CN106479320A - A kind of rough ground mould inhibitor - Google Patents
A kind of rough ground mould inhibitor Download PDFInfo
- Publication number
- CN106479320A CN106479320A CN201611013662.8A CN201611013662A CN106479320A CN 106479320 A CN106479320 A CN 106479320A CN 201611013662 A CN201611013662 A CN 201611013662A CN 106479320 A CN106479320 A CN 106479320A
- Authority
- CN
- China
- Prior art keywords
- parts
- rough ground
- mould inhibitor
- agent
- aqueous epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of rough ground mould inhibitor, belongs to technical field of coatings, it is made up of the raw material of following parts by weight：Propineb, decis, A.SAP, Rosemary Oil, vermiculite, inorganic aluminate water-proof agent, HEMC, PH conditioning agent, aqueous epoxy resins, aqueous epoxy curing agent.Rough ground mould inhibitor of the present invention is made up through scientific compatibility of the raw material of environmental protection, not only itself environmental protection, also there is mould proof, anti-corrosion, degerming, deinsectization, anti-ant, protection against the tide, fire-retardant function, and rough ground mould inhibitor of the present invention also have low cost, easily construct, do not ftracture, the features such as safety and stability, effect are lasting.
Description
Technical field
The invention belongs to technical field of coatings, more particularly to a kind of rough ground mould inhibitor.
Background technology
As living standard is improved constantly, people require more and more higher to living environment, and house decoration project is also increasingly
Many.The laying of furred ceiling, wall and timber floor needs substantial amounts of rough ground as foundation, because consumer generally pays little attention to wood
Mould proof, moistureproof, anti-ant of keel etc. process, cause rough ground easily to go mouldy after making moist, snake, rot or by termite moth sting, no
The service life of furred ceiling, wall and timber floor is only affected, and endangers environment and health.
Have much with regard to technical research such as mildew preventing agent for woods.Disclosed in CN105619564A《A kind of willow mildew preventing agent for wood》
Middle employing Sodium p-aminobenzene sulfonat, nano magnesia, emamectin-benzoate, positive octadecyl alcolol, resorcinol, 2- (1-
Cyclohexenyl group) cyclohexanone, dipotassium glycyrrhizinate salt, polysaccharide and 50% BAS compatibility form, make with broad-spectrum sterilization and desinsection
With, have stronger killing and rejection ability to multiple rot fungis and insect, process nondiscolouring after timber, with excellent anti-corrosion,
Mould proof, insect prevention, Anti- tarnishing effect.Though the invention with broad-spectrum sterilization deinsectization act on, its active ingredient have oxidizable decomposition,
The defect such as adhesive force is weaker, the drug effect time limit is short, can only play transience inhibitory action to mould, insect pest, the wood to hidden installation
Keel have potential disease and send out risk；Disclosed in CN104441130A《A kind of mould proof, the insect-prevention treatment method of timber》Middle employing
Following steps：（1）Timber is processed under conditions of 85-90 DEG C, relative humidity 48-50% 3h；(2), by timber in 1-
1.5MPa, the acetum at 105 DEG C using 35% fumigate 30-45min；(3), treatment fluid is prepared；(4), step (2) is processed
Good timber is using treatment fluid in 35 DEG C of immersion treatment 2h；(5), the wood surface for handling step (4) well is using at quick lime
Reason；(6), the timber for handling step (5) well processes 3h under 78 DEG C, relative humidity 25-38%.The invention methods described is to wood
Pest and disease damage entrained by material has significant insect killing effect, but timber itself still has absorbability, easy mould growth and insect pest, and
Treatment fluid made by sealwort, cloves, the banksia rose, trilliaceae, the fruit of a cubeb litsea tree, Dysosma versipellis, three money three and rhizoma arisaematis is to later stage timber
Protected effect is poor, totally assumes that technique is loaded down with trivial details, yields poorly, the problems such as high cost, equipment requirement are high, the protection period is short；
Disclosed in CN105713132A《A kind of high rigidity aqueous woodware paint and preparation method thereof》Middle using acrylic resin dispersion liquid, become
Film auxiliary agent, defoamer, levelling agent, wetting agent, thickener and water make high rigidity woodcare paint.The invention woodcare paint has city
The characteristic that common woodcare paint has on face, but its do not contain termite food kill, tag, the active ingredient such as repellent, rough ground is come
Say there is ant moth, lacquer painting cracking equivalent risk.
