKY EYE INTELLIGENT TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI SKY EYE INTELLIGENT TECHNOLOGY Co Ltd filed Critical ANHUI SKY EYE INTELLIGENT TECHNOLOGY Co Ltd
Priority to CN201610748311.5A priority Critical patent/CN106479437A/en
Publication of CN106479437A publication Critical patent/CN106479437A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of antistatic high brightness aqueouss composite, its raw material includes complex wax, compound emulsifying agent, polyvinyl alcohol, triethanolamine oleate, sodium hydroxyethlcellulose, amido silicon oil, simethicone, 350cst silicone oil, 1000cst silicone oil, amido silicon oil, trihydroxyethyl methyl quaternary ammonium Methylsulfate, glyceryl tristearate, dodecylbenzene sodium sulfonate, potassium sorbate, N methyl pyrrolidone, wetting agent HX 3088, grinding agent and water.The present invention also proposes a kind of preparation method of above-mentioned antistatic high brightness aqueouss composite.It is raw material that the aqueouss composite of the present invention adopts complex wax to replace traditional single wax, and the aqueouss composite preparing has excellent antistatic property, and brightness is high, and combination property is strong.

Description

A kind of antistatic high brightness aqueouss composite and preparation method thereof
Technical field
The present invention relates to the technical field of composite, more particularly, to a kind of antistatic high brightness aqueouss composite and its Preparation method.
Background technology
Constantly improve with people's living standard, automobile also progressively enters into huge numbers of families.Cleaning automobile seriously consumes Water resource, for using water wisely, water conservation, for solving few use, to clean the problem of automobile, on existing market without water Occur in that aqueouss composite.With car quantity increase sharply and people's rhythm of life quickening, people are to automobile table The cleaning in face, adding lustre to keeps a public place clean proposes higher and higher requirement, but the carwash commonly used, waxing mode are still traditional high pressure at present Hydraulic giant rinses, and waxes after drying, the method for polishing.Waste time and energy, and price high it is impossible to meet actually used during need Ask, therefore need a kind of antistatic high brightness aqueouss composite of exploitation badly to solve the problems of the prior art.
Content of the invention
For solving technical problem present in background technology, the present invention proposes a kind of antistatic high brightness aqueouss composite And preparation method thereof, it is raw material that the aqueouss composite preparing adopts complex wax to replace traditional single wax, prepares Aqueouss composite there is excellent antistatic property, brightness is high, and combination property is strong.
A kind of antistatic high brightness aqueouss composite proposed by the present invention, its raw material includes by weight:Complex wax 15- 25 parts, compound emulsifying agent 3-9 part, polyvinyl alcohol 1-4 part, triethanolamine oleate 2-5 part, sodium hydroxyethlcellulose 3-5 part, amino Silicone oil 1-4 part, simethicone 2-5 part, 350cst silicone oil 1-4 part, 1000cst silicone oil 3-5 part, amido silicon oil 1-4 part, three hydroxyl second Ylmethyl quaternary ammonium Methylsulfate 2-5 part, glyceryl tristearate 3-5 part, dodecylbenzene sodium sulfonate 1-4 part, potassium sorbate 2-5 Part, N-Methyl pyrrolidone 3-6 part, wetting agent HX-3088 2-5 part, grinding agent 1-5 part, water 6-12 part.
Preferably, complex wax is by amide waxe, paraffin and palm wax 1-3 by weight:2-5:3-6 mixes.
Preferably, compound emulsifying agent is by dodecylbenzene sodium sulfonate, fatty alcohol-polyoxyethylene ether, alkylphenol-polyethenoxy Ether, nekal and Brij 35 sodium sulfate are by weight 2-4:1-3:2-5:3-6:1.5-3.5 Mix.
Preferably, the weight of complex wax, compound emulsifying agent, polyvinyl alcohol, triethanolamine oleate and sodium hydroxyethlcellulose Than for 18-22:4-8:2-3:3-4:3.5-4.5.
Preferably, its raw material includes by weight:Complex wax 18-22 part, compound emulsifying agent 4-8 part, polyvinyl alcohol 2-3 Part, triethanolamine oleate 3-4 part, sodium hydroxyethlcellulose 3.5-4.5 part, amido silicon oil 2-3 part, simethicone 3-4 part, 350cst silicone oil 2-3 part, 1000cst silicone oil 3.5-4.5 part, amido silicon oil 2-3 part, trihydroxyethyl methyl quaternary ammonium Methylsulfate 3- 4 parts, glyceryl tristearate 3.5-4.5 part, dodecylbenzene sodium sulfonate 2-3 part, potassium sorbate 3-4 part, N- crassitude Ketone 4-5 part, wetting agent HX-3088 3-4 part, grinding agent 2-4 part, water 8-10 part.
