CN106479025A - Expanded material for automobile door plate - Google Patents
Expanded material for automobile door plate Download PDFInfo
- Publication number
- CN106479025A CN106479025A CN201610928752.3A CN201610928752A CN106479025A CN 106479025 A CN106479025 A CN 106479025A CN 201610928752 A CN201610928752 A CN 201610928752A CN 106479025 A CN106479025 A CN 106479025A
- Authority
- CN
- China
- Prior art keywords
- parts
- door plate
- expanded material
- automobile door
- didg
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of expanded material for automobile door plate, including the component of following weight portion：35 ~ 40 parts of polyethylene, 3 ~ 5 parts of natural flaky graphite, 3 ~ 6 parts of benzoin ethyl ether, 2 ~ 5 parts of TDE, 5 ~ 8 parts of eicosane amide, 3 ~ 5 parts of hexylidene diisocyanate, 8 ~ 10 parts of carbon fibre reinforced plastic, 1 ~ 4 part of Aska-Rid., 2 ~ 5 parts of white oil, 2 ~ 5 parts of cuttlefish bone meal, 1 ~ 3 part of Canola oil, 3 ~ 6 parts of DIDG and 3 ~ 5 parts of chopped basalt fibre.By the way, intensity of the present invention is high, in addition also has preferable sound insulation value.
Description
Technical field
The present invention relates to expanded material technical field, more particularly to a kind of expanded material for automobile door plate.
Background technology
Developing rapidly with social economy, the living standard more and more higher of people, the family having private car is also more next
More.When buying automobile, the people not known the business is concentrated mainly on vehicle dynamic quality, appearance looks elegant to the focus of automobile to people
The aspects such as degree, fuel economy, functional diversity, the people knowing the business also can pay close attention to automobile braking performance, manipulation stability, ride comfort with
And by aspects such as property, wherein, automotive trim aspect is increasingly paid close attention to by people now, automotive upholstery many is by foaming
Material is made, and existing this expanded material could be improved.
Content of the invention
The invention mainly solves the technical problem of providing a kind of expanded material for automobile door plate, intensity is high, in addition
Also there is preferable sound insulation value.
For solving above-mentioned technical problem, one aspect of the present invention is：There is provided a kind of for automobile door plate
Expanded material, including the component of following weight portion：35 ~ 40 parts of polyethylene, 3 ~ 5 parts of natural flaky graphite, benzoin ethyl ether 3 ~ 6
Part, 2 ~ 5 parts of TDE, 5 ~ 8 parts of eicosane amide, 3 ~ 5 parts of hexylidene diisocyanate, carbon fibre reinforced plastic 8 ~ 10
Part, 1 ~ 4 part of Aska-Rid., 2 ~ 5 parts of white oil, 2 ~ 5 parts of cuttlefish bone meal, 1 ~ 3 part of Canola oil, 3 ~ 6 parts of DIDG and short
Cut 3 ~ 5 parts of basalt fibre.
In a preferred embodiment of the present invention, including the component of following weight portion：35 parts of polyethylene, natural flakey stone
3 parts of ink, 3 parts of benzoin ethyl ether, 2 parts of TDE, 5 parts of eicosane amide, 3 parts of hexylidene diisocyanate, carbon fiber
8 parts of reinforced plastics, 1 part of Aska-Rid., 2 parts of white oil, 2 parts of cuttlefish bone meal, 1 part of Canola oil, 3 parts of DIDG and be chopped
3 parts of basalt fibre.
In a preferred embodiment of the present invention, including the component of following weight portion：36 parts of polyethylene, natural flakey stone
4 parts of ink, 5 parts of benzoin ethyl ether, 3 parts of TDE, 7 parts of eicosane amide, 4 parts of hexylidene diisocyanate, carbon fiber
9 parts of reinforced plastics, 2 parts of Aska-Rid., 4 parts of white oil, 3 parts of cuttlefish bone meal, 2 parts of Canola oil, 5 parts of DIDG and be chopped
4 parts of basalt fibre.
In a preferred embodiment of the present invention, including the component of following weight portion：40 parts of polyethylene, natural flakey stone
5 parts of ink, 6 parts of benzoin ethyl ether, 5 parts of TDE, 8 parts of eicosane amide, 5 parts of hexylidene diisocyanate, carbon fiber
10 parts of reinforced plastics, 4 parts of Aska-Rid., 5 parts of white oil, 5 parts of cuttlefish bone meal, 3 parts of Canola oil, 6 parts of DIDG and short
Cut 5 parts of basalt fibre.
The invention has the beneficial effects as follows：The present invention is used for the expanded material of automobile door plate, and intensity is high, in addition also has preferably
Sound insulation value.