Content of the invention
It is an object of the invention to, for above-mentioned the deficiencies in the prior art, provide a kind of rough ground mould inhibitor.Present invention wood
Keel mould inhibitor is made up through scientific compatibility of the raw material of environmental protection, not only itself environmental protection, also has mould proof, anti-corrosion, removes
Bacterium, deinsectization, anti-ant, protection against the tide, fire-retardant function, and rough ground mould inhibitor of the present invention also have low cost, easily construction, do not open
Split, the features such as safety and stability, effect are lasting.
For solving above-mentioned technical problem, the technical solution used in the present invention is：
A kind of rough ground mould inhibitor, is made up of the raw material of following parts by weight：Propineb 3-12 part, decis 0.1-0.8 part,
A.SAP 1-2 part, Rosemary Oil 0.5-2 part, vermiculite 5-10 part, inorganic aluminate water-proof agent 6-10 part, hydroxyethyl methyl fiber
Plain 3-6 part, PH conditioning agent 0.2-1 part, aqueous epoxy resins 20-50 part, aqueous epoxy curing agent 30-50 part.
Further, a kind of above-mentioned rough ground mould inhibitor, is made up of the raw material of following parts by weight：Propineb 5-10 part,
Decis 0.3-0.6 part, A.SAP 1.2-1.8 part, Rosemary Oil 1-1.5 part, vermiculite 6-8 part, inorganic aluminate water-proof agent
7-9 part, HEMC 4-5 part, PH conditioning agent 0.5-0.8 part, aqueous epoxy resins 25-40 part, water-base epoxy are solid
Agent 35-45 part.
Further, a kind of above-mentioned rough ground mould inhibitor, is made up of the raw material of following parts by weight：8 parts of Propineb, bromine cyanogen
0.5 part of chrysanthemum ester, 1.5 parts of A.SAP, 1.3 parts of Rosemary Oil, 7 parts of vermiculite, 8 parts of inorganic aluminate water-proof agent, hydroxyethyl methyl are fine
5 parts of dimension element, 0.7 part of PH conditioning agent, 30 parts of aqueous epoxy resins, 38 parts of aqueous epoxy curing agent.
Further, above-mentioned a kind of rough ground mould inhibitor, the wherein preferred Epikote 3540-WY- of aqueous epoxy resins
One or more in 55A, Ba Ling CYDW-100, love Expo GE-95, love Expo GE-51.
Further, above-mentioned a kind of rough ground mould inhibitor, the wherein preferred EPlKURE 8535-W- of aqueous epoxy curing agent
50th, one or more in Ba Ling CYDHD-220, love Expo CU-600, Bayer N75.
Further, above-mentioned a kind of rough ground mould inhibitor, the preferred 80-200 mesh of the granularity of wherein vermiculite.
A kind of the above all raw material of rough ground mould inhibitor all can be bought by market, primary raw material is illustrated as
Under：
Propineb：English name propineb, chemical name acrylic bisdithiocarbamic zinc, white or micro-yellow powder.
More than 160 DEG C decomposition.Vapour pressure<1mPa(20℃).Relative density d23 1.813g/ml.Dissolubility (20 DEG C)：Water 0.01g/L,
In common solvent<0.1g/L.Stable upon storage under cold, drying condition.Propineb is a kind of wide spectrum, quick-acting protective fungicides
Agent, belongs to low toxicity bactericide, and bactericidal mechanism is the oxidation for suppressing pyruvic acid in pathogen body.Under the synergy of decis,
Not only can improve and scope, insect killing effect is killed, supplemented with tagging and ability being walked quickly and kept away, realize the multiple-protection of rough ground.
Decis：English name deltamethrin, chemical nameα- cyano-benzene oxygen benzyl（1R,3R）-3-（2,2- bis-
Bromo vinyl）- 2,2- dimethyl cyclopropane carboxylic acid's ester, is white tiltedly side's acicular crystal, 101 ~ 102 DEG C of fusing point, 300 DEG C of boiling point,
Water is practically insoluble under normal temperature, multiple organic solvents are dissolved in, more stable to light and air.Decis is in chrysanthemum ester insecticide
Virulence highest is a kind of, to the toxic effect of insect up to 100 times of DDT, 80 times of sevin, 550 times of malathion, right
40 times of sulphur phosphorus.Have and tag and stomach poison function, action of contace poison is rapid, knock down power by force, have repellent action to some insects.