Preferably, its raw material includes by weight:20 parts of complex wax, 6 parts of compound emulsifying agent, 2.5 parts of polyvinyl alcohol, Oleic acid 3.5 parts of triethanolamine, 4 parts of sodium hydroxyethlcellulose, 2.5 parts of amido silicon oil, 3.5 parts of simethicone, 2.5 parts of 350cst silicone oil, 4 parts of 1000cst silicone oil, 2.5 parts of amido silicon oil, 3.5 parts of trihydroxyethyl methyl quaternary ammonium Methylsulfate, 4 parts of glyceryl tristearate, 2.5 parts of dodecylbenzene sodium sulfonate, 3.5 parts of potassium sorbate, 4.5 parts of N-Methyl pyrrolidone, 3.5 parts of wetting agent HX-3088, 3 parts of grinding agent, 9 parts of water.
A kind of antistatic high brightness aqueouss composite material and preparation method thereof proposed by the present invention, comprises the steps:
S1, by complex wax, compound emulsifying agent, polyvinyl alcohol, triethanolamine oleate, trihydroxyethyl methyl quaternary ammonium sulphuric acid first Ester, glyceryl tristearate, dodecylbenzene sodium sulfonate, N-Methyl pyrrolidone and wetting agent HX-3088 mix homogeneously, heat up To 95-105 DEG C, carry out continuously stirred in temperature-rise period, be cooled to room temperature and obtain material a;
S2, material a is warming up to 70-80 DEG C, in material a, then adds amido silicon oil, simethicone, 350cst silicon Oil, 1000cst silicone oil and amido silicon oil mix homogeneously, then heat to 85-95 DEG C, carry out continuously stirred in temperature-rise period, It is subsequently adding sodium hydroxyethlcellulose and water, is cooled to 50-60 DEG C, add potassium sorbate and grinding agent, stirring, be cooled to room temperature Obtain antistatic high brightness aqueouss composite.
A kind of antistatic high brightness aqueouss composite of the present invention, its raw material includes complex wax, compound emulsifying agent, poly- second Enol, triethanolamine oleate, sodium hydroxyethlcellulose, amido silicon oil, simethicone, 350cst silicone oil, 1000cst silicone oil, ammonia Base silicone oil, trihydroxyethyl methyl quaternary ammonium Methylsulfate, glyceryl tristearate, dodecylbenzene sodium sulfonate, potassium sorbate, N- first Base ketopyrrolidine, wetting agent HX-3088, grinding agent and water.Wherein with complex wax as major ingredient, complex wax by amide waxe, paraffin and Palm wax mixes, and solves the problems, such as that single wax performance is not enough, gives aqueouss composite of the present invention excellent antistatic High brightness capabilities, and add compound emulsifying agent, polyvinyl alcohol, triethanolamine oleate, sodium hydroxyethlcellulose, amido silicon oil, two First silicone oil, 350cst silicone oil, 1000cst silicone oil, amido silicon oil, trihydroxyethyl methyl quaternary ammonium Methylsulfate, three glycerol stearate Ester, dodecylbenzene sodium sulfonate, potassium sorbate, N-Methyl pyrrolidone, wetting agent HX-3088, grinding agent and water are auxiliary agent, system It is raw material that the standby aqueouss composite obtaining adopts complex wax to replace traditional single wax, the aqueouss composite tool preparing There is excellent antistatic property, brightness is high, combination property is strong.
Specific embodiment
With reference to specific embodiment, the present invention is described in detail it should be appreciated that embodiment is served only for this is described Bright, rather than be used for limiting the invention, any modification made on the basis of the present invention, equivalent etc. are all at this In bright protection domain.
