CN106476349A - 一种中草药海藻纤维保健面料及其制备方法 - Google Patents

一种中草药海藻纤维保健面料及其制备方法 Download PDF

Info

Publication number
CN106476349A
CN106476349A CN201610821717.1A CN201610821717A CN106476349A CN 106476349 A CN106476349 A CN 106476349A CN 201610821717 A CN201610821717 A CN 201610821717A CN 106476349 A CN106476349 A CN 106476349A
Authority
CN
China
Prior art keywords
mucigel
parts
weight portions
alginate fibre
surface layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610821717.1A
Other languages
English (en)
Inventor
刘玲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Baoping Intelligent Service Outsourcing Co Ltd
Original Assignee
Wuhu Baoping Intelligent Service Outsourcing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Baoping Intelligent Service Outsourcing Co Ltd filed Critical Wuhu Baoping Intelligent Service Outsourcing Co Ltd
Priority to CN201610821717.1A priority Critical patent/CN106476349A/zh
Publication of CN106476349A publication Critical patent/CN106476349A/zh
Pending legal-status Critical Current

Abstract

一种中草药海藻纤维保健面料，属于纺织面料领域，包括面层、黏胶层和内层，所述的面层是由50‑60重量份的锦纶和30‑40重量份的氨纶组成；所述的内层是由50‑60重量份的海藻纤维和30‑40重量份的苎麻纤维组成；所述的黏胶层设置于面层和内层之间，由以下重量份数的原料组成：艾叶3‑5份、甘草3‑5份、天然橡胶10‑15份。该面料具有良好的保健性能，且药物附着性、持久性好，服用性能好。

Description

一种中草药海藻纤维保健面料及其制备方法
技术领域
本发明属于纺织面料领域，具体涉及一种中草药海藻纤维保健面料及其制备方法。
背景技术
纺织服装是人类赖以生存的最基本需求之一，随着人口数量的增长和生活质量的提高，对纺织面料的要求也越来越高。人们希望纺织面料在具有传统的御寒、美观等普通功能的同时，又具有特殊的辅助功能，如药用保健功能。纺织工业发展的关键在于新产品的开发。目前，纺织技术复合化是国际纺织技术发展的主要趋势，保健药品与纺织品相互结合，以获得新的服用性和功能性。采用新材料、新工艺、新技术开发具有多用途、高性能、高附加值的产品已成为纺织品新的发展趋势，但目前关于保健面料的研究，还有待进一步发展。近年来，已经有中药改良的保健材料面世，但是市面上难有持久畅销产品出现，究其原因主要有：药物附着性和持久性差，面料的服用性能差。
发明内容
为了解决上述问题，本发明提供了一种中草药海藻纤维保健面料，该面料具有良好的保健性能，且药物附着性、持久性好，服用性能好。
为了解决上述问题，本发明采用以下技术方案：
一种中草药海藻纤维保健面料，包括面层、黏胶层和内层，所述的面层是由50-60重量份的锦纶和30-40重量份的氨纶组成；所述的内层是由50-60重量份的海藻纤维和30-40重量份的苎麻纤维组成；所述的黏胶层设置于面层和内层之间，由以下重量份数的原料组成：艾叶3-5份、甘草3-5份、天然橡胶10-15份。
优选的，所述的天然橡胶为天然乳胶。
优选的，所述的黏胶层采用以下方法制备：将艾叶、甘草采用超细化粉体加工设备制成粒径为10-20um的粉体，再加入天然橡胶混合搅拌均匀。
一种中草药海藻纤维保健面料的制备方法，包括以下步骤：
步骤一：以锦纶为经纱，氨纶为纬纱，织造得面层；
步骤二：以海藻纤维为经纱，苎麻纤维为纬纱，织造得内层；
步骤三：将黏胶层均匀涂覆于面层的一面以及内层的一面上；
步骤四：将面层附着黏胶层的一面与内层附着黏胶层的一面用电熨斗熨烫粘合在一起。
优选的，步骤四中所述的电熨斗熨烫时间为3-5min。
优选的，所述的黏胶层厚度小于0.5mm。
本发明的有益效果在于：
1)本发明的保健面料的面层采用锦纶和氨纶交织而成，锦纶具有强度高、耐磨性好等特点，作为经纱；氨纶具有弹性好等特点，作为纬纱；交织而成的面层兼具了锦纶和氨纶的优点。
2)本发明的保健面料的内层采用海藻纤维和苎麻纤维交织而成，海藻纤维具有良好的亲肤性及远红外线放射效果；苎麻纤维具有优良的抗菌性能；经两者交织而成的内层兼具了两者的优点。
3)本发明的黏胶层中包含艾叶和甘草，艾叶可以缓解皮肤瘙痒等症状，甘草具有清热解毒的功效。
4)本发明的黏胶层设置于面层和内层之间，且添加天然橡胶粘合剂，使得药物的附着性和持久性更好。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚，下面对本发明作进一步地详细描述。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
一种中草药海藻纤维保健面料，包括面层、黏胶层和内层，所述的面层是由50重量份的锦纶和30重量份的氨纶组成；所述的内层是由50重量份的海藻纤维和30重量份的苎麻纤维组成；所述的黏胶层设置于面层和内层之间，由以下重量份数的原料组成：艾叶3份、甘草3份、天然橡胶10份。
所述的天然橡胶为天然乳胶。
所述的黏胶层采用以下方法制备：将艾叶、甘草采用超细化粉体加工设备制成粒径为10-20um的粉体，再加入天然橡胶混合搅拌均匀。
所述的黏胶层厚度小于0.5mm。
一种中草药海藻纤维保健面料的制备方法，包括以下步骤：
步骤一：以锦纶为经纱，氨纶为纬纱，织造得面层；
步骤二：以海藻纤维为经纱，苎麻纤维为纬纱，织造得内层；
步骤三：将黏胶层均匀涂覆于面层的一面以及内层的一面上；
步骤四：将面层附着黏胶层的一面与内层附着黏胶层的一面用电熨斗熨烫粘合在一起，熨烫时间为3min。
实施例2
一种中草药海藻纤维保健面料，包括面层、黏胶层和内层，所述的面层是由55重量份的锦纶和35重量份的氨纶组成；所述的内层是由55重量份的海藻纤维和35重量份的苎麻纤维组成；所述的黏胶层设置于面层和内层之间，由以下重量份数的原料组成：艾叶4份、甘草4份、天然橡胶12份。
所述的天然橡胶为天然乳胶。
所述的黏胶层采用以下方法制备：将艾叶、甘草采用超细化粉体加工设备制成粒径为10-20um的粉体，再加入天然橡胶混合搅拌均匀。
所述的黏胶层厚度小于0.5mm。
一种中草药海藻纤维保健面料的制备方法，包括以下步骤：
步骤一：以锦纶为经纱，氨纶为纬纱，织造得面层；
步骤二：以海藻纤维为经纱，苎麻纤维为纬纱，织造得内层；
步骤三：将黏胶层均匀涂覆于面层的一面以及内层的一面上；
步骤四：将面层附着黏胶层的一面与内层附着黏胶层的一面用电熨斗熨烫粘合在一起，熨烫时间为4min。
实施例3
一种中草药海藻纤维保健面料，包括面层、黏胶层和内层，所述的面层是由60重量份的锦纶和40重量份的氨纶组成；所述的内层是由60重量份的海藻纤维和40重量份的苎麻纤维组成；所述的黏胶层设置于面层和内层之间，由以下重量份数的原料组成：艾叶5份、甘草5份、天然橡胶15份。
所述的天然橡胶为天然乳胶。
所述的黏胶层采用以下方法制备：将艾叶、甘草采用超细化粉体加工设备制成粒径为10-20um的粉体，再加入天然橡胶混合搅拌均匀。
所述的黏胶层厚度小于0.5mm。
一种中草药海藻纤维保健面料的制备方法，包括以下步骤：
步骤一：以锦纶为经纱，氨纶为纬纱，织造得面层；
步骤二：以海藻纤维为经纱，苎麻纤维为纬纱，织造得内层；
步骤三：将黏胶层均匀涂覆于面层的一面以及内层的一面上；
步骤四：将面层附着黏胶层的一面与内层附着黏胶层的一面用电熨斗熨烫粘合在一起，熨烫时间为5min。