A.SAP antiseptic：Belong to natural organic anti-bacterial deodorant, using soybean extraction liquid as main composition.Its antibacterial effect shows
Write, deodorizing effect is strong, colourless, transparent, odorlessness is widely used in gynaecologic washing lotion, sanitary napkin, wet tissue, oral hygiene, napkin
Each fields such as paper, water purification, vegetables (eating use raw) thimerosal, hand cleanser, environment disinfected.A.SAP does not have volatility, can protect for a long time
Antibacterial effect is held, the term of validity reaches more than 5 years.By A.SAP antiseptic and the solidification of aqueous epoxy resins so that this
The timeliness phase of bright rough ground mould inhibitor reaches more than 15 years.
Rosemary Oil：English name Rosemary, is a kind of colourless to faint yellow volatile liquid, nontoxicity, do not stimulate,
Allergy will not be caused.Rosemary have refresh the mind, sharp liver and expelling toxin, diuresis, the effect such as pain relieving,
The effects such as with anti-oxidant, strong disinfecting, it is usually used in food processing preservative.
Vermiculite：English name Vermiculite, is a kind of natural, inorganic, nontoxic mineral matter, can be swollen under high temperature action
Swollen mineral, are commonly used for construction material, adsorbent, fire-retardant insulating material, mechanical lubrication agent, soil conditioner etc..The present invention
Add vermiculite in rough ground mould inhibitor, the low characteristic of burning-point after epoxy resin film forming can be improved, effectively reduce disaster hidden-trouble.
HEMC：English name methyl 2-hydroxyethyl cellulose, be in methylcellulose
（MC）Middle introducing oxirane substituent（MS0.3~0.4）It is obtained, its salt tolerance is better than unmodified polymer, the gel temperature of HEMC
Degree is also high compared with MC.HEMC has very high stability, and itself does not have pollution.The above cellulose has
Very high stability, there is no pollution in itself.It is introduced in aqueous epoxy resins, the network chain molecular weight to crosslinking curing has been carried
Height, crosslink density decline, and the film of formation has certain toughening effect, can strengthen toughness and water-retaining property, have weight to crack resistence
Want meaning.
Aqueous epoxy resins：Refer to that epoxy resin is dispersed in the dispersion with water as continuous phase in the form of particulate or drop and is situated between
The stable dispersion system that joins in matter.With adaptable, good environmental protection, real Water-borne modification, operational good the features such as.
Which has high adhesive force to numerous grounds, and the film corrosion resistance after solidification and chemical resistance are excellent, and apply
Film shrinks little, hardness is high, wearability is good, electrical insulation properties are excellent etc.；As epoxy resin is the thermosetting tree of linear structure
Fat, so must be added to aqueous epoxy curing agent before construction, issues biochemical cross-linking reaction, epoxy resin cure in room temperature environment
Just change originally solvable fusible property afterwards and become insoluble insoluble space net structure, show excellent performance.Comprehensive
Upper described, due to adopting technique scheme, a kind of beneficial effect of rough ground mould inhibitor of the present invention is：
1. using aqueous epoxy resins as a kind of carrier of rough ground mould inhibitor of the present invention, in the chemistry of aqueous epoxy curing agent
Under cross-linking reaction, change originally solvable fusible property and become insoluble insoluble space net structure, the film after solidification
There is bonding jail, the performances such as high, wear-resisting, the corrosion-resistant, chemical-resistant resistance of little, hardness are shunk, can effectively completely cut off outside air, water
Vapour, mould etc., make the parasite being attached in rough ground and worm's ovum anoxic, water shortage and lose activity.The Propineb of interpolation is one
Wide spectrum, quick-acting protective fungicides is planted, belongs to low toxicity bactericide, bactericidal mechanism is the oxidation for suppressing pyruvic acid in pathogen body.
Decis is that virulence highest is a kind of in chrysanthemum ester insecticide, with tagging and stomach poison function, with action of contace poison rapid, hit
The features such as power is strong, insecticidal spectrum is wide.Under synergy of the Propineb with decis, dissipation scope, intensity can be effectively lifted
And timeliness, and decis energy its toxicity of effective blockade after aqueous epoxy resins film forming, it is to avoid cause air pollution, and surface
The decis of remaining has repellent action to insect, can effectively prevent termite destruction film layer.The Rosemary Oil of interpolation is not
Only there is the effect of strong disinfecting, and the non-oxidizability of aqueous epoxy resins film layer, anti-corrosive properties can also be strengthened.The leech of interpolation
Stone and inorganic aluminate water-proof agent, can improve fire protection flame retarding and the water resistance of aqueous epoxy resins film layer.Add ethoxy first
Base cellulose can then improve the mechanical performance of film layer, strengthen stability and toughness, solve common aqueous epoxy resins at present
The problem of cracking.