In specific embodiment, the weight portion of complex wax can for 15 parts, 16 parts, 17 parts, 18 parts, 19 parts, 20 parts, 21 Part, 22 parts, 23 parts, 24 parts, 25 parts;The weight portion of compound emulsifying agent can be 3 parts, 4 parts, 5 parts, 6 parts, 7 parts, 8 parts, 9 parts;Poly- The weight portion of vinyl alcohol can be 1 part, 1.5 parts, 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts;The weight portion of triethanolamine oleate can Think 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts;The weight portion of sodium hydroxyethlcellulose can for 3 parts, 3.5 parts, 4 Part, 4.5 parts, 5 parts;The weight portion of amido silicon oil can be 1 part, 1.5 parts, 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts;Simethicone Weight portion can be 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts;The weight portion of 350cst silicone oil can for 1 part, 1.5 parts, 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts;The weight portion of 1000cst silicone oil can for 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 Part;The weight portion of amido silicon oil can be 1 part, 1.5 parts, 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts;Trihydroxyethyl methyl quaternary ammonium sulfur The weight portion of sour methyl ester can be 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts;The weight portion of glyceryl tristearate Can be 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts;The weight portion of dodecylbenzene sodium sulfonate can for 1 part, 1.5 parts, 2 parts, 2.5 Part, 3 parts, 3.5 parts, 4 parts;The weight portion of potassium sorbate can for 2 parts, 2.5 parts, 3 parts, 3.5 parts, 3.5 parts, 4 parts, 4.5 parts, 5 Part;The weight portion of N-Methyl pyrrolidone can be 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts, 5.5 parts, 6 parts;Wetting agent HX- 3088 weight portion can be 2 parts, 2.5 parts, 3 parts, 3.5 parts, 4 parts, 4.5 parts, 5 parts;The weight portion of grinding agent can for 1 part, 2 Part, 3 parts, 4 parts, 5 parts;The weight portion of water can be 6 parts, 7 parts, 8 parts, 9 parts, 10 parts, 11 parts, 12 parts.
Embodiment 1
A kind of antistatic high brightness aqueouss composite proposed by the present invention, its raw material includes by weight:Complex wax 20 Part, 6 parts of compound emulsifying agent, 2.5 parts of polyvinyl alcohol, 3.5 parts of triethanolamine oleate, 4 parts of sodium hydroxyethlcellulose, amido silicon oil 2.5 parts, 3.5 parts of simethicone, 2.5 parts of 350cst silicone oil, 4 parts of 1000cst silicone oil, 2.5 parts of amido silicon oil, trihydroxyethyl methyl 3.5 parts of quaternary ammonium Methylsulfate, 4 parts of glyceryl tristearate, 2.5 parts of dodecylbenzene sodium sulfonate, 3.5 parts of potassium sorbate, N- first 4.5 parts of base ketopyrrolidine, 3.5 parts of wetting agent HX-3088,3 parts of grinding agent, 9 parts of water.
Wherein, complex wax is by amide waxe, paraffin and palm wax by weight 2:3.5:4.5 mixing.Compound emulsifying agent By dodecylbenzene sodium sulfonate, fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, nekal and dodecyl Polyoxyethylenated alcohol sodium sulfate by weight 3:2:3.5:4.5:2.5 mixing.
A kind of antistatic high brightness aqueouss composite material and preparation method thereof proposed by the present invention, comprises the steps:
S1, by complex wax, compound emulsifying agent, polyvinyl alcohol, triethanolamine oleate, trihydroxyethyl methyl quaternary ammonium sulphuric acid first Ester, glyceryl tristearate, dodecylbenzene sodium sulfonate, N-Methyl pyrrolidone and wetting agent HX-3088 mix homogeneously, heat up To 100 DEG C, carry out in the process heating up continuously stirred, be cooled to room temperature and obtain material a;
S2, material a is warming up to 75 DEG C, then add in material a amido silicon oil, simethicone, 350cst silicone oil, 1000cst silicone oil and amido silicon oil mix homogeneously, then heat to 90 DEG C, and the process of intensification does not stop to stir, and is subsequently adding carboxylic second Base sodium cellulosate and water, are cooled to 55 DEG C, add potassium sorbate and grinding agent, stirring, and being cooled to room temperature, to obtain antistatic highlighted Degree aqueouss composite.
Embodiment 2
A kind of antistatic high brightness aqueouss composite proposed by the present invention, its raw material includes by weight:Complex wax 15 Part, 9 parts of compound emulsifying agent, 1 part of polyvinyl alcohol, 5 parts of triethanolamine oleate, 3 parts of sodium hydroxyethlcellulose, 4 parts of amido silicon oil, two 2 parts of first silicone oil, 4 parts of 350cst silicone oil, 3 parts of 1000cst silicone oil, 4 parts of amido silicon oil, trihydroxyethyl methyl quaternary ammonium Methylsulfate 2 Part, 5 parts of glyceryl tristearate, 1 part of dodecylbenzene sodium sulfonate, 5 parts of potassium sorbate, 3 parts of N-Methyl pyrrolidone, wetting agent HX-30885 part, 1 part of grinding agent, 12 parts of water.