Specific embodiment
The enforcement it is clear that described will be clearly and completely described to the technical scheme in the embodiment of the present invention below
Example is only a part of embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, this area is common
All other embodiment that technical staff is obtained under the premise of not making creative work, broadly falls into the model of present invention protection
Enclose.
The embodiment of the present invention includes：
Embodiment one：
A kind of expanded material for automobile door plate, including the component of following weight portion：35 parts of polyethylene, natural flaky graphite
3 parts, 3 parts of benzoin ethyl ether, 2 parts of TDE, 5 parts of eicosane amide, 3 parts of hexylidene diisocyanate, carbon fiber increase
Strong 8 parts of plastics, 1 part of Aska-Rid., 2 parts of white oil, 2 parts of cuttlefish bone meal, 1 part of Canola oil, 3 parts of DIDG and be chopped profound
3 parts of military rock fiber.
Embodiment two：
A kind of expanded material for automobile door plate, including the component of following weight portion：36 parts of polyethylene, natural flaky graphite
4 parts, 5 parts of benzoin ethyl ether, 3 parts of TDE, 7 parts of eicosane amide, 4 parts of hexylidene diisocyanate, carbon fiber increase
Strong 9 parts of plastics, 2 parts of Aska-Rid., 4 parts of white oil, 3 parts of cuttlefish bone meal, 2 parts of Canola oil, 5 parts of DIDG and be chopped profound
4 parts of military rock fiber.
Embodiment three：
A kind of expanded material for automobile door plate, including the component of following weight portion：40 parts of polyethylene, natural flaky graphite
5 parts, 6 parts of benzoin ethyl ether, 5 parts of TDE, 8 parts of eicosane amide, 5 parts of hexylidene diisocyanate, carbon fiber increase
Strong 10 parts of plastics, 4 parts of Aska-Rid., 5 parts of white oil, 5 parts of cuttlefish bone meal, 3 parts of Canola oil, 6 parts of DIDG and be chopped
5 parts of basalt fibre.
The invention has the beneficial effects as follows：The present invention is used for the expanded material of automobile door plate, and intensity is high, in addition also has preferably
Sound insulation value.
The foregoing is only embodiments of the invention, not thereby limit the present invention the scope of the claims, every using this
Equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in the technology neck of other correlations
Domain, is included within the scope of the present invention.
Claims (4)
1. a kind of expanded material for automobile door plate is it is characterised in that include the component of following weight portion：Polyethylene 35 ~ 40
Part, 3 ~ 5 parts of natural flaky graphite, 3 ~ 6 parts of benzoin ethyl ether, 2 ~ 5 parts of TDE, 5 ~ 8 parts of eicosane amide, Asia are own
3 ~ 5 parts of group diisocyanate, 8 ~ 10 parts of carbon fibre reinforced plastic, 1 ~ 4 part of Aska-Rid., 2 ~ 5 parts of white oil, 2 ~ 5 parts of cuttlefish bone meal, mustard
1 ~ 3 part of flower seed oil, 3 ~ 6 parts of DIDG and 3 ~ 5 parts of chopped basalt fibre.
2. the expanded material for automobile door plate according to claim 1 is it is characterised in that include the group of following weight portion
Part：35 parts of polyethylene, 3 parts of natural flaky graphite, 3 parts of benzoin ethyl ether, 2 parts of TDE, 5 parts of eicosane amide,
3 parts of hexylidene diisocyanate, 8 parts of carbon fibre reinforced plastic, 1 part of Aska-Rid., 2 parts of white oil, 2 parts of cuttlefish bone meal, Canola oil 1
Part, 3 parts of DIDG and 3 parts of chopped basalt fibre.
3. the expanded material for automobile door plate according to claim 1 is it is characterised in that include the group of following weight portion
Part：36 parts of polyethylene, 4 parts of natural flaky graphite, 5 parts of benzoin ethyl ether, 3 parts of TDE, 7 parts of eicosane amide,
4 parts of hexylidene diisocyanate, 9 parts of carbon fibre reinforced plastic, 2 parts of Aska-Rid., 4 parts of white oil, 3 parts of cuttlefish bone meal, Canola oil 2
Part, 5 parts of DIDG and 4 parts of chopped basalt fibre.
4. the expanded material for automobile door plate according to claim 1 is it is characterised in that include the group of following weight portion
Part：40 parts of polyethylene, 5 parts of natural flaky graphite, 6 parts of benzoin ethyl ether, 5 parts of TDE, 8 parts of eicosane amide,
5 parts of hexylidene diisocyanate, 10 parts of carbon fibre reinforced plastic, 4 parts of Aska-Rid., 5 parts of white oil, 5 parts of cuttlefish bone meal, Canola oil
3 parts, 6 parts of DIDG and 5 parts of chopped basalt fibre.