2. a kind of rough ground mould inhibitor of the present invention have inwardly kill, outwards walk quickly and keep away, the triple function of firm protection, while
Realization such as kills, blocks, walking quickly and keeping away at the function, improves the single feature of woodcare paint, preservative, mould inhibitor performance, at the same realize mould proof,
Anti-corrosion, degerming, deinsectization, anti-ant, protection against the tide, fire-retardant effect.
3. a kind of rough ground mould inhibitor of the present invention is made up through scientific compatibility of the raw material of environmental protection, not only itself green
Environmental protection, with mould proof, anti-corrosion, degerming, deinsectization, anti-ant, protection against the tide, fire-retardant function, also have low cost, easily construct, do not ftracture,
Safety and stability, timeliness phase are the features such as 15 years.
Specific embodiment
The present invention is further described with reference to specific embodiment.
Embodiment 1
A kind of rough ground mould inhibitor, is made up of the raw material of following parts by weight：3 parts of Propineb, 0.8 part of decis, A.SAP 1
Part, 2 parts of Rosemary Oil, 10 parts of 80 mesh vermiculite, 6 parts of inorganic aluminate water-proof agent, 6 parts of HEMC, PH conditioning agent
0.2 part, 50 parts of Epikote 3540-WY-55A, 30 parts of EPlKURE 8535-W-50.
Embodiment 2
A kind of rough ground mould inhibitor, is made up of the raw material of following parts by weight：12 parts of Propineb, 0.1 part of decis, A.SAP
2 parts, 0.5 part of Rosemary Oil, 50 parts of 200 mesh vermiculite, 10 parts of inorganic aluminate water-proof agent, 3 parts of HEMC, PH adjust
1 part of agent of section, 20 parts of Ba Ling CYDW-100,50 parts of Ba Ling CYDHD-220.
Embodiment 3
A kind of rough ground mould inhibitor, is made up of the raw material of following parts by weight：Propineb 5-10 part, 0.3 part of decis,
1.8 parts of A.SAP, 1 part of Rosemary Oil, 8 parts of 100 mesh vermiculite, 7 parts of inorganic aluminate water-proof agent, 5 parts of HEMC,
0.5 part of PH conditioning agent, 40 parts of Expo GE-95 of love, 35 parts of Expo CU-600 of love.
Embodiment 4
A kind of rough ground mould inhibitor, is made up of the raw material of following parts by weight：Propineb 5-10 part, 0.6 part of decis,
1.2 parts of A.SAP, 1.5 parts of Rosemary Oil, 6 parts of 120 mesh vermiculite, 9 parts of inorganic aluminate water-proof agent, HEMC 4
Part, 0.8 part of PH conditioning agent, 25 parts of Expo GE-51 of love, 45 parts of Bayer N75.
Embodiment 5
A kind of rough ground mould inhibitor, is made up of the raw material of following parts by weight：8 parts of Propineb, 0.5 part of decis, A.SAP
1.5 parts, 1.3 parts of Rosemary Oil, 7 parts of 150 mesh vermiculite, 8 parts of inorganic aluminate water-proof agent, 5 parts of HEMC, PH adjust
0.7 part of agent of section, 30 parts of Expo GE-51 of love, 38 parts of Bayer N75.
A kind of rough ground mould inhibitor that makes above-mentioned 5 kinds of embodiments separately below, carries out mould proof, anti-ant contrast test,
Its test is as follows：
First, mould proof contrast test：
A sales volume preferably certain brand woodcare paint is bought from large-scale building materials market, as the painting of this contrast test control group 1
Material, embodiment group 1-5 are corresponded to using a kind of rough ground mould inhibitor obtained in above-described embodiment 1-5.Take 7 pieces of 300 × 300 × 10mm
Dry China fir block, be respectively coated with above-mentioned 6 kinds of coating by respective construction technology, control group 2 is empty table control group, by 7 groups of tests
Block be placed under equivalent environment dry standby after 24h.With reference to GB《Mould inhibitor preventing and treating timber mould and the test method of Stain fungi》
Prescriptive procedure is processed for 7 groups of test block of examination, is put into temperature for 25-28 DEG C, and property is to cultivating 4 weeks in the constant incubator of humidity 85%
Afterwards, range estimation examination bacterium infection area and blue change degree.Test block is covered according to the whether tested bacterium infection in test block surface and mycelium
Killed value is divided 5 grades by area, is divided and is shown in Table 1, and killed value is lower, then preventing efficiency is bigger.The fungicidal properties examination of 7 groups of test group
Test and the results are shown in Table 2.