Wherein, complex wax is by amide waxe, paraffin and palm wax by weight 1:5:3 mix.Compound emulsifying agent is by ten Dialkyl benzene sulfonic acids sodium, fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, nekal and dodecyl alcohol gather Oxygen ethylene ether sodium sulfate by weight 2:3:2:6:1.5 mixing.
A kind of antistatic high brightness aqueouss composite material and preparation method thereof proposed by the present invention, comprises the steps:
S1, by complex wax, compound emulsifying agent, polyvinyl alcohol, triethanolamine oleate, trihydroxyethyl methyl quaternary ammonium sulphuric acid first Ester, glyceryl tristearate, dodecylbenzene sodium sulfonate, N-Methyl pyrrolidone and wetting agent HX-3088 mix homogeneously, heat up To 95 DEG C, the process of intensification does not stop to stir, and is cooled to room temperature and obtains material a;
S2, material a is warming up to 80 DEG C, then add in material a amido silicon oil, simethicone, 350cst silicone oil, 1000cst silicone oil and amido silicon oil mix homogeneously, then heat to 85 DEG C, carry out continuously stirred, Ran Houjia in the process heating up Enter sodium hydroxyethlcellulose and water, be cooled to 60 DEG C, add potassium sorbate and grinding agent, stirring, be cooled to room temperature obtain anti-quiet Electric high brightness aqueouss composite.
Embodiment 3
A kind of antistatic high brightness aqueouss composite proposed by the present invention, its raw material includes by weight:Complex wax 25 Part, 3 parts of compound emulsifying agent, 4 parts of polyvinyl alcohol, 2 parts of triethanolamine oleate, 5 parts of sodium hydroxyethlcellulose, 1 part of amido silicon oil, two 5 parts of first silicone oil, 1 part of 350cst silicone oil, 5 parts of 1000cst silicone oil, 1 part of amido silicon oil, trihydroxyethyl methyl quaternary ammonium Methylsulfate 5 Part, 3 parts of glyceryl tristearate, 4 parts of dodecylbenzene sodium sulfonate, 2 parts of potassium sorbate, 6 parts of N-Methyl pyrrolidone, wetting agent HX-30882 part, 5 parts of grinding agent, 6 parts of water.
Wherein, complex wax is by amide waxe, paraffin and palm wax by weight 3:2:6 mix.Compound emulsifying agent is by ten Dialkyl benzene sulfonic acids sodium, fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, nekal and dodecyl alcohol gather Oxygen ethylene ether sodium sulfate by weight 4:1:5:3:3.5 mixing.
A kind of antistatic high brightness aqueouss composite material and preparation method thereof proposed by the present invention, comprises the steps:
S1, by complex wax, compound emulsifying agent, polyvinyl alcohol, triethanolamine oleate, trihydroxyethyl methyl quaternary ammonium sulphuric acid first Ester, glyceryl tristearate, dodecylbenzene sodium sulfonate, N-Methyl pyrrolidone and wetting agent HX-3088 mix homogeneously, heat up To 105 DEG C, carry out in the process heating up continuously stirred, be cooled to room temperature and obtain material a;
S2, material a is warming up to 70 DEG C, then add in material a amido silicon oil, simethicone, 350cst silicone oil, 1000cst silicone oil and amido silicon oil mix homogeneously, then heat to 95 DEG C, and the process of intensification does not stop to stir, and is subsequently adding carboxylic second Base sodium cellulosate and water, are cooled to 50 DEG C, add potassium sorbate and grinding agent, stirring, and being cooled to room temperature, to obtain antistatic highlighted Degree aqueouss composite.
Embodiment 4
A kind of antistatic high brightness aqueouss composite proposed by the present invention, its raw material includes by weight:Complex wax 18 Part, 8 parts of compound emulsifying agent, 2 parts of polyvinyl alcohol, 4 parts of triethanolamine oleate, 3.5 parts of sodium hydroxyethlcellulose, 3 parts of amido silicon oil, 3 parts of simethicone, 3 parts of 350cst silicone oil, 3.5 parts of 1000cst silicone oil, 3 parts of amido silicon oil, trihydroxyethyl methyl quaternary ammonium sulphuric acid first 3 parts of ester, 4.5 parts of glyceryl tristearate, 2 parts of dodecylbenzene sodium sulfonate, 4 parts of potassium sorbate, 4 parts of N-Methyl pyrrolidone, Wetting agent HX-30884 part, 2 parts of grinding agent, 10 parts of water.