Claims (9)

1.一种中草药海藻纤维保健面料，其特征在于：包括面层、黏胶层和内层，所述的面层是由50-60重量份的锦纶和30-40重量份的氨纶组成；所述的内层是由50-60重量份的海藻纤维和30-40重量份的苎麻纤维组成；所述的黏胶层设置于面层和内层之间，由以下重量份数的原料组成：艾叶3-5份、甘草3-5份、天然橡胶10-15份。
2.根据权利要求1所述的一种中草药海藻纤维保健面料，其特征在于：所述的面层是由50重量份的锦纶和30重量份的氨纶组成；所述的内层是由50重量份的海藻纤维和30重量份的苎麻纤维组成；所述的黏胶层是由以下重量份数的原料组成：艾叶3份、甘草3份、天然橡胶10份。
3.根据权利要求1所述的一种中草药海藻纤维保健面料，其特征在于：所述的面层是由55重量份的锦纶和35重量份的氨纶组成；所述的内层是由55重量份的海藻纤维和35重量份的苎麻纤维组成；所述的黏胶层是由以下重量份数的原料组成：艾叶4份、甘草4份、天然橡胶12份。
4.根据权利要求1所述的一种中草药海藻纤维保健面料，其特征在于：所述的面层是由60重量份的锦纶和40重量份的氨纶组成；所述的内层是由60重量份的海藻纤维和40重量份的苎麻纤维组成；所述的黏胶层是由以下重量份数的原料组成：艾叶5份、甘草5份、天然橡胶15份。
5.根据权利要求1-4任一项所述的一种中草药海藻纤维保健面料，其特征在于：所述的天然橡胶为天然乳胶。
6.根据权利要求1-4任一项所述的一种中草药海藻纤维保健面料，其特征在于：所述的黏胶层采用以下方法制备：将艾叶、甘草采用超细化粉体加工设备制成粒径为10-20um的粉体，再加入天然橡胶混合搅拌均匀。
7.一种权利要求6所述的中草药海藻纤维保健面料的制备方法，其特征在于，包括以下步骤：
步骤一：以锦纶为经纱，氨纶为纬纱，织造得面层；
步骤二：以海藻纤维为经纱，苎麻纤维为纬纱，织造得内层；
步骤三：将黏胶层均匀涂覆于面层的一面以及内层的一面上；
步骤四：将面层附着黏胶层的一面与内层附着黏胶层的一面用电熨斗熨烫粘合在一起。
8.根据权利要求7所述的一种中草药海藻纤维保健面料制备方法，其特征在于：步骤四中所述的电熨斗熨烫时间为3-5min。
9.根据权利要求7所述的一种中草药海藻纤维保健面料制备方法，其特征在于：所述的黏胶层厚度小于0.5mm。
CN201610821717.1A 2016-09-14 2016-09-14 一种中草药海藻纤维保健面料及其制备方法 Pending CN106476349A (zh)