1 test block of table is gone mouldy grade scale
2 fungus test result of table
Knowable to the data of table 2：The killed value of control group 1 is in 3-4 level, and anti-mildew effect is 23-48%, illustrates to use woodcare paint
Control group anti-mold effect poor；The killed value of control group 2 is in 5 grades, and anti-mildew effect is 0, illustrates not use any coating
Blank control group nothing mould proof ability；The killed value of embodiment 1-5 is 0-1 level, and anti-mildew effect is 93-100%, and this is described
A kind of bright rough ground mould inhibitor has preferable anti-mold effect.
2nd, anti-ant contrast test：
A sales volume preferably certain brand woodcare paint is bought from large-scale building materials market, as the painting of this contrast test control group 1
Material, embodiment group 1-5 are corresponded to using a kind of rough ground mould inhibitor obtained in above-described embodiment 1-5.Take 7 pieces of 300 × 300 × 10mm
Dry China fir block, be respectively coated with above-mentioned 6 kinds of coating by respective construction technology, control group 2 is empty table control group, by 7 groups of tests
Block be placed under equivalent environment dry standby after 24h.Take Workers of Coptotermes formosanus Shiraki and eastern subterranean termite is each 210, be bisected into 7 groups at random.
Under the conditions of forcing and taking food, the weight-loss ratio of each group test block after recording a week, its result of the test are shown in Table 3.
The weight-loss ratio of 3 test block of table（%）
Knowable to the data and process of the test of table 3：Woodenware lacquer coat has certain anti-in the case of not being destroyed to termite
Moth effect, embodiment group is tagged because coating has, stomach kills effect, and two kinds of termites of process of the test are all dead.Control group 1, right
63%, 72%, 0 is respectively according to group 2, the weight-loss ratio mean value of embodiment group, it is right illustrate blank is compared using the control group 1 of woodcare paint
According to group 2 with certain anti-ant effect, and embodiment group not only has effect effect of walking quickly and keeping away to termite, also has function of tagging.
Claims (6)
1. a kind of rough ground mould inhibitor, it is characterised in that：It is made up of the raw material of following parts by weight：Propineb 3-12 part, bromine cyanogen
Chrysanthemum ester 0.1-0.8 part, A.SAP 1-2 part, Rosemary Oil 0.5-2 part, vermiculite 5-10 part, inorganic aluminate water-proof agent 6-10 part,
HEMC 3-6 part, PH conditioning agent 0.2-1 part, aqueous epoxy resins 20-50 part, aqueous epoxy curing agent 30-50
Part.
2. a kind of rough ground mould inhibitor according to claim 1, it is characterised in that：It is made up of the raw material of following parts by weight：
Propineb 5-10 part, decis 0.3-0.6 part, A.SAP 1.2-1.8 part, Rosemary Oil 1-1.5 part, vermiculite 6-8 part, no
Machine aluminate water-proof agent 7-9 part, HEMC 4-5 part, PH conditioning agent 0.5-0.8 part, aqueous epoxy resins 25-40
Part, aqueous epoxy curing agent 35-45 part.
3. a kind of rough ground mould inhibitor according to claim 1, it is characterised in that：It is made up of the raw material of following parts by weight：
8 parts of Propineb, 0.5 part of decis, 1.5 parts of A.SAP, 1.3 parts of Rosemary Oil, 7 parts of vermiculite, inorganic aluminate water-proof agent 8
Part, 5 parts of HEMC, 0.7 part of PH conditioning agent, 30 parts of aqueous epoxy resins, 38 parts of aqueous epoxy curing agent.
4. according to a kind of rough ground mould inhibitor described in claim 1 or 2 or 3, it is characterised in that：The aqueous epoxy resins are
One or more in Epikote3540-WY-55A, Ba Ling CYDW-100, love Expo GE-95, love Expo GE-51.
5. according to a kind of rough ground mould inhibitor described in claim 1 or 2 or 3, it is characterised in that：The water-base epoxy solidification
Agent is EPlKURE 8535-W-50, Ba Ling CYDHD-220, one or more liked in Expo CU-600, Bayer N75.
6. according to a kind of rough ground mould inhibitor described in claim 1 or 2 or 3, it is characterised in that：The granularity of the vermiculite is
80-200 mesh.