Wherein, complex wax is by amide waxe, paraffin and palm wax by weight 1.5:4:4 mix.Compound emulsifying agent by Dodecylbenzene sodium sulfonate, fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, nekal and dodecyl alcohol Polyethenoxy ether sodium sulfate by weight 2.5:2.5:3:5:1.8 mixing.
A kind of antistatic high brightness aqueouss composite material and preparation method thereof proposed by the present invention, comprises the steps:
S1, by complex wax, compound emulsifying agent, polyvinyl alcohol, triethanolamine oleate, trihydroxyethyl methyl quaternary ammonium sulphuric acid first Ester, glyceryl tristearate, dodecylbenzene sodium sulfonate, N-Methyl pyrrolidone and wetting agent HX-3088 mix homogeneously, heat up To 98 DEG C, carry out continuously stirred during heating up, be cooled to room temperature and obtain material a;
S2, material a is warming up to 78 DEG C, then add in material a amido silicon oil, simethicone, 350cst silicone oil, 1000cst silicone oil and amido silicon oil mix homogeneously, then heat to 88 DEG C, and the process of intensification does not stop to stir, and is subsequently adding carboxylic second Base sodium cellulosate and water, are cooled to 58 DEG C, add potassium sorbate and grinding agent, stirring, and being cooled to room temperature, to obtain antistatic highlighted Degree aqueouss composite.
Embodiment 5
A kind of antistatic high brightness aqueouss composite proposed by the present invention, its raw material includes by weight:Complex wax 22 Part, 4 parts of compound emulsifying agent, 3 parts of polyvinyl alcohol, 3 parts of triethanolamine oleate, 4.5 parts of sodium hydroxyethlcellulose, 2 parts of amido silicon oil, 4 parts of simethicone, 2 parts of 350cst silicone oil, 4.5 parts of 1000cst silicone oil, 2 parts of amido silicon oil, trihydroxyethyl methyl quaternary ammonium sulphuric acid first 4 parts of ester, 3.5 parts of glyceryl tristearate, 3 parts of dodecylbenzene sodium sulfonate, 3 parts of potassium sorbate, 5 parts of N-Methyl pyrrolidone, Wetting agent HX-30883 part, 4 parts of grinding agent, 8 parts of water.
Wherein, complex wax is by amide waxe, paraffin and palm wax by weight 2.5:3:5 mix.Compound emulsifying agent by Dodecylbenzene sodium sulfonate, fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, nekal and dodecyl alcohol Polyethenoxy ether sodium sulfate by weight 3.5:1.5:4:4:3.2 mixing.
A kind of antistatic high brightness aqueouss composite material and preparation method thereof proposed by the present invention, comprises the steps:
S1, by complex wax, compound emulsifying agent, polyvinyl alcohol, triethanolamine oleate, trihydroxyethyl methyl quaternary ammonium sulphuric acid first Ester, glyceryl tristearate, dodecylbenzene sodium sulfonate, N-Methyl pyrrolidone and wetting agent HX-3088 mix homogeneously, heat up To 102 DEG C, carry out continuously stirred during heating up, be cooled to room temperature and obtain material a;
S2, material a is warming up to 72 DEG C, then add in material a amido silicon oil, simethicone, 350cst silicone oil, 1000cst silicone oil and amido silicon oil mix homogeneously, then heat to 92 DEG C, and the process of intensification does not stop to stir, and is subsequently adding carboxylic second Base sodium cellulosate and water, are cooled to 52 DEG C, add potassium sorbate and grinding agent, stirring, and being cooled to room temperature, to obtain antistatic highlighted Degree aqueouss composite.
The above, the only present invention preferably specific embodiment, but protection scope of the present invention is not limited thereto, Any those familiar with the art the invention discloses technical scope in, technology according to the present invention scheme and its Inventive concept equivalent or change in addition, all should be included within the scope of the present invention.

Claims (7)

1. a kind of antistatic high brightness aqueouss composite is it is characterised in that its raw material includes by weight:Complex wax 15-25 Part, compound emulsifying agent 3-9 part, polyvinyl alcohol 1-4 part, triethanolamine oleate 2-5 part, sodium hydroxyethlcellulose 3-5 part, amino silicone Oily 1-4 part, simethicone 2-5 part, 350cst silicone oil 1-4 part, 1000cst silicone oil 3-5 part, amido silicon oil 1-4 part, trihydroxyethyl Methyl quaternary ammonium Methylsulfate 2-5 part, glyceryl tristearate 3-5 part, dodecylbenzene sodium sulfonate 1-4 part, potassium sorbate 2-5 Part, N-Methyl pyrrolidone 3-6 part, wetting agent HX-3088 2-5 part, grinding agent 1-5 part, water 6-12 part.
2. antistatic high brightness aqueouss composite according to claim 1 it is characterised in that complex wax by amide waxe, Paraffin and palm wax are by weight 1-3:2-5:3-6 mixes.
3. antistatic high brightness aqueouss composite according to claim 1 and 2 it is characterised in that compound emulsifying agent by Dodecylbenzene sodium sulfonate, fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene, nekal and dodecyl alcohol Polyethenoxy ether sodium sulfate is by weight 2-4:1-3:2-5:3-6:1.5-3.5 mixing.
4. the antistatic high brightness aqueouss composite according to any one of claim 1-3 it is characterised in that complex wax, The weight of compound emulsifying agent, polyvinyl alcohol, triethanolamine oleate and sodium hydroxyethlcellulose is than for 18-22:4-8:2-3:3-4: 3.5-4.5.
5. the antistatic high brightness aqueouss composite according to any one of claim 1-4 is it is characterised in that its raw material is pressed Weight portion includes:Complex wax 18-22 part, compound emulsifying agent 4-8 part, polyvinyl alcohol 2-3 part, triethanolamine oleate 3-4 part, carboxylic second Base sodium cellulosate 3.5-4.5 part, amido silicon oil 2-3 part, simethicone 3-4 part, 350cst silicone oil 2-3 part, 1000cst silicone oil 3.5-4.5 part, amido silicon oil 2-3 part, trihydroxyethyl methyl quaternary ammonium Methylsulfate 3-4 part, glyceryl tristearate 3.5-4.5 Part, dodecylbenzene sodium sulfonate 2-3 part, potassium sorbate 3-4 part, N-Methyl pyrrolidone 4-5 part, wetting agent HX-30883-4 Part, grinding agent 2-4 part, water 8-10 part.
6. the antistatic high brightness aqueouss composite according to any one of claim 1-5 is it is characterised in that its raw material is pressed Weight portion includes:20 parts of complex wax, 6 parts of compound emulsifying agent, 2.5 parts of polyvinyl alcohol, 3.5 parts of triethanolamine oleate, carboxyethyl are fine Plain 4 parts of the sodium of dimension, 2.5 parts of amido silicon oil, 3.5 parts of simethicone, 2.5 parts of 350cst silicone oil, 4 parts of 1000cst silicone oil, amido silicon oil 2.5 parts, 3.5 parts of trihydroxyethyl methyl quaternary ammonium Methylsulfate, 4 parts of glyceryl tristearate, 2.5 parts of dodecylbenzene sodium sulfonate, 3.5 parts of potassium sorbate, 4.5 parts of N-Methyl pyrrolidone, 3.5 parts of wetting agent HX-3088,3 parts of grinding agent, 9 parts of water.
7. the antistatic high brightness aqueouss composite material and preparation method thereof described in a kind of any one according to claim 1-6, its feature It is, comprise the steps:
S1, by complex wax, compound emulsifying agent, polyvinyl alcohol, triethanolamine oleate, trihydroxyethyl methyl quaternary ammonium Methylsulfate, three Tristerin, dodecylbenzene sodium sulfonate, N-Methyl pyrrolidone and wetting agent HX-3088 mix homogeneously, are warming up to 95- 105 DEG C, carry out continuously stirred in temperature-rise period, be cooled to room temperature and obtain material a;
S2, material a is warming up to 70-80 DEG C, then add in material a amido silicon oil, simethicone, 350cst silicone oil, 1000cst silicone oil and amido silicon oil mix homogeneously, then heat to 85-95 DEG C, continuously stirred in temperature-rise period, are subsequently adding Sodium hydroxyethlcellulose and water, are cooled to 50-60 DEG C, add potassium sorbate and grinding agent, stirring, be cooled to room temperature obtain anti-quiet Electric high brightness aqueouss composite.
CN201610748311.5A 2016-08-27 2016-08-27 A kind of antistatic high brightness aqueouss composite and preparation method thereof Pending CN106479437A (en)